CN104650403A - 耐高温减震橡胶垫 - Google Patents

耐高温减震橡胶垫 Download PDF

Info

Publication number
CN104650403A
CN104650403A CN201510073091.6A CN201510073091A CN104650403A CN 104650403 A CN104650403 A CN 104650403A CN 201510073091 A CN201510073091 A CN 201510073091A CN 104650403 A CN104650403 A CN 104650403A
Authority
CN
China
Prior art keywords
parts
rubber
rubber pad
high temperature
temperature resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510073091.6A
Other languages
English (en)
Inventor
苏志强
谢宇强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Ju Long Science And Technology Ltd
Original Assignee
Liuzhou Ju Long Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Ju Long Science And Technology Ltd filed Critical Liuzhou Ju Long Science And Technology Ltd
Priority to CN201510073091.6A priority Critical patent/CN104650403A/zh
Publication of CN104650403A publication Critical patent/CN104650403A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温减震橡胶垫，涉及橡胶材料技术领域。本发明耐高温减震橡胶垫由以下重量份数的原料制备而成：天然橡胶20份～30份，硅橡胶10份～25份，顺丁橡胶15份～30份，硬脂酸4份～10份，氧化锌2份～7份，纳米二氧化硅1份～5份，防老剂1份～5份，促进剂0.5份～5份，高铝粉0.3份～3份。本发明耐高温减震橡胶垫选用天然橡胶、硅橡胶和顺丁橡胶作为基体材料，选用耐高温性能强的纳米二氧化硅和高铝粉等物质作为助剂，所制备的减震垫硬度、拉伸强度、减震性能、耐老化性能均较优良，耐高温性能得到显著提高。

Description

耐高温减震橡胶垫
技术领域
本发明涉及橡胶材料技术领域，尤其是一种耐高温减震橡胶垫。
背景技术
现实生活中振动无处不在，但是振动也会对人们的生活产生许多不利的影响，因此需要采取必要的方法去消除震动带来的影响。橡胶的特点是既有高弹态，又有高粘态，使它在缓冲、减震和动态密封方面的作用无以伦比，橡胶部件广泛用于隔离振动和吸收冲击，通常减轻震动的办法是采用减震橡胶垫，减震橡胶垫在机车上的应用品种和数量越来越多，对其质量要求也越来越高，例如对于车辆、机械工业等，要求其具有动倍率低，耐老化能性、绝缘性高、耐高温性能强。而现有的减震橡胶垫，其耐高温性能较差，难以适用于特殊工况条件，因此，需要一种耐高温减震橡胶垫来满足实际工作的需要。
发明内容
本发明的目的是提供一种耐高温减震橡胶垫，这种耐高温减震橡胶垫可以解决现有减震橡胶垫耐高温性能差的问题。
为了解决上述问题，本发明采用的技术方案是：
本发明耐高温减震橡胶垫由以下重量份数的原料制备而成：天然橡胶20份～30份，硅橡胶10份～25份，顺丁橡胶15份～30份，硬脂酸4份～10份，氧化锌2份～7份，纳米二氧化硅1份～5份，防老剂1份～5份，促进剂0.5份～5份，高铝粉0.3份～3份。
上述技术方案中，更具体的方案还可以是：上述防老剂为N-苯基-β-萘胺或者4.4一双（2.2-二甲基苄基）二苯胺。
进一步的，上述促进剂为乙酰丙酮，三苯基膦，三乙酰丙酮铝中的一种或几种。
进一步的，原料的重量份数为：天然橡胶25份，硅橡胶10份，顺丁橡胶15份，硬脂酸4份，氧化锌2份，纳米二氧化硅1份，防老剂3份，促进剂0.5份，高铝粉0.3份。
进一步的，原料的重量份数为：天然橡胶20份，硅橡胶18份，顺丁橡胶23份，硬脂酸7份，氧化锌7份，纳米二氧化硅3份，防老剂1份，促进剂3份，高铝粉1.5份。
更进一步的，原料的重量份数为：天然橡胶30份，硅橡胶25份，顺丁橡胶30份，硬脂酸10份，氧化锌4份，纳米二氧化硅5份，防老剂5份，促进剂5份，高铝粉3份。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
本发明耐高温减震橡胶垫选用天然橡胶、硅橡胶和顺丁橡胶作为基体材料，选用耐高温性能强的纳米二氧化硅和高铝粉等物质作为助剂，以N-苯基-β-萘胺或者4.4一双（2.2-二甲基苄基）二苯胺作为防老剂，以乙酰丙酮，三苯基膦，三乙酰丙酮铝中的一种或几种作为促进剂，所制备的减震垫硬度、拉伸强度、减震性能、耐老化性能均较优良，耐高温性能得到显著提高。
具体实施方式
下面结合实施例对本发明作进一步详述：
实施例1
本实施例耐高温减震橡胶垫由以下重量份数的原料制备而成：天然橡胶25份，硅橡胶10份，顺丁橡胶15份，硬脂酸4份，氧化锌2份，纳米二氧化硅1份，防老剂3份，促进剂0.5份，高铝粉0.3份。
实施例2
本实施例耐高温减震橡胶垫由以下重量份数的原料制备而成：天然橡胶20份，硅橡胶18份，顺丁橡胶23份，硬脂酸7份，氧化锌7份，纳米二氧化硅3份，防老剂1份，促进剂3份，高铝粉1.5份。
实施例3
本实施例耐高温减震橡胶垫由以下重量份数的原料制备而成：天然橡胶30份，硅橡胶25份，顺丁橡胶30份，硬脂酸10份，氧化锌4份，纳米二氧化硅5份，防老剂5份，促进剂5份，高铝粉3份。
为了验证上述3个实施例所得耐高温减震橡胶垫的物理性能，分别对硬度、拉伸强度、断裂伸长率等指标进行检测，检测结果见表1：
表1 耐高温减震橡胶垫的物理性能

Claims (6)

1.一种耐高温减震橡胶垫，其特征在于由以下重量份数的原料制备而成：天然橡胶20份～30份，硅橡胶10份～25份，顺丁橡胶15份～30份，硬脂酸4份～10份，氧化锌2份～7份，纳米二氧化硅1份～5份，防老剂1份～5份，促进剂0.5份～5份，高铝粉0.3份～3份。
2.根据权利要求1所述的耐高温减震橡胶垫，其特征在于所述防老剂为N-苯基-β-萘胺或者4.4一双（2.2-二甲基苄基）二苯胺。
3.根据权利要求1所述的耐高温减震橡胶垫，其特征在于所述促进剂为乙酰丙酮，三苯基膦，三乙酰丙酮铝中的一种或几种。
4.根据权利要求1所述的耐高温减震橡胶垫，其特征在于所述原料的重量份数为：天然橡胶25份，硅橡胶10份，顺丁橡胶15份，硬脂酸4份，氧化锌2份，纳米二氧化硅1份，防老剂3份，促进剂0.5份，高铝粉0.3份。
5.根据权利要求1所述的耐高温减震橡胶垫，其特征在于所述原料的重量份数为：天然橡胶20份，硅橡胶18份，顺丁橡胶23份，硬脂酸7份，氧化锌7份，纳米二氧化硅3份，防老剂1份，促进剂3份，高铝粉1.5份。
6.根据权利要求1所述的耐高温减震橡胶垫，其特征在于所述原料的重量份数为：天然橡胶30份，硅橡胶25份，顺丁橡胶30份，硬脂酸10份，氧化锌4份，纳米二氧化硅5份，防老剂5份，促进剂5份，高铝粉3份。
CN201510073091.6A 2015-02-12 2015-02-12 耐高温减震橡胶垫 Pending CN104650403A (zh)