CN104673471B - 一种可用作铝合金封存防护的铝合金切削液 - Google Patents
一种可用作铝合金封存防护的铝合金切削液 Download PDFInfo
- Publication number
- CN104673471B CN104673471B CN201310612921.9A CN201310612921A CN104673471B CN 104673471 B CN104673471 B CN 104673471B CN 201310612921 A CN201310612921 A CN 201310612921A CN 104673471 B CN104673471 B CN 104673471B
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- cutting fluid
- safekeeping
- aluminium alloy
- protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:pH调节剂2‑6%、乳化稳定剂6‑15%、天然润滑酯3‑6%、金属缓蚀剂1‑2%、酰胺1‑3%、磷酸酯1‑3%、抗硬水稳定剂1‑3%、助乳化剂3‑6%、基础油47‑59%、去离子水5‑13%。该铝合金切削液能够自动在铝合金表面形成一层金属保护膜,它可以迅速隔离开残留在铝合金表面的残渣和脏液,不会产生白斑,它可以使铝合金与空气隔绝,防止铝合金表面被氧化,并且长期成膜,可以保持很长一段时间不会被氧化,另外,提高了切削液的长期稳定性和抗菌性能。它在满足各种铝合金加工要求的同时,还能保持加工工件不变色,使用寿命长。
Description
技术领域
本发明具体是一种可用作铝合金封存防护的铝合金切削液。它是一种类似于防护油防护机理的多功能铝合金切削液,适用于各种型号的铝合金,并且加工后能保持长时间不变色,克服了传统的铝合金切削液加工后易氧化变色的缺点。
背景技术
目前有很多款加工铝合金的切削液,它们都能满足市场上的大多数的铝合金,但是每款针对的铝合金型号都是有区别的,因为铝合金里面组成和含量有区别的话,所需要应对的切削液也就需要随之改变,有些是针对6系列的铝,但是对于7系航空铝就没有办法克服不变色的现象,有些是针对3系列的铝,但是在加工ADC12的铝就满足不了加工要求,加工之后就会有变色现象,因此我们现在需要克服的是铝合金种类以及金属含量变化所带来的加工困难,我们需要的是一款能针对所有铝合金加工都能保持不变色,并且保持最佳的加工精度。
发明内容
本发明的目的在于提供一种可用作铝合金封存防护的铝合金切削液,它能够满足市场上绝大多数型号的铝合金,无需型号对应,一款解决所有铝合金加工问题,所谓封存防护铝合金切削液,是在工件加工完之后,它能够自动在铝合金表面形成一层金属保护膜,它可以迅速隔离开残留在铝合金表面的残渣和脏液,不会产生白斑,它可以使铝合金与空气隔绝,防止铝合金表面被氧化,并且可以保持很长一段时间不会被氧化,它针对的市面上各种型号的铝合金,能够在满足各种铝合金加工要求的同时,还能保持加工工件不变色,使用寿命长。
为实现上述目的,本发明提供如下技术方案:
一种可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:
pH调节剂 4%
乳化稳定剂 10%
天然润滑酯 6%
金属缓蚀剂 1.5%
酰胺 2.5%
磷酸酯 2.4%
抗硬水稳定剂 1.8%
助乳化剂 3.7%
基础油 57%
去离子水 11.1%。
作为本发明进一步的方案:所述可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:
pH调节剂 3.5%
乳化稳定剂 8%
天然润滑酯 4.6%
金属缓蚀剂 2%
酰胺 2.8%
磷酸酯 1.6%
抗硬水稳定剂 2.8%
助乳化剂 5.3%
基础油 57.5%
去离子水 11.9%。
作为本发明进一步的方案:所述pH调节剂包括多羟多胺类有机碱、无机碱;所述多羟多胺类有机碱包括三乙醇胺,所述无机碱包括氢氧化钾。
作为本发明进一步的方案:所述乳化稳定剂包括阴离子表面活性剂、多元醇系列。
作为本发明再进一步的方案:所述阴离子表面活性剂包括妥尔油酸、天然磺酸钠,所述多元醇包括16碳多元醇。
作为本发明进一步的方案:所述天然润滑酯为天然植物油酸酯,具有良好的润滑性能;所述天然植物油酸酯包括油酸三乙醇胺酯、丙二醇油酸酯。
作为本发明进一步的方案:所述金属缓蚀剂为含苯三唑衍生物复合剂,对有色金属具有优异的保护性能。
作为本发明再进一步的方案:所述含苯三唑衍生物复合剂包括甲基苯丙三氮唑。
作为本发明进一步的方案:所述酰胺为自制特殊抑菌高稳定型酰胺,对体系的稳定起着决定性因素,包括油酸二乙醇胺、炔基琥珀酰胺。
作为本发明进一步的方案:所述磷酸酯为自制高性能低成本磷酸酯,它对铝合金保护起着很大的作用,包括烷基磷酸酯、烷基聚氧乙烯醚亚磷酸单酯和烷基聚氧乙烯醚亚磷酸双酯。
作为本发明进一步的方案:所述抗硬水稳定剂包括醚羧酸,他能够对整个体系的长久抗硬水稳定性起到决定性的作用,包括醚羧酸。
作为本发明进一步的方案:所述助乳化剂能够使得酯类更容易乳化,并且能够更好的帮助上述乳化剂之间的配伍,使得体系更加的稳定,包括二乙二醇单丁醚、二丙二醇丁醚、二十一碳二元酸。
与现有技术相比,本发明的有益效果是:该铝合金切削液通过特殊乳化剂将酰胺、磷酸酯、表面活性剂、抗硬水稳定剂以及助乳化剂按特殊的配比调制,使得它具有优异的铝合金成膜性,能够自动在铝合金表面形成一层金属保护膜,它可以迅速隔离开残留在铝合金表面的残渣和脏液,不会产生白斑,它可以使铝合金与空气隔绝,防止铝合金表面被氧化,并且长期成膜,可以保持很长一段时间不会被氧化,另外,提高了切削液的长期稳定性和抗菌性能。它针对的市面上各种型号的铝合金,能够在满足各种铝合金加工要求的同时,还能保持加工工件不变色,使用寿命长。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
本发明实施例中,一种可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:
pH调节剂 3.5%
乳化稳定剂 8%
天然润滑酯 4.6%
金属缓蚀剂 2%
酰胺 2.8%
磷酸酯 1.6%
抗硬水稳定剂 2.8%
助乳化剂 5.3%
基础油 57.5%
去离子水 11.9%。
实施例2
本发明实施例中,一种可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:
pH调节剂 4%
乳化稳定剂 10%
天然润滑酯 6%
金属缓蚀剂 1.5%
酰胺 2.5%
磷酸酯 2.4%
抗硬水稳定剂 1.8%
助乳化剂 3.7%
基础油 57%
去离子水 11.1%。
实施例3
本发明实施例中,一种可用作铝合金封存防护的铝合金切削液,包括以下质量百分比的组分:
pH调节剂 6%
乳化稳定剂 15%
天然润滑酯 6%
金属缓蚀剂 2%
酰胺 3%
磷酸酯 3%
抗硬水稳定剂 2.5%
助乳化剂 4%
基础油 50%
去离子水 8.5%。
所述可用作铝合金封存防护的铝合金切削液的制备方法:按上述实施例所述的比例先将pH调节剂、金属缓蚀剂溶解在去离子水中,澄清透明后备用;将酰胺、磷酸酯、表面活性剂、抗硬水稳定剂以及助乳化剂调配好;最后将基础油、乳化稳定剂、天然润滑酯以及上述两种调好的液体混合加热至50℃使其充分反应均匀,最终得透明亮棕色液体,即得可用作铝合金封存防护的铝合金切削液。
所述可用作铝合金封存防护的铝合金切削液的使用方法:所得铝合金切削液按加工负荷来确定使用配比浓度,使用轻负荷加工时,铝合金切削液与水的配制比例为1:20,中等负荷至重负荷加工时,铝合金切削液与水的配制比例为7-10%。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种可用作铝合金封存防护的铝合金切削液,其特征在于,包括以下质量百分比的组分:
所述pH调节剂为多羟多胺类有机碱和无机碱;所述乳化稳定剂为阴离子表面活性剂和多元醇系列;所述天然润滑酯为天然植物油酸酯;所述金属缓蚀剂为含苯三唑衍生物复合剂;所述酰胺为油酸二乙醇胺和炔基琥珀酰胺;所述磷酸酯为烷基磷酸酯;所述抗硬水稳定剂为醚羧酸;所述助乳化剂为二乙二醇单丁醚、二丙二醇丁醚和二十一碳二元酸。
2.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,包括以下质量百分比的组分:
3.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,所述多羟多胺类有机碱为三乙醇胺,所述无机碱为氢氧化钾。
4.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,所述阴离子表面活性剂为妥尔油酸和天然磺酸钠,所述多元醇为16碳多元醇。
5.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,所述天然植物油酸酯为油酸三乙醇胺酯和丙二醇油酸酯。
6.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,所述含苯三唑衍生物复合剂为甲基苯丙三氮唑。
7.根据权利要求1所述的可用作铝合金封存防护的铝合金切削液,其特征在于,所述烷基磷酸酯为烷基聚氧乙烯醚亚磷酸单酯和烷基聚氧乙烯醚亚磷酸双酯。