CN104712113A - Anion painting method of wall surface - Google Patents
Anion painting method of wall surface Download PDFInfo
- Publication number
- CN104712113A CN104712113A CN201510067684.1A CN201510067684A CN104712113A CN 104712113 A CN104712113 A CN 104712113A CN 201510067684 A CN201510067684 A CN 201510067684A CN 104712113 A CN104712113 A CN 104712113A
- Authority
- CN
- China
- Prior art keywords
- cement
- mortar
- lime
- anion
- negative ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an anion painting method of a wall surface. The anion painting method of the wall surface comprises the first step of brushing a wall with neat cement, the second step of brushing the wall with cement lime mortar 13 mm thick for priming and brooming or drawing lines, the third step of brushing the wall with anion powder cement lime mortar 5 mm thick for top facing, compaction and finishing, wherein the anion powder cement lime mortar is a mixture of anion powder, cement, lime and mortar, and the mass ratio of the anion powder to the cement to the lime to the mortar is 0.2 to 1 to 0.3 to 2.5, and the fourth step of brushing the wall with latex paint; the anion powder in the third step comprises, by weight, 70 parts of tourmaline, 10-20 parts of neodymium oxide and 10-20 parts of tetraterbium heptaoxide. According to the anion painting method of the wall surface, the construction is simple and convenient, after painting the wall surface with the anion painting method, anions can be released continuously, formaldehyde is eliminated, air is purified, indoor air is refreshing, and the human health is facilitated.
Description
Technical field
The present invention relates to a kind of paint staining of metope, particularly relate to a kind of anion paint staining of metope.
Background technology
In all house decoration projects, painter's work is also a very important important stage, and it is also last procedure of hard dress.General painter's work is also the face-saving project in finishing, and painting technology is not only related to attractive in appearance, is also related to safe and sanitary.
Patent of invention CN103147543A discloses a kind of anion paint staining of concrete wall, is made up of following step: (1) brushes plain-water slurry on concrete wall; (2) brush 13mm solid cement lime mortar bottoming brooming or mark track; (3) 5mm thick negative ion powder cement lime mortar cover float finish is brushed; (4) brush blooming or emulsion paint; Cement lime mortar described in step (2) is the mixture of cement, lime and mortar, and wherein the mass ratio of cement, lime, mortar is 1:0.3:3; The mortar of negative ion powder cement lime described in step (3) is the mixture of negative ion powder, cement, lime and mortar, and wherein the mass ratio of negative ion powder, cement, lime, mortar is 0.2:1:0.3:2.5.The method anion effect is not remarkable.
Summary of the invention
For above shortcomings in prior art, technical problem to be solved by this invention is to provide a kind of anion paint staining of metope, and anion is respond well.
Technical problem to be solved by this invention, is achieved by the following technical solution:
The anion paint staining of metope, is made up of following step:
(1) plain-water slurry is brushed on the wall;
(2) brush 13mm solid cement lime mortar bottoming brooming or mark track, described cement lime mortar is the mixture of cement, lime and mortar, and wherein the mass ratio of cement, lime, mortar is 1:0.3:3;
(3) 5mm thick negative ion powder cement lime mortar cover float finish is brushed, described negative ion powder cement lime mortar is the mixture of negative ion powder, cement, lime and mortar, and wherein the mass ratio of negative ion powder, cement, lime, mortar is 0.2:1:0.3:2.5;
(4) brush emulsion paint;
Negative ion powder in described step (3), comprises the one in tourmaline, neodymia and terbium peroxide or its mixture.
Preferably, described negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, neodymia 10-20 part, terbium peroxide 10-20 part.
The present invention constructs simple and convenient, and after adopting method of the present invention to paint metope, sustainable anion releasing, eliminates formaldehyde, purify air, make indoor air pure and fresh pleasant, useful health.
Detailed description of the invention
Below by specific embodiment, the invention will be further described, but the present invention not limited by following examples.
Embodiment 1
The anion paint staining of metope, is made up of following step:
(1) plain-water slurry is brushed on the wall;
(2) brush 13mm solid cement lime mortar bottoming brooming or mark track, described cement lime mortar is the mixture of cement, lime and mortar, and wherein the mass ratio of cement, lime, mortar is 1:0.3:3;
(3) 5mm thick negative ion powder cement lime mortar cover float finish is brushed, described negative ion powder cement lime mortar is the mixture of negative ion powder, cement, lime and mortar, and wherein the mass ratio of negative ion powder, cement, lime, mortar is 0.2:1:0.3:2.5;
(4) brush emulsion paint;
In described step (3), negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, neodymia 15 parts, terbium peroxide 15 parts.
Embodiment 2
The anion paint staining of metope, with embodiment 1.
Difference is: described negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, neodymia 30 parts.
Embodiment 3
The anion paint staining of metope, with embodiment 1.
Difference is: described negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, terbium peroxide 30 parts.
Comparative example 1
The anion paint staining of metope, with embodiment 1.
Difference is: described negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, ceria 30 parts.
Comparative example 2
Chinese invention patent CN103147543A embodiment 2 is adopted to construct.
Test case:
" the JCT 2040-2010 anion function indoor decoration material " standard of employing, carry out negative aeroion and induce measurement examination, concrete test data is in table 1.
Table 1: negative aeroion induces and measures examination tables of data
| The negative aeroion amount of inducing, individual/s.cm 2 | |
| Embodiment 1 | 925 |
| Embodiment 2 | 805 |
| Embodiment 3 | 840 |
| Comparative example 1 | 895 |
| Comparative example 2 | 715 |
Comparing embodiment 1 and embodiment 2-3, tourmaline and neodymia and terbium peroxide composite, successful is better than tourmaline and neodymia is composite or tourmaline and terbium peroxide composite.
As the common practise of this area, nano titanium oxide, ceria, lanthana, oxidation are wrong, neodymia respectively with tourmaline compound, negative aeroion tells on as the strongest with the compound of ceria, terbium peroxide, lanthana effect are general, and neodymia, titanium oxide reduce the air-anion concentration that tourmaline produces on the contrary.But the present invention finds unexpectedly, comparing embodiment 1 and comparative example 1, adopt tourmaline and neodymia and terbium peroxide composite, effect is better than tourmaline and ceria is composite.
Claims (2)
1. the anion paint staining of metope, is made up of following step:
(1) plain-water slurry is brushed on the wall;
(2) brush 13mm solid cement lime mortar bottoming brooming or mark track, described cement lime mortar is the mixture of cement, lime and mortar, and wherein the mass ratio of cement, lime, mortar is 1:0.3:3;
(3) 5mm thick negative ion powder cement lime mortar cover float finish is brushed, described negative ion powder cement lime mortar is the mixture of negative ion powder, cement, lime and mortar, and wherein the mass ratio of negative ion powder, cement, lime, mortar is 0.2:1:0.3:2.5;
(4) brush emulsion paint;
Negative ion powder comprises one in tourmaline, neodymia and terbium peroxide or its mixture in described step (3).
2. the anion paint staining of metope as claimed in claim 1, it is characterized in that, described negative ion powder is made up of following weight parts raw material: 70 parts, tourmaline, neodymia 10-20 part, terbium peroxide 10-20 part.