CN104926300A - 温度稳定型电容器Sr4SmTiNb9O30陶瓷及其制备方法 - Google Patents

温度稳定型电容器Sr4SmTiNb9O30陶瓷及其制备方法 Download PDF

Info

Publication number
CN104926300A
CN104926300A CN201510186954.0A CN201510186954A CN104926300A CN 104926300 A CN104926300 A CN 104926300A CN 201510186954 A CN201510186954 A CN 201510186954A CN 104926300 A CN104926300 A CN 104926300A
Authority
CN
China
Prior art keywords
ceramic capacitor
temperature
capacitor material
hours
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510186954.0A
Other languages
English (en)
Inventor
胡长征
孙振
朱其华
方亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin University of Technology
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN201510186954.0A priority Critical patent/CN104926300A/zh
Publication of CN104926300A publication Critical patent/CN104926300A/zh
Pending legal-status Critical Current

Abstract

本发明公开了温度稳定型陶瓷电容器材料Sr4SmTiNb9O30及其制备方法。将SrCO3，Sm2O3，TiO2和Nb2O5预先球磨，细化原料，根据化学计量比为Sr4SmTiNb9O30进行配料，经过预烧、二次球磨等工序，利用固相反应法制备得到陶瓷电容器材料Sr4SmTiNb9O30。本发明方法可获得优良的温度稳定型陶瓷电容器材料；本发明方法简单，节能减排，成本适中，适合批量生产。

Description

温度稳定型电容器Sr4SmTiNb9O30陶瓷及其制备方法
技术领域
本发明涉及温度稳定型陶瓷电容器材料Sr4SmTiNb9O30及其制备方法，属于电子元器件的陶瓷材料技术领域。
背景技术
陶瓷电容器是电子信息技术的重要基础器件，随着电子器件的飞速发展，要求陶瓷电容器能够在更宽的温度范围内保持稳定的介电性能。在军工、航天航空以及勘探等领域里，对于能承受高温的电子元器件有很大需求。目前大多数陶瓷电容器材料容量温度特性具有一定的局限性。因此，研发具有较宽温度稳定性的介质陶瓷材料，具有重要的实际应用价值。另外，大多数陶瓷电容器基于钙钛矿结构，本发明采用钨青铜结构，有助于扩展电容器陶瓷的材料类型。
发明内容
本发明的目的是提供一种温度稳定型陶瓷电容器材料Sr4SmTiNb9O30及其制备方法。
本发明涉及的温度稳定型陶瓷电容器材料的化学组成式为：Sr4SmTiNb9O30。
上述温度稳定型陶瓷电容器材料的制备方法具体步骤为：
（1）将纯度大于99.9%的SrCO3，Sm2O3，TiO2和Nb2O5为起始原料，按照SrCO3：Sm2O3：TiO2：Nb2O5 =4: 0.5：1: 4.5的摩尔比进行配料，加入无水乙醇中，混合球磨48小时，烘干制得混合均匀的粉料；
(2）将步骤(1）制得的粉料在1000～1250℃预烧4个小时，制得预烧后的粉体；
(3）将步骤(2）预烧后的粉体，在无水乙醇中球磨48小时混合均匀，烘干；加入5~10wt%聚乙烯醇水溶液进行造粒，过60目筛后压制成型，然后置于高温炉空气气氛中，在1100～1400℃烧结4～10小时后自然冷却至室温，即得所述陶瓷电容器材料Sr4SmTiNb9O30。
所述的聚乙烯醇水溶液的优选浓度为8wt%。
4.本发明提供所述温度稳定型陶瓷电容器材料，温度稳定性好。本发明采用传统的固相法制备陶瓷材料，在中温下烧结即可获得性能优良的温度稳定型陶瓷材料，且工艺简单，成本低廉，对环境友好。在我国，介质陶瓷材料正处在不断发展之中，尤其是像很多此类温度较为稳定的特种介质陶瓷，研究尚未完善，仍未实现规模化产业化。本发明所提供的陶瓷电容器材料及其制备方法，具有良好的产业化前景。
附图说明
1.图1为本发明实施例制得的Sr4SmTiNb9O30陶瓷电容器材料的X射线图谱；
2.图2为本发明实施例制得的Sr4SmTiNb9O30陶瓷电容器材料的表面显微形貌照片；
3.图3为本发明实施例制得的Sr4SmTiNb9O30陶瓷电容器材料的介电常数随温度变化规律；
4.图4为本发明实施例制得的Sr4SmTiNb9O30陶瓷电容器材料的温度与电容变化率关系。
具体实施方式
1. 将纯度大于99.9%的SrCO3，Sm2O3，TiO2和Nb2O5原料按化学计量比为Sr4SmTiNb9O30配料放入球磨罐中, 选择氧化锆球和尼龙罐；所加粉体质量为磨球质量的8%；球磨时间为48个小时，转速为350转/分钟，球磨介质为无水乙醇；所得产物置于100℃的烘箱中烘干5小时，先以5℃/分的升温速率升至1200℃预烧4小时；取出预烧后的粉体研碎，再以无水乙醇为球磨介质球磨48小时混合均匀，烘干后研磨成粉状，用质量百分浓度为5％的聚乙醇水溶液作为有机粘结剂造粒，过60目筛后在100MPa 压强下压成直径为12mm，厚度为1mm 的圆片状生坯；将圆片状生坯以1.5℃/分的升温速率升至550℃，保温4小时排出胶体再以5℃/分的升温速率升至1300℃，保温10小时，随炉自然冷却至室温，得到陶瓷电容器材料Sr4SmTiNb9O30。
将本实施例制得的陶瓷电容器材料两侧均烧上银电极，制成圆片电容器，然后测试并计算该介质材料的相对介电常数随温度的变化。如附图3所示，Sr4SmTiNb9O30陶瓷材料的相对介电常数随温度的变化规律，附4直观地展示了Sr4SmTiNb9O30陶瓷材料在很宽的温度区间内具有平稳的温度特性，进一步证明其可作为一种温度稳定型陶瓷电容器材料。

Claims (2)

1.一种温度稳定型的陶瓷电容器材料，其特征在于所述陶瓷电容器材料的化学组成式为Sr4SmTiNb9O30；
所述陶瓷电容器材料的制备方法具体步骤为：
(1）将纯度大于99.9%的SrCO3，Sm2O3，TiO2和Nb2O5为起始原料，按照SrCO3：Sm2O3：TiO2：Nb2O5 =4: 0.5：1: 4.5的摩尔比进行配料，加入无水乙醇中，混合球磨48小时，烘干制得混合均匀的粉料；
(2）将步骤(1）制得的粉料在1000～1250℃预烧4个小时，制得预烧后的粉体；
(3）将步骤(2）预烧后的粉体，在无水乙醇中球磨48小时混合均匀，烘干；加入5~10wt%聚乙烯醇水溶液进行造粒，过60目筛后压制成型，然后置于高温炉空气气氛中，在1100～1400℃烧结4～10小时后自然冷却至室温，即得所述陶瓷电容器材料Sr4SmTiNb9O30。
2.根据权利要求1所述的陶瓷电容器材料的制备方法，其特征在于所述的聚乙烯醇水溶液的浓度为8wt%。
CN201510186954.0A 2015-04-20 2015-04-20 温度稳定型电容器Sr4SmTiNb9O30陶瓷及其制备方法 Pending CN104926300A (zh)