CN104861234A - 一种耐磨丁苯橡胶材料 - Google Patents

一种耐磨丁苯橡胶材料 Download PDF

Info

Publication number
CN104861234A
CN104861234A CN201510207157.6A CN201510207157A CN104861234A CN 104861234 A CN104861234 A CN 104861234A CN 201510207157 A CN201510207157 A CN 201510207157A CN 104861234 A CN104861234 A CN 104861234A
Authority
CN
China
Prior art keywords
parts
butadiene rubber
wear
rubber
styrene butadiene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510207157.6A
Other languages
English (en)
Inventor
项宗武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Original Assignee
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd filed Critical ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority to CN201510207157.6A priority Critical patent/CN104861234A/zh
Publication of CN104861234A publication Critical patent/CN104861234A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种耐磨丁苯橡胶材料，按重量份计，包括以下组分：丁苯橡胶62-65份、丁腈橡胶27-30份、三元乙丙橡胶15-21份、硫磺1.2-2份、促进剂CZ 1-1.5份、促进剂TMTD 0.8-1.4份、防老剂4020 0.5-1份、防老剂RD 1.1-1.5份、硅烷偶联剂1.5-2份、炭黑20-26份、高岭土15-18份、软化剂1-3份。本发明以丁苯橡胶为主体橡胶，加入适量丁腈橡胶和三元乙丙橡胶，大大增强了橡胶材料的耐磨性能；防老剂4020与防老剂RD的使用能够提高本发明的耐老化和耐氧化性能。

Description

一种耐磨丁苯橡胶材料
技术领域
本发明属于橡胶领域，具体是一种耐磨丁苯橡胶材料。
背景技术
丁苯橡胶又称聚苯乙烯丁二烯共聚物，其物理机构性能，加工性能及制品的使用性能接近于天然橡胶，有些性能如耐磨、耐热、耐老化及硫化速度较天然橡胶更为优良，可与天然橡胶及多种合成橡胶并用，广泛用于轮胎、胶带、胶管、电线电缆、医疗器具及各种橡胶制品的生产等领域，但其耐磨性能不理想，其使用范围受到限制。
发明内容
本发明的目的在于克服现有技术缺陷，提供一种耐磨丁苯橡胶材料。
本发明的目的可以通过以下技术方案实现：
一种耐磨丁苯橡胶材料，按重量份计，包括以下组分：丁苯橡胶62-65份、丁腈橡胶27-30份、三元乙丙橡胶15-21份、硫磺1.2-2份、促进剂CZ 1-1.5份、促进剂TMTD 0.8-1.4份、防老剂4020 0.5-1份、防老剂RD 1.1-1.5份、硅烷偶联剂1.5-2份、炭黑20-26份、高岭土15-18份、软化剂1-3份。
作为进一步优选，本发明按重量份计，包括以下组分：丁苯橡胶63.5份、丁腈橡胶28.5份、三元乙丙橡胶18份、硫磺1.6份、促进剂CZ 1.2份、促进剂TMTD 1.1份、防老剂4020 0.75份、防老剂RD 1.3份、硅烷偶联剂1.8份、炭黑23份、高岭土16.5份、软化剂2份。
本发明所述软化剂为邻苯二甲酸二丁酯。
本发明的有益效果：本发明以丁苯橡胶为主体橡胶，加入适量丁腈橡胶和三元乙丙橡胶，大大增强了橡胶材料的耐磨性能；防老剂4020与防老剂RD的使用能够提高本发明的耐老化和耐氧化性能。
具体实施方式
为了便于本领域技术人员理解，下面结合具体实施例对本发明作进一步的说明。
实施例1
耐磨丁苯橡胶材料，按重量份计，包括以下组分：丁苯橡胶63.5份、丁腈橡胶28.5份、三元乙丙橡胶18份、硫磺1.6份、促进剂CZ 1.2份、促进剂TMTD 1.1份、防老剂4020 0.75份、防老剂RD 1.3份、硅烷偶联剂1.8份、炭黑23份、高岭土16.5份、邻苯二甲酸二丁酯2份。
实施例2
耐磨丁苯橡胶材料，按重量份计，包括以下组分：丁苯橡胶62份、丁腈橡胶27份、三元乙丙橡胶15份、硫磺1.2份、促进剂CZ 1份、促进剂TMTD 0.8份、防老剂4020 0.5份、防老剂RD 1.1份、硅烷偶联剂1.5份、炭黑20份、高岭土15份、邻苯二甲酸二丁酯1份。
实施例3
耐磨丁苯橡胶材料，按重量份计，包括以下组分：丁苯橡胶62-65份、丁腈橡胶30份、三元乙丙橡胶21份、硫磺2份、促进剂CZ 1.5份、促进剂TMTD 1.4份、防老剂4020 1份、防老剂RD 1.5份、硅烷偶联剂2份、炭黑26份、高岭土18份、邻苯二甲酸二丁酯3份。
以上内容仅仅是对本发明所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。

Claims (3)

1.一种耐磨丁苯橡胶材料，其特征在于，按重量份计，包括以下组分：丁苯橡胶62-65份、丁腈橡胶27-30份、三元乙丙橡胶15-21份、硫磺1.2-2份、促进剂CZ 1-1.5份、促进剂TMTD 0.8-1.4份、防老剂4020 0.5-1份、防老剂RD 1.1-1.5份、硅烷偶联剂1.5-2份、炭黑20-26份、高岭土15-18份、软化剂1-3份。
2.根据权利要求1所述的耐磨丁苯橡胶材料，其特征在于，按重量份计，包括以下组分：丁苯橡胶63.5份、丁腈橡胶28.5份、三元乙丙橡胶18份、硫磺1.6份、促进剂CZ 1.2份、促进剂TMTD 1.1份、防老剂4020 0.75份、防老剂RD 1.3份、硅烷偶联剂1.8份、炭黑23份、高岭土16.5份、软化剂2份。
3. 根据权利要求1所述的耐磨丁苯橡胶材料，其特征在于，所述软化剂为邻苯二甲酸二丁酯。
CN201510207157.6A 2015-04-28 2015-04-28 一种耐磨丁苯橡胶材料 Pending CN104861234A (zh)