CN1047400C - Prodn process of color-flame candle - Google Patents
Prodn process of color-flame candle Download PDFInfo
- Publication number
- CN1047400C CN1047400C CN95111973A CN95111973A CN1047400C CN 1047400 C CN1047400 C CN 1047400C CN 95111973 A CN95111973 A CN 95111973A CN 95111973 A CN95111973 A CN 95111973A CN 1047400 C CN1047400 C CN 1047400C
- Authority
- CN
- China
- Prior art keywords
- threads
- candle
- color
- candle body
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a daily household article, particularly to a manufacturing method of a colored flame candle. A candle wick is prepared by dipping pure cotton threads, ester threads or artificial fibre mixture threads in an ethanol solution or a water solution of a halide, an organic compound, an oxide and a hydroxide of coloring metal, such as Li, Na, K, Sr, Cu, Co, Cr, etc., drying the pure cotton threads, the ester threads or the artificial fibre mixture threads, plating perfume and coating a layer of main combustion agent formed by mixing ethyl carbamate, trimethyl citrate, hard acid perfume and a candle body. A colored flame which is brilliant and flowery during combustion simultaneously emits aromatic odor.
Description
The present invention relates to daily living article, particularly relate to a kind of manufacture method of color flame candles.
Current candle as illumination, its flame presents a kind of single yellow, though different modeling, price are lower, can't satisfy the pursuit of the growing U.S. of people in the modern life.For improving the enjoyment of people to U.S., many in recent years people are being devoted to invent a kind of color flame candles, only since 1986, disclosed on domestic " patent of invention " communique just have an application about the color flame candles patent surplus in the of 20, for example: number of patent application is 86105303,88108610.X, 88108720.3,91106031.6,89101946.4,89106515.6,90101749,91105492.8,91111832.2,92106266.1,921078028.X, 93111850.6,94102000.2, in the above-mentioned patent application, promptly there is liquid color flame candles that the solid state color flame candle is also arranged, its prescription and manufacture method respectively possess some good points, but it is many all to exist used chemical reagent kind, the production cost height, technical process is long, the lead nitrate that mixes some harmful health of human body that also has, reagent such as methyl alcohol, therefore, limited the commercialization of color flame candles.
The objective of the invention is to propose a kind of with candle wick dip treating in the ethanolic soln of color development metal Li, Na, K, Sr, Cu, halogenide such as Co, Cr, organic compound, oxide compound, oxyhydroxide or the aqueous solution, to light up and add urethanum, trimethyl citrate in the body, make a kind of candle that can send coloured flame, make it to reach and reduce cost, simplify technology, the purpose of effect excellence.
The objective of the invention is to be achieved through the following technical solutions:
Candle wick is textile line, ester line or regenerated fiber union twist yarn, in the ethanolic soln of the halogenide of color development metal such as Li, Na, K, Sr, Cu, Co, Cr etc., organic compound, oxide compound, oxyhydroxide or the aqueous solution, flood dry and spraying plating spices and be coated with one deck main fuel and make; Main fuel is mixed with the candle body mutually by urethanum, trimethyl citrate, stearic acid spices to be formed; Above-mentioned blended candle body raw material melts in 60-80 ℃ of water-bath, makes the technology of candle routinely and casts different shape candle body; This finished product adopts vacuum sealed package.
Advantage of the present invention and positively effect are:
The color flame candles that the present invention is given is made up of color development core and main fuel and an amount of essence, compares with existing technology, and is colored pure and bright-coloured, numerous in variety; All coloured flame only need be with a kind of main fuel and the corresponding halogenide of a kind of color development metal, oxide compound, oxyhydroxide or organic compound.Do not need to add again other reagent, therefore, simple, the grasp easily of manufacture craft, the agents useful for same kind is few, cost of manufacture is low.
To provide embodiment below, the present invention will be further described:
[example]: the making method of blushed flame candle
20-30 is propped up, 20-25 root ester line or cotton thread or union twist yarn, impregnated in 60-90min in the lithium halide ethanolic soln of 15-25% at normal temperatures, the taking-up nature dries or is dry in 40-90 ℃ of baking oven, then from 45-57 ℃ of molten state urethanum by back spraying plating essence, dry the back the color development core place standby.With weight ratio is that 96-98% main fuel and 2-4% stearic acid consolute in 45-70 ℃ of water-bath makes temperature reduce to 47-50 ℃ and uses the wax-pattern cast molding till the fusant clarification, is finished product.
The making method of flame candles such as other colours such as green, yellow, blue, purple, oyster white is described identical with last example 1, just selects for use with the corresponding chromogenic reagent of color to get final product.
Claims (1)
1. the manufacture method of color flame candles, it is characterized in that candle wick is textile line, ester line or regenerated fiber union twist yarn, in the ethanolic soln of the halogenide of color development metal Li, Na, K, Sr, Cu, Co, Cr, organic compound, oxide compound, oxyhydroxide or the aqueous solution, flood dry and spraying plating spices and be coated with one deck main fuel and make; Main fuel is that urethanum mixes with stearic acid spices and candle body mutually with trimethyl citrate, wherein urethanum and trimethyl citrate account for 96%-98%, stearic acid perfumes comprise 2%-4%, above-mentioned blended candle body raw material melts in 60-80 ℃ of water-bath casts the candle body.