CN104614395A - 硅烷交联聚乙烯电缆料的热收缩性能测试方法 - Google Patents

硅烷交联聚乙烯电缆料的热收缩性能测试方法 Download PDF

Info

Publication number
CN104614395A
CN104614395A CN201510036858.8A CN201510036858A CN104614395A CN 104614395 A CN104614395 A CN 104614395A CN 201510036858 A CN201510036858 A CN 201510036858A CN 104614395 A CN104614395 A CN 104614395A
Authority
CN
China
Prior art keywords
sample
cable material
testing according
water
testing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510036858.8A
Other languages
English (en)
Inventor
洪向明
关江伟
舒康玉
于西
帅立丹
王海涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG WANMA MACROMOLECULE MATERIAL CO Ltd
Original Assignee
ZHEJIANG WANMA MACROMOLECULE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG WANMA MACROMOLECULE MATERIAL CO Ltd filed Critical ZHEJIANG WANMA MACROMOLECULE MATERIAL CO Ltd
Priority to CN201510036858.8A priority Critical patent/CN104614395A/zh
Publication of CN104614395A publication Critical patent/CN104614395A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅烷交联聚乙烯电缆料的热收缩性能测试方法，利用单螺杆挤出机将硅烷交联电缆料挤出，将基础的胶体置于运转中的辊筒之上制样，截取每段20cm为标准试样，置于90℃水浴锅中，水浴3小时，水浴后取出标准试样擦干，置于130℃烘箱中加热1小时，烘干后，取出试样，测量长度L，计算收缩率。本发明方法操作方便、简单实用、实验时间较短。

Description

硅烷交联聚乙烯电缆料的热收缩性能测试方法
技术领域
本发明属于电缆器材技术领域，具体涉及一种硅烷交联聚乙烯电缆料的热收缩性能测试方法。
背景技术
现代化建设对电力的需求越来越大，交联聚乙烯绝缘电力电缆以其工作温度高、绝缘特性好、耐过载能力强等特点，正逐步取代传统PVC绝缘电力电缆。低压XLPE电缆大多采用硅烷交联法与辐照交联法或过氧化物交联法。硅烷交联法具有设备投资少、适应性强和工艺简单等有点。
但小规格硅烷交联聚乙烯绝缘电力电缆，由于绝缘材料和导体的接触面积相对较小，尤其是单芯导体表面光滑附着力不够时，绝缘层的热收缩较大，很难达到GB/T12706-2008标准中的不大与4％的要求，有事实测的XLPE绝缘热收缩甚至达到20％，严重影响产品质量。因此，硅烷交联聚乙烯电缆料生产时非常需要一个热收缩性能测试方法，用来判断硅烷交联聚乙烯电缆料的热收缩性能好坏，以控制与改善产品质量。
发明内容
本发明旨在提供一种硅烷交联聚乙烯电缆料的热收缩性能测试方法，目的在于解决现有技术存在的不足，该方法具有操作方便、简单实用、实验时间短的特点。
本发明具体通过以下技术方案实现：
硅烷交联聚乙烯电缆料的热收缩性能测试方法，具体包括以下步骤：
1)将硅烷交联电缆料进行喂料，利用单螺杆挤出机挤出，调节挤出工艺温度，待挤出机挤出熔体正常后，调节挤出速度至出胶速度为22.5±0.5g/min；
2)出胶量稳定之后，将胶体置于运转中的辊筒之上，调节辊筒转速；
3)制样速度稳定后，调节辊筒间距；
4)持续制得上述样片若干米，截取每段20cm为标准试样；
5)将标准试样置于90℃水浴锅中，水浴3小时；
6)水浴后取出标准试样擦干，置于130℃烘箱中加热1小时；
7)烘干后，取出试样，测量长度L，计算收缩率。
具体的，步骤(1)中单螺杆挤出机的设定温度为140-220℃。
具体的，步骤(2)中辊筒调节后的制样速度为3.33cm/s。
具体的，步骤(3)中调节辊筒间距之后的样片厚度控制为0.45±0.05mm。
具体的，步骤(5)中试样擦干后，置于石灰中，连同石灰一起放入烘箱烘烤。
具体的，步骤(7)中收缩率计算公式为：收缩率＝(20－L)×100％/20。
本发明的有益效果为：1)本方法所使用设备常规，且设备数量少；2)本方法简单，检测步骤少，实验过程精细、严谨；3)本发明中的实验方法已多次反复测试，所得结果偏差极少，且数据稳定；4)本实验方法所得结果多次与多家电缆生产企业进行反馈及验证，本实验方法与电缆成品(以硅烷交联聚乙烯电缆料生产的电缆线)检测结果非常吻合。
具体实施方式
下面结合实施例对本发明做进一步的说明，以下所述，仅是对本发明的较佳实施例而已，并非对本发明做其他形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更为同等变化的等效实施例。凡是未脱离本发明方案内容，依据本发明的技术实质对以上实施例所做的任何简单修改或等同变化，均落在本发明的保护范围内。
实施例1
硅烷交联聚乙烯电缆料的热收缩性能测试方法，具体包括以下步骤：
1)将硅烷交联电缆料M(非低收缩电缆料，常规硅烷交联两步法电缆料)进行喂料，利用单螺杆挤出机挤出，调节挤出工艺温度为220℃，待挤出机挤出熔体正常后，调节挤出速度至出胶速度为22.5±0.5g/min；
2)出胶量稳定之后，将胶体置于运转中的辊筒之上，调节辊筒转速，调节后的制样速度为3.33cm/s；
3)制样速度稳定后，调节辊筒间距，厚度控制为0.45±0.05mm；
4)持续制得上述样片若干米，截取每段20cm为标准试样；
5)将标准试样置于90℃水浴锅中，水浴3小时；
6)水浴后取出标准试样擦干，避免试样与烘箱中的金属接触，防止粘连，可将试样置于石灰中，连同石灰一起置于130℃烘箱中加热1小时；
7)烘干后，取出试样，测量长度L116.8cm、L216.8cm、L316.7cm、L416.7cm，按照公式收缩率＝(20－L)×100％/20计算，结果分别为16％、16％、16.5％、16.5％；计算平均值：16.25％。
电缆成品收缩率的检测结果为16％、16.5％、16.5％、16.5％；计算平均值：16.375％，与本发明方法结果几乎无差异。
实施例2
硅烷交联聚乙烯电缆料的热收缩性能测试方法，具体包括以下步骤：
1)将硅烷交联电缆料N(低收缩料，特殊硅烷交联两步法电缆料)进行喂料，利用单螺杆挤出机挤出，调节挤出工艺温度为140℃，待挤出机挤出熔体正常后，调节挤出速度至出胶速度为22.5±0.5g/min；
2)出胶量稳定之后，将胶体置于运转中的辊筒之上，调节辊筒转速，调节后的制样速度为3.33cm/s；
3)制样速度稳定后，调节辊筒间距，厚度控制为0.45±0.05mm；
4)持续制得上述样片若干米，截取每段20cm为标准试样；
5)将标准试样置于90℃水浴锅中，水浴3小时；
6)水浴后取出标准试样擦干，避免试样与烘箱中的金属接触，防止粘连，可将试样置于石灰中，连同石灰一起置于130℃烘箱中加热1小时；
7)烘干后，取出试样，测量长度L119.8cm、L219.8cm、L319.8cm、L419.7cm，按照公式收缩率＝(20－L)×100％/20计算，结果为1％、1.5％、1.5％、1.5％；计算平均值：1.375％。
电缆成品收缩率的检测结果为1％、1％、1.5％、1.5％；计算平均值：1.25％，与本发明方法结果相当。
综上所述，本发明硅烷交联聚乙烯电缆料的热收缩性能测试方法所得结果偏差极少，且数据稳定，与电缆成品(以硅烷交联聚乙烯电缆料生产的电缆线)检测结果非常吻合，具有极大的推广使用价值。

Claims (6)

1.硅烷交联聚乙烯电缆料的热收缩性能测试方法，其特征在于，具体包括以下步骤：
1)将硅烷交联电缆料进行喂料，利用单螺杆挤出机挤出，调节挤出工艺温度，待挤出机挤出熔体正常后，调节挤出速度至出胶速度为22.5±0.5g/min；
2)出胶量稳定之后，将胶体置于运转中的辊筒之上，调节辊筒转速；
3)制样速度稳定后，调节辊筒间距；
4)持续制得若干米，截取每段20cm为标准试样；
5)将标准试样置于90℃水浴锅中，水浴3小时；
6)水浴后取出标准试样擦干，置于130℃烘箱中加热1小时；
7)烘干后，取出试样，测量长度L，计算收缩率。
2.根据权利要求1所述的测试方法，其特征在于：步骤(1)中单螺杆挤出机的设定温度为140-220℃。
3.根据权利要求1所述的测试方法，其特征在于：步骤(2)中辊筒调节后的制样速度为3.33cm/s。
4.根据权利要求1所述的测试方法，其特征在于：步骤(3)中调节辊筒间距之后的样片厚度控制为0.45±0.05mm。
5.根据权利要求1所述的测试方法，其特征在于：步骤(5)中试样擦干后，置于石灰中，连同石灰一起放入烘箱烘烤。
6.根据权利要求1所述的测试方法，其特征在于：步骤(7)中收缩率计算公式为：收缩率＝(20－L)×100％/20。
CN201510036858.8A 2015-01-24 2015-01-24 硅烷交联聚乙烯电缆料的热收缩性能测试方法 Pending CN104614395A (zh)