CN104909410B - 一种低比表面三氧化钨的制备方法 - Google Patents

一种低比表面三氧化钨的制备方法 Download PDF

Info

Publication number
CN104909410B
CN104909410B CN201510339260.6A CN201510339260A CN104909410B CN 104909410 B CN104909410 B CN 104909410B CN 201510339260 A CN201510339260 A CN 201510339260A CN 104909410 B CN104909410 B CN 104909410B
Authority
CN
China
Prior art keywords
temperature
calcining
specific surface
tungstic acid
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510339260.6A
Other languages
English (en)
Other versions
CN104909410A (zh
Inventor
廖小丽
谢金明
余春荣
朱亚模
李继红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangwu HC Starck Tungsten Products Co ltd
Jiangxi Tungsten Holding Group Co ltd
Original Assignee
Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd filed Critical Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd
Priority to CN201510339260.6A priority Critical patent/CN104909410B/zh
Publication of CN104909410A publication Critical patent/CN104909410A/zh
Application granted granted Critical
Publication of CN104909410B publication Critical patent/CN104909410B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种低比表面三氧化钨的制作方法，包括：以铵钨化合物为原料，在中进行有氧煅烧，采用梯度式控制炉膛温度，煅烧过程设有2‑6个温度控制带，进料端300℃‑400℃，出料端温度700℃‑800℃，后温度带与前温度带温差0℃‑500℃温度梯度；炉膛内真空度（0.1‑1.5）×104Pa，进行有氧煅烧；煅烧原料铵钨化合物费氏粒度Fsss：30‑60μm，原料进料速度50‑250kg/h；冷却出炉后过筛，即得得比表面积≤1m2/g的三氧化钨产品。

Description

一种低比表面三氧化钨的制备方法
技术领域
本发明涉及氧化钨的制备方法，特别是一种低比表面三氧化钨的制备方法。
本申请中术语“铵钨化合物”是钨同（杂）多酸铵盐化合物及其煅烧产物的统称。
本申请中，术语APT 为“仲钨酸铵”的简称。
背景技术
钨是一种难熔的有色金属，也是一种重要的战略资源，因其具有熔点高、硬度大、延性强、耐磨和耐腐蚀等优良性能而得到广泛应用。
钨粉末是钨的中间产品，作为钨制品及硬质合金生产的原料，对后续产品的质量产生极其重要的影响。随着科技的进步，用户对钨粉末的要求在不断地提高，钨粉、碳化钨粉技术正向着超细（纳米）化、超粗化、超纯化、集中化方向发展。三氧化钨作为生产钨粉、碳化钨粉的原料，对钨粉的粒度控制发挥着重要的作用，许多研究表明低比表面的三氧化钨有利于制取粗颗粒的钨粉。
发明内容
本发明要解决的技术问题是提供一种低比表面三氧化钨的制备方法，低比表面的三氧化钨有利于制取粗颗粒的钨粉。
为解决上述技术问题，本发明的技术方案是：一种低比表面三氧化钨的制作方法，包括下列步骤：
[1] 以铵钨化合物为原料，在负压密闭的煅烧炉中进行有氧煅烧，采用梯度式控制炉膛温度，煅烧过程设有2-6个温度控制带，进料端300℃-400℃，出料端温度700℃-800℃，后温度带与前温度带温差0℃-500℃温度梯度；
[2] 炉膛内真空度（0.1-1.5）×104Pa，进行有氧煅烧；
[3] 煅烧原料铵钨化合物费氏粒度Fsss：30-60μm，原料进料速度50-250kg/h；
[4] 煅烧时间为20-50min；
[5] 炉料通过煅烧炉设有的冷却水夹套冷却降温后出炉，随后过筛即得比表面积≤1m2/g的三氧化钨产品。
所述煅烧炉为回转炉或者无舟皿带式连续煅烧炉。所述炉料冷却降温后出炉后过筛的筛网密度根据产品粒度要求来确定筛网目数。
本发明的有益效果是：本发明生产出来的三氧化钨具有低比表面，能够有效提高后续产品钨粉、碳化钨粉的粒度。
附图说明
下面结合附图和实施例对本发明进一步说明。
图1 是低比表面三氧化钨制备工艺的示意图。
具体实施方式
实施例1如图1所示：将费氏为30μm的铵钨化合物置入进料仓中，通过螺旋给料机以125kg/h为速度送入真空度（0.5-0.8）×104Pa的回转炉中，进行有氧煅烧，温度控制为：一带300℃、二带300℃、三带650℃、四带650℃、五带700℃、六带750℃。经过回转炉煅烧后，冷却过筛，可得比表面积为0.8m2/g的三氧化钨。
实施例2如图1所示：将费氏为50μm的铵钨化合物置入进料仓中，通过螺旋给料机以200kg/h为速度送入真空度（1.0-1.3）×104Pa的回转炉中，进行有氧煅烧，温度控制为：一带400℃、二带400℃、三带700℃、四带800℃、五带800℃、六带800℃。经过回转炉煅烧后，冷却过筛，可得比表面积为0.4m2/g的三氧化钨。
实施例3如图1所示：将费氏为45μm的铵钨化合物置入进料仓中，通过螺旋给料机以160kg/h为速度送入真空度（0.8-1.2）×104Pa的回转炉中，进行有氧煅烧，温度控制为：一带350℃、二带350℃、三带700℃、四带750℃、五带800℃、六带800℃。经过回转炉煅烧后，冷却过筛，可得比表面积为0.5m2/g的三氧化钨。

Claims (3)

1.一种低比表面三氧化钨的制备方法，包括：
［1］以铵钨化合物为原料，在负压密闭的煅烧炉中进行有氧煅烧，采用梯度式控制炉膛温度，煅烧过程中设置6 个温度控制带，进料端温度300℃ -400℃，出料端温度700℃ -800℃，后温度带与前温度带温差0℃ -500℃温度梯度；
［2］炉膛内真空度（0.1-1.5）×104Pa，进行有氧煅烧；
［3］煅烧原料铵钨化合物费氏粒度Fsss：30-60μm 原料进料速度50-250kg/h；
［4］煅烧时间为20-50min；
［5］炉料通过煅烧炉设有的冷却水夹套冷却降温后出炉，随后过筛即得比表面积≤1m2/g 的三氧化钨产品。
2.根据权利要求1所述的一种低比表面三氧化钨的制备方法，其特征在于：所述煅烧炉为回转炉或者无舟皿带式连续煅烧炉。
3.根据权利要求1所述的一种低比表面三氧化钨的制备方法，其特征在于：所述炉料冷却降温后出炉后过筛的筛网密度根据产品粒度要求来确定筛网目数。
CN201510339260.6A 2015-06-18 2015-06-18 一种低比表面三氧化钨的制备方法 Expired - Fee Related CN104909410B (zh)