CN104818477A - 一种抑菌防腐金属表面处理剂 - Google Patents

一种抑菌防腐金属表面处理剂 Download PDF

Info

Publication number
CN104818477A
CN104818477A CN201510168692.5A CN201510168692A CN104818477A CN 104818477 A CN104818477 A CN 104818477A CN 201510168692 A CN201510168692 A CN 201510168692A CN 104818477 A CN104818477 A CN 104818477A
Authority
CN
China
Prior art keywords
add
water
minute
stirring
stirred
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510168692.5A
Other languages
English (en)
Inventor
朱兴堂
朱亮亮
陈军彦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU TIMES ELECTRONICS Co Ltd
Original Assignee
BENGBU TIMES ELECTRONICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU TIMES ELECTRONICS Co Ltd filed Critical BENGBU TIMES ELECTRONICS Co Ltd
Priority to CN201510168692.5A priority Critical patent/CN104818477A/zh
Publication of CN104818477A publication Critical patent/CN104818477A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抑菌防腐金属表面处理剂，它是由下述重量份的原料组成的：水解聚马来酸酐0.4-0.6、甘油三酯0.02-0.04、聚乙烯醇10-15、丝胶4-6、硼酸0.07-0.1、六水硝酸钇0.05-0.1、硅烷偶联剂KH-550 0.4-1、水160-200、抗坏血酸钙0.1-0.2、椰油酸二乙醇酰胺1-2、吡啶硫酮锌0.2-1、卡松0.1-0.3、二甲基硅油0.08-0.1。本发明将水溶性高分子聚乙烯醇、丝胶混合，再通过硅烷化处理，硅烷在水解后可以在金属表面形成吸附型膜层从而隔绝环境中的水分子和氧分子起到防护作用，通过硼酸改性可以提高共混膜的抗张强度和热稳定性。

Description

一种抑菌防腐金属表面处理剂
技术领域
    本发明主要涉及金属表面处理剂领域，尤其涉及一种抑菌防腐金属表面处理剂。
背景技术
金属表面处理剂指对金属表面进行各种处理的化学药剂的总称。 金属表面处理包括了除油、除锈、磷化、防锈等基体前处理，是为金属涂层技术、金属防护技术做准备的，基体前处理质量对此后涂层制备和金属的使用有很大的影响，其中的水溶性防锈剂则可溶解在水中形成水溶液，金属经这种水溶液处理后能防止腐蚀生锈。它们的防锈作用可分为三类。
①金属与防锈剂生成不溶而致密的氧化物薄膜，因而阻止了金属的阳极溶解或促进金属的钝化，从而抑制金属的腐蚀。这类防锈剂又称为钝化剂，如亚硝酸钠、重铬酸钾等。在使用时，应保证足够的用量。用量不足时，不能形成完整的氧化物薄膜，在未被遮盖的很小的金属表面上，腐蚀电流密度增大，易造成局部腐蚀严重。②金属与防锈剂生成难溶的盐类，从而使金属与腐蚀介质隔离，免于锈蚀。例如：有的磷酸盐能与铁作用生成不溶性的磷酸铁盐；有的硅酸盐能和铁、铝作用生成不溶性的硅酸盐等。③金属与防锈剂生成难溶性的络合物，覆盖在金属表面而保护金属免于腐蚀。例如：苯并三氮唑与铜能生成螯合物Cu(C6H4N3)2,既不溶于水也不溶于油，因而能保护铜的表面。
发明内容
本发明目的就是提供一种抑菌防腐金属表面处理剂。
本发明是通过以下技术方案实现的：
一种抑菌防腐金属表面处理剂，它是由下述重量份的原料组成的：
水解聚马来酸酐0.4-0.6、甘油三酯0.02-0.04、聚乙烯醇10-15、丝胶4-6、硼酸0.07-0.1、六水硝酸钇0.05-0.1、硅烷偶联剂KH-550 0.4-1、水160-200、抗坏血酸钙0.1-0.2、椰油酸二乙醇酰胺1-2、吡啶硫酮锌0.2-1、卡松0.1-0.3、二甲基硅油0.08-0.1。
一种抑菌防腐金属表面处理剂的制备方法，包括以下步骤：
（1）取丝胶，加入上述水重量的30-40%，搅拌均匀后加入硅烷偶联剂KH-550、六水硝酸钇，600-1000转/分搅拌分散10-20分钟，得硅烷液；
（2）将吡啶硫酮锌、卡松混合，搅拌均匀后加入甘油三酯，加热到40-50℃，加入剩余水重量的40-50%，保温搅拌10-20分钟，得抑菌液；
（3）将上述抑菌液与硅烷液混合，搅拌均匀后加入上述聚乙烯醇、硼酸，65-70℃下保温搅拌60-70分钟，得丝胶乳液；
（4）将椰油酸二乙醇酰胺、抗坏血酸钙混合，60-70℃下保温搅拌2-3分钟；
（5）将上述处理后的各原料混合，400-500转/分搅拌3-6分钟，加入剩余各原料，800-1000转/分搅拌分散30-40分钟，即得所述金属表面处理剂。
本发明的优点是：
本发明将水溶性高分子聚乙烯醇、丝胶混合，再通过硅烷化处理，硅烷在水解后可以在金属表面形成吸附型膜层，从而隔绝环境中的水分子和氧分子起到防护作用，然后通过硼酸改性可以提高共混膜的抗张强度和热稳定性，而加入的稀土金属离子会与金属基材表面发生吸氧腐蚀产生的OH-络合产生不溶性络合物，该络合物会进一步脱水形成氧化物沉淀到基材表面，减缓腐蚀的电极反应；
本发明加入的抑菌液对于厌氧菌，硫酸盐还原菌等的滋生、繁殖有很好的抑制和杀灭的作用，可以有效的提高产品的贮存稳定性以及使用中的稳定性。
具体实施方式
实施例1：
一种抑菌防腐金属表面处理剂，它是由下述重量份的原料组成的：
水解聚马来酸酐0.6、甘油三酯0.04、聚乙烯醇10-15、丝胶6、硼酸0.07、六水硝酸钇0.05、硅烷偶联剂KH-550 0.4、水200、抗坏血酸钙0.2、椰油酸二乙醇酰胺1、吡啶硫酮锌0.2、卡松0.3、二甲基硅油0.08。
一种抑菌防腐金属表面处理剂的制备方法，其特征在于包括以下步骤：
（1）取丝胶，加入上述水重量的40%，搅拌均匀后加入硅烷偶联剂KH-550、六水硝酸钇，1000转/分搅拌分散20分钟，得硅烷液；
（2）将吡啶硫酮锌、卡松混合，搅拌均匀后加入甘油三酯，加热到50℃，加入剩余水重量的50%，保温搅拌20分钟，得抑菌液；
（3）将上述抑菌液与硅烷液混合，搅拌均匀后加入上述聚乙烯醇、硼酸，70℃下保温搅拌70分钟，得丝胶乳液；
（4）将椰油酸二乙醇酰胺、抗坏血酸钙混合，70℃下保温搅拌2分钟；
（5）将上述处理后的各原料混合，500转/分搅拌6分钟，加入剩余各原料，800-1000转/分搅拌分散30分钟，即得所述金属表面处理剂。
性能测试：
取本发明的表面处理剂分别处理铝合金、铜铁合金板材做实验，两种板材的规格均为80mm×100mm×4mm，将该板材横向切开，进行喷洒试验，所用试剂为浓度为5% 的氯化钠溶液，试验时间300 小时，测量在切割线一侧形成的鼓泡宽度，结果鼓泡宽度为0 ；
耐盐性：
将上述分别处理的两种板材浸泡在浓度为5% 的氯化钠溶液中，浸泡300 小时，材料表面基本无变化，浸泡300 小时，无锈斑出现。

Claims (2)

1.一种抑菌防腐金属表面处理剂，其特征在于它是由下述重量份的原料组成的：
水解聚马来酸酐0.4-0.6、甘油三酯0.02-0.04、聚乙烯醇10-15、丝胶4-6、硼酸0.07-0.1、六水硝酸钇0.05-0.1、硅烷偶联剂KH-550 0.4-1、水160-200、抗坏血酸钙0.1-0.2、椰油酸二乙醇酰胺1-2、吡啶硫酮锌0.2-1、卡松0.1-0.3、二甲基硅油0.08-0.1。
2.一种如权利要求1所述的抑菌防腐金属表面处理剂的制备方法，其特征在于包括以下步骤：
（1）取丝胶，加入上述水重量的30-40%，搅拌均匀后加入硅烷偶联剂KH-550、六水硝酸钇，600-1000转/分搅拌分散10-20分钟，得硅烷液；
（2）将吡啶硫酮锌、卡松混合，搅拌均匀后加入甘油三酯，加热到40-50℃，加入剩余水重量的40-50%，保温搅拌10-20分钟，得抑菌液；
（3）将上述抑菌液与硅烷液混合，搅拌均匀后加入上述聚乙烯醇、硼酸，65-70℃下保温搅拌60-70分钟，得丝胶乳液；
（4）将椰油酸二乙醇酰胺、抗坏血酸钙混合，60-70℃下保温搅拌2-3分钟；
（5）将上述处理后的各原料混合，400-500转/分搅拌3-6分钟，加入剩余各原料，800-1000转/分搅拌分散30-40分钟，即得所述金属表面处理剂。
CN201510168692.5A 2015-04-10 2015-04-10 一种抑菌防腐金属表面处理剂 Pending CN104818477A (zh)