CN104530855A - Water-based rust conversion and prevention paint - Google Patents

Water-based rust conversion and prevention paint Download PDF

Info

Publication number
CN104530855A
CN104530855A CN201410667256.8A CN201410667256A CN104530855A CN 104530855 A CN104530855 A CN 104530855A CN 201410667256 A CN201410667256 A CN 201410667256A CN 104530855 A CN104530855 A CN 104530855A
Authority
CN
China
Prior art keywords
water
parts
raw material
stirred
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410667256.8A
Other languages
Chinese (zh)
Inventor
周长
李寿国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan City Jin Han Coating Manufacturing Co Ltd
Original Assignee
Maanshan City Jin Han Coating Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan City Jin Han Coating Manufacturing Co Ltd filed Critical Maanshan City Jin Han Coating Manufacturing Co Ltd
Priority to CN201410667256.8A priority Critical patent/CN104530855A/en
Publication of CN104530855A publication Critical patent/CN104530855A/en
Pending legal-status Critical Current

Abstract

The invention discloses a water-based rust conversion and prevention paint. The water-based rust conversion and prevention paint is composed of following raw materials, by weight, 0.3 to 1 part of isophorone oxide, 10 to 13 parts of alkyd resin, 1 to 2 parts of tea saponin, 1 to 2 parts of 2-mercaptobenzimidazol, 0.3 to 0.5 part of steel slag powder, 0.7 to 1 part of chilli powder, 0.8 to 2 parts of polyhexamethylene guanidine, 3 to 4 parts of barium metaborate, 4 to 6 parts of bauxite, 0.7 to 1 part of polyacrylamide, 1 to 2 parts of monopotassium phosphate, 4 to 5 parts of iso-octyl methacrylate, 100 to 110 parts of waterborne acrylic emulsion, 0.5 to 1 part of sodium hexametaphosphate, 2 to 3 parts of an auxiliary agent, 0.1 to 0.2 part of simethicone, and 6 to 10 parts of deionized water. The water-based rust conversion and prevention paint possesses excellent corrosion resistance; when the water-based rust conversion and prevention paint is used, direct spraying or painting can be performed without surface processing; rust resistance is excellent; and water is taken as the solvent, so that the water-based rust conversion and prevention paint is capable of avoiding environment pollution caused by solvent based coatings.

Description

A kind of water-based anti-rust paint for rusty surfaces
Technical field
The main technical field of coatings of the present invention, particularly relates to a kind of water-based anti-rust paint for rusty surfaces.
Background technology
At present, major part coating is solvent based coating, in solvent based coating containing have an appointment 50% organic solvent, a large amount of VOC gas can be discharged after these paint spay-coatings, not only healthy to end user of serious harm, also can pollute air, damage ecotope, and existing rust-inhibiting paint cost is high, and performance is single, as or only high temperature resistant or only corrosion-resistant or only there is flame retardant resistance, significantly limit the Application Areas of rust proof paint thus.
Summary of the invention
The object of the invention is just to provide a kind of water-based anti-rust paint for rusty surfaces.
The present invention is achieved by the following technical solutions:
A kind of water-based anti-rust paint for rusty surfaces, is made up of the raw material of following weight parts:
Oxidation isophorone 0.3-1, Synolac 10-13, tea saponin 1-2,2-thiol group benzimidazolyl 1-2, steel-making slag powder 0.3-0.5, red chilly powder 0.7-1, polyhexamethylene guanidine 0.8-2, barium metaborate 3-4, bauxitic clay 4-6, polyacrylamide 0.7-1, potassium primary phosphate 1-2, Isooctyl methacrylate 4-5, aqueous acrylic emulsion 100-110, Sodium hexametaphosphate 99 0.5-1, auxiliary agent 2-3, dimethyl silicone oil 0.1-0.2, deionized water 6-10;
Described auxiliary agent is made up of the raw material of following weight parts:
Chlorinated polyether resin 20-30, calcium aluminate powder 4-6, zinc borate 2-3, propandiol butyl ether 5-8, Trimethoprim lactate 1-2, tetradecanoic acid soda soap 5-7, Natvosol 1-2, deionized water 6-10;
Natvosol is joined in deionized water, after stirring, add Trimethoprim lactate, calcium aluminate powder, be stirred to water and do; Mixed with tetradecanoic acid soda soap by propandiol butyl ether, be uniformly mixed 3-5 minute, add chlorinated polyether resin, be stirred to normal temperature at 40-50 DEG C, add each raw material of residue, 200-300 rev/min is stirred 10-20 minute, obtains described auxiliary agent.
A preparation method for water-based anti-rust paint for rusty surfaces, comprises the following steps:
By Synolac, aqueous acrylic emulsion, tea saponin, 2-thiol group benzimidazolyl, Sodium hexametaphosphate 99, dimethyl silicone oil mixing, 300-400 rev/min of dispersed with stirring 10-20 minute, obtains slurries;
Bauxitic clay, steel-making slag powder, red chilly powder, potassium primary phosphate are mixed to join in deionized water, are uniformly mixed 2-3 minute at 50-60 DEG C, add polyacrylamide, be stirred to normal temperature;
By each raw material mixing after above-mentioned process, add each raw material of residue, pour at 0 DEG C in stirred pot, slowly stir and be warming up to room temperature, stir 2-3 hour, obtain described water-based anti-rust paint for rusty surfaces.
Advantage of the present invention is:
Rust-inhibiting paint of the present invention has excellent erosion resistance, and in use, without the need to carrying out surface treatment, directly carrying out spraying or brushing, favorable rust preventing effect, take water as solvent, overcomes the pollution of solvent based coating to environment.
Embodiment
Embodiment 1
A kind of water-based anti-rust paint for rusty surfaces, it is made up of the raw material of following weight parts:
Oxidation isophorone 0.3, Synolac 13, tea saponin 1,2-thiol group benzimidazolyl 1, steel-making slag powder 0.5, red chilly powder 0.7, polyhexamethylene guanidine 0.8, barium metaborate 3, bauxitic clay 4, polyacrylamide 0.7, potassium primary phosphate 1, Isooctyl methacrylate 5, aqueous acrylic emulsion 110, Sodium hexametaphosphate 99 0.5, auxiliary agent 2, dimethyl silicone oil 0.2, deionized water 10;
Described auxiliary agent is made up of the raw material of following weight parts:
Chlorinated polyether resin 30, calcium aluminate powder 6, zinc borate 2, propandiol butyl ether 8, Trimethoprim lactate 2, tetradecanoic acid soda soap 7, Natvosol 1, deionized water 10;
Natvosol is joined in deionized water, after stirring, add Trimethoprim lactate, calcium aluminate powder, be stirred to water and do; Mixed with tetradecanoic acid soda soap by propandiol butyl ether, be uniformly mixed 5 minutes, add chlorinated polyether resin, be stirred to normal temperature at 50 DEG C, add each raw material of residue, 00 rev/min is stirred 20 minutes, obtains described auxiliary agent.
A preparation method for water-based anti-rust paint for rusty surfaces, comprises the following steps:
By Synolac, aqueous acrylic emulsion, tea saponin, 2-thiol group benzimidazolyl, Sodium hexametaphosphate 99, dimethyl silicone oil mixing, 400 revs/min of dispersed with stirring 20 minutes, obtain slurries;
Bauxitic clay, steel-making slag powder, red chilly powder, potassium primary phosphate are mixed to join in deionized water, are uniformly mixed 3 minutes at 60 DEG C, add polyacrylamide, be stirred to normal temperature;
By each raw material mixing after above-mentioned process, add each raw material of residue, pour at 0 DEG C in stirred pot, slowly stir and be warming up to room temperature, stir 2 hours, obtain described water-based anti-rust paint for rusty surfaces.
Performance test:
Paint film uniform hue, smooth;
Salt water resistance (3% sodium-chlor, 24h): not bubble, do not come off, without blushing;
Abrasion resistance: 5000 times are not show-through.

Claims (2)

1. a water-based anti-rust paint for rusty surfaces, is characterized in that what it was made up of the raw material of following weight parts:
Oxidation isophorone 0.3-1, Synolac 10-13, tea saponin 1-2,2-thiol group benzimidazolyl 1-2, steel-making slag powder 0.3-0.5, red chilly powder 0.7-1, polyhexamethylene guanidine 0.8-2, barium metaborate 3-4, bauxitic clay 4-6, polyacrylamide 0.7-1, potassium primary phosphate 1-2, Isooctyl methacrylate 4-5, aqueous acrylic emulsion 100-110, Sodium hexametaphosphate 99 0.5-1, auxiliary agent 2-3, dimethyl silicone oil 0.1-0.2, deionized water 6-10;
Described auxiliary agent is made up of the raw material of following weight parts:
Chlorinated polyether resin 20-30, calcium aluminate powder 4-6, zinc borate 2-3, propandiol butyl ether 5-8, Trimethoprim lactate 1-2, tetradecanoic acid soda soap 5-7, Natvosol 1-2, deionized water 6-10;
Natvosol is joined in deionized water, after stirring, add Trimethoprim lactate, calcium aluminate powder, be stirred to water and do; Mixed with tetradecanoic acid soda soap by propandiol butyl ether, be uniformly mixed 3-5 minute, add chlorinated polyether resin, be stirred to normal temperature at 40-50 DEG C, add each raw material of residue, 200-300 rev/min is stirred 10-20 minute, obtains described auxiliary agent.
2. a preparation method for water-based anti-rust paint for rusty surfaces as claimed in claim 1, is characterized in that comprising the following steps:
By Synolac, aqueous acrylic emulsion, tea saponin, 2-thiol group benzimidazolyl, Sodium hexametaphosphate 99, dimethyl silicone oil mixing, 300-400 rev/min of dispersed with stirring 10-20 minute, obtains slurries;
Bauxitic clay, steel-making slag powder, red chilly powder, potassium primary phosphate are mixed to join in deionized water, are uniformly mixed 2-3 minute at 50-60 DEG C, add polyacrylamide, be stirred to normal temperature;
By each raw material mixing after above-mentioned process, add each raw material of residue, pour at 0 DEG C in stirred pot, slowly stir and be warming up to room temperature, stir 2-3 hour, obtain described water-based anti-rust paint for rusty surfaces.
CN201410667256.8A 2014-11-20 2014-11-20 Water-based rust conversion and prevention paint Pending CN104530855A (en)