CN104862679A - 一种锂基抑菌金属表面处理剂 - Google Patents
一种锂基抑菌金属表面处理剂 Download PDFInfo
- Publication number
- CN104862679A CN104862679A CN201510162923.1A CN201510162923A CN104862679A CN 104862679 A CN104862679 A CN 104862679A CN 201510162923 A CN201510162923 A CN 201510162923A CN 104862679 A CN104862679 A CN 104862679A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- lithium
- minute
- silk gum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种锂基抑菌金属表面处理剂，它是由下述重量份的原料组成的：聚乙烯醇15-20、茶皂素0.4-0.5、锂基润滑脂3-4、二茂铁甲酸0.4-1、六氢化邻苯二甲酸酐0.1-0.2、DBNPA0.1-0.12、山梨酸钾0.5-1、六甲基磷酰胺0.1-0.2、亚硫酸氢钠1-2、丝胶6-8、硼酸0.08-0.1、甲基苯并三氮唑10-20、去离子水180-200。本发明将水溶性高分子聚乙烯醇与丝胶混合，通过硼酸改性可以提高共混膜的抗张强度和热稳定性，加入以甲基苯并三氮唑为主料的缓蚀碱液，可以使得吸附在金属表面的膜更加均匀稳定，保护金属材料免受大气及水中有害介质的腐蚀，起到更好的缓蚀效果，加入的DBNPA、山梨酸钾与其他多种金属表面处理剂添加剂具有兼容性，可以有效的抵御细菌和真菌污染。
Description
技术领域
本发明主要涉及金属表面处理剂领域，尤其涉及一种锂基抑菌金属表面处理剂。
背景技术
金属表面处理剂指对金属表面进行各种处理的化学药剂的总称。 金属表面处理包括了除油、除锈、磷化、防锈等基体前处理，是为金属涂层技术、金属防护技术做准备的，基体前处理质量对此后涂层制备和金属的使用有很大的影响，其中的水溶性防锈剂则可溶解在水中形成水溶液，金属经这种水溶液处理后能防止腐蚀生锈。它们的防锈作用可分为三类。
①金属与防锈剂生成不溶而致密的氧化物薄膜，因而阻止了金属的阳极溶解或促进金属的钝化，从而抑制金属的腐蚀。这类防锈剂又称为钝化剂，如亚硝酸钠、重铬酸钾等。在使用时，应保证足够的用量。用量不足时，不能形成完整的氧化物薄膜，在未被遮盖的很小的金属表面上，腐蚀电流密度增大，易造成局部腐蚀严重。②金属与防锈剂生成难溶的盐类，从而使金属与腐蚀介质隔离，免于锈蚀。例如：有的磷酸盐能与铁作用生成不溶性的磷酸铁盐；有的硅酸盐能和铁、铝作用生成不溶性的硅酸盐等。③金属与防锈剂生成难溶性的络合物，覆盖在金属表面而保护金属免于腐蚀。例如：苯并三氮唑与铜能生成螯合物Cu(C6H4N3)2,既不溶于水也不溶于油，因而能保护铜的表面。
发明内容
本发明目的就是提供一种锂基抑菌金属表面处理剂。
本发明是通过以下技术方案实现的：
一种锂基抑菌金属表面处理剂，它是由下述重量份的原料组成的：
聚乙烯醇15-20、茶皂素0.4-0.5、锂基润滑脂3-4、二茂铁甲酸0.4-1、六氢化邻苯二甲酸酐0.1-0.2、DBNPA0.1-0.12、山梨酸钾0.5-1、六甲基磷酰胺0.1-0.2、亚硫酸氢钠1-2、丝胶6-8、硼酸0.08-0.1、甲基苯并三氮唑10-20、去离子水180-200。
一种锂基抑菌金属表面处理剂的制备方法，包括以下步骤：
（1）取山梨酸钾、DBNPA，加入上述去离子水重量的60-70%，搅拌均匀，加入丝胶，50-60℃下保温搅拌10-20分钟，加入聚乙烯醇、硼酸，65-70℃下保温搅拌50-60分钟，得丝胶乳液；
（2）将甲基苯并三氮唑加入到其重量3-5倍的稀碱液中，加热到60-70℃，加入六甲基磷酰胺，搅拌至常温，得缓蚀碱液；
（3）将茶皂素加入到剩余的去离子水中，搅拌均匀后加入锂基润滑脂、亚硫酸氢钠，55-60℃下搅拌混合10-20分钟，得锂基乳液；
（4）将上述缓蚀碱液、丝胶乳液混合，搅拌均匀后加入锂基乳液、二茂铁甲酸，300-400转/分搅拌分散10-16分钟，得锂基缓蚀液；
（5）将上述缓蚀抗磨液与剩余各原料混合，700-800转/分搅拌分散20-30分钟，即得所述金属表面处理剂。
一种丝胶增稠金属表面处理剂，所述的稀碱液为0.1mol/l的氢氧化钠或0.1mol/l的碳酸钠水溶液。
本发明的优点是：
本发明将水溶性高分子聚乙烯醇与丝胶混合，通过硼酸改性可以提高共混膜的抗张强度和热稳定性，加入以甲基苯并三氮唑为主料的缓蚀碱液，可以使得吸附在金属表面的膜更加均匀稳定，保护金属材料免受大气及水中有害介质的腐蚀，起到更好的缓蚀效果，加入的DBNPA、山梨酸钾与其他多种金属表面处理剂添加剂具有兼容性，可以有效的抵御细菌和真菌污染。
具体实施方式
实施例1：
一种锂基抑菌金属表面处理剂，它是由下述重量份的原料组成的：
聚乙烯醇20、茶皂素0.5、锂基润滑脂4、二茂铁甲酸0.4、六氢化邻苯二甲酸酐0.2、山梨酸钾0.5、DBNPA0.12、六甲基磷酰胺0.2、亚硫酸氢钠2、丝胶6-8、硼酸0.08、甲基苯并三氮唑20、去离子水200。
一种锂基抑菌金属表面处理剂的制备方法，包括以下步骤：
（1）取山梨酸钾、DBNPA，加入上述去离子水重量的70%，搅拌均匀，加入丝胶，60℃下保温搅拌20分钟，加入聚乙烯醇、硼酸，70℃下保温搅拌50分钟，得丝胶乳液；
（2）将甲基苯并三氮唑加入到其重量3倍的稀碱液中，加热到70℃，加入六甲基磷酰胺，搅拌至常温，得缓蚀碱液；
（3）将茶皂素加入到剩余的去离子水中，搅拌均匀后加入锂基润滑脂、亚硫酸氢钠，60℃下搅拌混合20分钟，得锂基乳液；
（4）将上述缓蚀碱液、丝胶乳液混合，搅拌均匀后加入锂基乳液、二茂铁甲酸，400转/分搅拌分散16分钟，得锂基缓蚀液；
（5）将上述缓蚀抗磨液与剩余各原料混合，800转/分搅拌分散30分钟，即得所述金属表面处理剂。
一种丝胶增稠金属表面处理剂，所述的稀碱液为0.1mol/l的碳酸钠水溶液。
性能测试：
性能测试：
取本发明的表面处理剂分别处理铝合金、铜铁合金板材做实验，两种板材的规格均为80mm×100mm×4mm，将该板材横向切开，进行喷洒试验，所用试剂为浓度为5% 的氯化钠溶液，试验时间300 小时，测量在切割线一侧形成的鼓泡宽度，结果鼓泡宽度为0 ；
耐盐性：
将上述分别处理的两种板材浸泡在浓度为5% 的氯化钠溶液中，浸泡300 小时，材料表面基本无变化，浸泡300 小时，无锈斑出现。
Claims (3)
1.一种锂基抑菌金属表面处理剂，其特征在于它是由下述重量份的原料组成的：
聚乙烯醇15-20、茶皂素0.4-0.5、锂基润滑脂3-4、二茂铁甲酸0.4-1、六氢化邻苯二甲酸酐0.1-0.2、DBNPA0.1-0.12、山梨酸钾0.5-1、六甲基磷酰胺0.1-0.2、亚硫酸氢钠1-2、丝胶6-8、硼酸0.08-0.1、甲基苯并三氮唑10-20、去离子水180-200。
2.一种如权利要求1所述的锂基抑菌金属表面处理剂的制备方法，其特征在于包括以下步骤：
（1）取山梨酸钾、DBNPA，加入上述去离子水重量的60-70%，搅拌均匀，加入丝胶，50-60℃下保温搅拌10-20分钟，加入聚乙烯醇、硼酸，65-70℃下保温搅拌50-60分钟，得丝胶乳液；
（2）将甲基苯并三氮唑加入到其重量3-5倍的稀碱液中，加热到60-70℃，加入六甲基磷酰胺，搅拌至常温，得缓蚀碱液；
（3）将茶皂素加入到剩余的去离子水中，搅拌均匀后加入锂基润滑脂、亚硫酸氢钠，55-60℃下搅拌混合10-20分钟，得锂基乳液；
（4）将上述缓蚀碱液、丝胶乳液混合，搅拌均匀后加入锂基乳液、二茂铁甲酸，300-400转/分搅拌分散10-16分钟，得锂基缓蚀液；
（5）将上述缓蚀抗磨液与剩余各原料混合，700-800转/分搅拌分散20-30分钟，即得所述金属表面处理剂。
3.根据权利要求1所述的一种丝胶增稠金属表面处理剂，其特征在于所述的稀碱液为0.1mol/l的氢氧化钠或0.1mol/l的碳酸钠水溶液。