CN102382718A - LED (Light Emitting Diode) color glittery candle cup and production process thereof - Google Patents
LED (Light Emitting Diode) color glittery candle cup and production process thereof Download PDFInfo
- Publication number
- CN102382718A CN102382718A CN2011102758814A CN201110275881A CN102382718A CN 102382718 A CN102382718 A CN 102382718A CN 2011102758814 A CN2011102758814 A CN 2011102758814A CN 201110275881 A CN201110275881 A CN 201110275881A CN 102382718 A CN102382718 A CN 102382718A
- Authority
- CN
- China
- Prior art keywords
- wax
- candle
- optical fiber
- cup
- led
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an LED (Light Emitting Diode) color glittery candle cup and a production process thereof, wherein a traditional candle structure is modified, a light-triggered switch is taken as a switch of an electronic lightening component, the switching on and off of the electronic lightening component are controlled directly by candle lights, and the switching on and off of a lightening diode do not need to be manually operated, thus the use of the LED color glittery candle cup is convenient. An optical fiber of the LED color glittery candle cup is combusted along with the combustion of a combustion core, is not left on a combustion end surface of the candle cup and does not influence the ornamental and the decorative. A coating outside the optical fiber prevents the optical fiber from being corroded, can reduce the sensitivity of the optical fiber to lights and prevents other natural lights from triggering and switching on the electronic lightening component. A cotton pad below a circuit board is used for preventing a welding point from being broken due to puncture. Anti-flaming sleeves of the optical fiber and the lower part of the combustion core have a fixing function and also have an anti-flaming function so as to prevent the damage caused by combustion and explosion of the electronic lightening component because the electronic lightening component at the bottom of a candle body is combusted when the combustion core of the candle cup is combusted to the end.
Description
Technical field
The present invention relates to a kind of glass of wax and production technique thereof, especially relate to a kind of LED colour flash cup wax and production technique thereof that has illumination and decorative effect simultaneously, belong to the daily living article field.
Background technology
Candle prolongs with getting off as a kind of traditional lighting apparatus always, and moreover, people also are used for many celebrating occasions to candle, like birthday party, variety show, various red-letter day, to increase its celebrating atmosphere; People also like occasion that candle is used to have good luck.The candle light that sends that various in the market candles only are confined to candle after lighting; Supply to use in the various occasion; The kind of candle and structure are comparatively single, also have candle body is dyed shades of colour, perhaps adopt electric candle completely; Its flare is not the nature flame, is that the electronics flare is luminous.Along with development of science and technology and people's demand, a kind of electric light of imitative candle has appearred.But this candle lamp decoration simulated effect is not good enough, mainly exists following shortcoming " candle flame " to be in a kind of independent normal bright state or is not to be current under the normal bright state to go out when bright, and simulated effect is true to nature inadequately.
Summary of the invention
To the deficiency that prior art exists, technical problem to be solved by this invention is, a kind of LED colour flash cup wax and production technique thereof are provided, and solved the problem of existing candle function singleness and job insecurity, improved the security of candle use.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is a kind of LED colour flash cup wax; Its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin 30-99.7%; Paraffin nucleator 0.1-50%, high penetration degree vegetable wax 0.1-50%, candle stablizer 0.1-50%.
A kind of LED colour flash cup wax production technique, may further comprise the steps:
(1) take by weighing each raw material according to formula rate, with raw material according to the fusing of heating successively of the order of high penetration degree paraffin, paraffin nucleator, high penetration degree vegetable wax, candle stablizer;
(2) stirred in 5-10 minute with the whisking appliance stirring, change wax liquid over to the insulation groove;
(3) make the wax post: take out the wax liquid that makes in the part steps (2), be poured into mould, mold material is acrylic or cast aluminium or stainless steel here, and dimensional requirement is than the little 2-3cm of end article;
(4) optical fiber is inserted in the plastic casing of electronic emitters, optical fiber is tightly touched on the photo-sensitive cell of LED lamp; With fire-retardant cover is the bottom that metal sleeve is set to plastic casing, and the metal sleeve material is aluminium or aluminizes or copper here, wick is also inserted in the metal tube again, then metal tube is clamped;
(5) element that will go up after a step assembles is set in the wax post, lets wick and optical fiber through the hole on the wax post;
(6) with the ready wax liquid of step (2), temperature is controlled at 90-100 ℃, in glass cylinder, pours into wax liquid, gets final product after the cooling.
Optimize, above-mentioned LED colour flash cup wax production technique, its step (2) keeps homo(io)thermism.
Optimize, above-mentioned LED colour flash cup wax production technique, in its step (3), exceed very thin one deck when pouring into wax liquid earlier when making the wax post, cooled off 10-15 minute, mend one deck 85-95 ℃ of wax liquid again, cooled off again 15-20 minute.
Optimize, above-mentioned LED colour flash cup wax production technique, wax post bottom is smooth in its step (5), the LED lamp housing does not expose the wax post.
Optimize, above-mentioned LED colour flash cup wax production technique, stir once more before in its step (6) the wax liquid that stirs being shifted.
Optimize, above-mentioned LED colour flash cup wax production technique, prune optical fiber in its step (6) after the cooling again to being 0-3mm apart from the liquid level distance.
The candle of manufacturing of the present invention improves on traditional candle structure, owing to adopt the switch of light trigger switch as electronic emitters, and directly with the break-make of candle light control electronic emitters, shutoff that must the manual operation photodiode, easy to use; Its optical fiber burns along with the burning of combustion core, can not remain on the candle combustion end face, can not influence its sight and ornamental; Use candle body that the prescription of wax liquid of the present invention makes and wax post transparence just in time, make the luminous energy of candle combustion see through optical fiber, other natural lights then can not see through optical fiber and then trigger the connection electronic emitters; The candle of fusing drips to table top and contaminate environment when adopting glass cylinder can not cause burning in addition, and making full use of candle does not again waste; And the photodiode of emitting electron spare can send colored light when candle is lighted; Make the candle body present the dim effect of seven color conversions; Decoration function is very good, give the intensive aesthetic feeling, has increased the happy atmosphere of family, public place of entertainment and occasion in various different red-letter day; The existing fixed action of fire-retardant cover of optical fiber and combustion core bottom plays a part fire-retardant again, prevents that combustion core when candle is burned to ignite when last to be positioned at the electronic emitters bottom the candle body, causes firing of electronic emitters and causes danger.
Embodiment
Embodiment 1
The present invention is a kind of LED colour flash cup wax, and its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin, like 56# paraffin 30%; The paraffin nucleator is like Microcrystalline Wax 50%; High penetration degree vegetable wax is like soya wax 10%; The candle stablizer is like polyvinyl resin 10%.
A kind of LED colour flash cup wax production technique, may further comprise the steps:
(1) take by weighing each raw material according to formula rate, with raw material according to the fusing of heating successively of the order of high penetration degree paraffin, paraffin nucleator, high penetration degree vegetable wax, candle stablizer;
(2) stirred in 5-10 minute with the whisking appliance stirring, change wax liquid over to the insulation groove, keep homo(io)thermism;
(3) make the wax post: take out the wax liquid that makes in the part steps (2); Be poured into mould, exceed very thin one deck when pouring into wax liquid earlier, cooled off 10-15 minute; Mend one deck 85-95 ℃ of wax liquid again; Cooled off 15-20 minute, mold material is acrylic or cast aluminium or stainless steel here again, and dimensional requirement is than the little 2-3cm of end article;
(4) optical fiber is inserted in the plastic casing of electronic emitters, optical fiber is tightly touched on the photo-sensitive cell of LED lamp; Metal sleeve is set to the bottom of plastic casing, and the metal sleeve material is aluminium or aluminizes or copper here, wick is also inserted in the metal tube again, then metal tube is clamped;
(5) element that will go up after a step assembles is set in the wax post, lets wick and optical fiber through the hole on the wax post, and wax post bottom is smooth, and the LED lamp housing does not expose the wax post;
(6) with the ready wax liquid of step (2), temperature is controlled at 90-100 ℃, stirs once more, in glass cylinder, pours into wax liquid, prunes optical fiber after the cooling again to getting final product for 0-3mm apart from the liquid level distance.
Embodiment 2
Identical no longer tired the stating of part among present embodiment and the embodiment 1, difference is: the present invention is a kind of LED colour flash cup wax, its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin; Like 58# paraffin 99.7%, the paraffin nucleator is like Triple Pressed Stearic Acid 0.1%; High penetration degree vegetable wax; Like palm wax 0.1%, the candle stablizer is like acrylic resin 0.1%.
Embodiment 3
Identical no longer tired the stating of part among present embodiment and the embodiment 1, difference is: the present invention is a kind of LED colour flash cup wax, its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin, like 56# paraffin 50%; The paraffin nucleator is like ethene-vinyl acetate copolymer resins 10%; High penetration degree vegetable wax is like soya wax 20%; The candle stablizer is like polyvinyl resin 20%.
Embodiment 4
Identical no longer tired the stating of part among present embodiment and the embodiment 1, difference is: the present invention is a kind of LED colour flash cup wax, its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin; Like 58# paraffin 30%, the paraffin nucleator is like Triple Pressed Stearic Acid 5%; High penetration degree vegetable wax; Like palm wax 50%, the candle stablizer is like acrylic resin 15%.
Embodiment 5
Identical no longer tired the stating of part among present embodiment and the embodiment 1, difference is: the present invention is a kind of LED colour flash cup wax, its wax liquid is processed by the raw material of following weight ratio: high penetration degree paraffin, like 56# paraffin 30%; The paraffin nucleator is like ethene-vinyl acetate copolymer resins 10%; High penetration degree vegetable wax is like soya wax 10%; The candle stablizer is like polyvinyl resin 50%.
The above only is to preferred embodiment of the present invention, is not to be that the present invention is done other forms of restriction, and any professional and technical personnel of being familiar with possibly utilize the technology contents of above-mentioned announcement to change or be modified as the equivalent embodiment of equivalent variations.But every the present invention program's content that do not break away to any simple modification, equivalent variations and remodeling that above embodiment did, still belongs to protection scope of the present invention according to technical spirit of the present invention.
Claims (7)
1. LED colour flash cup wax is characterized in that: the wax liquid of said cup wax is processed by the raw material of following weight ratio: high penetration degree paraffin 30-99.7%, paraffin nucleator 0.1-50%, high penetration degree vegetable wax 0.1-50%, candle stablizer 0.1-50%.
The described LED colour flash of claim 1 a cup wax production technique, may further comprise the steps:
(1) take by weighing each raw material according to formula rate, with raw material according to the fusing of heating successively of the order of high penetration degree paraffin, paraffin nucleator, high penetration degree vegetable wax, candle stablizer;
(2) stirred in 5-10 minute with the whisking appliance stirring, change wax liquid over to the insulation groove;
(3) make the wax post: take out the wax liquid that makes in the part steps (2), be poured into mould, mold material is acrylic or cast aluminium or stainless steel here, and dimensional requirement is than the little 2-3cm of end article;
(4) optical fiber is inserted in the plastic casing of electronic emitters, optical fiber is tightly touched on the photo-sensitive cell of LED lamp; Metal sleeve is set to the bottom of plastic casing, and the metal sleeve material is aluminium or aluminizes or copper here, wick is also inserted in the metal tube again, then metal tube is clamped;
(5) element that will go up after a step assembles is set in the wax post, lets wick and optical fiber through the hole on the wax post;
(6) with the ready wax liquid of step (2), temperature is controlled at 90-100 ℃, in glass cylinder, pours into wax liquid, gets final product after the cooling.
3. LED colour flash cup wax according to claim 2 production technique, it is characterized in that: described step (2) keeps homo(io)thermism.
4. LED colour flash cup wax according to claim 2 production technique; It is characterized in that: in the described step (3), exceed very thin one deck when pouring into wax liquid earlier when making the wax post, cooled off 10-15 minute; Mend one deck 85-95 ℃ of wax liquid again, cooled off again 15-20 minute.
5. LED colour flash cup wax according to claim 2 production technique, it is characterized in that: wax post bottom is smooth in the described step (5), and the LED lamp housing does not expose the wax post.
6. LED colour flash cup wax according to claim 2 production technique, it is characterized in that: stir once more before in the described step (6) the wax liquid that stirs being shifted.
7. LED colour flash cup wax according to claim 2 production technique, it is characterized in that: prune optical fiber in the described step (6) after the cooling again to being 0-3mm apart from the liquid level distance.