CN104609731B - There is the processing technology of the crystallite stone material of colored lines - Google Patents
There is the processing technology of the crystallite stone material of colored lines Download PDFInfo
- Publication number
- CN104609731B CN104609731B CN201510025069.4A CN201510025069A CN104609731B CN 104609731 B CN104609731 B CN 104609731B CN 201510025069 A CN201510025069 A CN 201510025069A CN 104609731 B CN104609731 B CN 104609731B
- Authority
- CN
- China
- Prior art keywords
- coloring
- stone material
- molten slurry
- rod
- crystallite stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the raw material of the crystallite stone material for preparing a) is mixed by a kind of processing technology of the crystallite stone material with colored lines；B) coloring agent is made coloring rod；C) raw material of crystallite stone material is sent into cell furnace, heating melting obtains molten slurry；D) by the molten slurry of coloring rod insertion flowing, flow through the molten slurry near coloring rod and can dissolve coloring rod and be infected with color；E) using rolling process by coloring after molten slurry make semi-finished product；F) heat treatment is carried out to semi-finished product, obtains the crystallite stone material with colored lines.Processing technology disclosed by the invention is easy to use, works well, and can produce rich color, there is the crystallite stone material of colored lines.The present invention can be used to make crystallite stone material.
Description
Technical field
The present invention relates to a kind of processing technology of the crystallite stone material with colored lines.
Background technology
Devitrified glass stone material have moisture resistance, anticorrosion, do not aoxidize, colour-fast, no color differnece, intensity height, glossiness height etc. excellent
Characteristic, is increasingly widely applied in building field.The processing technology of existing devitrified glass stone material, usually by crystallite glass
Granule into after granule is sprinkling upon addition fixative on mould, is finally fired and forms by glass water quenching.Expect with not homochromy
The crystallite stone material of color and floral designs, needs to be printed in adobe colorant frit using half tone, covers then at surface transparent molten
Block, then sinters.Process is complicated, and can be only applied to the crystallite stone material of sintering process, for the crystallite produced using rolling process
Stone material does not have interpolation floral designs method easy to use.
Content of the invention
For the deficiencies in the prior art, the invention provides a kind of easy to use, work well, color can be produced rich
The processing technology of crystallite stone material rich, that there is colored lines.
The technical scheme that the present invention solves technical problem is as follows：
There is the processing technology of the crystallite stone material of colored lines, it is characterised in that comprise the following steps in order：
A) raw material of the crystallite stone material for preparing is mixed；
B) coloring agent is made coloring rod；
C) raw material of crystallite stone material is sent into cell furnace, heating melting obtains molten slurry；
D) by the molten slurry of coloring rod insertion flowing, flow through the molten slurry near coloring rod and can dissolve coloring rod and be infected with
Color；
E) using rolling process by coloring after molten slurry make semi-finished product；
F) heat treatment is carried out to semi-finished product, obtains the crystallite stone material with colored lines.
Further, the coloring rod described in step d) is swung along the vertical direction of molten slurry flow direction, makes molten slurry with wave
Striped.
Further, the coloring rod described in step d) has more than one, successively along molten slurry flow direction arrangement, each coloring
Rod is swung along the vertical direction of molten slurry flow direction, makes molten slurry with wave stripe.
Or, also include step d ') to coloring after molten slurry be stirred and make original linear fringe produce change.
Further, the coloring agent described in step b) includes copper, ferrum, nickel, titanium, manganese, chromium, cobalt, vanadium and above-mentioned this eight kinds
The oxide or chloride of element.
Wherein, the processing technology of the coloring rod described in step b), comprises the following steps：
i）By oxide or chloride containing copper, ferrum, nickel, titanium, manganese, chromium, cobalt, vanadium and this eight kinds of elements above-mentioned with
The raw material of crystallite stone material is mixed, and obtains colouring rod raw material；
ii）Coloring rod raw material sintering process is made band the colorful one and colours rod.
Processing technology disclosed by the invention is easy to use, works well, and can produce rich color, there is colored lines
Crystallite stone material.The present invention can be used to make crystallite stone material.
Specific embodiment
The technique effect of the design, concrete structure and generation of the present invention is carried out below with reference to embodiment clear, complete
Ground description, to be completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is the one of the present invention
Section Example, rather than whole embodiments, based on embodiments of the invention, those skilled in the art is not paying creativeness
The other embodiment obtained on the premise of work, belongs to the scope of protection of the invention.In addition, be previously mentioned in text is all
/ annexation is connect, not singly refers to that component directly connects, and referred to and can be coupled by adding or reducing according to the situation that is embodied as
Auxiliary, constitutes more excellent draw bail.Each technical characteristic in the invention, on the premise of not conflicting conflict
Can be with combination of interactions.
There is the processing technology of the crystallite stone material of colored lines, it is characterised in that comprise the following steps in order：
A) raw material of the crystallite stone material for preparing is mixed；
B) coloring agent is made coloring rod；
C) raw material of crystallite stone material is sent into cell furnace, heating melting obtains molten slurry；
D) by the molten slurry of coloring rod insertion flowing, flow through the molten slurry near coloring rod and can dissolve coloring rod and be infected with
Color；
E) using rolling process by coloring after molten slurry make semi-finished product；
F) heat treatment is carried out to semi-finished product, obtains the crystallite stone material with colored lines.
The crystallite stone material that above-mentioned steps are made carries the linear fringe pattern with coloring rod same color, entirely
Process is simple and convenient.
It is further used as preferred embodiment, vertical direction pendulum of the coloring rod described in step d) along molten slurry flow direction
Dynamic, molten slurry is made with wave stripe.When there is complex root coloring rod, for avoiding which from interfering, can be successively by which along molten slurry stream
Dynamic direction arranges, and each coloring rod is along the vertical direction swing or static of molten slurry flow direction, can make molten slurry with complexity
Beautiful candy strip.
As another preferred embodiment, step can also be included：D ') to coloring after molten slurry be stirred and make original
Some linear fringes produce change.Coloring rod is different into the mode of pattern from swinging, using mixing tool to coloring after molten
Slurry is stirred and can form protean random pattern, it is also possible to arrange symmetrical stirring to melt the center line of slurry as boundary's mirror image
Utensil, makes molten slurry form symmetrical candy strip.
Be further used as preferred embodiment, the coloring agent described in step b) include copper, ferrum, nickel, titanium, manganese, chromium, cobalt,
Vanadium and the oxide or chloride of this eight kinds of elements above-mentioned.
Wherein, the processing technology of the coloring rod described in step b), comprises the following steps：
i）By oxide or chloride containing copper, ferrum, nickel, titanium, manganese, chromium, cobalt, vanadium and this eight kinds of elements above-mentioned with micro-
The raw material of spar material is mixed, and obtains colouring rod raw material；
ii）Coloring rod raw material sintering process is made band the colorful one and colours rod.
Above the better embodiment of the present invention is illustrated, but the invention is not limited to the enforcement
Example, those of ordinary skill in the art without prejudice to spirit of the invention on the premise of can also made a variety of equivalent modifications or replaced
Change, the modification of these equivalents or replacement are all contained in the application claim limited range.
Claims (4)
1. there is the processing technology of the crystallite stone material of colored lines, it is characterised in that comprise the following steps in order：
a）The raw material of the crystallite stone material for preparing is mixed；
b）Coloring agent is made coloring rod；
c）The raw material of crystallite stone material is sent into cell furnace, heating melting obtains molten slurry；
d）By in the molten slurry of coloring rod insertion flowing, flow through the molten slurry near coloring rod and can dissolve coloring rod and be infected with color；
e）Using rolling process by coloring after molten slurry make semi-finished product；
f）Heat treatment is carried out to semi-finished product, the crystallite stone material with colored lines is obtained；
The processing technology of described coloring rod is comprised the following steps：
i）By oxide or chloride and microlite containing copper, ferrum, nickel, titanium, manganese, chromium, cobalt, vanadium and this eight kinds of elements above-mentioned
The raw material of material is mixed, and obtains colouring rod raw material；
ii）Coloring rod raw material sintering process is made band the colorful one and colours rod.
2. the processing technology of the crystallite stone material with colored lines according to claim 1, it is characterised in that：Step d) institutes
The coloring rod that states is swung along the vertical direction of molten slurry flow direction, makes molten slurry with wave stripe.
3. the processing technology of the crystallite stone material with colored lines according to claim 2, it is characterised in that：Step d) institutes
The coloring rod that states has more than one, successively along molten slurry flow direction arrangement, Vertical Square of each coloring rod along molten slurry flow direction
To swing, molten slurry is made with wave stripe.
4. the processing technology of the crystallite stone material with colored lines according to claim 1, it is characterised in that also include：
D ') to coloring after molten slurry be stirred and make original linear fringe produce change.