CN104609799A - 一种单组份防水环保混凝土 - Google Patents
一种单组份防水环保混凝土 Download PDFInfo
- Publication number
- CN104609799A CN104609799A CN201510013686.2A CN201510013686A CN104609799A CN 104609799 A CN104609799 A CN 104609799A CN 201510013686 A CN201510013686 A CN 201510013686A CN 104609799 A CN104609799 A CN 104609799A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- concrete
- water
- cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种单组份防水环保混凝土,其组成原料的重量份为:普通硅酸盐水泥60-75、黄砂30-35、红壤土28-30、香菇栽培料8-15、铝粉浆4-5、三氧化二锑2-4、镧粉1-3、钼粉1-3、硼化锆3-4、硫酸钡5-6、醋酸丁酸纤维素液0.4-1.0、海藻酸钠1.2-1.5、煤焦油1-3、纤维素醚0.5-1.5和水适量;本发明混凝土组分单一,配方简单,通过添加金属粉末、金属氧化物粉末,能够有效地防止因混凝土温度、内部裂缝,而且其中的香菇栽培料,提高了混凝土的密实性、堆积密度、抗渗性。
Description
技术领域
本发明涉及建筑材料领域,尤其涉及一种单组份防水环保混凝土。
背景技术
混凝土具有原料丰富,价格低廉,生产工艺简单的特点,因而使其用量越来越大。同时混凝土还具有抗压强度高,耐久性好,强度等级范围宽等特点;这些特点使其使用范围十分广泛,不仅在各种土木工程中使用,就是造船业,机械工业,海洋的开发,地热工程等;近年来,随着我国超高层建筑的不断开工,超高层建筑的高度不断被刷新,其基础底板受力状态不断加重,结构越来越厚,混凝土强度等级要求越来越高,总胶凝材料用量也越来越多,混凝土水化热也就更高,所以就容易引起超厚结构混凝土的开裂。
发明内容
本发明的目的在于提供一种单组份防水环保混凝土。
为了实现上述目的本发明采用如下技术方案:
单组份防水环保混凝土,其组成原料的重量份为:普通硅酸盐水泥60-75、黄砂30-35、红壤土28-30、香菇栽培料8-15、铝粉浆4-5、三氧化二锑2-4、镧粉1-3、钼粉1-3、硼化锆3-4、硫酸钡5-6、醋酸丁酸纤维素液0.4-1.0、海藻酸钠1.2-1.5、煤焦油1-3、纤维素醚0.5-1.5和水适量。
所述的香菇栽培料的配方为:板栗壳4-5、芦苇2-3、玉米芯10-12、大豆粕4-5、熟石灰2-4、沸石粉8-10、铁矿粉10-12、镁粉2-4、生活垃圾炭化灰5-10、红糖3-5、磷酸二氢钾0.4-0.6、过磷酸钙0.5-0.6、腐植酸钾0.8-1.0、棕榈壳3-5。
单组份防水环保混凝土,其组成原料的重量份为:普通硅酸盐水泥68、黄砂32、红壤土28、香菇栽培料12、铝粉浆4.5、三氧化二锑3、镧粉2、钼粉2、硼化锆4、硫酸钡5、醋酸丁酸纤维素液0.7、海藻酸钠1.4、煤焦油2、纤维素醚1和水适量。
本发明的有益效果:
本发明混凝土组分单一,配方简单,通过添加金属粉末、金属氧化物粉末,能够有效地防止因混凝土温度、内部裂缝,而且其中的香菇栽培料,提高了混凝土的密实性、堆积密度、抗渗性。
具体实施方式
实施例1:单组份防水环保混凝土,其组成原料的重量份(kg)为:普通硅酸盐水泥68、黄砂32、红壤土28、香菇栽培料12、铝粉浆4.5、三氧化二锑3、镧粉2、钼粉2、硼化锆4、硫酸钡5、醋酸丁酸纤维素液0.7、海藻酸钠1.4、煤焦油2、纤维素醚1和水适量。
所述的香菇栽培料的配方(kg)为:板栗壳4.5、芦苇2.5、玉米芯12、大豆粕4.5、熟石灰3、沸石粉9、铁矿粉12、镁粉3、生活垃圾炭化灰8、红糖4、磷酸二氢钾0.5、过磷酸钙0.5、腐植酸钾0.8、棕榈壳4。
本发明通过添加金属粉末、金属氧化物粉末,能够有效地防止因混凝土温度、内部裂缝,而且其中的香菇栽培料,提高了混凝土的密实性、堆积密度、抗渗性。
Claims (2)
1.一种单组份防水环保混凝土,其特征在于其组成原料的重量份为:普通硅酸盐水泥60-75、黄砂30-35、红壤土28-30、香菇栽培料8-15、铝粉浆4-5、三氧化二锑2-4、镧粉1-3、钼粉1-3、硼化锆3-4、硫酸钡5-6、醋酸丁酸纤维素液0.4-1.0、海藻酸钠1.2-1.5、煤焦油1-3、纤维素醚0.5-1.5和水适量;
所述的香菇栽培料的配方为:板栗壳4-5、芦苇2-3、玉米芯10-12、大豆粕4-5、熟石灰2-4、沸石粉8-10、铁矿粉10-12、镁粉2-4、生活垃圾炭化灰5-10、红糖3-5、磷酸二氢钾0.4-0.6、过磷酸钙0.5-0.6、腐植酸钾0.8-1.0、棕榈壳3-5。
2.根据权利要求1所述的单组份防水环保混凝土,其特征在于其组成原料的重量份为:普通硅酸盐水泥68、黄砂32、红壤土28、香菇栽培料12、铝粉浆4.5、三氧化二锑3、镧粉2、钼粉2、硼化锆4、硫酸钡5、醋酸丁酸纤维素液0.7、海藻酸钠1.4、煤焦油2、纤维素醚1和水适量。