CN104877510A - 一种防腐抗菌油漆及其制备方法 - Google Patents
一种防腐抗菌油漆及其制备方法 Download PDFInfo
- Publication number
- CN104877510A CN104877510A CN201510259149.6A CN201510259149A CN104877510A CN 104877510 A CN104877510 A CN 104877510A CN 201510259149 A CN201510259149 A CN 201510259149A CN 104877510 A CN104877510 A CN 104877510A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- mixed solution
- nitro
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防腐抗菌油漆及其制备方法，该防腐抗菌油漆包括以下原料：香茅草提取液，丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉。制备方法：按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，搅拌,以10℃/min匀速加热至80-100℃并保温，继续升温至120-150℃，保温得第一混合液；第一混合液自然冷却后，加入香茅草提取液，在60-80℃下搅拌后，得第二混合液；将第二混合液投入研磨机中研磨，过筛得防腐抗菌油漆。本发明油漆防腐抗菌效果好，制备方法简单，适合产业化。
Description
技术领域
本发明涉及化工技术领域，具体涉及一种防腐抗菌油漆及其制备方法。
背景技术
油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。现实生活中，很多物品的表面需要用油漆来处理，不仅提高了物品的美感，还有效地延长了物品的寿命。
但随着生活水平的提高，人们对健康状况更加在意，在选取物品的时候，通常选择环保材料，同时，需求材料本身的抑菌能力有着较高的要求。现有的防腐抗菌油漆虽然防腐能力好，但是抗菌上多采用抗菌剂，对人体仍有一定的伤害。所以需要研发一种防腐效果好，抗菌环保的油漆。
发明内容
针对现有技术的不足，本发明目的在于提供一种防腐抗菌油漆及其制备方法，该油漆成本低廉，防腐抗菌效果好，并且制备过程简单，易于产业化。
为解决现有问题，本发明采取的技术方案为：
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液2-6份，丙烯腈12-20份，沸石粉12-16份，乙酸乙酯8-10份，硝化棉1-5份，甘油4-8份，甲基丙烯酸甲酯6-12份，冰醋酸6-8份，双乙酰苯胺2-6份，磺化油5-9份，铁粉1-5份。
作为优选的是，包括以下按重量份数计的原料：香茅草提取液4份，丙烯腈18份，沸石粉15份，乙酸乙酯9份，硝化棉3份，甘油6份，甲基丙烯酸甲酯10份，冰醋酸7份，双乙酰苯胺4份，磺化油7份，铁粉3份。
作为改进的是，还包括柏油0.2-0.8份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，搅拌10-20min,以10℃/min匀速加热至80-100℃并保温10-20min，继续升温至120-150℃，保温5-10min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在60-80℃下搅拌5-10min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨10-15min，过筛得防腐抗菌油漆。
作为制备方法优选的是，步骤1，搅拌转速为2000-2500rpm。
作为制备方法优选的是，步骤2，搅拌转速为5000-8000rpm。
有益效果
本发明防腐抗菌油漆采用香茅草提取液作为主要的抗菌成分，成本低廉，所得油漆抗菌效果好，柏油的添加，提高了油漆的防腐能力，另外，本发明制备方法简单，采用分段加热提高了原料的利用率和油漆的质地。
具体实施方式
下面结合实施例对本发明作进一步描述。以下实施例只是用于更加清楚地说明本发明的性能，而不能仅局限于下面的实施例。
实施例1
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液2份，丙烯腈12份，沸石粉12份，乙酸乙酯8份，硝化棉1份，甘油4份，甲基丙烯酸甲酯6份，冰醋酸6份，双乙酰苯胺2份，磺化油5份，铁粉1份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，以2000rpm的转速搅拌10min,以10℃/min匀速加热至80℃并保温10min，继续升温至120℃，保温5min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在60℃下以5000rpm的转速搅拌5min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨10min，过筛得防腐抗菌油漆。
实施例2
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液4份，丙烯腈18份，沸石粉15份，乙酸乙酯9份，硝化棉3份，甘油6份，甲基丙烯酸甲酯10份，冰醋酸7份，双乙酰苯胺4份，磺化油7份，铁粉3份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，以2200rpm的转速搅拌15min,以10℃/min匀速加热至90℃并保温15min，继续升温至140℃，保温8min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在75℃下以7000rpm搅拌8min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨13min，过筛得防腐抗菌油漆。
实施例3
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液6份，丙烯腈20份，沸石粉16份，乙酸乙酯10份，硝化棉5份，甘油8份，甲基丙烯酸甲酯12份，冰醋酸8份，双乙酰苯胺6份，磺化油9份，铁粉5份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，以2500rpm的转速搅拌20min,以10℃/min匀速加热至100℃并保温20min，继续升温至150℃，保温10min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在80℃下以8000rpm的转速搅拌10min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨15min，过筛得防腐抗菌油漆。
实施例4
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液4份，丙烯腈18份，沸石粉15份，乙酸乙酯9份，硝化棉3份，甘油6份，甲基丙烯酸甲酯10份，冰醋酸7份，双乙酰苯胺4份，磺化油7份，铁粉3份，柏油0.2份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，以2200rpm的转速搅拌15min,以10℃/min匀速加热至90℃并保温15min，继续升温至140℃，保温8min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在75℃下以7000rpm搅拌8min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨13min，过筛得防腐抗菌油漆。
对比例1
一种防腐抗菌油漆，包括以下按重量份数计的原料：香茅草提取液4份，丙烯腈18份，沸石粉15份，乙酸乙酯9份，硝化棉3份，甘油6份，甲基丙烯酸甲酯10份，冰醋酸7份，双乙酰苯胺4份，磺化油7份，铁粉3份。
上述防腐抗菌油漆的制备方法，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，以2200rpm的转速搅拌15min,加热至140℃，保温8min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在75℃下以7000rpm搅拌8min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨13min，过筛得防腐抗菌油漆。
性能测试
按照国标对本发明实施例1-4和对比例1所得油漆进行测试，所得数据如下表所示：
从上述表格可以看出，本发明防腐抗菌油漆的抑菌效果好，制备过程中采用分段加热提高了原料的利用率，所得油漆质地均匀，表干时间短，另外，柏油的添加提高了油漆的防腐能力，非常实用。
Claims (5)
1.一种防腐抗菌油漆，其特征在于，包括以下按重量份数计的原料：香茅草提取液2-6份，丙烯腈12-20份，沸石粉12-16份，乙酸乙酯8-10份，硝化棉1-5份，甘油4-8份，甲基丙烯酸甲酯6-12份，冰醋酸6-8份，双乙酰苯胺2-6份，磺化油5-9份，铁粉1-5份。
2.根据权利要求1所述的防腐抗菌油漆，其特征在于，包括以下按重量份数计的原料：香茅草提取液4份，丙烯腈18份，沸石粉15份，乙酸乙酯9份，硝化棉3份，甘油6份，甲基丙烯酸甲酯10份，冰醋酸7份，双乙酰苯胺4份，磺化油7份，铁粉3份。
3.权利要求1所述的防腐抗菌油漆的制备方法，其特征在于，包括以下步骤：
步骤1，按照重量份数称取原料，并将丙烯腈，沸石粉，乙酸乙酯，硝化棉，甘油，甲基丙烯酸甲酯，冰醋酸，双乙酰苯胺，磺化油，铁粉投入到反应釜中，搅拌10-20min,以10℃/min匀速加热至80-100℃并保温10-20min，继续升温至120-150℃，保温5-10min，得第一混合液；
步骤2，第一混合液自然冷却后，加入香茅草提取液，在60-80℃下搅拌5-10min后，得第二混合液；
步骤3，将第二混合液投入研磨机中研磨10-15min，过筛得防腐抗菌油漆。
4.根据权利要求3所述的防腐抗菌油漆的制备方法，其特征在于：步骤1，搅拌转速为2000-2500rpm。
5.根据权利要求3所述的防腐抗菌油漆的制备方法，其特征在于：步骤2，搅拌转速为5000-8000rpm。