CN107523425A - A kind of method for production of colorful flame candle - Google Patents
A kind of method for production of colorful flame candle Download PDFInfo
- Publication number
- CN107523425A CN107523425A CN201710833020.0A CN201710833020A CN107523425A CN 107523425 A CN107523425 A CN 107523425A CN 201710833020 A CN201710833020 A CN 201710833020A CN 107523425 A CN107523425 A CN 107523425A
- Authority
- CN
- China
- Prior art keywords
- wick
- water
- candle
- preparation
- dissolved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of method for production of colorful flame candle.Prepare colour former；Prepare color development wick；Prepare burning wick；The preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development wicks it is parallel be placed on burning wick both sides, urethanes is poured into mould, octagon candle is obtained after cooling.A kind of method for production of colorful flame candle of the present invention, production method is simple, raw material sources are extensive, and cost is low, and the flame of various colors can be produced after colorful flame candle point, and the volatile materials pettiness given off, the health of people and animals will not be damaged, be suitable for family, restaurant's decoration is used, the problem of luminous face color is single is compensate for, is the ideal in celebrating place.
Description
Technical field
The present invention relates to a kind of method for production of colorful flame candle, belong to colorful flame candle technical field.
Background technology
Candle kind at present on domestic and international market is more, but raw material is all paraffin, and its moulding is different with wax body color, and
Flame is single glassy yellow.A kind of pioneering brightness in China is big, easily light, flame color and luster is plentiful gorgeous and it is red to send,
The light such as green, yellow, purple.It is placed in glass container, is usually a kind of exquisite ornament, multicoloured fire can be sent after lighting
Flame, to the preferable celebrating use in the public place of entertainment such as beautification people's lives, particularly festivals or holidays, birthday, dinner party and hotel, dance hall
Product.
Candle kind at present on domestic and international market is more, but raw material is all paraffin, and its moulding is different with wax body color, and
Flame is single glassy yellow.
The content of the invention
In view of this, the present invention is a kind of colorful flame candle and production method, and it is the villaumite for utilizing the metals such as lithium, potassium, copper,
Sent at certain temperature made of different colours flame principle.The present invention is made up of candle body and candle wick, wherein, candle body is with ammonia
Base ester class organic compound is matrix, incorporation 1-1.5% (weight) metal chloride composition.Production method of the present invention is simple,
Raw material sources are extensive, and cost is low, and the flame of various colors can be produced after colorful flame candle point, and the volatile materials pettiness given off,
The health of people and animals will not be damaged, be suitable for family, restaurant's decoration is used.It is single that the present invention effectively compensate for luminous face color
Problem, it is the ideal in celebrating place.
The present invention solves above-mentioned technical problem by following technological means, and a kind of method for production of colorful flame candle, it is following
Step：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2-3mm, 65-75 DEG C of urethanes then poured into mould, after cooling
Obtain octagon candle.
Platinum catalyst powder 0.01-0.02g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Its conformal intensity of the present invention is high, and exterior of commodity is good, sends gorgeous colored flare during burning.Also can be by above-mentioned
Method is placed in cup, and different colorful flame candle is made in the mould of each flower-shape, cylinder.
The beneficial effects of the invention are as follows：Production method is simple, and raw material sources are extensive, and cost is low, can be produced after colorful flame candle point
The flame of various colors, and the volatile materials pettiness given off, will not damage to the health of people and animals, be suitable for family,
Restaurant's decoration is used, and compensate for the problem of luminous face color is single, is the ideal in celebrating place.
Embodiment
Below with reference to specific embodiment, the present invention is described in detail, a kind of side of manufacturing of colorful flame candle of the present embodiment
Method, it is following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2-3mm, 65-75 DEG C of urethanes then poured into mould, after cooling
Obtain octagon candle.
Platinum catalyst powder 0.01-0.02g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Embodiment 1
A kind of method for production of colorful flame candle, it is following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2.1mm, 69 DEG C of urethanes then poured into mould, after cooling
To octagon candle.
Platinum catalyst powder 0.015g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Embodiment 2
A kind of method for production of colorful flame candle, it is following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2.5mm, 71 DEG C of urethanes then poured into mould, after cooling
To octagon candle.
Platinum catalyst powder 0.017g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Embodiment 3
A kind of method for production of colorful flame candle, it is following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2.9mm, 72 DEG C of urethanes then poured into mould, after cooling
To octagon candle.
Platinum catalyst powder 0.019g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Embodiment 4
A kind of method for production of colorful flame candle, it is following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, gathered
The mass ratio of the alcohol and water of vinethene two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, in the solution
Add alumina powder and stir, add hydrazine and sodium hydroxide to stir, then plus water places a night, makes the alumina powder of precipitation
It is separated from water, obtains platinum catalyst powder, chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water is 0.1：5：
0.2：0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, is immersed in colour former, then at 120 DEG C
Under enter drying, be so repeated 3 times, 2 grams of colour formers adhered to per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75
Copolymer is formed, is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then
Take out and air-dry, color development wick is made；
(4) preparation of burning wick, after being twisted with No. 20 3, cotton threads, it is immersed in and is dissolved in 5 liters by 1 gram of platinum catalyst powder
In prepared by water solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development lamps
Stamen it is parallel be placed on burning wick both sides, be spaced 2.2mm, 74 DEG C of urethanes then poured into mould, after cooling
To octagon candle.
Platinum catalyst powder 0.011g in every meter of burning wick in the step (4).
The volume of octagon silicon rubber mould is 600mL, octagonal a length of 42mm per one side.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of technical solution of the present invention, it all should cover at this
Among the right of invention.
Claims (3)
1. a kind of method for production of colorful flame candle, it is characterised in that be following steps：
(1) preparation of colour former, lithium chloride, polyvinylether glycol is dissolved in the water and obtain colour former, lithium chloride, polyethylene
The mass ratio of the alcohol and water of ether two is 12：0.1：87；
(2) preparation of oxidation catalyst, the concentration for chloroplatinic acid being dissolved in water to chloroplatinic acid is 0.5g/L, is added in the solution
Alumina powder simultaneously stirs, and adds hydrazine and sodium hydroxide to stir, and then plus water places a night, makes the alumina powder and water of precipitation
Separation, obtains platinum catalyst powder, and chloroplatinic acid, alumina powder, hydrazine, the mass ratio of sodium hydroxide and water are 0.1：5：0.2：
0.1：2200；
(3) preparation of color development wick, wick is obtained with No. 20 3, cotton threads are twisted, immerses in colour former, then enters at 120 DEG C
Dry, be so repeated 3 times, adhere to 2 grams of colour formers per rice lamp core, vinyl acetate and ethene according to mass ratio 25：75 form
Copolymer, it is dissolved in trichloro ethylene, treatment fluid is made, the candle wick of attachment colour former is soaked 1 time in treatment fluid, then taken out
Air-dry, color development wick is made；
(4) burn the preparation of wick, with 3, No. 20 cotton threads it is twisted after, be immersed in 5 liters of water are dissolved in by 1 gram of platinum catalyst powder and
In obtained solution, by being drying to obtain；
(5) preparation of colorful flame candle finished product, burning wick is placed in octagon silicon rubber mould center, then two color development wicks is put down
Capable is placed on burning wick both sides, is spaced 2-3mm, 65-75 DEG C of urethanes then is poured into mould, obtained after cooling
Octagon candle.
A kind of 2. method for production of colorful flame candle according to claim 1, it is characterised in that：Every meter of combustion in the step (4)
Burn platinum catalyst powder 0.01-0.02g in wick.
A kind of 3. method for production of colorful flame candle according to claim 1, it is characterised in that：The appearance of octagon silicon rubber mould
Product is 600mL, octagonal a length of 42mm per one side.