CN104559403A - 一种内墙用腻子 - Google Patents
一种内墙用腻子 Download PDFInfo
- Publication number
- CN104559403A CN104559403A CN201410758691.1A CN201410758691A CN104559403A CN 104559403 A CN104559403 A CN 104559403A CN 201410758691 A CN201410758691 A CN 201410758691A CN 104559403 A CN104559403 A CN 104559403A
- Authority
- CN
- China
- Prior art keywords
- putty
- parts
- interior wall
- lignocellulose
- sodium bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种内墙用腻子，包括以下重量份的原料：钙粉70-100份、羟丙基甲基纤维素2-10份、木质纤维素1-5份、颜料0.5-2份、硅藻泥1-5份、钠质膨润土5-10份。将上述原料按照上述配方配好，置于搅拌机中进行搅拌，搅拌均匀后分袋密封；使用时与水搅拌即可。本发明的羟丙基甲基纤维素和木质纤维素起到骨架的作用，增加腻子的使用强度；硅藻泥和钠质膨润土具有优异的防潮、耐化学性能，腻子刷于内墙后，墙面不起皮、不起鼓、不脱落，并且优异的耐磨性和耐水洗。
Description
技术领域
本发明涉及一种涂料，具体涉及一种内墙用腻子，属于化工涂料技术领域。
背景技术
腻子是平整墙体表面的一种装饰凝材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品。涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。采用少量漆基、大量填料及适量的着色颜料配制而成，所用颜料主要是铁红、炭黑、铬黄等。填料主要是重碳酸钙、滑石粉等。可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆层干透后，施涂于底漆层表面。要求附着性好、烘烤过程中不产生裂纹。
当前纵观国内整个弹性涂料市场，大部分的产品只限于具备高弹性的特征，其耐水性和防水性较差，拉伸强度低，附着力一般。由于其不耐水、不防水，在经过雨水冲刷后其
漆膜将会整体剥落，或由于含水率的不同造成开裂或剥落，雨水便渗入墙面，腐蚀墙面。同
时由于弹性涂料的耐沾污性较差，施工之后容易受到悬浮在大气中的粉尘、油性物质的污
染使漆膜表面受到污染。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种通用性强、强度高、耐粘度强、耐磨性好、耐水洗的内墙用腻子，具有优良的耐潮性能、不起鼓、不脱落，并且不伤手、对人体没有任何危害。
为了达到上述目的，本发明采用的技术方案是：
一种内墙用腻子，包括以下重量份的原料：钙粉70-100份、羟丙基甲基纤维素2-10份、木质纤维素1-5份、颜料0.5-2份、硅藻泥1-5份、钠质膨润土5-10份。
优选的，所述的钙粉为重质碳酸钙粉和灰钙粉的混合物，其重量比为2:1。
优选的，所述的颜料为酚菁蓝、酚菁绿、铁黄、透明氧化铁、钛白粉中的任意一种。本发明的颜料色泽鲜艳、分散性好、易于加工。
优选的，所述的透明氧化铁的规格为≦0.01微米。氧化铁颗粒直径≦0.01微米时，颜料在有机介质中的遮盖力显著下降，称为透明氧化铁，具有更好的保色性。
优选的，所述的羟丙基甲基纤维素的粘度为5万-7万豪帕.秒。
将上述原料按照上述配方配好，置于搅拌机中进行搅拌，搅拌均匀后分袋密封；使用时与水搅拌即可。
本发明的羟丙基甲基纤维素和木质纤维素起到骨架的作用，增加腻子的使用强度；硅藻泥和钠质膨润土具有优异的防潮、耐化学性能，腻子刷于内墙后，墙面不起皮、不起鼓、不脱落，并且优异的耐磨性和耐水洗。
具体实施方式
实施例1：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉50份、灰钙粉25份、羟丙基甲基纤维素2份、木质纤维素1份、硅藻泥1份、钠质膨润土5份、酚菁蓝1份。
实施例2：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉50份、灰钙粉25份、羟丙基甲基纤维素2份、木质纤维素1份、硅藻泥1份、钠质膨润土5份、酚菁绿1份。
实施例3：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉50份、灰钙粉25份、羟丙基甲基纤维素2份、木质纤维素1份、硅藻泥1份、钠质膨润土5份、铁黄1份。
实施例4：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉50份、灰钙粉25份、羟丙基甲基纤维素2份、木质纤维素1份、硅藻泥1份、钠质膨润土5份、透明氧化铁1份。
实施例5：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉50份、灰钙粉25份、羟丙基甲基纤维素2份、木质纤维素1份、硅藻泥1份、钠质膨润土5份、钛白粉1份。
实施例6：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉60份、灰钙粉30份、羟丙基甲基纤维素5份、木质纤维素2份、硅藻泥2份、钠质膨润土7份、钛白粉1份。
实施例7：
一种内墙用腻子，包括以下重量份的原料：重质碳酸钙粉64份、灰钙粉32份、羟丙基甲基纤维素8份、木质纤维素4份、硅藻泥4份、钠质膨润土9份、钛白粉1.5份。
将本发明实施例1-7的配方配置腻子粉，将原料按照重量份配比好，置于搅拌机中进行搅拌，搅拌均匀，与水按照常规配比搅拌均匀刷涂墙面后检测个腻子粉性能：结果如表1所示：
表1：实施例1-7所得腻子粉性能指标
上述实例只是为说明本发明的技术构思以及技术特点，并不能以此限制本发明的保护范围。凡根据本发明的实质所做的等效变换或修饰，都应该涵盖在本发明的保护范围之内。
Claims (5)
1.一种内墙用腻子，其特征在于，包括以下重量份的原料：钙粉70-100份、羟丙基甲基纤维素2-10份、木质纤维素1-5份、颜料0.5-2份、硅藻泥1-5份、钠质膨润土5-10份。
2.根据权利要求1所述的内墙用腻子，其特征在于，所述的钙粉为重质碳酸钙粉和灰钙粉的混合物，其重量比为2:1。
3.根据权利要求1所述的内墙用腻子，其特征在于，所述的颜料为酚菁蓝、酚菁绿、铁黄、透明氧化铁、钛白粉中的任意一种。
4.根据权利要求1所述的内墙用腻子，其特征在于，所述的透明氧化铁的规格为≦0.01微米。
5.根据权利要求1所述的内墙用腻子，其特征在于，所述的羟丙基甲基纤维素的粘度为5万-7万豪帕.秒。