CN104673139A - 汽车内饰和篷布环保粘合剂 - Google Patents
汽车内饰和篷布环保粘合剂 Download PDFInfo
- Publication number
- CN104673139A CN104673139A CN201310633542.8A CN201310633542A CN104673139A CN 104673139 A CN104673139 A CN 104673139A CN 201310633542 A CN201310633542 A CN 201310633542A CN 104673139 A CN104673139 A CN 104673139A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- friendly adhesive
- tarpaulin
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种汽车内饰和篷布环保粘合剂，其特征在于由组分A（主剂）(聚乙酸乙烯酯乳液70～90份、羧基丁苯胶乳15～25份和十二烷基笨磺酸钠0.5～2份)和组分B（交联剂）(多苯基多异氰酸酯80～100份和对甲苯磺酰氯5～15份)组成。本发明的胶粘剂具有良好的耐水性和耐热性，不产生化学残留和污染，对人体健康无害，可作为汽车内装饰和汽车篷布的胶粘剂。
Description
技术领域
本发明涉及一种胶粘剂，特别是一种汽车内饰和篷布环保粘合剂粘合剂，属于化学化工技术领域。
背景技术
汽车现今已愈发普遍，且我国汽车行业正以相当快的速度在发展，汽车数量不断上升，其辅助行业也正不断发展。汽车内饰和汽车篷布越来越广泛地被应用，过程中需使用胶粘剂，带动了胶粘剂行业的发展。但目前所使用的汽车内饰和篷布环保粘合剂胶粘剂刺激气味大，耐水性和耐热性差，不仅给人的身体健康带来了一定的威胁，而且给环境带来了压力，这使我们不得不正视胶粘剂的性能及安全性的问题。
本发明的汽车内饰和篷布环保粘合剂粘合剂所采用的原料易得，生产成本低廉，且具有良好的耐水性和耐热性，刺激气味小，不产生有害气体。
发明内容
本发明的目的在于克服现有技术的不足，提供一种具有良好耐水性和耐热性，刺激气味小，不产生有害气体的汽车内饰和篷布环保粘合剂粘合剂。
为了达到上述目的，本发明采取了如下技术方案：
一种汽车内饰和篷布环保粘合剂粘合剂，由组分A（主剂）【聚乙酸乙烯酯乳液70～90份、羧基丁苯胶乳15～25份和十二烷基笨磺酸钠0.5～2份】和组分B（交联剂）【多苯基多异氰酸酯80～100份和对甲苯磺酰氯5～15份】组成。
优选地，一种汽车内饰和篷布环保粘合剂粘合剂，由组分A（主剂）【聚乙酸乙烯酯乳液75～85份、羧基丁苯胶乳17～23份和十二烷基笨磺酸钠0.8～1.5份】和组分B（交联剂）【多苯基多异氰酸酯85～95份和对甲苯磺酰氯8～12份】组成。
所述汽车内饰和篷布环保粘合剂粘合剂，组分A和组分B的质量比或者体积比为100:15。
所述汽车内饰和篷布环保粘合剂粘合剂，通过下列步骤制得：
（1）组分A：取聚乙酸乙烯酯乳液，加入反应釜中并启动搅拌，然后加入羧基丁苯胶乳、十二烷基笨磺酸钠，于室温下搅拌15min，混合后得到主剂。
（2）组分B：取多苯基多异氰酸酯加入干燥的反应釜中并启动搅拌，然后加入对甲苯磺酰氯，于室温下搅拌10min，混合后得到交联剂。
具体实施方式
实施例1：
一种汽车内饰和篷布环保粘合剂粘合剂，由组分A（主剂）【聚乙酸乙烯酯乳液70份、羧基丁苯胶乳25份和十二烷基笨磺酸钠1.5份】和组分B（交联剂）【多苯基多异氰酸酯80份和对甲苯磺酰氯7份】组成。
其制作方法是：
（1）组分A：取聚乙酸乙烯酯乳液，加入反应釜中并启动搅拌，然后加入羧基丁苯胶乳、十二烷基笨磺酸钠，于室温下搅拌15min，混合后得到主剂。
（2）组分B：取多苯基多异氰酸酯加入干燥的反应釜中并启动搅拌，然后加入对甲苯磺酰氯，于室温下搅拌10min，混合后得到交联剂。
实施例2：
一种汽车内饰和篷布环保粘合剂粘合剂，由组分A（主剂）【聚乙酸乙烯酯乳液80份、羧基丁苯胶乳20份和十二烷基笨磺酸钠1份】和组分B（交联剂）【多苯基多异氰酸酯90份和对甲苯磺酰氯10份】组成。
其制作方法是同实施例1。
实施例3：
一种汽车内饰和篷布环保粘合剂粘合剂，由组分A（主剂）【聚乙酸乙烯酯乳液90份、羧基丁苯胶乳15份和十二烷基笨磺酸钠2份】和组分B（交联剂）【多苯基多异氰酸酯100份和对甲苯磺酰氯15份】组成。
其制作方法是同实施例1。
本发明的粘合剂所采用的原料易得，生产成本低廉，且具有良好的耐水性和耐热性，主要用于汽车内饰和篷布环保粘合剂的胶粘，刺激气味小，不产生有害气体，属于环境友好型胶粘剂。
通过下面给出的本发明实施了可进一步了解发明，以下实施例仅为本发明的几个具体实施例，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。
Claims (4)
1.一种汽车内饰和篷布环保粘合剂粘合剂，其特征在于，按质量份计由组分A（主剂）【聚乙酸乙烯酯乳液70～90份、羧基丁苯胶乳15～25份和十二烷基笨磺酸钠0.5～2份】和组分B（交联剂）【多苯基多异氰酸酯80～100份和对甲苯磺酰氯5～15份】组成。
2.根据权利要求1所述的汽车内饰和篷布环保粘合剂粘合剂，其特征在于，组分A和组分B的质量比或者体积比为100:15。
3.根据权利要求1和2所述的汽车内饰和篷布环保粘合剂粘合剂，其特征在于，按质量份计由组分A（主剂）【聚乙酸乙烯酯乳液75～85份、羧基丁苯胶乳17～23份和十二烷基笨磺酸钠0.8～1.5份】和组分B（交联剂）【多苯基多异氰酸酯85～95份和对甲苯磺酰氯8～12份】组成。
4.根据权利要求1和2所述的汽车内饰和篷布环保粘合剂粘合剂，其特征在于，通过下列步骤制得：
（1）组分A：取聚乙酸乙烯酯乳液，加入反应釜中并启动搅拌，然后加入羧基丁苯胶乳、十二烷基笨磺酸钠，于室温下搅拌15min，混合后得到主剂。
（2）组分B：取多苯基多异氰酸酯加入干燥的反应釜中并启动搅拌，然后加入对甲苯磺酰氯，于室温下搅拌10min，混合后得到交联剂。