CN104558693A - 植物淀粉环保餐盒及其制备方法 - Google Patents
植物淀粉环保餐盒及其制备方法 Download PDFInfo
- Publication number
- CN104558693A CN104558693A CN201310497365.5A CN201310497365A CN104558693A CN 104558693 A CN104558693 A CN 104558693A CN 201310497365 A CN201310497365 A CN 201310497365A CN 104558693 A CN104558693 A CN 104558693A
- Authority
- CN
- China
- Prior art keywords
- percent
- potato starch
- mixture
- bagasse
- stearic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种植物淀粉环保餐盒,下组分组成为(重量百分比):20-30%甘蔗渣、5-15%甘油、5-10%硬脂酸、50-70%土豆淀粉,所述的植物淀粉环保餐盒的制备方法,包括以下步骤:(1)将土豆淀粉过50目筛;(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;(3)将20-30%甘蔗渣、5-15%甘油、5-10%硬脂酸、50-70%土豆淀粉混合,搅拌均匀,制得混合物;(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔中,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。
Description
技术领域
本发明涉及一种绿色环保用品及其制备方法,尤其是一种植物淀粉环保餐盒及其制备方法。
背景技术
人们在外出就餐时常常会用到一次性快餐盒,目前被广泛使用的快餐盒多为发泡塑料饭盒,其生产原料为聚苯乙烯、发泡剂、光敏剂等,对人体具有一定的危害,并且难以降解,容易造成环境污染,虽然市场上存在一些可降解快餐盒,但由于价格较高,难以得到推广。
发明内容
为了解决上述问题,本发明提供了一种植物淀粉环保餐盒及其制备方法。
植物淀粉环保餐盒,由以下组分组成(重量百分比):
20-30%甘蔗渣
5-15%甘油
5-10%硬脂酸
50-70%土豆淀粉
植物淀粉环保餐盒的制备方法,包括以下步骤:
(1)将土豆淀粉过50目筛;
(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;
(3)将20-30%甘蔗渣、5-15%甘油、5-10%硬脂酸、50-70%土豆淀粉混合,搅拌均匀,制得混合物;
(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔中,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。
本发明的有益效果是:生产原料为普通土豆淀粉以及甘蔗渣,来源十分广泛,成本低廉,生产过程简便,易于投产,生产的产品使用后可收集加热重新作为原料循环生产,即节约了原料、更解决了产品废弃带来的环境污染问题,有利环境保护。
具体实施方式
下面结合实施例对本发明作进一步的详述:
实施例一:
植物淀粉环保餐盒,组分组成(重量百分比):
20%甘蔗渣
10%甘油
10%硬脂酸
60%土豆淀粉
植物淀粉环保餐盒的制备方法,包括以下步骤:
(1)将土豆淀粉过50目筛;
(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;
(3)将20%甘蔗渣、10%甘油、10%硬脂酸、60%土豆淀粉混合,搅拌均匀,制得混合物;
(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔中,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。
实施例二:
植物淀粉环保餐盒,组分组成(重量百分比):
30%甘蔗渣
15%甘油
5%硬脂酸
50%土豆淀粉
植物淀粉环保餐盒的制备方法,包括以下步骤:
(1)将土豆淀粉过50目筛;
(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;
(3)将30%甘蔗渣、15%甘油、5%硬脂酸、50%土豆淀粉混合,搅拌均匀,制
得混合物;
(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔中,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。
实施例三:
植物淀粉环保餐盒,组分组成(重量百分比):
25%甘蔗渣
10%甘油
8%硬脂酸
57%土豆淀粉
植物淀粉环保餐盒的制备方法,包括以下步骤:
(1)将土豆淀粉过50目筛;
(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;
(3)将25%甘蔗渣、10%甘油、8%硬脂酸、57%土豆淀粉混合,搅拌均匀,制得混合物;
(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。
以上所述仅为本发明的优选实施方式,本发明的保护范围并不仅限于上述实施方式,凡是属于本发明原理的技术方案均属于本发明的保护范围。对于本领域的技术人员而言,在不脱离本发明的原理的前提下进行的若干改进,这些改进也应视为本发明的保护范围。
Claims (2)
1.植物淀粉环保餐盒,其特征是,由以下组分组成(重量百分比):
20-30%甘蔗渣,
5-15%甘油,
5-10%硬脂酸,
50-70%土豆淀粉。
2.如权利要求1所述的植物淀粉环保餐盒的制备方法,其特征是,包括以下步骤:
(1)将土豆淀粉过50目筛;
(2)将甘蔗渣在粉碎机中粉碎,温度90-100℃进行干燥,使得甘蔗渣的含水率在7%-9%,然后过100目筛;
(3)将20-30%甘蔗渣、5-15%甘油、5-10%硬脂酸、50-70%土豆淀粉混合,搅拌均匀,制得混合物;
(4)将步骤(3)的混合物加热至50℃定量输送到专用成型机中的模腔中,通过震动均匀布料,然后在低压下压制一次成型,经消毒、包装后即得成品。