CN104861409A - 抗静电abs塑料 - Google Patents

抗静电abs塑料 Download PDF

Info

Publication number
CN104861409A
CN104861409A CN201510270515.8A CN201510270515A CN104861409A CN 104861409 A CN104861409 A CN 104861409A CN 201510270515 A CN201510270515 A CN 201510270515A CN 104861409 A CN104861409 A CN 104861409A
Authority
CN
China
Prior art keywords
parts
plastic
abs plastic
antistatic
abs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510270515.8A
Other languages
English (en)
Inventor
袁峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Original Assignee
Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd filed Critical Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority to CN201510270515.8A priority Critical patent/CN104861409A/zh
Publication of CN104861409A publication Critical patent/CN104861409A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种抗静电ABS塑料。所述一种抗静电ABS塑料，包括下述重量份原料：ABS树脂100份；3-氨丙基三乙氧基硅烷0.5-1.5份；(3-月桂酰胺丙基)三甲基硫酸甲酯铵0.5-1.5份；月桂酸二乙醇酰胺0.2-0.6份；N,N-二(2-羟乙基)-十四酰胺0.2-0.6份。本发明的抗静电ABS塑料的抗静电性较优异，表面不易吸附灰尘，产品的综合性能较优异，可注塑加工成各种形状的汽车内饰件。

Description

抗静电ABS塑料
技术领域
本发明涉及一种ABS塑料，尤其涉及一种抗静电ABS塑料。
背景技术
ABS塑料是一种用途极广的热塑性工程塑料，是目前产量最大，应用最广泛的聚合物。ABS是丙烯腈、丁二烯和苯乙烯的三元共聚物，其英文名称是:Acrylonitrile Butadiene Styrene，Acrylonitrile(丙烯腈)、Butadiene(丁二烯)、Styrene(苯乙烯)，故称为ABS。ABS容易加工，且成品化学性状稳定、光泽度好，具有极强的抗冲击性、耐热耐低温性、以及优良的电气性能，可以进行表面着色、喷镀金属、电镀、焊接等加工。因此它被广泛用于汽车、电器、建材、玩具等领域产品的加工中。
但，通常ABS塑料的抗静电效果并不理想。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种抗静电ABS塑料。
本发明所要解决的技术问题是通过如下技术方案实现的：
一种抗静电ABS塑料，包括下述重量份原料：
ABS树脂                           100份；
3-氨丙基三乙氧基硅烷              0.5-1.5份；
(3-月桂酰胺丙基)三甲基硫酸甲酯铵  0.5-1.5份。
优选地，
一种抗静电ABS塑料，包括下述重量份原料：
本发明的抗静电ABS塑料，可以采用本领域的常规方法进行制备，如按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述抗静电ABS塑料。
具体的，可以为按配比称取各组分，在高速混合机中，室温下控制转速在300-400转/分钟，混合2-8分钟，160-190℃温度下经双螺杆挤出机挤出造粒，即获得所述抗静电ABS塑料。
本发明的抗静电ABS塑料的抗静电性较优异，表面不易吸附灰尘，产品的综合性能较优异，可注塑加工成各种形状的汽车内饰件。
具体实施方式
下面结合实施例对本发明作进一步描述。
下述实施例中，各原料介绍：
ABS树脂选用中国台湾奇美公司牌号PA-777B的注塑级ABS树脂。
3-氨丙基三乙氧基硅烷，硅烷偶联剂KH 550，CAS号：919-30-2。(3-月桂酰胺丙基)三甲基硫酸甲酯铵，又称抗静电剂LS，英文名：(3-lauramidopropyl)trimethyl ammonium methyl sulfate。
月桂酸二乙醇酰胺，CAS号：120-40-1。
N,N-二(2-羟乙基)-十四酰胺，CAS号：7545-23-5。
实施例1-4
按照表1中对应实施例1-4数据称取各原料。
在高速混合机中，室温下控制高速混合机转速在350转/分钟，混合5分钟，取出后转入双螺杆挤出机中，在180℃温度下挤出造粒，螺杆机转速控制在400转/分钟，即获得所述抗静电ABS塑料。
表1：抗静电ABS塑料配方表(单位：公斤)
原料 实施例1 实施例2 实施例3 实施例4
ABS树脂 100 100 100 100
3-氨丙基三乙氧基硅烷 1 1 1 1
(3-月桂酰胺丙基)三甲基硫酸甲酯铵 1 1 1 1
月桂酸二乙醇酰胺 - 0.6 - 0.3
N,N-二(2-羟乙基)-十四酰胺 - - 0.6 0.3
测试例
对实施例1-4的抗静电ABS塑料防静电性能进行测试，按照大众汽车Antistatic property acc.to PV3977进行，时间120s，温度23℃。各测试20次，剔除异常值，再取平均值。
表2：抗静电ABS塑料防静电性能测试表
  90℃/500h老化后
实施例1 0.42KV
实施例2 0.31KV
实施例3 0.29KV
实施例4 0.20KV
标准：≤0.3KV after 120S。
发明人通过大量实验得出，将抗静电剂(3-月桂酰胺丙基)三甲基硫酸甲酯铵、月桂酸二乙醇酰胺和N,N-二(2-羟乙基)-十四酰胺三者复配，抗静电效果明显，具有协同抗静电效果。
对实施例1-4的抗静电ABS塑料表面电阻率进行测试，按照GB/T1410-2006进行。
表3：ABS塑料抗静电性能测试表
  表面电阻率/Ω
实施例1 1.9×108
实施例2 1.2×108
[0037] 
实施例3 1.1×108
实施例4 0.7×108
表4：实施例4的抗静电ABS塑料基本性能测试表
试验条件 测试标准 测试数据 单位
比重 ASTM D-792 1.04 kg/cm3/23℃
熔体流动速率,220℃×10kg ASTM D-1238 6.8 g/10min
引张强度 ASTM D-638 440 kg/cm2
伸长率 ASTM D-638 14 ％
弯曲强度 ASTM D-790 710 kg/cm2
IZOD冲击强度,1/4〃 ASTM D-256 22 kg.cm/cm

Claims (2)

1.一种抗静电ABS塑料，包括下述重量份原料：
ABS树脂                             100份；
3-氨丙基三乙氧基硅烷                0.5-1.5份；
(3-月桂酰胺丙基)三甲基硫酸甲酯铵    0.5-1.5份。
2.一种抗静电ABS塑料，包括下述重量份原料：
CN201510270515.8A 2015-05-25 2015-05-25 抗静电abs塑料 Withdrawn CN104861409A (zh)