CN104755647B - 热镀锌钢板 - Google Patents

热镀锌钢板 Download PDF

Info

Publication number
CN104755647B
CN104755647B CN201380056703.XA CN201380056703A CN104755647B CN 104755647 B CN104755647 B CN 104755647B CN 201380056703 A CN201380056703 A CN 201380056703A CN 104755647 B CN104755647 B CN 104755647B
Authority
CN
China
Prior art keywords
hot
less
galvanized layer
steel plate
dip galvanizing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201380056703.XA
Other languages
English (en)
Chinese (zh)
Other versions
CN104755647A (zh
Inventor
铃木善继
宫田麻衣
长泷康伸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Engineering Corp
Original Assignee
NKK Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NKK Corp filed Critical NKK Corp
Publication of CN104755647A publication Critical patent/CN104755647A/zh
Application granted granted Critical
Publication of CN104755647B publication Critical patent/CN104755647B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Coating With Molten Metal (AREA)
CN201380056703.XA 2012-10-31 2013-10-21 热镀锌钢板 Active CN104755647B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012-239974 2012-10-31
JP2012239974A JP5825244B2 (ja) 2012-10-31 2012-10-31 溶融亜鉛めっき鋼板
PCT/JP2013/006202 WO2014068889A1 (ja) 2012-10-31 2013-10-21 溶融亜鉛めっき鋼板

Publications (2)

Publication Number Publication Date
CN104755647A CN104755647A (zh) 2015-07-01
CN104755647B true CN104755647B (zh) 2016-10-26

Family

ID=50626841

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201380056703.XA Active CN104755647B (zh) 2012-10-31 2013-10-21 热镀锌钢板

Country Status (7)

Country Link
JP (1) JP5825244B2 (es)
KR (1) KR101718469B1 (es)
CN (1) CN104755647B (es)
IN (1) IN2015DN02531A (es)
MX (1) MX348834B (es)
TW (1) TWI511875B (es)
WO (1) WO2014068889A1 (es)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5678951B2 (ja) * 2012-12-27 2015-03-04 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板
DE102014112126A1 (de) * 2014-08-25 2016-02-25 Voestalpine Stahl Gmbh Mikrolegierter Stahl und zusammengesetzte Platinen aus mikrolegiertem Stahl und pressgehärtetem Stahl
CN104195434B (zh) * 2014-09-22 2016-08-17 武汉钢铁(集团)公司 抗拉强度390MPa级轿车内部结构件用热镀锌高强钢及其生产方法
WO2016059742A1 (ja) * 2014-10-17 2016-04-21 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板
WO2016059743A1 (ja) * 2014-10-17 2016-04-21 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板
KR101897054B1 (ko) * 2014-10-17 2018-09-10 제이에프이 스틸 가부시키가이샤 고강도 용융 아연 도금 강판
CN106319416B (zh) * 2016-11-11 2018-11-23 攀钢集团攀枝花钢钒有限公司 一种热镀铝锌钢板锌花尺寸的控制方法
CN106521522B (zh) * 2016-11-11 2018-12-28 攀钢集团攀枝花钢钒有限公司 一种生产具有均匀锌花尺寸热镀铝锌钢板的方法
JP6835104B2 (ja) * 2017-01-26 2021-02-24 日本製鉄株式会社 めっき鋼線、スチールコード及びゴム−めっき鋼線複合体
JP6772930B2 (ja) * 2017-03-30 2020-10-21 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板および溶融亜鉛めっき鋼板の製造方法
TWI628310B (zh) * 2017-08-08 2018-07-01 中國鋼鐵股份有限公司 High-strength lubricating galvanized steel sheet and manufacturing method thereof
CN110629000A (zh) * 2018-06-25 2019-12-31 上海梅山钢铁股份有限公司 屈服强度280MPa级冷轧热镀锌钢板及其制造方法

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6372296B2 (en) * 1999-05-21 2002-04-16 University Of Cincinnati High aluminum galvanized steel
JP2002173754A (ja) * 2000-09-29 2002-06-21 Kawasaki Steel Corp 溶融亜鉛めっき鋼板およびその製造方法
JP3646685B2 (ja) * 2000-09-29 2005-05-11 Ｊｆｅスチール株式会社 スポット溶接性に優れた溶融亜鉛めっき鋼板およびその製造方法
JP4934946B2 (ja) 2003-03-28 2012-05-23 Ｊｆｅスチール株式会社 スポット溶接性及びプレス加工時の摺動性に優れた自動車用溶融亜鉛めっき鋼板の製造方法
EP2009127A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation
CN100591794C (zh) * 2008-07-31 2010-02-24 攀钢集团研究院有限公司 热镀锌钢板的镀锌方法
DE112009001879B4 (de) * 2008-07-30 2014-08-28 Pangang Group Panzhihua Iron & Steel Research Institute Co., Ltd. Produktionsverfahen für eine feuerverzinkte Stahlplatte
KR20100034118A (ko) * 2008-09-23 2010-04-01 포항공과대학교 산학협력단 마르텐사이트 조직을 가진 초고강도 용융아연도금 강판 및 그 제조 방법
WO2011161833A1 (ja) * 2010-06-21 2011-12-29 新日本製鐵株式会社 耐加熱黒変性に優れた溶融ａ１めっき鋼板及びその製造方法
CA2850094C (en) * 2011-09-30 2015-10-13 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet

Also Published As

Publication number Publication date
TW201434617A (zh) 2014-09-16
IN2015DN02531A (es) 2015-09-11
JP2014088605A (ja) 2014-05-15
WO2014068889A1 (ja) 2014-05-08
KR20150060904A (ko) 2015-06-03
TWI511875B (zh) 2015-12-11
CN104755647A (zh) 2015-07-01
JP5825244B2 (ja) 2015-12-02
MX348834B (es) 2017-06-30
MX2015005403A (es) 2015-08-05
KR101718469B1 (ko) 2017-03-21

Similar Documents

Publication Publication Date Title
CN104755647B (zh) 热镀锌钢板
CN104968824B (zh) 热镀锌钢板
JP5650222B2 (ja) 腐食に対する保護を与える金属コーティングが施された鋼部材を製造する方法、および鋼部材
JP6004102B2 (ja) ホットスタンプ成形体およびホットスタンプ成形体の製造方法
CN104838035B (zh) 热浸镀锌钢板
CN104040001B (zh) 合金化热镀锌钢板
CA2605486C (en) Hot dip galvannealed steel sheet and method of production of the same
CN110268088A (zh) 高强度热镀锌热轧钢板及其制造方法
CN107075653B (zh) 高强度热浸镀锌钢板
CN106795612B (zh) 高强度热浸镀锌钢板
JP7321370B2 (ja) 加工性及び耐食性に優れたアルミニウム系合金めっき鋼板及びその製造方法
JP2020041175A (ja) 熱間プレス用鋼板
CN114761602B (zh) 加工性和耐蚀性优异的铝基合金镀覆钢板及其制造方法
KR20120134709A (ko) 알루미늄계 도금층을 포함하는 용융 도금 강판 및 그 제조 방법
CN105274301B (zh) 一种屈服强度≥220MPa铁锌合金镀层钢板的生产方法
JP3643559B2 (ja) 加工性と加工部耐食性に優れた表面処理鋼板及びその製造方法
JP2000096262A (ja) 耐黒変性に優れた溶融亜鉛めっき鋼板およびその製造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant