CN104611619B - 一种高强度耐磨钢的冶炼方法 - Google Patents

一种高强度耐磨钢的冶炼方法 Download PDF

Info

Publication number
CN104611619B
CN104611619B CN201410798031.6A CN201410798031A CN104611619B CN 104611619 B CN104611619 B CN 104611619B CN 201410798031 A CN201410798031 A CN 201410798031A CN 104611619 B CN104611619 B CN 104611619B
Authority
CN
China
Prior art keywords
steel scrap
orientation
steel
screening
scrap
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410798031.6A
Other languages
English (en)
Other versions
CN104611619A (zh
Inventor
李建农
李介琴
李明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN XIANGYE MACHINERY MANUFACTURING Co Ltd
Original Assignee
HUNAN XIANGYE MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN XIANGYE MACHINERY MANUFACTURING Co Ltd filed Critical HUNAN XIANGYE MACHINERY MANUFACTURING Co Ltd
Priority to CN201410798031.6A priority Critical patent/CN104611619B/zh
Publication of CN104611619A publication Critical patent/CN104611619A/zh
Application granted granted Critical
Publication of CN104611619B publication Critical patent/CN104611619B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高强度耐磨钢的冶炼配方技术，包括如下步骤：1）筛选废钢I、筛选废钢II：利用光谱分析法在大量回收的废旧金属材料中分类筛选出筛选废钢I、筛选废钢II；2）定向回收废钢III、定向回收废钢IV：确定所述筛选废钢I、所述筛选废钢II的回收源头，定向收储其边角废料及钢屑，并分别储放定向回收废钢III和定向回收废钢IV；3）定量配料、定量投料：根据所生产的高强度耐磨钢的牌号要求，按百分比分别定量配料和定量投料。本发明的有益效果是节约了大量的合金元素或战略元素，大幅度的降低了生产成本。

Description

一种高强度耐磨钢的冶炼方法
技术领域
本发明属于特殊用途钢冶炼技术领域，更加具体地，涉及矿山、军用工程用特殊高强度耐磨钢的冶炼配方技术，即一种高强度耐磨钢的冶炼方法。
背景技术
长期以来，国内外在冶炼矿山机械、军工机械等特种工程机械的特殊用途钢，特别是高强度耐磨钢时，通常采用普通钢坯或废钢为原料，再依钢种要求按配比加入多种合金元素冶炼钢材，这些合金元素是从各种矿石中分别提炼得到的，其价格昂贵，甚至有些还属于国家战略资源，稀有程度高，这就造成了现有技术在冶炼高强度耐磨钢的数量、质量方面都不尽如人意，但是，目前对高强度耐磨钢等特殊用途钢的需求从品种、品质等方面都在不断提高，高强度耐磨钢的需求数量也在逐年成倍增长，高强度耐磨钢的供求矛盾日益尖锐。
发明内容
为了解决上述现有技术存在的问题，本发明提出了一种高强度耐磨钢的冶炼方法。
一种高强度耐磨钢的冶炼方法，包括如下步骤：
1)筛选废钢I、筛选废钢II：利用光谱分析法在大量回收的废旧金属材料中分类筛选出筛选废钢I、筛选废钢II；
2)定向回收废钢III、定向回收废钢IV：确定所述筛选废钢I、所述筛选废钢II的回收源头，定向收储其边角废料及钢屑，并分别储放定向回收废钢III和定向回收废钢IV；
3)定量配料、定量投料：根据所生产的高强度耐磨钢的牌号要求，按百分比分别定量配料和定量投料。
较佳地，所述筛选废钢I，其成分如下：C(0.2％)、Si(0.22％)、Mn(0.8％)、Cr(0.8％)、Mo(0.8％)、P≤0.03％、S≤0.03％、V(0.2％)、Ti(0.6％)。
较佳地，所述筛选废钢II，其成分如下：C(0.4％)、Si(0.24％)、Mn(0.9％)、Cr(0.9％)、Mo(0.9％)、P≤0.03％、S≤0.03％、V(0.8％)、Ti(0.7％)。
较佳地，所述定向回收废钢III，其成分如下：C(0.45％)、Si(0.4％)、Mn(1％)、Cr(1％)、Mo(0.9％)、P≤0.03％、S≤0.03％、V(0.2％)、Ti(0.6％)。
较佳地，所述定向回收废钢IV，其成分如下：C(0.5％)、Si(0.42％)、Mn(1％)、Cr(12％)、Mo(1％)、P≤0.03％、S≤0.03％、V(0.9％)、Ti(0.7％)。
较佳地，定量配料中，各成分的百分比例如下：筛选废钢I(24％)，筛选废钢II(14％)，定向回收废钢III(23％)，定向回收废钢IV(14％)，高碳锰铁(16.67％)，中碳锰铁(8.33％)。
本发明的有益效果是节约了大量的合金元素或战略元素，大幅度的降低了生产成本。
发明附图
图1是一种高强度耐磨钢的冶炼方法流程图。
具体实施方式
具体实施例
采用所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料，所述材料材质为ZGMn18Cr2MoVTi，所述材料奥氏体组织纯化，晶粒细，经检测抗拉强度≥850Mpa，相对于现有技术而言，其初始硬度基本一致，但同时使用10分钟后，所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料比现有技术生产的材料的表面硬度高100HRS，且其强度更好。
采用所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料，其合金成分控制如下，C(1.4～1.65％)、Si(0.8～1.2％)、Mn(16～18％)、Cr(1.4～2％)、Mo(0.6～0.8％)、P≤0.086％、S≤0.040％、V(0.3～0.5％)、Ti(0.3～0.5％)。
采用所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料，其配料炉料成分表如下：
配料炉料成分表
采用所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料，其配料成分表如下：
配料成分表
采用所述一种高强度耐磨钢的冶炼方法来生产圆锥机破碎壁材料，其具体技术步骤如下：
1)筛选废钢I、筛选废钢II：利用光谱分析法在大量回收的废旧金属材料中分类筛选出筛选废钢I、筛选废钢II；
2)定向回收废钢III、定向回收废钢IV：根据所述筛选废钢I、所述筛选废钢II的回收源头，定向收储其边角废料及钢屑，并分别储放定向回收废钢III和定向回收废钢IV；
3)定量配料、定量投料：根据所生产的高强度耐磨钢的牌号要求，按百分比分别定量配料和定量投料。

Claims (1)

1.一种高强度耐磨钢的冶炼方法，其特征在于所述方法包括如下步骤：
1)筛选废钢I、筛选废钢II：利用光谱分析法在大量回收的废旧金属材料中分类筛选出筛选废钢I、筛选废钢II；
2)定向回收废钢III、定向回收废钢IV：确定所述筛选废钢I、所述筛选废钢II的回收源头，定向收储其边角废料及钢屑，并分别储放定向回收废钢III和定向回收废钢IV；
3)定量配料、定量投料：将筛选废钢I24％，筛选废钢II14％，定向回收废钢III23％，定向回收废钢IV14％，高碳锰铁16.67％，中碳锰铁8.33％按重量比加入电炉熔炼；
其中，所述筛选废钢I的成分如下：C0.2％、Si0.22％、Mn0.8％、Cr0.8％、Mo0.8％、P≤0.03％、S≤0.03％、V0.2％、Ti0.6％；
所述筛选废钢II的成分如下：C0.4％、Si0.24％、Mn0.9％、Cr0.9％、Mo0.9％、P≤0.03％、S≤0.03％、V0.8％、Ti0.7％；
所述定向回收废钢III的成分如下：C0.45％、Si0.4％、Mn1％、Cr1％、Mo0.9％、P≤0.03％、S≤0.03％、V0.2％、Ti0.6％；
所述定向回收废钢IV的成分如下：C0.5％、Si0.42％、Mn1％、Cr12％、Mo1％、P≤0.03％、S≤0.03％、V0.9％、Ti0.7％。
CN201410798031.6A 2014-12-19 2014-12-19 一种高强度耐磨钢的冶炼方法 Active CN104611619B (zh)