CN104559855A - Eva热熔胶 - Google Patents

Eva热熔胶 Download PDF

Info

Publication number
CN104559855A
CN104559855A CN201310508437.1A CN201310508437A CN104559855A CN 104559855 A CN104559855 A CN 104559855A CN 201310508437 A CN201310508437 A CN 201310508437A CN 104559855 A CN104559855 A CN 104559855A
Authority
CN
China
Prior art keywords
ethylene
melt adhesive
eva
hot
adds
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310508437.1A
Other languages
English (en)
Inventor
林贤文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310508437.1A priority Critical patent/CN104559855A/zh
Publication of CN104559855A publication Critical patent/CN104559855A/zh
Pending legal-status Critical Current

Abstract

本发明实施例公开了一种EVA热熔胶，按质量比包括以下组分：乙烯-丙烯酸乙酯共聚物30%~50%;马来酸5%~8%;石蜡15%~30%;亚硫酸钙10%~20%；脂肪胺聚氧乙烯醚2%~5%。本发明采用马来酸对EVA胶进行熔融接枝改性，从而实现对尼龙织物及筛网具有较强的粘合性能。

Description

EVA热熔胶
技术领域
本发明涉及化工领域，尤其涉及一种EVA热熔胶的制造。
背景技术
热熔胶粘剂又称热熔胶，是一种无溶剂的热塑性固体胶粘剂。使用时通过加热熔化后获得流动性，浸润被粘物表面，冷却后能通过硬固或反应固化而实现粘合。
热熔胶与其他胶粘剂相比，具有粘接速度快，加热熔化后、接触被粘物表面时数秒内就能固化，适用于自动化及连续化生产工艺；不含溶剂，对人体无毒，不污染环境、运输及保管方便；可以粘合多种材料，可用于粘合木材、纸张、金属、玻璃、塑料、陶瓷、衣料、电子零部件、包装材料等，甚至对其他胶粘剂难以粘接的蜡纸等材料也可以粘合；耐化学药品性强，能耐水、盐水、油、酸、碱及汽油等侵蚀；可以重新加热使用，涂在被粘物体上的热熔胶，因冷却固化不能粘合时，或粘合部位需变化时，可以重新加热进行粘合操作等特性。
EVA热熔胶是一种不需溶剂、不含水份、100%的固体可熔性的聚合物，在常温下为固体，加热熔融到一定程度变为能流动且有一定粘性的液体粘合剂，其熔融后为浅棕色半透明体或本白色。 热熔胶主要成分，即基本树脂是乙烯与醋酸乙烯在高压下共聚而成的，再配以增粘剂、粘度调节剂、抗氧剂等制成热熔胶，然而现有EVA树脂作为基料，难以满足尼龙织物对粘合性能的要求。
发明内容
本发明实施例所要解决的技术问题在于，提供一种EVA热熔胶，按质量比包括以下组分：
      乙烯-丙烯酸乙酯共聚物              30%~50%
      马来酸                             5%~8%
    石蜡                               15%~30%
      亚硫酸钙                           10%~20%
      脂肪胺聚氧乙烯醚                   2%~5%。
为了解决上述技术问题，本发明实施例提供了一种制备所述EVA热熔胶的工艺，包括以下步骤：
（a）在反应釜中先加入石蜡、乙烯-丙烯酸乙酯共聚物及亚硫酸钙加热至130℃；
（b）加入脂肪胺聚氧乙烯醚；
（c）加入马来酸钙继续升温至170~180℃，搅拌并保温5小时；
（d）成型后冷却制得成品。
实施本发明，具有如下有益效果：
本发明采用马来酸对EVA胶进行熔融接枝改性，从而实现对尼龙织物及筛网具有较强的粘合性能。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将对本发明作进一步地详细描述。
实施例 1
乙烯-丙烯酸乙酯共聚物              39g
马来酸                             6g
石蜡                               30g
亚硫酸钙                           20g
 脂肪胺聚氧乙烯醚                   5g。
（a）在反应釜中先加入石蜡、乙烯-丙烯酸乙酯共聚物及亚硫酸钙加热至130℃；
（b）加入脂肪胺聚氧乙烯醚；
（c）加入马来酸钙继续升温至170~180℃，搅拌并保温5小时；
（d）成型后冷却制得成品。
实施例 2
乙烯-丙烯酸乙酯共聚物              50g
马来酸                             8g
石蜡                               30g
亚硫酸钙                           10g
 脂肪胺聚氧乙烯醚                   2g。
（a）在反应釜中先加入石蜡、乙烯-丙烯酸乙酯共聚物及亚硫酸钙加热至130℃；
（b）加入脂肪胺聚氧乙烯醚；
（c）加入马来酸钙继续升温至170~180℃，搅拌并保温5小时；
（d）成型后冷却制得成品。
以上所揭露的仅为本发明一种较佳实施例而已，当然不能以此来限定本发明之权利范围，因此依本发明权利要求所作的等同变化，仍属本发明所涵盖的范围。

Claims (2)

1.一种EVA热熔胶，其特征在于，按质量比包括以下组分：
       乙烯-丙烯酸乙酯共聚物              30%~50%
       马来酸                             5%~8%
     石蜡                               15%~30%
       亚硫酸钙                           10%~20%
       脂肪胺聚氧乙烯醚                   2%~5%。
2.一种制备权利要求1所述EVA热熔胶的工艺，其特征在于，包括以下步骤：
（a）在反应釜中先加入石蜡、乙烯-丙烯酸乙酯共聚物及亚硫酸钙加热至130℃；
（b）加入脂肪胺聚氧乙烯醚；
（c）加入马来酸钙继续升温至170~180℃，搅拌并保温5小时；
（d）成型后冷却制得成品。
CN201310508437.1A 2013-10-25 2013-10-25 Eva热熔胶 Pending CN104559855A (zh)