CN104556834A - Light-pollution-preventing seaweed mud coating for exterior walls and producing method thereof - Google Patents
Light-pollution-preventing seaweed mud coating for exterior walls and producing method thereof Download PDFInfo
- Publication number
- CN104556834A CN104556834A CN201310471127.7A CN201310471127A CN104556834A CN 104556834 A CN104556834 A CN 104556834A CN 201310471127 A CN201310471127 A CN 201310471127A CN 104556834 A CN104556834 A CN 104556834A
- Authority
- CN
- China
- Prior art keywords
- algae clay
- resin emulsion
- parts
- filler
- synthetic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Light-pollution-preventing seaweed mud coating for exterior walls and a producing method thereof are disclosed. The coating comprises following components by weight: 50-60 parts of water, 10-15 parts of synthetic resin emulsion, 15-25 parts of seaweed mud, 5-10 parts of acrylic acid, 5-10 parts of an antifreezing agent, 5-15 parts of a film former and 5-10 parts of a filler. According to the coating and the method, after an exterior wall is coated and decorated with the coating containing the seaweed mud, the seaweed mud surface is coarse and well-aligned and has different texture patterns and different colors, and light-absorbing compounds in materials change reflection and refraction of light and reduce light pollution.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of light pollution preventive algae clay exterior coating and production method.
Background technology
Coating is as a kind of material of house decoration by people's widespread use, and people can choose the coating of different colours according to hobby.Coating is generally emulsion form, holds transport by paint cylinder, dips in coat to cover with paint, lacquer, colour wash, etc. on metope during use with brush.According to the difference of boundary of works area, coating can be divided into exterior coating and interior wall coating.At present, clearly, especially light exterior coating can cause more serious light pollution to the reflection action of a lot of exterior coating.
Summary of the invention
In order to solve the technical problem existed in background technology, the present invention proposes a kind of light pollution preventive algae clay exterior coating and production method, to reduce the injury of impact of light pollution on environment and human body.
A kind of light pollution preventive algae clay exterior coating that the present invention proposes, comprises following composition according to parts by weight:
Water: 50-60 part; Synthetic resin emulsion: 10-15 part; Algae clay: 15-25 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part;
Wherein, described synthetic resin emulsion is stupid third resin emulsion or organosilicon acrylic resin emulsion; Described algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter; Described frostproofer comprises ethylene glycol, glycol ether or alcohol; Described film coalescence aid is one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol; Described filler is Wingdale.
Preferably, described light pollution preventive algae clay exterior coating comprises following composition according to parts by weight: water: 50-60 part; Synthetic resin emulsion: 11-15 part; Algae clay: 18-22 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part.
Preferably, described light pollution preventive algae clay exterior coating comprises following composition according to parts by weight: water: 50-60 part; Synthetic resin emulsion: 12-14 part; Algae clay: 19-21 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part.
According to above-mentioned light pollution preventive algae clay exterior coating, the present invention proposes a kind of production method of light pollution preventive algae clay exterior coating, comprise the following steps:
Synthetic resin emulsion and water are added stirrer, stirs 15 minutes with the rotating speed of 100-200 rev/min, solution is mixed;
Stir 30 minutes with the rotating speed of 300-500 rev/min, add vinylformic acid, frostproofer and membrane-forming agent while stirring;
Stir 30 minutes with the rotating speed of 500-600 rev/min, add algae clay while stirring;
Add filler, stir 2 hours with the rotating speed of 600-800 rev/min.
In the present invention, the paint finishing containing algae clay on outdoor wall surface after, algae clay surface irregularity is orderly, different veinpatterns designs, distinct colors, and the extinction material in material changes reflection, the refraction of light, decreases light pollution.
Embodiment
The embodiment of the present invention 1 provides a kind of light pollution preventive algae clay exterior coating, comprises following composition according to parts by weight:
Water: 50-60 part;
Synthetic resin emulsion: 10-15 part;
Algae clay: 15-25 part;
Vinylformic acid: 5-10 part;
Frostproofer: 5-10 part;
Membrane-forming agent: 5-15 part;
Filler: 5-10 part.
The embodiment of the present invention 2 provides a kind of light pollution preventive algae clay exterior coating, comprises following composition according to parts by weight:
Water: 50-60 part;
Synthetic resin emulsion: 11-15 part;
Algae clay: 18-22 part;
Vinylformic acid: 5-10 part;
Frostproofer: 5-10 part;
Membrane-forming agent: 5-15 part;
Filler: 5-10 part.
The embodiment of the present invention 3 provides a kind of light pollution preventive algae clay exterior coating, comprises following composition according to parts by weight:
Water: 50-60 part;
Synthetic resin emulsion: 12-14 part;
Algae clay: 19-21 part;
Vinylformic acid: 5-10 part;
Frostproofer: 5-10 part;
Membrane-forming agent: 5-15 part;
Filler: 5-10 part.
In above-described embodiment 1 to 3, synthetic resin emulsion can use stupid third resin emulsion, organosilicon acrylic resin emulsion.Algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter, comprises multiple inorganics, such as calcium sulfate, calcium phosphate, calcium carbonate, trimagnesium phosphate, iron carbonate.Described frostproofer comprises ethylene glycol, glycol ether or alcohol.Described film coalescence aid can be one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol.Filler is Wingdale.
The embodiment of the present invention 4 provides a kind of light pollution preventive algae clay exterior coating technological process of production, comprises the following steps:
Step 101, adds stirrer by synthetic resin emulsion and water, stirs 15 minutes with the rotating speed of 100-200 rev/min, and solution is mixed;
Step 102, stirs 30 minutes with the rotating speed of 300-500 rev/min, adds vinylformic acid, frostproofer and membrane-forming agent while stirring;
Step 103, stirs 30 minutes with the rotating speed of 500-600 rev/min, adds algae clay while stirring;
Step 104, adds filler, stirs 2 hours, get product with the rotating speed of 600-800 rev/min.
In the present invention, the paint finishing containing algae clay on outdoor wall surface after, algae clay surface irregularity is orderly, different veinpatterns designs, distinct colors, and the extinction material in material changes reflection, the refraction of light, decreases light pollution.
Embodiments provide the above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (4)
1. a light pollution preventive algae clay exterior coating, is characterized in that, comprises following composition: water according to parts by weight: 50-60 part; Synthetic resin emulsion: 10-15 part; Algae clay: 15-25 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part;
Wherein, described synthetic resin emulsion is stupid third resin emulsion or organosilicon acrylic resin emulsion; Described algae clay is the small-particle of diameter 0.001 ~ 0.25 millimeter; Described frostproofer comprises ethylene glycol, glycol ether or alcohol; Described film coalescence aid is one or more in propylene glycol monomethyl ether, propandiol butyl ether, alcohol ester 12, butyl or stupid methyl alcohol; Described filler is Wingdale.
2. light pollution preventive algae clay exterior coating according to claim 1, is characterized in that, comprise following composition: water according to parts by weight: 50-60 part; Synthetic resin emulsion: 11-15 part; Algae clay: 18-22 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part.
3. light pollution preventive algae clay exterior coating according to claim 2, is characterized in that, comprise following composition: water according to parts by weight: 50-60 part; Synthetic resin emulsion: 12-14 part; Algae clay: 19-21 part; Vinylformic acid: 5-10 part; Frostproofer: 5-10 part; Membrane-forming agent: 5-15 part; Filler: 5-10 part.
4. a production method for the light pollution preventive algae clay exterior coating according to any one of claim 1-4, is characterized in that, comprise the following steps:
Synthetic resin emulsion and water are added stirrer, stirs 15 minutes with the rotating speed of 100-200 rev/min, solution is mixed; Stir 30 minutes with the rotating speed of 300-500 rev/min, add vinylformic acid, frostproofer and membrane-forming agent while stirring; Stir 30 minutes with the rotating speed of 500-600 rev/min, add algae clay while stirring; Add filler, stir 2 hours with the rotating speed of 600-800 rev/min.