CN104862991A - Embossing pigment and production process - Google Patents
Embossing pigment and production process Download PDFInfo
- Publication number
- CN104862991A CN104862991A CN201510292011.6A CN201510292011A CN104862991A CN 104862991 A CN104862991 A CN 104862991A CN 201510292011 A CN201510292011 A CN 201510292011A CN 104862991 A CN104862991 A CN 104862991A
- Authority
- CN
- China
- Prior art keywords
- pigment
- pattern
- foaming
- aqueous foaming
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of textile coating and foaming printing, in particular to an embossing pigment and a production process. The pigment is prepared from aqueous foaming paste and white glue, wherein the aqueous foaming paste is prepared by milling 80 percent of transparent paste and 20 percent of aqueous foaming powder for many times through a three-roller machine; the white glue is prepared by mixing 35 percent of an acrylate polymer, 30 percent of titanium dioxide as a filler and 35 percent of water; the weight ratio of the aqueous foaming paste to the white glue is 4.5 to 5.5. According to the production process, the current foaming production process is adjusted; after foaming, the height is improved, the patterns and the texture are full and the stereoscopic impression is strong on vision, and the elasticity and the soft hand feeling of foaming printing of the traditional fabric are kept; the decorative effect is good, the adhesion is good, and the pigment is washable and is not easy to fade; the pigment is painted on the obtained embossed fabric pattern in different thicknesses in the form of block surfaces or lines according to different fabrics and each local requirement, so that the pattern has the stereoscopic impression, and the pigment can be manually painted and customized into all kinds of lines as required.
Description
[technical field]
The present invention relates to textile coating and textiles foamed printing technical field, specifically a kind of pigment for embossing technology and production technology.
[background technology]
Clothes, sheet, curtain that conventional fabrics Printing is made, towel, handkerchief etc. both can meet the daily demand of people, can give artistic treat again.Along with the continuous progress of science and technology and improving constantly of people's living standard, have textile printing product and upgraded higher requirement, particularly traditional plane PRINTED FABRIC is developed to and there is relief obvious PRINTED FABRIC, on fabric, namely form the foamed printing of three heap space space patterns or on suede heavy weave, form stamp that is transparent, that be rich in concave-convex sense flower pattern.
Foamed printing is also known as foaming stereo stamp, and Italy claims relief printing, and the decorative pattern printed on the textile has as applique, the three-dimensional style of flocking or the uniqueness as embroidery.China can produce foamed printing fabric the seventies in last century, but because of foaming printing paste manufacture craft require high, only have Germany and Japan to produce so far.At present, it is main that fabric foam process is applied to serigraphy, and due to the limitation of meshcount, the dilution factor of slurry is limited, so that affect the stability in the height and foaming process foamed; In addition, on the make need slurry to strike off, so effect flower pattern surfacing after print, the artistic effect of fluctuations cannot be reached.
Number of patent application be 201010265164.9 Chinese patent disclose a kind of foamed printing technique and formula thereof, described formula comprises following component and mass fraction: foaming printing paste 30-40%, adhesive 1-2%, mill base 2-10%, stamp brightener 40-50%; Its technique is first throwing forme, readjust the distribution bubble ink again, then stamp and drying, last hot pressing are scalded shaping.But formula rate stamp in actual mechanical process used in this foamed printing technique easily comes off, and tack is poor, foaming height is inadequate, and stereoeffect is poor, has certain limitation, can only be used for throwing forme, can not be used for manual drawing.
[summary of the invention]
The object of the invention is the defect in order to solve printing effect in existing fabric foam process, have adjusted existing foaming slurry and the ratio of PVA glue and manufacture craft, provide a kind of printing quality quality full, for the pigment of embossing technology and production technology.
To achieve these goals, design a kind of pigment for embossing technology, described pigment adopts aqueous foaming slurry and PVA glue composition, and aqueous foaming is starched and added 20% aqueous foaming powder by 80% interspongioplastic substance and repeatedly to mill through three rod machines and formed; PVA glue is mixed by 35% acrylic polymer, 30% filler titanium dioxide, 35% water, and the weight proportion of aqueous foaming slurry and PVA glue is 4.5:5.5.
The concrete production craft step of pigment is as follows:
A. aqueous foaming is starched with PVA glue with the proportioning of 4.5:5.5, first aqueous foaming slurry is put into, then put into PVA glue in same container;
B. use reinforcement electric mixer with the speed-adjustable stir of 1300 revs/min, until it mixes completely;
C. color paste toning is added;
D. use reinforcement electric mixer with the speed-adjustable stir of 2000 revs/min;
E. in 25 degree of room temperatures, dry indoor, opening shelves 2 hours;
F. the color material tanks modulated is entered paint bottle, seal stand-by.
Embossing technology concrete steps are as follows:
A. first pattern is replicated on fabric;
B. flat painting, is plotted in fabric on according to pattern by the mode that pigment is coated with marlinspike;
C. plastotype, according to each local requirement of pattern, with block face, or the form of lines, pigment is plotted on pattern with different thickness, makes pattern have third dimension;
D. dizzy dye, according to the requirement of pattern, does various different textural effect with paintbrush on the surface of layer, comprises smooth, coarse, sandstone, wood grain;
E. 3 hours are kept flat, until pigment parches;
F. the temperature of pressing machine is set to 160 degree;
G. the fabric after bone dry is placed pressing machine pressing 40 seconds.
The present invention has done a little adjustment to the ratio of existing foam slurry and PVA glue and manufacture craft, so that not only highly improve after foaming, visually pattern quality is plentiful, third dimension is strong, and, maintain the elasticity of conventional fabrics foamed printing and the feel of softness, good decorating effect, tack is good, can wash, difficult drop-off, the embossment woven design pattern obtained can according to different fabrics and each local requirement, with the form of block face or lines, pigment is plotted on pattern with different thickness, pattern is made to have third dimension, also can manual drawing as required, customize various lines.
[accompanying drawing explanation]
Fig. 1 is that process flow schematic diagram is made in the preparation of embossing technology pigment;
Fig. 2 is embossing technology Making programme figure;
Fig. 3 is the stamp adopting existing foaming technique to make;
Fig. 4 is the stamp adopting foaming technique of the present invention to make;
Specify Fig. 1 as Figure of abstract of the present invention.
[detailed description of the invention]
Below in conjunction with accompanying drawing, the invention will be further described, and the structure of this device and principle are very clearly concerning the people of this specialty.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
Embossing technology just a kind of paint, due to light, soft, difficult drop-off and her washability, she has more practicality.She can be used to the fields such as clothes, accessories, packaging, furniture and interior decoration.Compared with embroidering with tradition, she not only has perfect third dimension, richer card-cut charm, and she not only gives U.S. of a kind of mystery of traditional Chinese pattern, also with the Gothic solemnity in a kind of west.It will be further appreciated that, in the near future, the ink and wash of Chinese tradition probably shows with the form of embossment by she.
Embossing technology pigment formula in the present invention: material prescription is starched by TL700J aqueous foaming and PVA glue forms, the aqueous foaming slurry of its raw material TJ700J itself is add 20% aqueous foaming powder by 80% interspongioplastic substance repeatedly to mill through three rod machines and formed; PVA glue is Japanese Xin Zhong village rubber cement, and it has 35% acrylic polymer, 30% filler titanium dioxide, 35% water to mix.
Manufacturing process joined by embossing technology pigment:
1) aqueous foaming is starched with PVA glue with the proportioning of 4.5:5.5, first aqueous foaming slurry is put into, then put into PVA glue in same container;
2) with reinforcement electric mixer with 1300 turns the speed-adjustable stir that divides, until it mixes completely;
3) according to required color, suitable color paste toning is added;
4) with reinforcement electric mixer with 2000 turns the speed-adjustable stir that divides;
5) in 25 degree of room temperatures, dry indoor, opening shelves 2 hours;
6) color material tanks modulated is entered paint bottle, seal stand-by;
Embossing technology is the characteristic according to the different conditions of pigment after Overheating Treatment, is undertaken being coated with, moulding and the dizzy gimmick making contaminated by hand, special marlinspike, paintbrush.
The first step: first pattern is replicated on fabric;
Second step: flat painting, is plotted in fabric on according to pattern by the mode that pigment is coated with special marlinspike;
3rd step: plastotype, according to each local requirement of pattern, with block face, or the form of lines, pigment is plotted on pattern with different thickness, makes pattern have third dimension;
4th step: dizzy dye, according to the requirement of pattern, does various different textural effect on the surface of layer, as smooth, coarse, sandstone, wood grain etc. with paintbrush;
5th step: keep flat 3 hours, until pigment parches;
6th step: the temperature of pressing machine is set to 160 degree;
7th step: the fabric after bone dry is placed pressing machine pressing 40 seconds;
8th step: according to the needs of foaming, can previous step be repeated.
Claims (3)
1. for a pigment for embossing technology, it is characterized in that described pigment adopts aqueous foaming slurry and PVA glue composition, aqueous foaming is starched and is added 20% aqueous foaming powder by 80% interspongioplastic substance and repeatedly to mill through three rod machines and formed; PVA glue is mixed by 35% acrylic polymer, 30% filler titanium dioxide, 35% water, and the weight proportion of aqueous foaming slurry and PVA glue is 4.5:5.5.
2. a production technology for embossing technology pigment as claimed in claim 1, is characterized in that production craft step is as follows:
A. aqueous foaming is starched with PVA glue with the proportioning of 4.5:5.5, first aqueous foaming slurry is put into, then put into PVA glue in same container;
B. use reinforcement electric mixer with the speed-adjustable stir of 1300 revs/min, until it mixes completely;
C. color paste toning is added;
D. use reinforcement electric mixer with the speed-adjustable stir of 2000 revs/min;
E. in 25 degree of room temperatures, dry indoor, opening shelves 2 hours;
F. the color material tanks modulated is entered paint bottle, seal stand-by.
3. adopt an embossing technology for pigment as claimed in claim 1 or 2, it is characterized in that technique concrete steps are as follows:
A. first pattern is replicated on fabric;
B. flat painting, is plotted in fabric on according to pattern by the mode that pigment is coated with marlinspike;
C. plastotype, according to each local requirement of pattern, with block face, or the form of lines, pigment is plotted on pattern with different thickness, makes pattern have third dimension;
D. dizzy dye, according to the requirement of pattern, does various different textural effect with paintbrush on the surface of layer, comprises smooth, coarse, sandstone, wood grain;
E. 3 hours are kept flat, until pigment parches;
F. the temperature of pressing machine is set to 160 degree;
G. the fabric after bone dry is placed pressing machine pressing 40 seconds.