CN104831882A - Diatom ooze construction scheme - Google Patents
Diatom ooze construction scheme Download PDFInfo
- Publication number
- CN104831882A CN104831882A CN201510287652.2A CN201510287652A CN104831882A CN 104831882 A CN104831882 A CN 104831882A CN 201510287652 A CN201510287652 A CN 201510287652A CN 104831882 A CN104831882 A CN 104831882A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- construction
- metope
- scheme
- bucket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a diatom ooze construction scheme. The scheme comprises the steps that firstly, construction tools are prepared, wherein the construction tools comprise but are not limited in a stirrer, a water bucket, a trowel, an air measuring instrument and a PH tester; secondly finishing over wall surfaces is carried out, wherein the finishing over the wall surfaces enables the wall surfaces to guarantee smoothness, density and cleanness of a basal plane, and guarantees levelness and verticality of internal corners, external corners and lines, and the construction environment needs to meet the fact that the wall temperature ranges from 5 DEG C to 35 DEG C, the relative air humidity is smaller than or equal to 80%, and the PH value of the wall faces is smaller than or equal to 10; thirdly, diatom ooze is stirred in an assigned room, and construction is carried out on the wall faces through the obtained diatom ooze. According to the diatom ooze construction scheme, aiming at the construction process, the problem that currently construction of diatom ooze is difficult to carry out is solved, needed coating effects can be achieved through the construction scheme, the construction process is simple, the scheme is easy to learn, and labor force is reduced greatly.
Description
Technical field
The present invention relates to a kind of application of diatom ooze, particularly a kind of diatom ooze constructure scheme.
Background technology
Diatom ooze is a kind of natural protection type metope wall material; the main raw material(s) of diatom ooze is diatom ooze main raw material(s) is the natural materials that diatom ooze deposits; main component protein; be rich in multiple beneficial mineral matter; quality is light and soft; its particle surface has countless small hole, and porosity reaches more than 90%, has extremely strong physical absorption performance and ion-exchange performance.
The veinpatterns design of diatom ooze specialty need have special construction master worker construction, otherwise can not reach good effect, easily causes metope to come off, unsightly, wastes the problems such as material.
Summary of the invention
The object of the invention is to provide a kind of a kind of diatom ooze constructure scheme saving material form of construction work to solve above-mentioned the deficiencies in the prior art.
To achieve these goals, a kind of diatom ooze constructure scheme designed by the present invention, is characterized in that: comprise the following steps:
First, construction tool prepares, and it is including but not limited to agitator, bucket, trowel, air measuring instrument and PH tester; Secondly, metope is repaired, its metope is ensured basal plane is smooth, closely knit, clean, negative and positive angle and the horizontal flat heavily fortified point of lines straight; Require to meet to construction environment: body of wall temperature 5 DEG C-35 DEG C, relative air humidity is not more than 80%, the pH value of metope is not more than 10; Then, stir diatom ooze in designated room, agitating mode is as follows:
A, diatom ooze chest taken apart and opens inner packing and pour in the clean bucket of preprepared;
B, connect suitable clear water with another bucket;
C, clear water poured into before diatom ooze material bucket in;
D, to add water according to the ratio of 1:1;
E, hold agitator and put into bucket and stir, stir by clockwise, counterclockwise, upper and lower multiple method;
F, mixing time control at about 10 minutes;
Then constructed to metope by diatom ooze obtained above, form of construction work comprises zero diopter engineering method, spraying engineering method and artistic engineering method and to construct three kinds of modes.
Preferably, diatom ooze powder is poured for the step c in above-mentioned agitating mode into and first leave standstill 5 minutes.
Preferably, above-mentioned metope is repaired it and also comprises for hollowing or occur that the substrate of crackle must be anticipated, to substrate brushing putty after clean.
A kind of diatom ooze constructure scheme that the present invention obtains, for above-mentioned work progress, can simplify at present difficult to diatom ooze construction and not easily construction problem, by above-mentioned constructure scheme, it effectively can obtain the coating effect needed, work progress is simple, easy to learnly greatly reduces labour.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.
Embodiment:
A kind of diatom ooze constructure scheme provided by the invention, comprises the following steps:
First, construction tool prepares, and it is including but not limited to agitator, bucket, air measuring instrument and PH tester; Secondly, metope is repaired, its metope is ensured basal plane is smooth, closely knit, clean, negative and positive angle and the horizontal flat heavily fortified point of lines straight; Require to meet to construction environment: body of wall temperature 5 DEG C-35 DEG C, relative air humidity is not more than 80%, the pH value of metope is not more than 10; Then, stir diatom ooze in designated room, agitating mode is as follows:
A, diatom ooze chest taken apart and opens inner packing and pour in the clean bucket of preprepared;
B, connect suitable clear water with another bucket;
C, clear water poured into before diatom ooze material bucket in;
D, to add water according to the ratio of 1:1;
E, hold agitator and put into bucket and stir, stir by clockwise, counterclockwise, upper and lower multiple method;
F, mixing time approximately control at about 10 minutes;
Then constructed to metope by diatom ooze obtained above, form of construction work comprises zero diopter engineering method, spraying engineering method and artistic engineering method and to construct three kinds of modes.
Zero diopter engineering method construction point: the material be stirred is criticized and is coated on basal plane by first pass stainless steel trowel thinly, area is unsuitable excessive, 80cm width.Criticize painting second time followed by by same direction, guarantee that basic unit criticizes the smooth nothing of coating uniform and obviously criticizes tool marks and bubble generation; Coating should ensure at about 1mm-1.2mm, checks Bulk coat whether also repair in time by defectiveness in time.Treat that its coating surface receives water 85-90%(and finger pressure is not sticky and obvious impression), then use by same direction the stainless steel trowel that 0.2 ~ 0.5mm is thick, batch painting the 3rd time.Its coating layer thickness 0.8-1mm.Note the dynamics of push broach, firmly too not large, not press polish repeatedly, in batch painting process, light will become clear, and to see batch metope be coated with clearly, the concavo-convex vestige that finishing in time occurs.
Spraying engineering method construction point: before construction, whether close inspection putty layer meets the requirements; Whether the objects such as door and window, furniture, wood flooring protect; In accordance with the water distribution ratio of product, allotment must be described during material allotment; First prepare one piece of test plate (panel), adjust spray gun oil pump capacity and air pressure; Answer arm to move during spraying, accomplish that trick is caught up with, arrive soon, synchronously carry out, process in time of pinpointing the problems; Allotment water content of coating ratio must not be increased and decreased arbitrarily during spraying.The determination of spraying order and route affects whole spraying process, first determines its spraying point and spraying order before spraying.From total layout, should follow " first far away rear near, first up and then down, principle from inside outwards ".Generally can by metope after first ceiling, first indoor rear passageway, staircase spray.Spraying is divided into be carried out for 2 times.First pass spraying, mainly in order to cover bottom surface, prevents show-through; After first pass has sprayed, when not touching with one's hand with hand touch metope, second time can be sprayed.
Art engineering method construction point: zero diopter engineering method is relatively stable with spraying engineering method, is also convenient to grasp.Art engineering method is just complicated, even if use identical instrument, do identical skin texture, artistic effect also varies with each individual.Generally, artistic engineering method refers to the general name using various instrument to make various different-style skin texture.Be characterized in: do not have stationarity, identical veinpatterns design, different constructors, the style shown is different, thousand people thousand; The instrument used varies with each individual, consummate in craftsmanship, rich and varied; The quality of the textural effect shown, is closely related with the skill of constructor.Art engineering method, from the instrument used, has roller, trowel, hairbrush, silk screen etc. usually.From textures, to copy nature pattern, there is realistic gimmick, also have abstract performance, as flowers and plants, sandstone, wood grain, annual ring etc.
Preferably, pour diatom ooze powder into first leave standstill 5 minutes for the step c in above-mentioned agitating mode, because diatom ooze has good water absorption character, this can reduce mixing time and save labour.
Preferably, above-mentioned metope is repaired it also comprise for hollowing or occur that the substrate of crackle must be anticipated, to substrate brushing twice putty after clean, in order to remove coated article rugged defect on the surface, this step process need be carried out in order to a smooth metope attractive in appearance can be reached.
A kind of diatom ooze constructure scheme that the present invention obtains, for above-mentioned work progress, can simplify at present difficult to diatom ooze construction and not easily construction problem, by above-mentioned constructure scheme, it effectively can obtain the coating effect needed, work progress is simple, easy to learnly greatly reduces labour.
For general technical staff of the technical field of the invention; without departing from the inventive concept of the premise; its framework form can be flexible and changeable, just makes some simple deduction or replace, all should be considered as belonging to the scope of patent protection that the present invention is determined by submitted to claims.
Claims (3)
1. a diatom ooze constructure scheme, is characterized in that: comprise the following steps:
First, construction tool prepares, and it is including but not limited to agitator, at least two buckets, trowel, agitator, air measuring instrument and PH testers; Secondly, metope is repaired, its metope is ensured basal plane is smooth, closely knit, clean, negative and positive angle and the horizontal flat heavily fortified point of lines straight; Require to meet to construction environment: body of wall temperature 5 DEG C-35 DEG C, relative air humidity is not more than 80%, the pH value of metope is not more than 10; Then, stir diatom ooze in designated room, agitating mode is as follows:
A, diatom ooze chest taken apart and opens inner packing and pour in the clean bucket of preprepared;
B, connect suitable clear water with another bucket;
C, clear water poured into before diatom ooze material bucket in;
D, to add water according to the ratio of 1:1;
E, hold agitator and put into bucket and stir, stir by clockwise, counterclockwise, upper and lower multiple method;
F, mixing time control at about 10 minutes;
Then constructed to metope by diatom ooze obtained above, form of construction work comprises zero diopter engineering method, spraying engineering method and artistic engineering method and to construct three kinds of modes.
2. a kind of diatom ooze constructure scheme according to claim 1, is characterized in that: pour diatom ooze powder into for the step c in above-mentioned agitating mode and first leave standstill 5 minutes.
3. a kind of diatom ooze constructure scheme according to claim 1, is characterized in that: repair it for above-mentioned metope and also comprise for hollowing or occur that the substrate of crackle must be anticipated, to substrate brushing putty after clean.