CN104561860A - 一种高强铝合金的热处理工艺 - Google Patents

一种高强铝合金的热处理工艺 Download PDF

Info

Publication number
CN104561860A
CN104561860A CN201410350919.3A CN201410350919A CN104561860A CN 104561860 A CN104561860 A CN 104561860A CN 201410350919 A CN201410350919 A CN 201410350919A CN 104561860 A CN104561860 A CN 104561860A
Authority
CN
China
Prior art keywords
alloy
aluminum alloy
treatment
alloy parts
thermal treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410350919.3A
Other languages
English (en)
Other versions
CN104561860B (zh
Inventor
肖春红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Powermetal Industrial Co., Ltd.
Original Assignee
ANHUI SIXIANG ALUMINUM PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SIXIANG ALUMINUM PRODUCTS Co Ltd filed Critical ANHUI SIXIANG ALUMINUM PRODUCTS Co Ltd
Priority to CN201410350919.3A priority Critical patent/CN104561860B/zh
Publication of CN104561860A publication Critical patent/CN104561860A/zh
Application granted granted Critical
Publication of CN104561860B publication Critical patent/CN104561860B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高强铝合金的热处理工艺，使用如下步骤加工：（1）将铝合金工件在450-500℃下固溶处理2-3h；（2）将固溶处理好的铝合金工件在28-35℃下使用金属离子水溶液冷淬处理；（3）将冷淬处理好的铝合金工件在158-160℃下时效处理5-8h，本发明提供的高强铝合金的热处理工艺方法简单，加工成型的铝合金工件强度高，抗拉强度可达420Mpa以上，而且具有很好的防腐蚀性能，生产的铝合金汽车配件可以使用10年以上。

Description

一种高强铝合金的热处理工艺
技术领域
本发明属于合金热处理领域，具体涉及一种高强铝合金的热处理工艺。
背景技术
铝合金密度低，但强度比较高，接近或超过优质钢，塑性好，可加工成各种型材，具有优良的导电性、导热性和抗蚀性，工业上广泛使用，但是铝合金虽然质轻，但是在汽车零部件加工领域，铝合金的强度需要进一步加强，现在多通过对铝合金热处理来提高铝合金的强度。
发明内容
本发明的目的是提供一种高强铝合金的热处理工艺，工艺简单，大大提高了铝合金的强度，同时也提高了铝合金的防腐蚀性能。
本发明通过以下技术方案实现：
一种高强铝合金的热处理工艺，所述铝合金各组分含量为Si 0.0885%、Ti 0.084%、Mg 0.792%、Cu 0.074%、Fe 0.206%、Mn 0.44%、Cr 0.169%，余量为Al；使用如下步骤加工：（1）、将铝合金工件在450-500℃下固溶处理2-3h；（2）、将固溶处理好的铝合金工件在28-35℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158-160℃下时效处理5-8h，所述每1000ml水溶液中含有CrCl3 5.2-9.5g、CsF 3.5-6.8g、KNO3 7.8-12.5g、H3BO3 2.5-7g、NiCl2 2.6-4.8g，水溶液PH值在6-6.5。
使用氢氧化钠或者硫酸调节溶液的PH值。
一种高强铝合金的热处理工艺，使用如下步骤加工：（1）、将铝合金工件在475-500℃下固溶处理2-3h；（2）、将固溶处理好的铝合金工件在28-35℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158-160℃下时效处理5-8h，所述每1000ml水溶液中含有CrCl3 6.8g、CsF 5.6g、KNO3 12g、H3BO3 5.8g、NiCl2 3.5g，水溶液PH值在6-6.5。
本发明的有益效果：本发明提供的高强铝合金的热处理工艺方法简单，加工成型的铝合金工件强度高，抗拉强度可达420Mpa以上，而且具有很好的防腐蚀性能，生产的铝合金汽车配件可以使用10年以上。
具体实施方式
实施例1
一种高强铝合金的热处理工艺，所述铝合金各组分含量为Si 0.0885%、Ti 0.084%、Mg 0.792%、Cu 0.074%、Fe 0.206%、Mn 0.44%、Cr 0.169%，余量为Al；使用如下步骤加工：（1）、将铝合金工件在465℃下固溶处理3h；（2）、将固溶处理好的铝合金工件在30℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158℃下时效处理8h，所述每1000ml水溶液中含有CrCl3 6.6g、CsF 4.2g、KNO3 11.5g、H3BO3 3.6g、NiCl2 3.5g，水溶液PH值在6。处理后的铝合金工件拉伸强度为428Mpa。
实施例2
一种高强铝合金的热处理工艺，使用如下步骤加工：（1）、将铝合金工件在480℃下固溶处理2.5h；（2）、将固溶处理好的铝合金工件在28℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在159℃下时效处理7h，所述每1000ml水溶液中含有CrCl3 6.8g、CsF 5.6g、KNO3 12g、H3BO3 5.8g、NiCl2 3.5g，水溶液PH值在6-6.5。处理后的铝合金工件拉伸强度为487Mpa。
实施例3
一种高强铝合金的热处理工艺，使用如下步骤加工：（1）、将铝合金工件在495℃下固溶处理3h；（2）、将固溶处理好的铝合金工件在32℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158℃下时效处理7.5h，所述每1000ml水溶液中含有CrCl3 9.2g、CsF 5.6g、KNO3 9.3g、H3BO3 5.5g、NiCl2 3.2g，水溶液PH值在6-6.5。处理后的铝合金工件拉伸强度为436Mpa。
实施例4
一种高强铝合金的热处理工艺，使用如下步骤加工：（1）、将铝合金工件在500℃下固溶处理2.5h；（2）、将固溶处理好的铝合金工件在31℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在159℃下时效处理6h，所述每1000ml水溶液中含有CrCl3 8.7g、CsF 5.9g、KNO3 11.2g、H3BO3 6.3g、NiCl2 4g，水溶液PH值在6-6.5。处理后的铝合金工件拉伸强度为435Mpa。
实施例5
一种高强铝合金的热处理工艺，使用如下步骤加工：（1）、将铝合金工件在488℃下固溶处理2h；（2）、将固溶处理好的铝合金工件在29℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在160℃下时效处理8h，所述每1000ml水溶液中含有CrCl3 9.2g、CsF 4.3g、KNO3 8.7g、H3BO3 6.2g、NiCl2 3.3g，水溶液PH值在6-6.5。处理后的铝合金工件拉伸强度为467Mpa。

Claims (2)

1.一种高强铝合金的热处理工艺，所述铝合金各组分含量为Si 0.0885%、Ti 0.084%、Mg 0.792%、Cu 0.074%、Fe 0.206%、Mn 0.44%、Cr 0.169%，余量为Al；其特征在于，使用如下步骤加工：（1）、将铝合金工件在450-500℃下固溶处理2-3h；（2）、将固溶处理好的铝合金工件在28-35℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158-160℃下时效处理5-8h，所述每1000ml水溶液中含有CrCl3 5.2-9.5g、CsF 3.5-6.8g、KNO3 7.8-12.5g、H3BO3 2.5-7g、NiCl2 2.6-4.8g，水溶液PH值在6-6.5。
2.根据权利要求1所述的一种高强铝合金的热处理工艺，其特征在于，使用如下步骤加工：（1）、将铝合金工件在475-500℃下固溶处理2-3h；（2）、将固溶处理好的铝合金工件在28-35℃下使用CrCl3、CsF、KNO3、H3BO3水溶液冷淬处理；（3）、将冷淬处理好的铝合金工件在158-160℃下时效处理5-8h，所述每1000ml水溶液中含有CrCl3 6.8g、CsF 5.6g、KNO3 12g、H3BO3 5.8g、NiCl2 3.5g，水溶液PH值在6-6.5。
CN201410350919.3A 2014-07-23 2014-07-23 一种高强铝合金的热处理工艺 Active CN104561860B (zh)