CN104815986B - 一种片状锌粉的制备方法 - Google Patents
一种片状锌粉的制备方法 Download PDFInfo
- Publication number
- CN104815986B CN104815986B CN201510228650.6A CN201510228650A CN104815986B CN 104815986 B CN104815986 B CN 104815986B CN 201510228650 A CN201510228650 A CN 201510228650A CN 104815986 B CN104815986 B CN 104815986B
- Authority
- CN
- China
- Prior art keywords
- zinc powder
- air
- air current
- disintegrating machine
- broken
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种片状锌粉的制备方法,包括前处理、破碎、后处理步骤,具体包括:将气流分级破碎机中通入惰性气体置换2~4次以保证气流分级破碎机中氧含量小于1%,将粒度小于325目的雾化球形锌粉原料置入经前处理后的气流分级破碎机中进行破碎得到粒度10~30μm的物料颗粒,由气流推到旋风分离室分离得到目标物径厚比50~70的片状锌粉。本发明由于成品物料的收集均能实现全密闭,与大气完全隔绝,制备得到的锌粉活性高,片状化程度高。
Description
技术领域
本发明属于冶金技术领域,具体涉及一种片状锌粉的制备方法。
背景技术
片状锌粉是一种重要的防腐用片状颜料,主要用于配制各种水溶性无机盐涂料、有机富锌涂料等,广泛应用于汽车、家电、船舶、交通灯行业。片状锌粉是达克罗涂覆液中最重要的原料.达克罗要求的锌粉是片状的金属粉末,它对锌粉的大小和形貌都有特殊的要求,并要经过表面改性后球磨或研磨制得,所以片状锌粉的制备技术是一种高技术含量,附加值相对较高的金属粉体制备技术。
蒸发-冷凝法制备的锌粉粉度均匀,结晶良好,该工艺的主要缺点为膜层的厚度不易控制,气体流速及压力、加热温度、加热时间等因素对膜层的厚度均有影响,爆炸法制备的片状锌粉的纯度高,但是工艺的生产效率低、能耗大、成本高,并且存在着较大的安全隐患。球磨法是目前片状锌粉最常用的一种制备方法,该方法是将颗粒状的锌粉粉碎,并挤压成片状,按加入配料方式的不同可以将球磨法分为干式球磨法和湿式球磨法。干式球磨法的工艺简单,但是效率较低;湿式球磨法具有设备简单、研磨效果好、产品合格率高等优点,但是工艺比较复杂。因此,开发一种能解决上述技术问题的片状锌粉制备方法是非常必要的。
发明内容
本发明的目的在于提供一种片状锌粉的制备方法。
本发明的目的是这样实现的,包括前处理、破碎、后处理步骤,具体包括:
A、前处理:将气流分级破碎机中通入惰性气体置换2~4次以保证气流分级破碎机中氧含量小于1%;
B、破碎:将粒度小于325目的雾化球形锌粉原料置入经前处理后的气流分级破碎机中进行破碎得到粒度10 ~30μm的物料颗粒;
C、将破碎得到的物料颗粒由气流推到旋风分离室分离得到目标物径厚比50~70的片状锌粉。
本发明由于成品物料的收集均能实现全密闭,与大气完全隔绝,制备得到的锌粉活性高,片状化程度高。
本发明由气氛净化、原料准备、分级破碎、收集片状锌粉等工序组成。以粒度为-325目的雾化球形锌粉为原料,通过气体置换将气流破碎机内的空气排出,同时使氧含量达到要求范围0~1%;通过调节气流分级破碎机的分级变频器频率0~50Hz,以及冲击破碎压强0.8~1.2Mpa,使球状锌粉粉碎;待粉碎合格的细小颗粒被气流推到旋风分离室,集中到集粉罐里,最终制得径厚比(50~70)的片状锌粉。
附图说明
图1为本发明工艺流程示意图。
具体实施方式
下面结合实施例和附图对本发明作进一步的说明,但不以任何方式对本发明加以限制,基于本发明教导所作的任何变换或替换,均属于本发明的保护范围。
本发明所述的片状锌粉的制备方法,包括前处理、破碎、后处理步骤,具体包括:
A、前处理:将气流分级破碎机中通入惰性气体置换2~4次以保证气流分级破碎机中氧含量小于1%;
B、破碎:将粒度小于325目的雾化球形锌粉原料置入经前处理后的气流分级破碎机中进行破碎得到粒度10 ~30μm的物料颗粒;
C、将破碎得到的物料颗粒由气流推到旋风分离室分离得到目标物径厚比50~70的片状锌粉。
A步骤中的惰性气体为氮气和/或氩气。
B步骤中所述的气流分级破碎机的频率为0~50Hz。
B步骤中所述的气流分级破碎机的冲击破碎压强为0.8~1.2MPa。
实施例1
1.打开气流破碎机主机,通入99.95%的氮气气体,置换3次,将气流破碎机内的空气排出,使氧含量小于0.02%;
2.采用粒度为-325目的雾化球形锌粉为原料,放入分级破碎机的料斗里。
3.调节气流分级破碎机的分级变频器的频率10Hz,以及冲击破碎压强0.8Mpa,使球状锌粉粉碎;
4.待粉碎合格的细小颗粒被气流推到旋风分离室,集中到集粉罐里,得到径厚比平均为51的片状锌粉,片状化程度为93%。
实施例2
1.打开气流破碎机主机,通入99.95%的氮气气体,置换3次,将气流破碎机内的空气排出,使氧含量小于0.02%;
2.采用粒度为-325目的雾化球形锌粉为原料,放入分级破碎机的料斗里;
3.调节气流分级破碎机的分级变频器的频率15Hz,以及冲击破碎压强1.0Mpa,使球状锌粉粉碎;
4.待粉碎合格的细小颗粒被气流推到旋风分离室,集中到集粉罐里,得到径厚比平均为62的片状锌粉,片状化程度为96%。
实施例3
1.打开气流破碎机主机,通入99.95%的氮气气体,置换3次,将气流破碎机内的空气排出,使氧含量小于0.02%;
2.采用粒度为-325目的雾化球形锌粉为原料,放入分级破碎机的料斗里。
3.调节气流分级破碎机的分级变频器的频率20Hz,以及冲击破碎压强1.2Mpa,使球状锌粉粉碎;
4.待粉碎合格的细小颗粒被气流推到旋风分离室,集中到集粉罐里,得到径厚比平均68的片状锌粉,片状化程度为98%。
Claims (2)
1.一种片状锌粉的制备方法,其特征在于包括前处理、破碎、后处理步骤,具体包括:
A、前处理:将气流分级破碎机中通入惰性气体置换2~4次以保证气流分级破碎机中氧含量小于1%;
B、破碎:将粒度小于325目的雾化球形锌粉原料置入经前处理后的气流分级破碎机中进行破碎得到粒度10~30μm的物料颗粒;所述气流分级破碎机的频率为0~50Hz、冲击破碎压强为0.8~1.2MPa;
C、将破碎得到的物料颗粒由气流推到旋风分离室分离得到目标物径厚比50~70的片状锌粉。
2.根据权利要求1所述的片状锌粉的制备方法,其特征在于A步骤中的惰性气体为氮气和/或氩气。