CN1047912C - 植物纤维花盆及其生产方法 - Google Patents
植物纤维花盆及其生产方法 Download PDFInfo
- Publication number
- CN1047912C CN1047912C CN95111976A CN95111976A CN1047912C CN 1047912 C CN1047912 C CN 1047912C CN 95111976 A CN95111976 A CN 95111976A CN 95111976 A CN95111976 A CN 95111976A CN 1047912 C CN1047912 C CN 1047912C
- Authority
- CN
- China
- Prior art keywords
- content
- filler
- dispersant
- water repellent
- aluminum sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及的是植物纤维花盆及其生产方法,特别是用于苗木育苗一次性使用的可降解的植物纤维花盆及其生产方法,是以植物纤维草浆板为主要原料,配以改性剂处理,经真空吸附网模成形制成。生产工艺简单,成本低,可回收利用和自行降解,克服了烧制的泥制花盆在使用中的缺点,使用时可带盆直接移栽。
Description
本发明涉及的是植物纤维花盆及其生产方法,特别是用于苗木育苗一次性使用的可降解的植物纤维花盆及其生产方法,是以植物纤维草浆板为主要原料,配以改性剂处理,经真空吸附网模成形制成。
目前,苗木栽培和种养所使用的花盆都是烧制的泥盆,这种烧制的泥盆虽然其能满足使用要求,但对于苗木栽培应用来说并非理想,特别是在育苗期,苗木移盆移栽时,需要把苗木带培植土从泥盆中移出,这不仅费时费力,而且容易造成花盆破碎,培植土散失,损伤苗木的根须,影响苗木成活和活力,对圆艺工作者来说不仅劳动强度大,也很麻烦,并且泥盆育苗损耗大,成本高。
本发明的目的是提供一种植物纤维花盆及其生产方法,特别是用于苗木育苗一次性使用的可降解的植物纤维花盆及其生产方法。
本发明以草浆板为主要原料,配以改性剂处理,经真空吸附网模成形制成,形成植物纤维制成的可回收利用和自然降解的花盆。
本发明植物纤维花盆组成即原料配比组成为:(重量比)
草浆∶抗水剂∶填充剂∶分散剂∶沉淀剂=100∶3.5-5.5∶7-9∶0.3∶6-9
本发明植物纤维花盆生产工艺方法包括:
1、碎浆:草浆原料水力碎浆机碎浆;
2、磨浆:磨浆机磨浆;
3、调浆处理:加入抗水剂、填充剂、分散剂、沉淀剂,浆料打浆度(或称叩解度)40-42°SR,调浆料浓度0.5-0.8%,PH值6.0-6.4;
4、真空吸附网模成形:真空滤网模成型机成形,网目50-65目;
5、干燥处理;干燥箱干燥,干燥温度60-110℃,开始时在30-40℃烘30分钟,然后升至110℃,产品干度80-85%;
6、定形处理:模压定形;
7、模切:得成品。
本发明草浆原料为漂白亚硫酸盐草浆(GB3148-82)。
本发明抗水剂包括氧化淀粉液、分散松香胶、516树酯(三聚氰胺甲醛树脂)。填充剂为滑石粉。分散剂为尿素。沉淀剂为硫酸铝。产品降解度的控制是由调浆处理时所加入的抗水剂来调整。
实施例1:
原料配比;草浆板100kg、含量50%的分散松香胶6kg(松香3kg)、含量10%的氧化淀粉液25kg(淀粉2.5kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液45kg(硫酸铝9kg)。按前述生产方法工艺进行生产,在调浆处理时将抗水剂、填充剂、分散剂依次或一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。
实施例2:
原料配比;草浆板100kg、含量50%的分散松香胶4kg(松香2kg)、含量10%的氧化淀粉液10kg(淀粉1.0kg)、含量50%的516树脂溶液1.0kg(516树酯0.5kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液30kg(硫酸铝6kg)。按前述生产方法工艺进行生产,在调浆处理时将抗水剂、填充剂、分散剂依次可一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。
实施例3:
原料配比;草浆板100kg、含量50的分散松香胶4kg(松香2kg)、含量10%的氧化淀粉液10kg(淀粉1.0kg)、含量50%的516树脂溶液2.0kg(516树酯1kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液30kg(硫酸铝6kg)。按前述生产方法工艺进行生产,在调浆处理时将抗水剂、填充剂、分散剂依次或一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。
本发明生产工艺简单,主原料植物纤维完全采用草浆,价格便易,成本低,可生产制做各种形状的花盆,特别是用于苗木育苗一次性使用的可降解的植物纤维花盆,可自行降解,不污染环境,克服了烧制的泥制花盆在使用中的缺点,使用时可带盆直接移栽,本植物纤维花盆重量轻,价格低,是泥盆重量的十五分之一,价格低于泥盆一半。另外本生产方法还可用来生产用于仪器、仪表等物品的包装容器制品,替代泡沫塑料包装物,可回收利用和自行降解。
Claims (5)
1、植物纤维花盆,其特征在于其组成配比为:(重量比)
草浆∶抗水剂∶填充剂∶分散剂∶沉淀剂=100∶3.5-5.5∶7-9∶0.3∶6-9
草浆原料为漂白亚硫酸盐草浆(GB3148-82);抗水剂包括氧化淀粉、分散松香胶、516树酯;填充剂为滑石粉;分散剂为尿素;沉淀剂为硫酸铝。
2、根椐权利要求1所述的植物纤维花盆的生产方法,其特征是:
原料组成配比为:
草浆∶抗水剂∶填充剂∶分散剂∶沉淀剂=100∶3.5-5.5∶7-9∶0.3∶6-9
草浆原料为漂白亚硫酸盐草浆;抗水剂包括氧化淀粉、分散松香胶、516树酯;填充剂为滑石粉;分散剂为尿素;沉淀剂为硫酸铝;
生产工艺方法为:
(1)碎浆:草浆原料水力碎浆机碎浆;
(2)磨浆:磨浆机磨浆;
(3)调浆处理:加入抗水剂、填充剂、分散剂、沉淀剂,浆料打浆度40-42°SR,调浆料浓度0.5=0.8%,PH值6.0-6.4;
(4)真空吸附网模成形:真空滤网模成型机成形,网目50-65目;
(5)干燥处理:干燥箱干燥,干燥温度60-110℃,开始时在30-40℃烘30分钟,然后升至110℃,产品干度80-85%;
(6)定形处理:模压定形;
(7)模切:得成品。
3、根椐权利要求2所述的植物纤维花盆的生产方法,其特征是:
原料配比为:草浆板100kg、含量50%的分散松香腔6kg(松香3kg)、含量10%的氧化淀粉液25kg(淀粉2.5kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液45kg(硫酸铝9kg);在调浆处理时将抗水剂、填充剂、分散剂依次或一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。
4、根据权利要求2所述的植物纤维花盆的生产方法,其特征是:
原料配比为:草浆板100kg、含量50%的分散松香胶4kg(松香2kg)、含量10%的氧化淀粉液10kg(淀粉1.0kg)、含量50%的516树脂溶液1.0kg(516树酯0.5kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液30kg(硫酸铝6kg);在调浆处理时将抗水剂、填充剂、分散剂依次可一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。
5、根椐权利要求2所述的植物纤维花盆的生产方法,其特征是:
原料配比为:草浆板100kg、含量50%的分散松香胶4kg(松香2kg)、含量10%的氧化淀粉液10kg(淀粉1.0kg)、含量50%的516树脂溶液2.0kg(516树酯1kg)、含量30%的滑石粉液26.7kg(滑石粉8kg)、含量10%的尿素溶液3.0kg(尿素0.3kg)、含量20%的硫酸铝溶液30kg(硫酸铝6kg);在调浆处理时将抗水剂、填充剂、分散剂依次或一同加入浆液中搅拌均匀,再加入沉淀剂并搅拌均匀。