CN104725048A - 一种高强度石墨复合材料 - Google Patents
一种高强度石墨复合材料 Download PDFInfo
- Publication number
- CN104725048A CN104725048A CN201310702086.8A CN201310702086A CN104725048A CN 104725048 A CN104725048 A CN 104725048A CN 201310702086 A CN201310702086 A CN 201310702086A CN 104725048 A CN104725048 A CN 104725048A
- Authority
- CN
- China
- Prior art keywords
- high strength
- composite material
- powder
- graphite composite
- strength graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种高强度石墨复合材料。其技术方案是：在于原料组份重量百分比如下：1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%。其特征是：按重量百分比1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%，将上述原料混合；在2000-2500℃，压力为16-35MPa下热压成型，恒温时间为8-12分钟即可。本发明优点是具有高强度、较高热稳定性、较低电阻率、挥发份和热膨胀系数。
Description
技术领域
本发明提供了一种高强度石墨复合材料。
背景技术
石墨材料具有良好的导电性、低的热膨胀系数、耐热冲击性和热稳定性。因而被广泛用于化工、核能等领域。天然石墨与其它石油焦、沥青焦相比，具有较高热稳定性，较低电阻率、挥发份和热膨胀系数。
发明内容
本发明的目的根据以上优点来提供一种高强度石墨复合材料。其技术方案是：在于原料组份重量百分比如下：1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%。其特征是：按重量百分比1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%，将上述原料混合；在2000-2500℃，压力为16-35MPa下热压成型，恒温时间为8-12分钟即可。
本发明优点是具有高强度、较高热稳定性、较低电阻率、挥发份和热膨胀系数。
具体实施方式
下面结合实施例来说明。
实施例1：一种石墨复合材料，其特征在于原料组份重量百分比如下：1um天然石墨粉，40%，1Si粉3%，粘结剂20%。其特征是：按重量百分比1天然石墨粉，40%，1粉3%，粘结剂20%，将上述原料混合；在2000，压力为16MPa下热压成型，恒温时间为8分钟即可。
实施例2：一种石墨复合材料，其特征在于原料组份重量百分比如下： 60um天然石墨粉， 60%， 30Si粉5%，粘结剂30%。其特征是：按重量百分比60um天然石墨粉， 60%， 30Si粉5%，粘结剂30%，将上述原料混合；在2500℃，压力为35MPa下热压成型，恒温时间为12分钟即可。
Claims (2)
1.一种高强度石墨复合材料，其特征在于原料组份重量百分比如下：1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%。
2.根据权利要求1所述的一种高强度石墨复合材料，其特征是：按重量百分比1-60um天然石墨粉，40%-60%，1-30Si粉3%-5%，粘结剂20%-30%，将上述原料混合；在2000-2500℃，压力为16-35MPa下热压成型，恒温时间为8-12分钟即可。