CN104592610A - 含有二氧化硅的v带底胶配方 - Google Patents
含有二氧化硅的v带底胶配方 Download PDFInfo
- Publication number
- CN104592610A CN104592610A CN201510033261.8A CN201510033261A CN104592610A CN 104592610 A CN104592610 A CN 104592610A CN 201510033261 A CN201510033261 A CN 201510033261A CN 104592610 A CN104592610 A CN 104592610A
- Authority
- CN
- China
- Prior art keywords
- parts
- dioxide
- agent
- rubber
- belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于橡胶带技术领域,特指一种含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:橡胶:100份;二氧化硅:10—90份;填充剂:0—200份;助剂:10—110份;本发明由于二氧化硅在橡胶中生热小,使V带在高速运行时的带体温度比原配方降低了5℃以上,使V带传动效率提高;由于运行中降低了带体温度,V带使用寿命提高30%以上;降低了对环境的污染。
Description
技术领域:
本发明属于橡胶带技术领域,特指一种含有二氧化硅的V带底胶配方。
背景技术:
V带底胶是V带的“心脏”,占V带总重量的70%以上。目前,V带底胶采用的配方里采用炭黑进行补强。但是,原配方采用炭黑补强存在着如下的缺点:
1、由于炭黑在橡胶中生热大,因V带在传动过程中高速运转,运转时炭黑在V带的底胶中生产大量热量,使V带运行时带体温度升高,传动效率降低,浪费能源;
2、运行带体温度高,加速带体老化,影响使用寿命。
3、炭黑在加工过程中对环境污染严重。
发明内容:
本发明的目的是提供一种减少生热,节约能源,减少环境污染,提高产品使用寿命,降低产品成本的含有二氧化硅的V带底胶配方。
本发明是这样实现的:
含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:10—90份;
填充剂:0—200份;
助剂:10—110份。
优选地,含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:60份;
填充剂:53份;
助剂:30份;
其中,所述的助剂的具体组合物及份数如下:
硫磺:2份;
促进剂HMC:1份;
促进剂NS:1.5份;
偶联剂:5份;
增硬补强剂:3份;
氧化锌:8份;
硬脂酸:2份;
防老剂:2份;
增粘剂:5.5份。
上述的填充剂是:煤粉或页岩。
优选地,含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:50份;
填充剂:65份;
助剂:27.5份;
其中,所述的助剂的具体组合物及份数如下:
古马隆:8份;
松焦油:3份;
硫磺:2份;
PEC-4000(聚乙二醇):2份;
促进剂M:1份;
促进剂CZ:2份;
氧化锌:5份;
硬脂酸:2.5份;
防老剂RD:1份;
防老剂4010:1份。
上述的填充剂包括陶土及碳酸钙,其中,陶土及碳酸钙的具体份数如下:
陶土:40份;
碳酸钙:25份。
本发明相比现有技术突出的优点是:
1、本发明由于二氧化硅在橡胶中生热小,使V带在高速运行时的带体温度比原配方降低了5℃以上,使V带传动效率提高;
2、本发明由于运行中降低了带体温度,V带使用寿命提高30%以上;
3、本发明降低了对环境的污染。
具体实施方式:
下面以具体实施例对本发明作进一步描述:
含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:10—90份;
填充剂:0—200份;
助剂:10—110份。
进一步地:含有二氧化硅的V带底胶配方,由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:50—60份;
填充剂:0—100份;
助剂:30—70份。
只要在上述组合物给定的范围内任意取值,均可达到本发明的积极效果,具体举例参见表1、表2。
表1:具体实施例举例:
单位:kg
组合物 | 例1 | 例 | 例 | 例 | 例 | 例 | 例 | 例 | 例 |
橡胶 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
二氧化硅 | 50 | 40 | 55 | 60 | 65 | 70 | 80 | 90 | 10 |
古马隆 | 8 | 7.5 | 8.5 | 9 | 10 | 9 | 7 | 8 | 10 |
松焦油 | 3 | 2.5 | 3.5 | 4 | 4.5 | 3 | 2 | 4 | 5 |
硫磺 | 2 | 1.5 | 3 | 3.5 | 4 | 3 | 2 | 3 | 3 |
PEC-4000 | 2 | 1.5 | 2.5 | 3 | 3.5 | 3 | 2 | 3 | 3 |
促进剂M | 1 | 0.5 | 1.5 | 2 | 2.5 | 1 | 1 | 2 | 2 |
促进剂CZ | 2 | 1.5 | 2.5 | 3 | 3.5 | 2 | 3 | 3 | 3 |
氧化锌 | 5 | 4.5 | 5.5 | 6 | 6.5 | 5 | 5 | 6 | 5 |
硬脂酸 | 2.5 | 2 | 3 | 3.5 | 4 | 3 | 3 | 4 | 3 |
防老剂RD | 1 | 0.5 | 2 | 2.5 | 3 | 2 | 1 | 2 | 2 |
防老剂4010 | 1 | 0.5 | 2 | 2.5 | 3 | 2 | 1 | 2 | 2 |
陶土 | 40 | 40 | 41 | 42 | 43 | 40 | 40 | 43 | 55 |
碳酸钙 | 25 | 30 | 26 | 27 | 28 | 25 | 26 | 27 | 40 |
表2:具体实施例举例:
单位:kg
组合物 | 例1 | 例 | 例 | 例 | 例 | 例 | 例 | 例 | 例 |
橡胶 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
二氧化硅 | 50 | 60 | 70 | 80 | 90 | 40 | 30 | 20 | 10 |
硫磺 | 2.5 | 2 | 3 | 4 | 2 | 4 | 2 | 3 | 2.5 |
氧化锌 | 7.5 | 8 | 8.5 | 8.5 | 9 | 6 | 6.5 | 6 | 7 |
硬脂酸 | 2.5 | 2 | 3 | 4 | 2.5 | 5 | 2.5 | 3 | 4 |
煤粉或页岩 | 55 | 53 | 55 | 53 | 40 | 60 | 80 | 100 | 100 |
促进剂HMC | 1 | 1 | 3 | 1 | 2 | 2 | 1 | 2.5 | 3 |
促进剂NS | 1.5 | 1.5 | 2.5 | 1 | 2 | 2 | 1.5 | 1.5 | 2 |
偶联剂 | 5.5 | 5 | 6 | 5 | 6 | 5 | 5 | 6 | 6.5 |
增硬补强剂 | 3 | 3 | 4 | 3 | 4 | 3 | 3 | 4.5 | 5 |
增粘剂 | 6 | 5.5 | 6.5 | 6 | 5.5 | 6 | 5 | 7 | 7 |
防老剂 | 2.5 | 2 | 3 | 3 | 2 | 3 | 2.5 | 2 | 3 |
上述实施例仅为本发明的较佳实施例之一,并非以此限制本发明的实施范围,故:凡依本发明的形状、结构、原理所做的等效变化,均应涵盖于本发明的保护范围之内。
Claims (5)
1.含有二氧化硅的V带底胶配方,其特征在于:由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:10—90份;
填充剂:0—200份;
助剂:10—110份。
2.根据权利要求1所述的含有二氧化硅的V带底胶配方,其特征在于:由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:60份;
填充剂:53份;
助剂:30份;
其中,所述的助剂的具体组合物及份数如下:
硫磺:2份;
促进剂HMC:1份;
促进剂NS:1.5份;
偶联剂:5份;
增硬补强剂:3份;
氧化锌:8份;
硬脂酸:2份;
防老剂:2份;
增粘剂:5.5份。
3.根据权利要求2所述的含有二氧化硅的V带底胶配方,其特征在于:所述的填充剂是:煤粉或页岩。
4.根据权利要求1所述的含有二氧化硅的V带底胶配方,其特征在于:由如下重量份数的组合物制备而成:
橡胶:100份;
二氧化硅:50份;
填充剂:65份;
助剂:27.5份;
其中,所述的助剂的具体组合物及份数如下:
古马隆:8份;
松焦油:3份;
硫磺:2份;
PEC-4000:2份;
促进剂M:1份;
促进剂CZ:2份;
氧化锌:5份;
硬脂酸:2.5份;
防老剂RD:1份;
防老剂4010:1份。
5.根据权利要求4所述的含有二氧化硅的V带底胶配方,其特征在于:所述的填充剂包括陶土及碳酸钙,其中,陶土及碳酸钙的具体份数如下:
陶土:40份;
碳酸钙:25份。