CN104630763B - 银器发黑剂 - Google Patents
银器发黑剂 Download PDFInfo
- Publication number
- CN104630763B CN104630763B CN201510023846.1A CN201510023846A CN104630763B CN 104630763 B CN104630763 B CN 104630763B CN 201510023846 A CN201510023846 A CN 201510023846A CN 104630763 B CN104630763 B CN 104630763B
- Authority
- CN
- China
- Prior art keywords
- parts
- silverware
- sodium
- blackening agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种银器发黑剂,属银器制作加工技术领域,解决银器表面发黑处理技术问题。本品由重量份数的组分配制而成:硫化钠1~3份;蛋氨酸2~5份;硫脲1~3份;氯化铵或硫酸铵1~ 5份;柠檬酸钠1~ 5份;硫酸钠10~20份;六偏磷酸钠 1~2;十二烷基硫酸钠0.1~0.2份。使用时,取本品加水溶解成25~35%的水溶液使用。本剂储存稳定,操作方便、安全无毒。
Description
技术领域
本发明涉及一种用于银器加工的粉剂,尤其是一种对银器进行表面发黑处理的银器发黑剂。
背景技术
银饰有亮银、原色银、乌银等主要种类,乌银通过人工硫化,在银饰表面氧化做旧形成黑色物质附着层。乌银风格独特,或古朴典雅,黑白对比突出,受到很多时尚人士的喜爱。
乌银传统制作工艺为在银表面用乌银合金覆盖,然后灼烧将乌银合金融化,在银饰表面附着黑亮表层。乌银合金主要为银,其他组分为铜和硫,某些情况中还有铅组份,当加热时各组分物质熔化混合形成黑亮乌银表面。
银器长时间佩戴或自然存放,银与空气或人体汗液接触后,其表面亦会形成黑色物质。这种黑色物质主要成分是硫化银,及少量的氯化银和氧化银等。这种表面形成的黑色物质也会对银器起到一定装饰作用,使银饰具有年代感。
现代银饰制作工艺中,为快速获得黑色表层,可采用重铬酸钾等氧化性物质溶液浸泡银饰,使其快速形成黑色表面。
艺术化地在银器表面形成黑色物质附着层,能使银器独具装饰感。但是传统乌银工艺操作复杂,乌银合金制备成本高;银饰自然佩戴或放置发黑耗时太长,无法实现工艺化;重铬酸钾溶液浸泡发黑工艺存在铬重金属污染,另外氧化剂亦存在储存不稳地,成膜附着力差等缺点。
发明内容
本发明要解决的技术问题是提供一种安全无毒,储存稳定,运输和操作方便,能快速对银器进行表面发黑处理的银器发黑剂。
为解决上述技术问题,本发明主要由重量份数的组分配制而成:硫化钠1~3份;蛋氨酸2~5份;硫脲1~3份;氯化铵或硫酸铵1~ 5份。
优选的,本发明还含有下述重量份数的组分:柠檬酸钠1~ 5份;硫酸钠10~20份;六偏磷酸钠 1~2;十二烷基硫酸钠0.1~0.2份。
更优选的,所述组分的重量份数为:硫化钠2份;蛋氨酸3份;硫脲2份;氯化铵或硫酸铵5份;柠檬酸钠3份;硫酸钠15份;六偏磷酸钠 1;十二烷基硫酸钠0.1份。
以上各组分,按配方组成,其中颗粒碎成粉末,混合均匀,制成本发明的银器发黑剂。
使用时,取本品加水溶解成25~35%的水溶液。将银器表面浸入本品水溶液5~15min,待银器表面变黑后,将银器取出用清水冲洗干净并用干净绒布擦干;或用毛笔或毛刷沾取本品水溶液按图案要求画于银器表面,等待5~15min,待银器所涂表面变黑后将银器冲洗干净并擦干即可。
采用上述技术方案所产生的有益效果在于:银器发黑剂使用时,其中硫脲可加速银器表面单质银被氧化成银离子,银离子进而与硫离子形成硫化银黑色物质附着在银器表面。本品无剧毒有害物质,安全无隐患;本品主要活性成分被干燥稳定剂稀释和包围并形成粉剂,储存稳定,运输方便;随用随配制成水溶液,操作方便,并可快速形成以硫化银为主的黑色物质附着在银器表面,达到银器发黑的目的。所述银器发黑剂中硫化钠和蛋氨酸为硫化剂,均提供硫离子与银离子形成硫化银,硫化钠较蛋氨酸作用快,蛋氨酸较硫化钠稳定,两者形成互补作用;硫脲为锈蚀剂,可加速单质银被空气氧化失去电子形成银离子;氯化铵或硫酸铵为弱酸性,辅助硫脲促进单质银失去电子形成银离子;柠檬酸钠为弱碱性,与氯化铵或硫酸铵形成酸碱缓冲体系,改善硫化钠稳定性;硫酸钠为干燥稳定剂,能吸附游离水,使本品粉剂保持干燥,同时硫酸钠为稀释剂,将本品主要活性组分稀释和包围,使本品粉剂方便混合制备并保障储存稳定;六偏磷酸钠与十二烷基硫酸钠均为润湿剂并形成协同效应,使本品水溶液能润湿银器表面。
具体实施方式
下面结合具体实施例对本发明作进一步详细的说明。
实施例1:本银器发黑剂:硫化钠2份;蛋氨酸3份;硫脲2份;氯化铵或硫酸铵5份;柠檬酸钠3份;硫酸钠15份;六偏磷酸钠 1;十二烷基硫酸钠0.1份。
以上各组分,按配方组成,其中颗粒碎成粉末,混合均匀,制成本发明的银器发黑剂。
使用时,取本品加水溶解成35%的水溶液使用。将银器表面浸入本品水溶液5min,待银器表面变黑后,将银器取出用清水冲洗干净并用干净绒布擦干。
实施例2:本银器发黑剂:硫化钠3份;蛋氨酸2份;硫脲1份;氯化铵或硫酸铵2份;柠檬酸钠2份;硫酸钠12份;六偏磷酸钠 1;十二烷基硫酸钠0.1份。
以上各组分,按配方组成,其中颗粒碎成粉末,混合均匀,制成本发明的银器发黑剂。
使用时,取本品加水溶解成30%的水溶液使用。将银器表面浸入本品水溶液10min,待银器表面变黑后,将银器取出用清水冲洗干净并用干净绒布擦干。
实施例3:本银器发黑剂:硫化钠2份;蛋氨酸5份;硫脲3份;氯化铵或硫酸铵4份;柠檬酸钠2份;硫酸钠16份;六偏磷酸钠 2;十二烷基硫酸钠0.2份。
以上各组分,按配方组成,其中颗粒碎成粉末,混合均匀,制成本发明的银器发黑剂。
使用时,取本品加去离子水溶解成35%的水溶液使用。用毛笔沾取本品水溶液画于银器表面,等待12min,待银器所涂表面变黑后将银器冲洗干净并擦干。
实施例4:本银器发黑剂:硫化钠3份;蛋氨酸3份;硫脲3份;氯化铵或硫酸铵3份;柠檬酸钠3份;硫酸钠17份;六偏磷酸钠 1;十二烷基硫酸钠0.2份。
以上各组分,按配方组成,其中颗粒碎成粉末,混合均匀,制成本发明的银器发黑剂。
使用时,取本品加去离子水溶解成28%的水溶液使用。用毛笔沾取本品水溶液画于银器表面,等待15min,待银器所涂表面变黑后将银器冲洗干净并擦干。
Claims (2)
1.一种银器发黑剂,其特征在于,其由重量份数的组分配制而成:硫化钠1~3份;蛋氨酸2~5份;硫脲1~3份;氯化铵或硫酸铵1~5份;柠檬酸钠1~5份;硫酸钠10~20份;六偏磷酸钠1~2份;十二烷基硫酸钠0.1~0.2份。
2.根据权利要求1所述的银器发黑剂,其特征在于,所述组分的重量份数为:硫化钠2份;蛋氨酸3份;硫脲2份;氯化铵或硫酸铵5份;柠檬酸钠3份;硫酸钠15份;六偏磷酸钠1份;十二烷基硫酸钠0.1份。