CN1045973C - 聚氨酯树脂及硬质聚氨酯泡沫体的制备方法 - Google Patents

聚氨酯树脂及硬质聚氨酯泡沫体的制备方法 Download PDF

Info

Publication number
CN1045973C
CN1045973C CN95100858A CN95100858A CN1045973C CN 1045973 C CN1045973 C CN 1045973C CN 95100858 A CN95100858 A CN 95100858A CN 95100858 A CN95100858 A CN 95100858A CN 1045973 C CN1045973 C CN 1045973C
Authority
CN
China
Prior art keywords
polyvalent alcohol
molecule
hydroxyl
polyurethane foam
aliphatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN95100858A
Other languages
English (en)
Other versions
CN1109070A (zh
Inventor
尾崎智
伊豆川作
川上晴比古
增田隆良
木村正幸
野泽俊夫
桥场正彦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Chemicals Inc
Original Assignee
Mitsui Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Chemicals Inc filed Critical Mitsui Chemicals Inc
Publication of CN1109070A publication Critical patent/CN1109070A/zh
Application granted granted Critical
Publication of CN1045973C publication Critical patent/CN1045973C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明方法使用特定的多元醇、聚亚氧烷基多元醇、脂肪族胺和/或链烷醇胺作为原料，并加入有机多元羧酸或其酸酐和烯化氧制得新的多元醇；由所述新的多元醇和有机多异氰酸酯制得聚氨酯树脂；和使用低公害的氢氯氟烃或氢氟烃发泡剂制得硬质聚氨酯泡沫体。使用本发明的多元醇制备硬质聚氨酯泡沫体可在好的操作效率和低公害下进行。所得泡沫体的性能和使用通常的氯氟烃制得的硬质聚氨酯泡沫体的性能相同。本发明的硬质聚氨酯泡沫体可用作绝热和结构隔热材料。

Description

聚氨酯树脂及硬质聚氨酯泡沫体的制备方法
本发明涉及一种聚氨酯树脂、硬质聚氨酯泡沫体的制备方法。
更进一步地说，本发明用多元醇制备一种在低公害的发泡剂，即氢氯氟烃(在下文简写成HCFC)，和氢氟烃(在下文简写成HFC)中具有抗溶解性的聚氨酯树脂的原料。这种多元醇，通过使用上述的发泡剂可以提供硬质聚氨酯泡沫体及其复合材料。
上述获得的硬质聚氨酯泡沫体与通常使用氯氟烃(在下文中简写成CFC)发泡剂而获得的聚氨酯具有相同的优良性能。因此，本发明的硬质聚氨酯泡沫体常用作绝热材料或电冰箱、冷冻货物仓库、隔热板材、船舶和车辆的绝热结构材料。
在通常的聚氨酯泡沫体生产过程中，通常使用氟里昂，尤其是CFC-11(三氯氟甲烷)和CFC-12(二氯二氟甲烷)(它们均属于CFC)进行发泡。人们已经公认这些材料是一种有害的。破坏环境的材料，它分解了地球的臭氧层，增加了温室效应。因此，近来对这些物质的生产和使用已进行了限制。同时已集中注意到以HCFC-123(2,2-二氯-1,1,1-三氟乙烷)，HCFC-141b(1,1-二氯-1-氟乙烷)以及辅助的HFC-134a(1,1,1,2-四氟乙烷),HFC-152a(1,1-二氯乙烷)为代用品来替代CFC-11和CFC-12。然而，这些代用品与CFC-11和CFC-12相比，对聚氨酯具有较大的溶解能力，因而易于显著地破坏聚氨酯泡沫体的性能(例如减少封闭气孔的含量和降低泡沫体的强度)。尤其是作为硬质聚氨酯泡沫体特点的绝热性能大大地降低了。这是由于在发泡反应过程中上述的氟里昂溶解了泡沫体的封闭气孔壁之缘故。
因此，期望得到一种新颖的聚氨酯树脂。通常用作聚氨酯树脂原料的聚亚氧烷基多元醇，用增加烯化氧添加量的方法来降低其粘度。由此，在聚氨酯泡沫体生产过程中容易进行操作。但是，过量的烯化氧添加物导致聚氨酯树脂溶解在HCFC-123和HCFC-141b和HFC之中，因此使用这些发泡剂事实上变成不可能的，另一方面，当烯化氧添加量减少时，多元醇变成固体的或极粘滞的，难于进行操作。
日本专利发明特开昭57-151613(1982)和特开昭57-151614(1982)披露了如下一种方法，为降低胺基多元醇和芳香基聚酯多元醇混合物的粘度(后者未添加入烯化氧)，掺混入一种低分子量多元醇。
综上所述，为了保持在HCFC-123,HCFC-141b和HCF中的抗溶解性，聚氨酯泡沫体生产的操作效率必然大受损失。迄今尚未找到一种具有适于发泡操作的粘度，并在HCFC-123、HCFC-141b和HFC中的混合和分散能力优良的聚亚氧烷基多元醇。
本发明涉及一种新颖的多元醇，它是通过使用一种特定的多元醇，聚亚氧烷基多元醇，脂肪族胺和/或链烷醇胺为原料，并添加一种有机多元羧酸或其酸酐以及烯化氧而得到的；一种聚氨酯树脂，它是通过上述新型的多元醇和有机多异氰酸酯而制得的；一种硬质聚氨酯泡沫体，它是通过使用一种低公害的氢氯氟烃或氧氟烃发泡剂而制得的；以及使用它们制得的一种复合材料。
使用本发明多元醇制备硬质聚氨酯泡沫体的生产过程能实现高的操作效率和低的公害。另外，由此制得的泡沫体的性能与使用通常的氯氟烃而制得的硬质聚氨酯泡沫体的性能是相同的。因此，本发明的硬质聚氨酯泡沫体对于绝热材料和结构绝热材料是很有用的。
本发明目的是提供聚氨酯树脂及硬质聚氨酯泡沫体的制备方法，它和使用常规氯氟烃的相比，尽管使用了低公害的氢氯氟烃和/或氢氟烃，它仍给出相同的聚氨酯发泡操作效率和综合的发泡体性能。
为了达到上述目的，本发明者进行了充分的调查研究而完成了本发明。
本发明从以下(1)至(5)几个方面进行说明。
(1)一种多元醇，其制备过程包括使用在一个分子中具有至少一个酯键合和/或酰胺键合的化合物或者它们的混合物作为原料，并且进一步添加一种烯化氧，所说的化合物是由一种有机多元羧酸或其酸酐和选自下列一组化合物中的单个化合物或其混合物进行反应而获得的：
(a)在一个分子中含有3-8个羟基的一种多元醇，
(b)在一个分子中含有3-8个羟基的聚亚氧烷基多元醇，
(c)在一个分子中含有2-6个伯胺基和/或仲胺基，并用下列通式(Ⅰ)表示的一种脂肪族胺：
Figure C9510085800061
其中R为在一个分子中含1-6个碳原子的亚烷基，n是0或1-4的整数，和
(d)一种如通式(Ⅱ)或通式(Ⅲ)所示的链烷醇胺：
H2N-R1OH     (Ⅱ)
HN=(R1OH)2    (Ⅲ)其中R1为具有1-6个碳原子的亚烷基。
(2)一种聚氨酯树脂，它是由一种多元醇和一种有机多异氰酸酯混合和反应而获得的，它包括部分使用或全部使用上述(1)中所述的多元醇。
(3)一种硬质聚氨酯泡沫体，它是由一种有机多异氰酸酯和一种含有多元醇、发泡剂、催化剂、泡调整剂及其它添加剂的树脂预混物进行混合和反应而获得的，它包括部分使用或全部使用上述(1)中所述的多元醇，而所说的发泡剂是选自由氢氯氟烃、氢氟烃组成的一组中的单个发泡剂或混合发泡剂，或者含有其它发泡剂，如果需要的话，或由它们和一种助发泡剂(水和/或低沸点化合物)组成的混合发泡剂，
(4)一种制备硬质聚氨酯泡沫体的方法，它是将一种有机多异氰酸酯和一种含有多元醇、发泡剂、催化剂、泡调整剂及其它添加剂的树脂预混物进行混合和反应的，它包括部分使用或全部使用上述(1)中所述的多元醇，而所说的发泡剂是选自由氢氯氟烃，氢氟烃组成的一组中的单个发泡剂或混合发泡剂，或者含有其它发泡剂，如果需要的话，或由它们和一种助发泡剂(水和/或低沸点化合物)组成的混合发泡剂。
(5)一种制备硬质聚氨酯泡沫体复合材料的方法，它是将一种有机多异氰酸酯和一种含有多元醇、发泡剂、催化剂、泡调整剂及其它添加剂的树脂预混物进行混合，并使所述的硬质聚氨酯泡沫体在一种面材上或者一个由多面面材围成的阴模内成型，构成所述的复合材料，它包括部分使用或全部使用上述(1)中所述的多元醇，而所说的发泡剂是选自由氢氯氟烃、氢氟烃组成的一组中的单个发泡剂或混合发泡剂，或者含有其它发泡剂，如果需要的话，或由它们和一种助发泡剂(水和/或低沸点化合物)组成的混合发泡剂。
在本发明的方法中使用的多元醇(a)或聚亚氧烷基多元醇，每个分子中有3-8个羟基，该羟基与有机多元羧酸或其酸酐反应生成一种至少有一个酯键合的化合物作为原料。接着加入烯化氧进一步与该化合物反应生成一种至少有一个酯骨架的多元醇。
在本发明方法中使用的典型多元醇(a)包括甘油，三羟甲基丙烷，1,2,6-己三醇，三乙醇胺，季戊四醇，四羟甲基环己烷，甲基葡糖苷，2,2,2,6-四(羟基)环己醇，山梨糖醇，甘露糖醇和半乳糖醇。聚亚氧烷基多元醇(b)能够通过把烯化氧添加到上述多元醇中而获得。这些化合物可单独使用或者混合使用。
有机多元羧酸及其酸酐的典型例子包括琥珀酸，邻苯二酸，苯偏三酸，苯均四酸，甲基四氧化邻苯二酸，马来酸以及这些多元羧酸的酸酐。这些化合物可以单独使用也可以混合使用。
本发明中使用的烯化氧包括如：环氧乙烷，环氧丙烷和环氧丁烷。这些环氧化物可以单独使用也可以混合使用，可以同时加入也可以逐次地加入。
本发明中使用的多元醇正如上所述，是通过如下的加成反应获得的，即在一个分子中含有3-8个羟基的多元醇(a)和/或聚亚氧烷基多元醇(b)中，相对于每一个羟基，先与0.125-1.0摩尔的有机多元羧酸或其酸酐反应，然后再与1.0-3.0摩尔的烯化氧反应而制得的。
当在一个分子中的羟基数小于3时，所生成的聚氨酯泡沫体趋向低的的泡沫强度。另一方面，当在一个分子中的羟基数超过8时，产生了太多的酯键合，多元醇的粘度太高，因而发泡操作中的操作效率很低。
当相对于多元醇(a)和/或聚亚氧烷基多元醇(b)中每一个羟基的有机多元羧酸或其酸酐的添加量小于0.125摩尔时，通过与多异氰酸酯反应而得到的硬质聚氨酯泡沫体在氟里昂中的溶解度增加了，其物理性能受损失，尽管它与HCFC及HFC的混合和分散能力与通常的多元醇一样。相反地，当有机多元羧酸或其酸酐超过1.0摩尔时，产生高粘度的多元醇，它在HCFC和HFC中的混合和分散能力变差，因而产生了使聚氨酯泡沫体变脆的毛病。
当相对于原料中每一个羟基和/或羧基的烯化氧添加量小于1.0摩尔时，该多元醇含有许多残留在分子中的游离羟基和/或羧基，所生成的聚氨酯的物理性能很差。相反地，当相对于每一个羟基的烯化氧添加量超过3.0摩尔时，所生成的聚氨酯泡沫在氟里昂中的溶解度增加了，其物理性能受损失，尽管多元醇具有低的粘度和在HCFC和HFC中具有很好的混合和分散能力。
用于本发明中的有机多元羧酸或其酸酐和烯化氧和多元醇(a)和/或聚亚氧烷基多元醇(b)中的羟基间加成反应的催化剂为通式(Ⅳ)或通式(Ⅴ)表示的胺化合物：
NR2R2R3              (Ⅳ)
R2R3N(CH2)mNR2R3              (Ⅴ)其中R2和R3是氢原子或选自1-6个碳原子的烷基-CH2CH2OH和-CH2CH(CH3)OH中的一个基团，但是在通式(Ⅳ)中，R2和R3不能同时为氢原子，m是1-6的整数。
典型的胺化合物包括：二丁胺，乙二胺，四亚甲基二，一乙醇胺，二乙醇胺，三乙醇胺，异丙醇胺，三乙胺，三正丙胺，二正丙胺，正胺，正戊胺，N,N-二甲基乙醇胺，异丁胺，异戊胺和甲基二乙胺。
金属氢氧化物也可用作上述加成反应的催化剂。碱金属氢氧化物的典型例子包括氢氧化锂、氢氧化钠、氢氧化钾、氢氧化镁、氢氧化钙和氢氧化钡。
上述的胺和金属氢氧化物催化剂能单独使用或混合使用。
用于本发明的上述催化剂，相对于每100重量份的多元醇(a)和/或聚亚氧烷基多元醇(b)，其量为0.1-2.0重量份。
本发明的多元醇按如下方法获得，即将多元醇(a)和/或聚亚烷基多元醇(b)，有机多元羧酸或其酸酐和催化剂加入高压釜中，使这些原料进行反应，然后逐渐地加入烯化氧使之进行加成反应。优选的反应温度为90-130℃，温度低于90℃，反应难以进行。相反地，温度超过130℃，易于产生副反应。
用于本发明的脂肪族胺为伯胺和/或仲胺基团。在一个分子中这两种基团的总数为2-6，这些胺基与有机羧酸或其酸酐反应。烯化氧进一步与所生成的中间体反应生成具有酰胺基和酯骨架的多元醇(该骨架是由羧基和烯化氧反应而生成的)。本发明中用作另一种原料的脂肪族胺(c)如通式(Ⅰ)所示：
Figure C9510085800111
其中R是1-6个碳原子的亚烷基，n是0或1-4的整数。
上述适用的典型脂肪族胺(c)包括：乙二胺、二亚乙基三胺、三亚乙基四胺、四亚乙基五胺和五亚乙基六胺。这些脂肪族胺可单独使用或混合使用。
如上所述，用于本发明的另一种多元醇按如下方法制得，即在一个分子中含有2-6个伯胺基和/或仲胺基的每一个脂肪族胺(c)中，添加入0.166-1.0摩尔的有机多元羧酸或其酸酐，随后再添加1.0-3.0摩尔的烯化氧而得到。
当一个分子中的伯胺和/或仲胺基团数小于2时，所生成的聚氨酯泡沫体的泡沫强度低。反之，在一个分子中的胺基数超过6时，酰胺基和酯的键合增加，因而生成的多元醇的粘度增大，在发泡操作中在操作效率方面产生了相反的效果。
当相对于每一个伯胺和/或仲胺基团，和其反应的有机多元羧酸或其酸酐的量小于0.166摩尔时，所生成的聚氨酯泡沫体的性能易于受损坏，尽管其在HCFC-123、HCFC-141b和HFC中的混合和分散能力和通常的聚亚烷基多元醇相同。反之，当有机多元羧酸或其酸酐的量超过1.0摩尔时，导致多元醇粘度增大，在HCFC中混合和分散能力降低以及所生成的聚氨酯泡沫体变脆等缺点。
当相对于每一个伯胺和/或仲胺基团，和其反应的烯化氧的量小于1.0摩尔时，反应之后残留有未反应的胺基和羧基。并且它与有机多异氰酸酯的反应性变坏。反之，其量超过3.0摩尔时，聚亚氧烷基多元醇的粘度降低，所生成的聚氨酯泡沫体的性能变坏，尽管它在HCFC-123,HCFC-141b和HFC中混合和分散能力得到改善。
用于本发明中的有机多元羧酸或其酸酐和烯化氧对脂肪族胺(c)进行加成反应的催化剂与上述的多元醇(a)和/或聚亚氧烷基多元醇(b)的反应中所用的催化剂相同。
用于制备多元醇的反应温度和其它反应条件也和上述的相同。
除了伯胺基和/或仲胺基外，还具有羟基的、并用下列通式(Ⅱ)和通式(Ⅲ)表示的链烷醇胺(d)也可用于本发明的方法中：
      H2N-R1OH   (Ⅱ)
      HN=(R1OH)2  (Ⅲ)其中R1是1-6个碳原子的亚烷基。
适用于本发明的典型的链烷醇胺(d)包括：一乙醇胺、二乙醇胺、一异丙醇胺、一丁醇胺和二己醇胺。
链烷醇胺(d)可以单独与有机多元羧酸或其酸酐反应，也可以与选自多元醇(a)。聚亚氧烷基多元醇(b))和脂肪族胺(c)中的单个化合物或多个化合物混合之后再与有机多元羧酸或其酸酐反应而制得原料。在上述的原料中加入烯化氧并与之反应而得到多元醇。
本发明的多元醇可单独使用也可与其它多元醇混合使用。
被混合使用的其它多元醇，相对于每100重量份的总的多元醇，其量为0-70重量份。
适用的典型的其它多元醇有羟基值为200-800mg KOH/g的聚醚多元醇，它是由烯化氧和多元醇和/或多羟基化合物(如乙二醇、丙二醇、二乙三醇、三乙二醇、二丙二醇、甘油、三羟甲基丙烷、1,3,6-己三醇、季戊四醇、山梨糖醇、蔗糖、双酚A、酚醛清漆、羟基化的1,2-聚丁二烯和羟基化1,4-聚丁二烯)；链烷醇胺(如二乙醇胺和三乙醇胺)；胺类(如乙二胺、二亚乙基三胺、氨、苯胺、甲苯二胺、二甲苯二胺、二胺基二苯基甲烷)以及其它含有至少两个活泼氢原子的化合物进行加成聚合而制得的。适用于制备这些聚亚氧烷基多元醇的烯化氧有环氧乙烷、环氧丙烷、环氧丁烷和苯乙烯氧化物。聚四亚甲基醚二醇、聚酯多元醇(由多元醇和有机多元羧酸或其酸酐制得)以及聚己内酯共聚酯多元醇也可使用。
适用于本发明方法中的有机多异氰酸酯没有作特别的强行限制。
通常公知的有机多异氰酸酯，例如芳族的、脂族的和脂环族的多异氰酸酯及其改性的产品均可使用。适用的典型的多异氰酸酯包括：苯二异氰酸酯、二苯甲烷二异氰酸酯、粗的二苯甲烷二异氰酸酯、甲苯二异氰酸酯、粗的甲苯二异氰酸酯、二甲苯二异氰酸酯、六亚甲基二异氰酸酯、异佛尔酮二异氰酸酯、氢化二苯甲烷二异氰酸酯、氢化甲苯二异氰酸酯、三苯甲烷三异氰酸酯、甲苯三异氰酸酯、多亚甲基一多苯基多异氰酸酯、改性的多异氰酸酯(如碳化二亚胺改性的二苯甲烷二异氰酸酯)以及以异氰酸酯封端的预聚物(它可由上述的多异氰酸酯和聚亚氧烷基多元醇或聚合物多元醇以NCO/活泼氢的当量比为2-20进行反应而制得的，其异氰酸酯含量为5-35％(重量))。
这些多异氰酸酯可以单独使用或混合使用。
该多异氰酸酯相对树脂预混物中羟基的当量比在0.8-5.0范围内。当量比超过5.0导致未反应的多异氰酸酯的残留。反之，当量比小于0.8导致未反应的聚亚氧烷基多元醇的残留。因此上述的范围是最可取的。
用于本发明的发泡剂为氢氯氟烃和氢氟烃。
典型的氢氯氟烃包括：2,2-二氯-1,1,1-三氟乙烷(HCFC-123)、1,1-二氯-1-氟乙烷(HCFC-141b)和-氯二氟甲烷。代表性的氢氟烃包括；1,1,1,2-四氟乙烷和1,1-二氟乙烷。这些发泡剂可以单独使用或混合使用。当需要时可以结合使用水和/或低沸点化合物及其它的助发泡剂。
相对于每100重量份的树脂预混物，水的用量通常为0.5-5.0重量份。典型的低沸点化合物包括：二氯甲烷和其它低沸点的烃(沸点为10-50℃)以及它们的混合物。通用的氯氟烃也可以结合使用。
在本发明的硬质聚氨酯泡沫体制备中可以使用的催化剂包括如：胺催化剂，例如三乙胺、三丙胺、三异丙胺、三丁胺、三辛胺、十六烷基二甲胺、N-甲基吗啉、N-乙基吗啉、N-十八烷基吗啉、-乙醇胺、二乙醇胺、三乙醇胺、N-甲基二乙醇胺、N,N-二甲基乙醇胺、二亚乙基三胺、N,N,N′,N′-四甲基亚乙基二胺、N,N,N′,N′-四甲基亚丙基二胺、N,N,N′,N′-四甲基丁烷二胺、N,N,N′,N′-四甲基-1,3-丁烷二胺，N,N,N′,N′-四甲基六亚甲基二胺、双〔2-(N,N-二甲基胺基)乙基〕醚、N,N-二甲基苄胺、N,N-二甲基环己胺、N,N,N′,N′,N′-五甲基二亚乙基三胺、三亚乙基二胺、伯胺和仲胺的三亚乙基二胺氧化烯加成物的甲酸和其它酸的盐，氮杂环化合物(如N,N-二烷基哌嗪)和各种各样的N,N′,N′-三烷基胺基烷基六氧化三嗪，例如β-胺基羰基催化剂(在日本特开昭52-043517(1977)中透露的)和β-胺基腈催化剂(在日本特开昭53-014279(1978)中透露的)；以及有机金属催化剂，例如乙酸锡、辛酸亚锡、油酸亚锡、月桂酸亚锡、二乙酸二丁基锡、二月桂酸二丁基锡、二氯化二丁基锡、辛酸铅、环烷酸铅、环烷酸镍以及环烷酸钴。
这些催化剂可以单独使用或结合使用。催化剂使用量在0.001-10.0重量份范围内(相对于100重量份的多元醇)。
用于本发明中的泡调整剂为通常公知的有机硅氧烷表面活性剂。典型的泡调节剂包括日本的Unicar Co.,Ltd.的产品：L-520、L-540、L-5340、L-5410、L-5420、L-5710和L-5720；Toray Silicone Co.,Ltd.的产品：SH-190、SH-192、SH-193、SH-194和SH-195；Shinetsu silicone Co.,Ltd.的产品：F-305、F-306、F-317、F-341和F-345以及Toshiba silicone Co.,Ltd.的产品：TFA-4200。
所用泡调节剂的量在0.1-20重量份范围内(相对于100重量份的多元醇和有机多异氰酸酯的总和)。
可用的阻燃剂有三(2-氯代乙基)磷酸酯、三(二氯代丙基)磷酸酯、三(二溴代丙基)磷酸酯、Daihachi Chemical Co.,Ltd.的产品：CR-505和CR-507，和AkzoJapan Co.,Ltd的产品：Fyrol-6。
如果需要的话，其它的在聚氨酯中通常使用的添加剂，例如增塑剂、填料、抗氧剂、稳定剂、紫外线吸收剂及吸热剂也可以加入。
为了实施本发明，将多元醇、催化剂、泡调节剂、阻燃剂、发泡剂(如1,1-二氯-1-氟乙烷(HCFC-141b)、1,1-二氯-2,2,2-三氟乙烷(HCFC-123)、1,1,1,2-四氟乙烷、1,1-二氟乙烷、一氯二氟甲烷及其它添加剂按上述量混合成泡沫预混物。
使用聚氨酯调和机器，使树脂预混物迅进而连续地与有机多异氰酸酯按恒定比混合，其条件是NCO/活泼氢当量比为0.8-5.0。
将制得的混合物连续地注入阴模或模具内。注入之后，硬质聚氨酯泡沫体的液态原料在几分钟之内发泡、固化。
本发明的硬质聚氨酯泡沫体可用于绝热材料或电冰箱、隔热板材、船舶和车辆的结构材料。
实施例1
将120克乙二胺和200克琥珀酸酐加入到一个2升的高压釜中。用氮气替换高压釜内的空气。将混合物加热到120℃，加入1.7克的三乙胺并进行混合，然后逐渐加入232克的环氧丙烷。反应3个小时后，从反应体系中除去未反应的环氧丙烷。由此获得521克的多元醇，其羟值为586mg KOH/g，粘度为35000厘泊/25℃，酸值为0.1mg KOH/g(在表2中为多元醇No.1)。其结果列于表2中。
(聚氨酯树脂的制备)
将所制得的12.00克多元醇、有机多异氰酸酯(MDI-CR,NCO％为31.0,Mitsui Toatsu ChemicalsIno.的产品)和0.12克的Kaolizer No.1(胺催化剂，Kao Co.,Ltd.的产品)按表3、表7和表8中所列的配比。在室温下进行反应，并测量出所制得的聚氨酯树脂对氟里昂的吸收率。其结果列于同一表中。
(硬质聚氨酯泡沫体的制备)
将1.0克水1.5克硅氧烷表面活性剂L-5420(NipponUnicar Co.,Ltd.的产品)，3.0克KaolizerNo.1(Kao Co.,Ltd.的产品)以及在表4和表9中所列举的相应量的氟里昂加入到所制得的100克多元醇中，进行混合，制得预混物。将所制得的预混物和同一表中所列举的相应量的多异氰酸酯(MDI-CR，粗二苯甲烷二异氰酸酯，Mitsui ToatsuChemlcals Inc.的产品)，在室温下混合，并进行反应，然后注入到模具中，制得硬质聚氨酯泡沫体。
在制备树脂预混物中，观察氟里昂和多元醇间的混合和分散能力(操作效率)，并测量硬质聚氨酯泡沫体的密闭微孔的含量。其结果列于同一表中。
在比较实施例中所用的多元醇的组分和性能列于表1中。
                  表1多元醇No.                  (1′)              (2′)多元醇                     甘油                甘油
                                           蔗糖烯化氧                环氧丙烷             环氧丙烷羟值(mg KOH/g)             450                  450粘度(厘泊/25℃)            480                 8500实施例2-78和比较实施例1-24
按实施例1所述的相同步骤来制备多元醇。
当使用金属氢氧化物催化剂时，用酸中和反应了的物料。
根据原料体积的大小选用2-4升的高压釜。
实施例2-33，比较例1～12(表2-4)涉及的是由脂肪族胺(c)制得的多元醇，实施例34～78，比较实施例13～24(表5～10)涉及的是由多元醇(a)或聚亚氧烷基多元醇(b)制得的多元醇。
由表1到表10中可以看出，根据本发明的方法所制得的多元醇，甚至在使用氢氯氟烃(如HCFC-123、HCFC-141b)或氢氟烃(如HFC-134b)作为发泡剂的发泡体系中，也能保持预混物制备中的操作效率并和使用氯氟烃的通常聚氨醇发泡体系的具有相同的硬质聚氨酯泡沫体性能。
                                                           表2
                       实施例                                                      比较实施例
   1    2    3     4     5     6    7     8    9    10    11     1     2     3     4
多元醇NO.   (1)   (2)   (3)    (4)    (5)    (6)   (7)    (8)   (9)    00  01*  (3*)  (4*)  (5*)  (6*)
脂肪族胺(g)
乙二胺   120
二亚乙基三胺   206   206    206   103    206    206     206     206     206    206
三亚乙基四胺    292    292
五亚乙基六胺   464    464
PCAA(g)
琥珀酸酐   200   200   200    200    200    200   200    200   300    200     200     600     60    200
邻苯二酸酐    296
催化剂(g)
三乙胺   1.7   2.3   3.3    2.2    2.8    2.8    3.0   1.4    2.8    3.6     1.6     3.6     1.6    2.7
二甲基乙醇胺   4.1
KOH    2.2    2.8    3.0   1.4    2.7
烯化氧(g)
环氧丙烷   232   348   696    1044    464    1392   696    1392   522    696     116     116     348    1392
环氧乙烷    528
产量(g)   521   710   1047    1380    883     1780   1293    1874   898    870   1070     512     897     547    1620
注：PCAA多元羟酸酐
                                                       表3(聚氨酯树脂)
                                       实施例             比较实施例
  12     13     14     15     16     17     18      19     20     21     22     5      6     7     8
多元醇NO.   (1)    (2)     (3)     (4)     (5)     (6)    (7)     (8)    (9)     00     00  (3*)  (4*)  (5*)  (6*)
羟值(mg KOH/g)    586     555     382     291     587     284    545     373     170     451     351     681     297     709     215
粘度(厘泊/25℃)  35000   33000   23000   15000   38000     850  39000   11000    5600    9800   34000    7300  189000   13100    5300
酸值(mg KOH/g)    0.1     0.2     0.0     0.0     0.2     0.0    0.1     0.0     0.0     0.2     0.2     101      57     0.0     0.0
树脂配方(g)
多元醇  12.00   12.00   12.00   12.00   12.00   12.00  12.00   12.00   12.00   12.00   12.00   12.00   12.00   12.00   12.00
MDI-CR  17.07   16.17   12.13    8.48   17.09    8.27  15.87   10.86    4.95   13.14   10.22   22.78   10.31   20.05    6.26
Kaolizer NO.1   0.12    0.12    0.12    0.12    0.12    0.12   0.12    0.12    0.12    0.12    0.12    0.12    0.12    0.12    0.12
氟里昂的吸收率
CFC-11
0小时  20.19   28.29   23.25   20.60   29.21   20.39  27.99   22.98   17.07   25.26   22.34   34.90   22.43   32.17   18.38
24小时  20.10   29.29   23.25   20.60   29.21   20.39  27.99   22.98   17.07   25.26   22.34     :      :   32.19   18.40
吸收率(％)   0.0     0.0     0.0     0.0     0.0     0.0    0.0     0.0    0.0    0.0     0.0     :      :    0.06     0.1
HCFC-123
0小时  20.19   28.29   23.25   20.60   29.21   20.39  27.99   22.98   17.07   25.26   22.34   34.90   22.43   32.17   18.39
24小时  20.20   28.29   23.27   20.60   20.21   20.40  27.99   22.98   17.09   25.26   22.35     :      :   32.85   18.63
吸收率(％)   0.03     0.0     0.1     0.0     0.0    0.05    0.0     0.0     0.1    0.0    0.04     :      :     2.1     1.4
HCFC-141b
0小时  20.19   28.29   23.25   20.60   29.21   20.39  27.99   22.98   17.07   25.26   22.34   34.90    22.43   32.17   18.38
24小时  20.20   28.29   23.26   20.60   29.22   20.40  28.01   22.98   17.08   25.27   22.36     :      :   32.50   18.62
吸收率(％)   0.03     0.0    0.04     0.0    0.03    0.05   0.07     0.0    0.06    0.04    0.09     :      :     1.0    1.3
注：*所获得树脂是脆的，不能得到数据。        氟里昂吸收率：将10g树脂浸入100g氟里昂中，在24
羟值：JIS K1557                                        小时后，所测出的树脂重量的增加量。
粘度：JIS K1557                          MDI-CR：粗的二苯甲烷二异氰酸酯(Mitsui
酸值：JIS K1557                                  Toatsu Chemlcals Inc.的产品)
Kaolizer NO.1：胺基催化剂(Kao)公司产品)
                                                                                       表4(聚氨酯泡沫体)
                                                 实施例               比较实施例
    23     24    25    26    27    28     29     30    31      32     33     9    10     11     12
多元醇No.    (1)    (2)   (3)   (4)   (5)   (6)    (7)    (8)   (9)      00     00  (3*)  (4*)  (5*)  (6*)
羟值(mg KOH/g)    585   291   587   284    545    373   170     451     351    681    297     700    215
粘度(CP/25℃)  35000  33000 28000 15000 38000   850  39000  11000  5600    9800   34000   7300 189000   13100   5300
酸值(mg KOH/g)    0.1    0.2   0.0   0.0   0.2   0.0    0.1    0.0   0.0     0.2     0.2    101     57     0.0    0.0
泡沫体配方(g)
多元醇                                                     100.0
H2O                                                       1.0
L-5420                                                       1.5
Kaolizer No.1                                                       3.0
氟里昂     33     31    25    23    33    23     31      26    19      28      25     36    23     36     21
MDI-CR    171    162   117    93   171   911    160     115    61     135     109    196    95    203     23
操作效率 都很好
CFC-11
HCFC-123
HCFC-141b
封闭微孔含量(％)
CFC-11   88.5    88.8   88.2   88.6   88.6  88.5   87.9    89.5  88 5    87.5    89.1 不可测量
HCFC-123   85.9    85.1   85.4   85.6   85.7  86.2   85.1    86.4  84.2    84.0    87.5
HCFC-141b   86.1    86.7   86.5   85.1   86.9  87.5   85.8    86.9  85.3    86.1    88.2
注：L-5420硅的泡调节剂(Nihon-Unicar Ltd.的产品)
封闭微孔含量：贝克曼气体比较比重计(TOSHIBA Comp.制造)。ASTM D-2856)
                                                                                       表5
                                                        实施例
   34   35    36    37    38    39    40    41    42    43     44    45    46    47    48
多元醇No.   (12)  (13)   (14)   (15)   (16)   (17)   (18)   (19)   (20)   (21)    (22)   (23)   (24)   (25)   (26)
原料(g)
甘油基多元醇(A)    731   531    376    281    632   765   185
山梨醇基多元醇   1124
蔗糖基多元醇   1233    804
三乙醇胺   526
甘油基多元醇(B)     369   185   255
芳族胺基多元醇    50
二乙醇胺    421   213 (多元醇No.22)50
PCAA(g)
琥珀酸酐    467   354    251    564   355    238    169    441    510
邻苯二酸酐    624     297    297   297   297
催化剂(g)
三乙胺    2.2   4.5    2.2    2.2   2.2    2.2    2.2    2.2    2.2     4.5    4.5   4.5   4.5    4.5
二甲基乙醇胺    2.2
KOH    2.2   2.2    2.2    2.2    2.2
烯化氧(g)
环氧丙烷   2538   616    872    654   618    828    784   1024    976     824    782   810   718
环氧乙烷    672
产重(g)   3721  1475   1481   1463  1479   2050   2090   2110   2150   1390     1472   1475  1171  1432
注：PCAA：多元羧酸酐。
                                         表6
                          比较实施例
      13       14        15      16
  多元醇No.     (7′)     (8′)      (9′)   (10′)
  原料(g)
  甘油基多元醇(A)      806      443      1032     262
  山梨醇基多元醇
  蔗糖基多元醇
  三乙醇胺
  甘油基多元醇(B)
  芳族胺基多元醇
  二乙醇胺
  PCAA(g)
  琥珀酸酐      538      886        69     175
  邻苯二酸酐
  催化剂(g)
  三乙胺      4.5       4.5        4.5     2.2
  二甲基乙醇胺
  KOH     2.2
  烯化氧(g)
  环氧丙烷       156       171        399    1063
  环氧乙烷
  产量(g)      1461      1488       1470    1469
注：PCAA：多元羧酸酐。
                                                                      表7(聚氨酯树脂)
                                             实施例
    49     50     51     52      53     54     55     56     57     58     59     60     61     62     63
多元醇No.    (12)    (13)    (14)    (15)     (16)    (17)    (18)    (19)    (20)   (21)    (22)    (23)    (24)    (25)    (26)
羟值(mg KOH/g)     397    363     236     202      365     366     347     256     357    440    451    473    450    461     460
粘度(厘泊/25℃)    1400    810     630   17300    17000   21000   22000   36000   11000   1000   5100   5080   6200   8000   10000
酸值(mg KOH/g)     0.1    0.0     0.0     0.0      0.1     0.1     0.0     0.1     0.1    0.0    0.0    0.0    0.0    0.0     0.0
树脂配方(g)
多元醇   12.00  12.00   12.00   12.00    12.00   12.00   12.00   12.00   12.00  12.00   12.00  12.00  12.00  12.00   12.00
MDl-CH   12.72  10.57    6.87    5.88    10.63   11.73   11.12    8.17   11.44  14.10   14.45  15.31  14.42  14.77   14.74
Kaolizer No.1    0.12   0.12    0.12    0.12     0.12    0.12    0.12    0.12    0.12   0.12    0.12   0.12   0.12   0.12    0.12
氟里昂吸收率
CFC-11
0小时   24.84   22.69   18.00   18.00    22.75    23.85   23.24   20.29   23.56  26.22   26.57  27.43  26.54  26.89   26.96
24小时   24.84   22.69   18.99   18.01    22.75    23.85   23.24   20.29   23.56  26.22   26.57  27.43  26.54  26.80   26.36
吸收率(％)     0.0     0.0     0.0     0.0      0.0      0.0     0.0     0.0     0.0    0.0    0.0    0.0    0.0    0.0     0.0
HCFC-123
0小时   24.94   22.69   18.09   18.00    22.75    23.85   23.24   20.29   23.56  26.22   26.57  27.43   26.54  26.89   26.86
24小时   24.84   22.69   19.00   18.01    22.75    23.85   23.24   20.29   23.56  26.22   26.50  27.46   26.55  26.90   26.83
吸收率(％)     0.0     0.0    0.05     0.0      0.0      0.0     0.0     0.0     0.0    0.0    0.08   0.11    0.04   0.04    0.07
HCFC-141b
0小时   24.84   22.60   18.99   18.00    22.75    23.85   23.24   20.29   23.56   26.22   26.57  27.43   26.54  26.89   26.36
24小时   24.84   22.69   18.99   18.00    22.75    23.85   23.24   20.29   23.56   26.22   26.59  27.45   26.55  26.91   26.87
吸收率(％)     0.0     0.0     0.0     0.0      0.0      0.0     0.0     0.0     0.0     0.0    0.08   0.07    0.04   0.07    0.04
                                   表8(聚氨酯树脂)
                            比较实施例
      17        18       19      20
多元醇No.     (7′)      (8′)      (9′)   (10′)
羟值(mg KOH/g)      321        155        685      171
粘度(厘泊/25℃)     2100       7160        980      480
酸值(mg KOH/g)      256        186        0.0      0.0
树脂配方(g)
多元醇     12.00      12.00      12.00    12.00
MDI-CR     16.81       9.93      19.95     4.98
Kaolizer No.1      0.12       0.12       0.12     0.12
氟里昂吸收率
CFC-11
0小时     28.93      22.05      32.07    17.10
24小时                       32.09    17.10
吸收率(％)                         0.1      0.0
HCFC-123
0小时      28.93      22.05      32.07    17.10
24小时                        32.89    17.86
吸收率(％)                          2.6      4.4
HCFC-141b
0小时      28.93      22.05      32.07    17.10
24小时                        32.55    17.60
吸收率(％)                          1.5      2.9
注：制得的树脂溶于氟里昂中，未得到数据。
                                                                                     表9(聚氨酯泡沫体)
                                                               实施例
   64     65    66    67     68     69     70     71     72     73     74     75    76     77     78
多元醇No.   (12)   (13)  (14)   (15)    (16)    (17)    (18)    (19)    (20)    (21)    (22)    (23)   (24)    (25)    (26)
羟值(mg KOH/g)    397    363   236   202     365     366     317     255     357     440     451     478    450     401     460
粘度(CP/25℃)    100    810   630  7300   17000   21000   22000   36000   11000    1000    5100    5080   6200    8000   10000
酸值(mg KOH/g)    0.1    0.0   0.0   0.0     0.1     0.1     0.0     0.1     0.1     0.0     0.0     0.0    0.0     0.0     0.0
泡沫体配方(g)
多元醇                                                         100.0
H2O                                                           1.0
L-5420                                                           1.5
Kaolizer No.1                                                           3.0
氟里昂     27     25    21    20     25     26      25      22     25     28      28     29     29     29      28
MDI-CR    121    112    78    70    112    113     103      83    110    132     135    142    135    138     137
操作效率 都很好
  CFC-11
  HCFC-123
  HCFC-141b
  封闭微孔(％)
  FC-11   88.6    88.5   87.9   88.3    88.2    88.1    87.6    89.8    88.9   87.3    89.0   88.7   88.1    87.9    87.2
  HCFC-123   85.6    85.2   85.6   84.6    85.1    85.3    84.2    85.0    83.2   84.3    88.7   88.5   87.8    87.5    87.1
  HCFC-141p   86.3    86.1   86.5   85.0    86.2    86.4    85.0    86.3    84.5   85.9    88.6   88.4   87.9    87.6    87.0
                                         表10(聚氨酯泡沫体)
                    比较实施例
    21     22       23      24
多元醇No.  (7′)  (8′)     (9′)  (10′)
羟值(mg KOH/g)    321    155       685     171
粘度(CP/25℃)   2100   7160       980     480
酸值(mg KOH/g)    256    186       0.0     0.0
泡沫体配方(g)
多元醇                          100.0
H2O                            1.0
L-5420                            1.5
Kaolizer No.1                            3.0
氟里昂     24     19       36     19
MDI-CR    101     57      197     61
操作效率 都很好
CFC-11
HCFC-123
HCFC-141b
封闭微孔含量(％) 不可测量
CFC-11
HCFC-123
HCFC-141b
〔硬质聚氨酯泡沫体的制备(表11-14)〕
按下述步骤制备硬质聚氨酯泡沫体，并检验其物理性能。
按表11-14所列配比各自制备树脂预混物。然后与上述表中所列的有机多异氰酸酯的规定量，在5000转/分的速率下迅速混合6秒钟。所得的混合物立即注入立式木盒中，其尺寸分别为200×200×200mm和300×300×35mm(厚度)。
将前一盒中硬质聚氨酯泡沫体用于测量其密度、抗压强度和尺寸稳定性，而将后一盒中的泡沫体用于测量其导热性。
预聚物的制备：
多元醇No.1′：将环氧丙烷加入甘油中而获得聚亚氧烷基多元醇，其羟值为450mg KOH/g，粘度为480厘泊/25℃。
TRC-90A：粗的甲苯二异氰酸酯，其NCO含量为39.0％(重量)。
混合预聚物的制备：
将890克的TRC-90A和110克的多元醇No.1′混合物在80℃下加热2个小时，然后冷却至室温。将所得的反应混合物与1000克MDI-CR混合制得混合的预聚物，其NCO含量为31.0％。
                                                             表11实施例和比较实施例
比较实施例 实施例 比较实施例 实施例 比较实施例 实施例 比较实施例 实施例 比较实施例 实施例
     25     79     80     26     81    62     27     83     84      23     65     96     29     87     88
配方(g)
MDI-CR             172             181              170             145              118
多元醇(2)(表2)             100
多元醇(5)(表2)             100
多元醇(7)(表2)              100
多元醇(10)(表2)             100
多元醇(11)(表2)             100
H2O             1.5             1.5              1.5             1.5             1.5
L-5420             1.5             1.5              1.5             1.5             1.5
Kaolizer NO.1             0.2             0.2              0.1             0.2             0.3
发泡剂
CFC-11      41     42     41      37     33
HCFC-141b     35     37     35     32     23
HCFC-123     49    51     40      44     39
HFC-134a
异戊烷
泡沫体性能
密度，自由发泡1)(kg/m3)     25.5    25.8    25.9    25.3    25.5   25.3    25.0    24.3    25.2    25.5    25.1    25.5    24.1    21.5    25.5
抗压强度1)(Kg/m2)     1.33    1.65    1.66    1.51    1.45   1.44    1.70    1.65    1.62    1.50    1.30    1.25    1.81    1.61    1.65
尺寸稳定性1)(％,-30℃×24/小时)      0.4    -0.9    -1.5    -0.6    -1.8   -1.8    -0.4    -0.9    -1.3    -0.2    -0.4    -1.0    -0.2    -0.8    -0.7
导热性2)(4.184kJ/m.hr℃)   0.0150  0.0163  0.0161  0.0165  0.0167 0.0168  0.0161  0.0163  0.0163  0.0163  0.0165  0.0167  0.0160  0.0161  0.0164
注：1)根据JIS A9514 2)根据JIS A1412
                                                                    表12实施例和比较实施例
比较实施例 实施例 比较实施例 实施例 比较实施例 实施例 比较实施例 实施例
     30     89      90     31       91     92     32     93     94      33     95      96
配方(g)
MDI-CR              150              145               115
混合预聚物               145
多元醇(2)
多元醇(5)
多元醇(7)
多元醇(10)              100            100              100
多元醇(11)
多元醇(23)(表5)              100
H2O              1.5             1.5            1.5              1.5
L-5420              1.3             1.5            1.5              1.5
Kaolizer NO.1              0.2             0.3            0.2              0.2
发泡剂
CFC-11      37     33     37     37
ECFC-141b     32      33     32     32
HCFC-123     41      45    40      40
HFC-134a     3
异戊烷      4
泡沫体性能
密度，自由发泡(kg/m3)     24.5    24.8     25.2    24.3      25.3    25.5    25.0    25.1    25.3     25.0    25.1     25.2
抗压强度(k/m2)     1.51    1.32     1.26    1.50      1.32    1.27    1.50    1.30    1.24     1.50    1.30     1.20
尺寸稳定性(％,-30℃×24小时)     -0.1    -0.3     -0.3    -0.2      -0.3    -0.5    -0.2    -0.4    -1.0     -0.2    -0.4     -1.0
导热性(4.184kJ/m.hr.℃    0.0152  0.0159   0.9161  0.0160    0.0162   0.0164   0.0163   0.0165   0.0167    0.0163   0.0165    0.0167
                                                                                       表13实施例和比较实施例
比较实施例 实施例 比较实施例 实施例 比较实施例 实施例 比较实施例 实施例 比较实施例 实施例
   34    97     98      35     99     100     36    101     102     37    103    104     38    105    106
配方(g)
MDI-CR          161             122            121              116             119
混合预聚物
多元醇(12)(表5)          100
多元醇(16)(表5)             100
多元醇(17)(表5)           100
多元醇(18)(表5)             100
多元醇(20)(表5)            100
多元醇(21)(表5)
H2O          1.5              1.5            1.5             1.5            1.5
L-5420          1.5              1.5            1.5             1.5            1.5
Kaolizer No.1          1.9              0.2            2.2             2.0            1.5
发泡剂
CFC-11    39      33     33     32     33
HCFC-141b    33     29     23     28     26
HCFC-123     47     40     40     39     39
泡沫体性能
密度，自由发泡(kg/m3)   25.0   25.3    25.4     24.8    25.0    25.1    25.0   25.0    25.2    24.6    24.7    25.2    24.4    24.5    25.0
抗压强度(kg/m2)   1.55   1.38    1.30     1.30    1.15    1.18    1.65   1.40    1.38    1.50    1.25    1.19    1.51    1.21    1.20
尺寸稳定性(％,-30℃×24小时)   -0.2   -1.5    -0.7     -0.6    -1.8    -2.0    -0.4   -1.0    -1.5    -0.2    -0.8    -1.0    -0.2    -0.7    -0.6
导热性(4,184kJ/m.hr℃  0.016 0.0165  0.0163   0.0168  0.0170  0.0171  0.0163 0.0165   0.0165   0.0165  0.0168  0.0170  0.0161  0.0162  0.0165
                                    表13实施例和比较实施例(续)
  比较实施例      实施例  比较实施例       实施例
     39   107  108      40    109     110
配方(g)
MDI-CR                      140
混合预聚物                       119
多元醇(12)(表5)
多元醇(16)(表5)
多元醇(17)(表5)
多元醇(18)(表5)
多元醇(20)(表5)                        100
多元醇(21)(表5)                      100
H2O                      1.5                        1.5
L-5420                      1.5                        1.5
Kaolizer No.1                      1.6                        1.6
发泡剂
                                                              表13实施例和比较实施例(续)
   比较实施例           实施例   比较实施例           实施例
39 107 108 40 109 110
CFC-11        36       33
HCFC-141b      31      28
HCFC-123      43      39
泡沫体性能
密度，自由发泡(kg/m3) 25.2 25.1 25.5 24.0 24.2 24.8
抗压强度(kg/m2)       1.61      1.40      1.38       1.51      1.20      1.20
尺寸稳定性(％,-30℃×24小时） -0.1 -1.0 -1.2 -0.1 -0.8 -0.8
导热性(4.184kJ/m.hr.℃) 0.0162 0.0164 0.0165 0.0159 0.0160 0.0161
                                                             表14比较实施例
     41          42       43     44        45       46
配方(g)
MDI-CR                      144                    144
多元醇(1′)(表1)                      100
多元醇(2′)(表1)                    100
H2O                      1.5                    1.5
L-5420                      1.5                    1.5
Kaolizer NO.1                      3.0                    2.8
发泡剂
CFC-11     37    37
HCFC-141b         30       30
HCFC-123         44        44
泡沫体性能密度，自由发泡(kg/m3) 24.5 25.0 25.0 25.0 25.1 25.3
抗压强度(Kg/m2)     1.51       0.98       1.05    1.61       1.00      0.95
尺寸稳定性(％,-30℃×24小时) -0.5 -3.6 -5.8 -1.0 -4.8 -7.2
导热性(4,184kJ/m.hr.℃) 0.0168 0.0179 0.0182 0.0165 0.0180 0.0183
(1)带有面料的硬质聚氨酯泡沫体复合材料的制备
根据上述的实施例进行本发明的带有面材的硬质聚氨酯泡沫体复合材料的制备。
在表1，表2和表5中所列举的实施例和比较实施例中的所制得的多元醇被用作硬质聚氨酯泡沫体的原料。
用于本发明的面材包括：波纹纸板，层压纸和其它纸制品；聚乙烯，聚丙烯，聚氯乙烯和其它合成树脂板，以及铝，钢及其它金属板。
1)带有一面面材的聚氨酯泡沫体复合材料
按照表15中所列举的相同配方，在下述条件下，将其喷涂在一面板上而制得带有一面面材硬质聚氨酯泡沫体。在表16中概括了所得产品的性能。喷涂器：Model-FF Head D Gum
        (Gusmer Co.,Ltd.的产品)
输出压力：50kg/cm2
液体温度：40℃
面板：    波纹纸板
                                    表15
           实施例111      112       113        比较实施例47       48        49
配方    (g)MDI-CR多元醇(2)(表2)多元醇(21)(表5)多元醇(1′)(表1)多元醇(2′)(表1)TCEPH2OL-5420Kaolizer No.1LL-690DCFC-11HCFC-141bHCFC-123 154      154       124100      10010010       10        100.5      0.5       0.51.5      1.5       1.51.5      1.5       3.00.1      0.1       0.13346        46 127      127       127100      10010010       10        100.5      0.5       0.51.5      1.5       1.55.0      5.0       5.00.1      0.1       0.1191723
注：TCEP：阻燃剂，三(2-氯代乙基)磷酸酯，Daihachi Chemical Co.产品。
LL-690D：催化剂，在邻苯二甲酸二辛酯中含有40％(重量)的辛酸铅的溶液。
                                           表16
              实施例111        112          113             比较实施例47          48           49
反应活性不剥落时间(秒)下垂现象表观状态粘附性泡沫体密度(kg/m3)抗压强度(kg/m2)导热性(4.184kJ/m.hr.℃)可燃性燃烧时间(秒)燃烧距离(mm) 4～5       4～5         4～5无         无           无好         好           好好         好           好36.5       37.0         37.03.33       3.35         3.250.0175     0.0172       0.017623         24           2318         17           18 5            5～6         5无           有           有好           好           好好           好           好38.0         39.0         39.03.25         3.10         2.950.0180       0.0190       0.018824           35           3319           20           21
注：下垂现象：它是这样的一种现象，当原料混合物喷涂到面板上进
          行发泡时，在其固化之前，原料沿垂直表面下垂或流
          下的现象。
可燃性(阻燃性)：根据AST MD1691进行测量的。2)带有多面面板的硬质聚氨酯泡沫体的制备在试验中，按表17中所列举的配方，在下述条件下，用连续加工的方法制备带有两面面板的硬质聚氨酯泡沫体复合材料板。
发泡机：高压泡沫涂布机Model-MQ
        (Hennecke Machinen Bau产品)
线速度：10米/分
温度：原料：30-40℃，固化炉：55℃
产品：1米宽×40毫米厚
      35毫米泡沫层
面材：顶面和底面均为层压纸。
产品的表面物理性能列于表18中。
                                         表17
              实施例114         115         116           比较实施例50        51          52
配方(g)MDI-CR多元醇(10)(表2)多元醇(11)(表2)多元醇(1′)(表1)多元醇(2′)(表1)TCEPH2OL-5420Kaolizer No.1CFC-11HCFC-141bHCFC-123 145         145         118100         10010010          10          101.5         1.5         1.51.5         1.5         1.50.2         0.2         0.33244          39 144       144         144100       10010010        10          101.5       1.5         1.51.5       1.5         1.53.0       3.0         2.8373044
                                           表18
               实施例114             115           116             比较实施例50         51         52
配方(表17)   114             115           116      50         51         52
面板和泡沫体之间的粘附性   好              好            好      好         好         好
泡沫体密度(kg/m3)   31.5            32.0          31.8      30.0       31.0       31.5
抗压强度(kg/cm2)   1.53            1.50          1.60      1.55       1.05       1.00
抗弯强度(kg/cm2)   2.40            2.30          2.35      2.45       1.95       1.85
导热性(4,184kJ/m.hr.℃) 0.0170          0.0172        0.0173 0.0170     0.0185     0.0186
可燃性燃烧时间(秒)燃烧距离(mm) 22              21            2116              14            15 23         30         3116         21         20
由这些结果可以看出，本发明的多元醇具有合适的反应活性。因此，发泡组分的混合物即使被喷涂到垂直面材上时也不会产生下垂现象，并且在所用泡沫材料喷涂的表面上有好的表观。也能得到泡沫体对面材的好的粘附力。由此获得的硬质泡沫体具有优良的阻燃性和低的导热性，并提供了性能优良的复合材料板。
被用于制备硬质聚氨酯泡沫体复合材料的配方列于表15和表17中。但是，该配方不仅限于上述的实施例，应该理解为列于实施例1-110中的配方都可用于制备聚氨酯泡沫体复合材料。

Claims (7)

1．一种聚氨酯树脂的制备方法，包括将有机多异氰酸酯与包含多元醇组分的树脂预混物进行混合和反应，该多元醇组分的制备是将至少一种在每一个分子中至少有一个酯键合和/或酰氨键合的化合物加成烯化氧，所说的化合物是由脂族有机多元羧酸或其酸酐和选自下列的一种或多种化合物进行反应而获得的：
(a)在一个分子中含有3-8个羟基的脂族多元醇，
(b)在一个分子中含有3-8个羟基的脂族聚亚氧烷基多元醇，和
(c)在一个分子中含有2-6个伯胺基和/或仲胺基，并用下列通式(Ⅰ)表示的脂族胺：
Figure C9510085800021
其中R是在一个分子中含1-6个碳原子的亚烷基，n是0或1-4的整数；
其中所述的多元醇组分作为所用多元醇的全部或一部分，为所用多元醇的30-100％(重量份)；
其中有机多异氰酸酯中的异氰酸酯基对多元醇中的羟基的当量比范围为0.8-5.0。
2．权利要求1的方法，其中多元醇与有机多异氰酸酯的反应是在催化剂存在下进行的。
3．权利要求1的方法，其中部分或全部的有机多异氰酸酯是以异氰酸酯为终端的预聚物。
4．一种制备硬质聚氨酯泡沫体的方法，包括将有机多异氰酸酯与一种树脂预混物进行混合和反应，该预混物包含：
多元醇组分，其为每一分子具有至少一个酯键合和/或酰氨键合的至少一种化合物加成烯化氧而制备的，所说的化合物是由脂族有机多元羧酸或其酸酐和选自下列的一种或多种化合物进行反应而获得的：
(a)在一个分子中含有3-8个羟基的脂族多元醇，
(b)在一个分子中含有3-8个羟基的脂族聚亚氧烷基多元醇，和
(c)在一个分子中含有2-6个伯胺基和/或仲胺基，并用下列通式(Ⅰ)表示的脂族胺：其中R是在一个分子中含1-6个碳原子的亚烷基，n是0或1-4的整数；催化剂，发泡剂，泡孔调节剂以及其他添加剂，其中所述多元醇组分构成所用多元醇的全部或一部分，为所用多元醇的30-100％(重量份)，所述的有机多异氰酸酯中的异氰酸酯基和多元醇中羟基的当量比范围为0.8-5.0，所述发泡剂是选自氢氯氟烃、氢氟烃的一种或混合物，以及它们和水作为辅助发泡剂的混合物。
5．权利要求4的方法，其中氢氯氟烃为2,2-二氯-1,1,1-三氟乙烷或1,1′-二氯-1-氟乙烷，氢氟烃为1,1,1,2-四氟乙烷或1,1-二氟乙烷。
6．权利要求4的方法，其中助发泡剂为低沸点化合物。
7．权利要求4的方法，其中部分或全部的有机多异氰酸酯为预聚物。
CN95100858A 1989-07-19 1995-02-28 聚氨酯树脂及硬质聚氨酯泡沫体的制备方法 Expired - Fee Related CN1045973C (zh)