CN104817937A - Energy-saving environment-friendly roller-coating paint for home appliance plates and application method thereof - Google Patents
Energy-saving environment-friendly roller-coating paint for home appliance plates and application method thereof Download PDFInfo
- Publication number
- CN104817937A CN104817937A CN201510256203.1A CN201510256203A CN104817937A CN 104817937 A CN104817937 A CN 104817937A CN 201510256203 A CN201510256203 A CN 201510256203A CN 104817937 A CN104817937 A CN 104817937A
- Authority
- CN
- China
- Prior art keywords
- paint
- roller coat
- polyester
- energy
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an energy-saving environment-friendly roller-coating paint for home appliance plates and an application method thereof. The paint comprises a white primer and a finish paint. The paint has the advantages of high adhesive force, favorable ductility, high temperature resistance and long service life, changes the processing technique of the metal plate products, simplifies the processing procedure, centrally completes the roller coating treatment on the home appliance plate, and does not need to independently arrange any spray workshop.
Description
Technical field
The present invention relates to a kind of appliance plate energy-conserving and environment-protective roller coat paint and manufacture method thereof, be mainly applicable to the application of the appliance plates such as refrigerator panel, backboard, air-conditioning panel, microwave oven panel.
Background technology
The coating process of existing appliance plate mainly adopts spraying technology: first by sheet-metal work that the punching press of appliance plate slab, deep-draw become antitheft door, metal bucket, iron pipe etc. shaping, then custom-designed painting workshop is delivered to, shaping sheet-metal work is sprayed, obtains the appliance plate products such as shaping refrigerator panel, backboard, air-conditioning panel, microwave oven panel.
Wherein, spraying is by spray gun or dish-style spraying gun, by means of pressure or centrifugal force, is dispersed into even and fine droplet, is applied over the coating process on coated article surface.
Subject matter in spraying is the coating cloud of high dispersing and the solvent (i.e. volatile organic contaminant, VOCs) evaporated, and both contaminate environment, are unfavorable for HUMAN HEALTH, waste coating again, cause financial loss.
Particularly, there is following defect in existing appliance plate spraying coating process:
1) paint consumption large, but utilization ratio is low, causes waste.In spraying process, due to paint non-refractory, the too high meeting of temperature causes painting variable color, so adopt low-temperature spray, causes each quantity for spray few, needs spraying just can complete the spraying of described forming metal slab products for 3 ~ 5 times, causes the waste to paint;
2) have volatile materials in the paint used in existing spraying coating process, in spraying process, cause the paint only having 30 ~ 40% to be attached on forming metal slab products, all the other are diffused in air, or drop on the ground, waste is serious, has pollution to environment, and spraying cost is high;
3) volatilize, the paint be diffused in air, then form volatile organic contaminant (VOCs), be detrimental to health.At painting workshop, paint the main source as volatile organic contaminant, be easy to cause acute poisoning in painting workshop in air during volatile organic compounds excessive concentration, the lighter there will be headache, dizziness, cough, Nausea and vomiting or is dead drunk liquor-saturated shape; Severe one there will be liver poisoning and even goes into a coma very soon, and what have also may be in peril of one's life.Treat for a long time, in the painting workshop of volatile organic compounds pollution, can chronic poisoning be caused, damage liver and neural system, cause general weakness, drowsiness, skin pruritus etc.What have also may cause endocrine disturbance, affects sexual function; Benzene and dimethylbenzene can also damage system, so that cause leukemia;
4) operation being first sprayed on processing can not be realized.If reprocess process after spraying, PASS and ductility can be caused not, can come off in the course of processing; And the bending degree of the metal sheet of spray paint (the curved performance of T) is general at 2T or more than 2T, requiring that 0T is (namely after metal sheet 180 ° bending, completely seamlessly to close up, paint does not burst and comes off) or 1T (namely after metal sheet twice 180 ° of bendings, outermost paint face does not come off, do not burst) situation time, the paint adopted in existing spraying coating process cannot meet the demands;
5) for existing spraying coating process, the metal sheet of machine-shaping sprays, for region baroque on profiled metal sheet (such as corner place, recess etc.), probably cannot a spray mo(u)lding, need repeatedly to spray, just can complete the spraying in complex structure region, cause metal sheet surface to paint skewness, affect follow-up use;
6) adopt spraying coating process, need each sheet-metal work producer will arrange painting workshop specially, environmental protection treatment pressure is large;
7) in existing spraying coating process adopt paint, be mostly Polyester Paint or F-C paint, these two kinds paint resistance of aging are poor, through long-time continuous sunshine, the surperficial situation that there will be yellowing, variable color of appliance plate;
8) existing Polyester Paint or F-C paint, heat-resisting ability is poor, and when adopting spot welding continuation processing or temperature to reach 230 DEG C, appliance plate surface paint there will be variable color, cracking phenomena.
Summary of the invention
For solving above-mentioned Problems existing, a kind of appliance plate energy-conserving and environment-protective roller coat is the object of the present invention is to provide to paint and using method, described PASS is strong, ductility good, high temperature resistant, long service life, change the complete processing of sheet-metal work, simplify machining clearance, appliance plate slab is concentrated roller coat process, without the need to arranging painting workshop separately.
For achieving the above object, the technical solution used in the present invention is:
An appliance plate energy-conserving and environment-protective roller coat paint, described paint comprises based white primer and finish paint; Described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 35 ~ 45%, barium sulfate slurry containing rust-stabilising pigment: 30 ~ 40%, polyester modification acrylic resin: 10 ~ 15%, polyester modified epoxy resin: 2 ~ 8%, solidifying agent: 1 ~ 5%, curing catalyst: 0.06 ~ 0.1%, flow agent: 0.4 ~ 0.6%, adhesion promoter: 1 ~ 2%, defoamer: 0.4 ~ 0.8%, mixed solvent: 1 ~ 5%; Described finish paint chemical composition mass percent is: starch in vain: 60 ~ 70%, aminoresin: 5 ~ 10%, polyester modification acrylic resin: 10 ~ 25%, colour of loess mill base: 0.01 ~ 0.05%, black wash: 0.01 ~ 0.05%, flow agent: 0.5 ~ 1.5%, defoamer: 0.5 ~ 1%, siccative: 0.1 ~ 1%, wax is starched: 1 ~ 5%, mixed solvent: 2 ~ 10%; In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 40 ~ 50%, toner: 40 ~ 50%, disintegrator: 1 ~ 5%, wilkinite: 0.1 ~ 0.2%, mixed solvent: 2 ~ 8%.
Preferably, described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 38 ~ 42%, barium sulfate slurry containing rust-stabilising pigment: 35 ~ 37%, polyester modification acrylic resin: 10 ~ 11%, polyester modified epoxy resin: 4 ~ 5%, solidifying agent: 3 ~ 4%, curing catalyst: 0.06 ~ 0.1%, flow agent: 0.4 ~ 0.6%, adhesion promoter: 1 ~ 2%, defoamer: 0.4 ~ 0.8%, mixed solvent: 3 ~ 4%; Described finish paint chemical composition mass percent is: starch in vain: 63 ~ 65%, aminoresin: 6 ~ 8%, polyester modification acrylic resin: 18 ~ 20%, colour of loess mill base: 0.01 ~ 0.03%, black wash: 0.01 ~ 0.03%, flow agent: 0.8 ~ 1%, defoamer: 0.5 ~ 0.8%, siccative: 0.2 ~ 0.4%, wax is starched: 1 ~ 2%, mixed solvent: 4 ~ 6%; In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 41 ~ 44%, toner: 44 ~ 46%, disintegrator: 3 ~ 5%, wilkinite: 0.1 ~ 0.2%, mixed solvent: 6 ~ 8%.
Preferably, described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 40%, barium sulfate slurry containing rust-stabilising pigment: 36.51%, polyester modification acrylic resin: 10.15%, polyester modified epoxy resin: 4.06%, solidifying agent: 3.55%, curing catalyst: 0.08%, flow agent: 0.56%, adhesion promoter: 1.02%, defoamer: 0.6%, mixed solvent: 3.47%; Described finish paint chemical composition mass percent is: starch in vain: 64.94%, aminoresin: 7.4%, polyester modification acrylic resin: 19.72%, colour of loess mill base: 0.02%, black wash: 0.01%, flow agent: 0.99%, defoamer: 0.6%, siccative: 0.3%, wax is starched: 1.5%, mixed solvent: 4.52%; In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 43.08%, toner: 45.54%, disintegrator: 4%, wilkinite: 0.15%, mixed solvent: 7.23%.
Further, described finish paint starch in vain in toner be titanium dioxide.
Separately, described middle-molecular-weihydroxyethyl polyester pulp is water-soluble polyurethane, and molecular weight is 8000 ~ 12000.
Separately have, described solidifying agent is modified amine curing agent.
Again, described defoamer is silicone based defoamer, mineral oil defoaming agent or its combination.
Further, described adhesion promoter is epoxy group(ing) siloxanes auxiliary agent, described flow agent is fluorine-carbon modified acrylate copolymer flow agent.
And described mixed solvent is two or more the mixture in ester class, ketone, aliphatic hydrocarbon, fatty alcohol, aromatic hydrocarbon solvent.
Simultaneously, the using method that the present invention also provides a kind of appliance plate energy-conserving and environment-protective roller coat to paint, comprise the steps: to carry out pre-treatment to appliance plate steel slab surface, then the mode of roller coat is adopted in steel slab surface, successively by the based white primer in described paint and finish paint application to appliance plate steel slab surface, obtain metallic paint plate, roller coat temperature 216 ~ 224 DEG C, roller coat number of times is 1 time.
Beneficial effect of the present invention is:
A) PASS obtained by is strong, ductility good, high temperature resistant (can nondiscoloration at 230 DEG C), long service life.
B) in the metal sheet slab stage namely by roller coat by oil paint coating provided by the present invention in metal sheet steel slab surface, form metallic paint slab, gained metallic paint slab directly can carry out following process, obtain shaping appliance plate, even if baroque appliance plate structure, also oil paint coating is completed in the slab stage, without the need to follow-up application, to instead of in existing technique " be first processed into appliance plate slab; and then spraying obtains shaping appliance plate " technique, paint and metal sheet strong adhesion, can not crack because of complete processing or come off.
C) owing to painting excellent sticking power and ductility; change the complete processing of sheet-metal work; simplify machining clearance; concentrate the roller coat process of metal sheet on a metal plate; without the need to arranging painting workshop separately again; sheet-metal work source mill does not have the discharge of waste water and gas, and environment protection detects only needs the source of centralized Control metal sheet to spray, and optimizes environment protection.
D) paint adopts the mode of roller coat, adopt the mode of disposable roller coat that paint roller is coated onto appliance plate steel slab surface, roller coat temperature controls between 216 ~ 224 DEG C, rate of drying is fast, by original 2 ~ 5 roller coat become 1 time shaping, the process for processing speed of 60m slab/min can be realized, greatly accelerate production rate, improve production efficiency, greatly reduce process period, good energy-conserving effect.
E) the roller coating technology replacement spraying coating process owing to being the shaping quick-drying of disposable roller coat, the availability painted during application can reach more than 90%, decrease the volatilization in air and waste, the VOCs that effective reduction causes paint volatilization to be formed because of spraying, VOCs quantity discharged≤420ppm in roller coat workshop, paint environment protecting is good.
F) the metallic paint slab products that roller coat application completes is processed, be made into various appliance plate finished product, the curved performance of metallic paint plate T can reach 0T (after the finished metal plate after roller coat 180 ° bending, completely seamlessly to close up, paint does not burst and comes off) or 1T (after metal sheet twice 180 ° of bendings, outermost paint face does not come off, and does not burst), ensure metal sheet quality.
Embodiment
Below by specific embodiment, the present invention is described further, but embodiment does not limit the scope of the invention.
Table 1 is based white primer chemical composition list in appliance plate energy-conserving and environment-protective roller coat paint described in the embodiment of the present invention.Table 2 is finish paint chemical composition list in appliance plate energy-conserving and environment-protective roller coat paint described in the embodiment of the present invention.Table 3 is pulp ingredient lists white in finish paint described in the embodiment of the present invention.
Based white primer chemical composition described in table 1. embodiment (unit: wt%)
The chemical composition (unit: wt%) of finish paint described in table 2. embodiment
The chemical composition (unit: wt%) of white slurry in finish paint described in table 3. embodiment
| Polyester modification resin D | Toner | Disintegrator | Wilkinite | Mixed solvent | |
| Embodiment 1 | 43.08 | 45.54 | 4 | 0.15 | 7.23 |
| Embodiment 2 | 48.23 | 43.36 | 1 | 0.20 | 7.21 |
| Embodiment 3 | 43.71 | 48.65 | 5 | 0.10 | 2.54 |
| Embodiment 4 | 40.28 | 50.00 | 3 | 0.20 | 6.52 |
| Embodiment 5 | 45.69 | 40.36 | 5 | 0.2 | 8.75 |
Metallic paint plate obtained after adopting appliance plate energy-conserving and environment-protective roller coat oil paint coating metal slabs provided by the present invention, the curved performance of T can reach 0T or 1T.Paint utilization rate is high, and every 30 kilograms of paint can application 1 ton of metal sheet slab.Do not ftracture under 230 ° of high temperature, nondiscoloration, resistance of aging is strong, is placed on the not yellowing in 10 ~ 15 years of outdoor consecutive sunlight, nondiscoloration.Acidproof corrosion resistance is strong, puts into 85 ° of water boil that 2H is raw is heated to 100 ° more gradually by being coated with product spray, product without variable color, fall to paint, foaming.After using the Nad solution soaking 24H of 5% at normal temperatures, product surface non-corroding, variable color and coating come off.Pure cotton cloth is dipped in full 95% alcohol to be wrapped on 500g counterweight, wipes examination 50 circulation with the stroke of speed (20mm) left and right of per minute 40-60 time at product surface, and nothing fades de-oiling.Detect according to the X method of drawing in the U.S. ASTM forming metal appliance plate being coated with paint provided by the present invention, can reach the 0=ASTM grade of ISO grade, notching edge is completely smooth, and what edge had not a particle of peels off.
It should be noted that, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted.Although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to the technical scheme of invention or equivalent replacement, and not depart from the scope of technical solution of the present invention, it all should be encompassed in right of the present invention.
Claims (10)
1. an appliance plate energy-conserving and environment-protective roller coat paint, it is characterized in that, described paint comprises based white primer and finish paint;
Described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 35 ~ 45%, barium sulfate slurry containing rust-stabilising pigment: 30 ~ 40%, polyester modification acrylic resin: 10 ~ 15%, polyester modified epoxy resin: 2 ~ 8%, solidifying agent: 1 ~ 5%, curing catalyst: 0.06 ~ 0.1%, flow agent: 0.4 ~ 0.6%, adhesion promoter: 1 ~ 2%, defoamer: 0.4 ~ 0.8%, mixed solvent: 1 ~ 5%;
Described finish paint chemical composition mass percent is: starch in vain: 60 ~ 70%, aminoresin: 5 ~ 10%, polyester modification acrylic resin: 10 ~ 25%, colour of loess mill base: 0.01 ~ 0.05%, black wash: 0.01 ~ 0.05%, flow agent: 0.5 ~ 1.5%, defoamer: 0.5 ~ 1%, siccative: 0.1 ~ 1%, wax is starched: 1 ~ 5%, mixed solvent: 2 ~ 10%;
In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 40 ~ 50%, toner: 40 ~ 50%, disintegrator: 1 ~ 5%, wilkinite: 0.1 ~ 0.2%, mixed solvent: 2 ~ 8%.
2. appliance plate energy-conserving and environment-protective roller coat paint according to claim 1, it is characterized in that, described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 38 ~ 42%, the barium sulfate slurry containing rust-stabilising pigment: 35 ~ 37%, polyester modification acrylic resin: 10 ~ 11%, polyester modified epoxy resin: 4 ~ 5%, solidifying agent: 3 ~ 4%, curing catalyst: 0.06 ~ 0.1%, flow agent: 0.4 ~ 0.6%, adhesion promoter: 1 ~ 2%, defoamer: 0.4 ~ 0.8%, mixed solvent: 3 ~ 4%;
Described finish paint chemical composition mass percent is: starch in vain: 63 ~ 65%, aminoresin: 6 ~ 8%, polyester modification acrylic resin: 18 ~ 20%, colour of loess mill base: 0.01 ~ 0.03%, black wash: 0.01 ~ 0.03%, flow agent: 0.8 ~ 1%, defoamer: 0.5 ~ 0.8%, siccative: 0.2 ~ 0.4%, wax is starched: 1 ~ 2%, mixed solvent: 4 ~ 6%;
In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 41 ~ 44%, toner: 44 ~ 46%, disintegrator: 3 ~ 5%, wilkinite: 0.1 ~ 0.2%, mixed solvent: 6 ~ 8%.
3. appliance plate energy-conserving and environment-protective roller coat paint according to claim 1, it is characterized in that, described based white primer chemical composition mass percent is: middle-molecular-weihydroxyethyl polyester pulp: 40%, the barium sulfate slurry containing rust-stabilising pigment: 36.51%, polyester modification acrylic resin: 10.15%, polyester modified epoxy resin: 4.06%, solidifying agent: 3.55%, curing catalyst: 0.08%, flow agent: 0.56%, adhesion promoter: 1.02%, defoamer: 0.6%, mixed solvent: 3.47%;
Described finish paint chemical composition mass percent is: starch in vain: 64.94%, aminoresin: 7.4%, polyester modification acrylic resin: 19.72%, colour of loess mill base: 0.02%, black wash: 0.01%, flow agent: 0.99%, defoamer: 0.6%, siccative: 0.3%, wax is starched: 1.5%, mixed solvent: 4.52%;
In described finish paint, white pulp Ingredient percent is: polyester modified organic silicon resin: 43.08%, toner: 45.54%, disintegrator: 4%, wilkinite: 0.15%, mixed solvent: 7.23%.
4. the appliance plate according to claim 1 or 2 or 3 with energy-conserving and environment-protective roller coat paint, it is characterized in that, described finish paint starch in vain in toner be titanium dioxide.
5. the energy-conserving and environment-protective roller coat paint of the appliance plate according to claim 1 or 2 or 3, it is characterized in that, described middle-molecular-weihydroxyethyl polyester pulp is water-soluble polyurethane, and molecular weight is 8000 ~ 12000.
6. the energy-conserving and environment-protective roller coat paint of the appliance plate according to claim 1 or 2 or 3, it is characterized in that, described solidifying agent is modified amine curing agent.
7. the energy-conserving and environment-protective roller coat paint of the appliance plate according to claim 1 or 2 or 3, is characterized in that, described defoamer is silicone based defoamer, mineral oil defoaming agent or its combination.
8. the energy-conserving and environment-protective roller coat paint of the appliance plate according to claim 1 or 2 or 3, it is characterized in that, described adhesion promoter is epoxy group(ing) siloxanes auxiliary agent, and described flow agent is fluorine-carbon modified acrylate copolymer flow agent.
9. the energy-conserving and environment-protective roller coat paint of the appliance plate according to claim 1 or 2 or 3, it is characterized in that, described mixed solvent is two or more the mixture in ester class, ketone, aliphatic hydrocarbon, fatty alcohol, aromatic hydrocarbon solvent.
10. the using method using the appliance plate as described in claim 1 or 2 or 3 to paint with energy-conserving and environment-protective roller coat, is characterized in that, comprise the steps:
Pre-treatment is carried out to appliance plate steel slab surface, then adopts the mode of roller coat in steel slab surface, successively by the based white primer in described paint and finish paint application to appliance plate steel slab surface, obtain metallic paint plate, roller coat temperature 216 ~ 224 DEG C, roller coat number of times is 1 time.