CN104529557B - A kind of method that enamel is drawn on boccaro ware - Google Patents
A kind of method that enamel is drawn on boccaro ware Download PDFInfo
- Publication number
- CN104529557B CN104529557B CN201510014483.5A CN201510014483A CN104529557B CN 104529557 B CN104529557 B CN 104529557B CN 201510014483 A CN201510014483 A CN 201510014483A CN 104529557 B CN104529557 B CN 104529557B
- Authority
- CN
- China
- Prior art keywords
- porcelain
- cream
- boccaro ware
- boccaro
- ware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of method that enamel is drawn on boccaro ware, including：Boccaro ware is provided；Prepare the first porcelain cream；The first porcelain cream is filled out at least a portion of the boccaro ware；The boccaro ware for filling out the first porcelain cream is carried out into first to calcine；The second porcelain cream different from the first porcelain cream is provided, and the second porcelain cream is filled out onto described at least a portion of the boccaro ware after the first calcining；The boccaro ware for filling out the second porcelain cream is carried out into second to calcine；Picture needed for being drawn in described at least a portion of boccaro ware after being calcined described second；Stippling is carried out to the picture with enamel color material color；The boccaro ware for carrying out stippling is subjected to the 3rd calcining；There is provided it is a kind of allow the bright and new beautiful compound of picture, and the compound is filled out onto described at least a portion of the boccaro ware after the 3rd calcining；The boccaro ware for filling out the compound is subjected to the 4th calcining, to burn till finished product.
Description
Technical field
The present invention relates to a kind of method that enamel is drawn on boccaro ware, belong to boccaro ware manufacture field.
Background technology
Between clear Kangxu year, the small bowl of colour enamels paid tribute by foreign countries firmly gets Kangxu Supreme Being's favor.Just pottery shape home is sprouted
Attempted on body, received this imperial envoy at that time there are the implements such as boccaro, ceramics, bronze, brass or copper ware.And the implements attempted earliest are then boccaros.But because
Boccaro is matt body, matt appearance, and color is compared with depth and stomata is more, is extremely difficult to decorate expression effect after decoration, does not view and admire
Property, finally replaced by porcelain enamel.
The content of the invention
It is an object of the invention to for defect of the boccaro outward appearance without glaze, there is provided a kind of side that enamel is drawn on boccaro ware
Method, can apply the characteristic language drawn on porcelain, allow picture gloss, floridity, rich in expressive force.
The technical scheme is that：
A kind of method that enamel is drawn on boccaro ware, comprises the following steps：
Boccaro ware is provided；
Prepare the first porcelain cream；
The first porcelain cream is filled out at least a portion of the boccaro ware；
The boccaro ware for filling out the first porcelain cream is carried out into first to calcine；
The second porcelain cream different from the first porcelain cream is provided, and the second porcelain cream is filled out to the boccaro after the first calcining
In described at least a portion of device；
The boccaro ware for filling out the second porcelain cream is carried out into second to calcine；
Picture needed for being drawn in described at least a portion of boccaro ware after being calcined described second；
Stippling is carried out to the picture with enamel color material color；
The boccaro ware for carrying out stippling is subjected to the 3rd calcining；
There is provided it is a kind of allow the bright and new beautiful compound of picture, and the compound is filled out to the boccaro ware after the 3rd calcining
In described at least a portion；
The boccaro ware for filling out the compound is subjected to the 4th calcining, to burn till finished product.
Preferably, the fineness of the first porcelain cream of the boccaro ware is filled out more than 300 mesh, and brightness is more than 75%.
Preferably, the thickness for filling out the first porcelain cream of the boccaro ware is 0.1-0.15 millimeters.
Preferably, the gross thickness of the first porcelain cream and the second porcelain cream of filling out the boccaro ware is 2 millimeters.
Preferably, the maximum temperature of first calcining, the second calcining, the 3rd calcining and the 4th calcining raises 10- successively
15℃。
Preferably, the initial temperature of first calcining, the second calcining, the 3rd calcining and the 4th calcining is 750 DEG C.
Preferably, the maximum temperature of first calcining is 780-800 DEG C.
Preferably, the second porcelain cream is glass white.
Preferably, the compound is glass white.
The present invention also provides a kind of boccaro ware, and at least a portion on the surface of the boccaro ware is used according to above technical side
Method any one of case, which is drawn, enamel.
By above technical scheme, the present invention can realize following technique effect.
Revolutionize boccaro matt, this characteristic of matt body.
While the original permeability of boccaro good advantage is kept, the bright color of colour enamels and rich in hand texture, solid
The effect of sense, so as to enrich the sight and collection of dark-red enameled pottery.
Painted enamel changes the Tao Shitao in tradition on dark-red enameled pottery, and porcelain is the idea of porcelain.Greatly illustrate Chinese pottery
The glamour of artistic speech.
The success of boccaro painted enamel, allows the royal traditional handicraft of lost centuries to be able to pass on and develop.
Brief description of the drawings
Fig. 1 is the boccaro painted enamel manufacture method schematic flow sheet of the present invention
Fig. 2-5 is dark-red enameled pottery outline drawing made according to the method for the present invention
Embodiment
Below by taking dark-red enameled pottery as an example, its manufacture method is illustrated.
As described in Figure 1, first dark-red enameled pottery is rinsed wet cloth one time, it is slightly cool.
Prepare that milky white porcelain cream is very thin to fill out last layer, carry out (780-800 DEG C) calcining of high temperature.
Filled out thereon again one time with other porcelain cream (optional glass white) again, carry out second and calcine, the temperature ratio of this calcining
It is high 10 DEG C for the first time.
Picture needed for drawing.
Stippling is carried out with enamel color material color.
High temperature furnace grilling, this grilling is higher 10-15 DEG C again than the temperature of previous calcining.
Glass white is filled out again, makes picture bright and new beautiful.
Carry out high-temperature calcination and burn till finished product, this grilling is higher 10-15 DEG C again than the temperature of previous calcining.The purple finally obtained
Sand kettle finished product is as shown in Figure 2-5.
Preferably, the milky white porcelain cream of the dark-red enameled pottery milky white porcelain cream general for this area is filled out, its fineness exists
More than 300 mesh, brightness is more than 75%.
Preferably, the thickness for filling out the milky white porcelain cream of the boccaro ware is 0.01 to 1.50 millimeters, preferably 0.10-
0.15 millimeter.
Preferably, the gross thickness of the milky white porcelain cream and other porcelain cream of filling out the boccaro ware is 2 millimeters.
Preferably, each calcining, the maximum temperature of grilling raise 10-15 DEG C successively.
Preferably, each calcining, the initial temperature of grilling are 750 DEG C.
Preferably, the maximum temperature of calcining is 780-800 DEG C.
Preferably, other porcelain cream is except using in addition to glass white, it is also possible to use this area, optional other are any suitable
Porcelain cream.
Preferably, in order to make picture bright and new beautiful, except be with above-mentioned glass white in addition to, it is also possible to use this area optional
Other any suitable compounds.
Boccaro painted enamel is big due to technology difficulty, need to be through high-temperature calcination several times, so as to add technical difficulty and be fabricated to
Product, risk is very big.It is of the invention compared with common boccaro, either sight or collection be not better than plus color boccaro
Implements.Just it is that boccaro painted enamel is made something perfect even more perfect extraordinary splendor, takes the fragrant entrance of kettle tea water tender tea leaves to ooze and cherish.
Claims (2)
1. a kind of method that enamel is drawn on boccaro ware, comprises the following steps：
Boccaro ware is provided；
Dark-red enameled pottery is rinsed one time with wet cloth；
The first porcelain cream is prepared, the first porcelain cream is milky white porcelain cream, and its fineness is more than 300 mesh, and brightness is more than 75%；
The first porcelain cream is filled out at least a portion of the boccaro ware, the first porcelain cream of the boccaro ware is filled out
Thickness is 0.1-0.15 millimeters；
The boccaro ware for filling out the first porcelain cream is carried out into first to calcine；
The second porcelain cream different from the first porcelain cream is provided, and the second porcelain cream is filled out to the boccaro ware after the first calcining
In described at least a portion, the second porcelain cream is glass white；Fill out the first porcelain cream and described second of the boccaro ware
The gross thickness of porcelain cream is 2 millimeters；
The boccaro ware for filling out the second porcelain cream is carried out into second to calcine；
Picture needed for being drawn in described at least a portion of boccaro ware after being calcined described second；
Stippling is carried out to the picture with enamel color material color；
The boccaro ware for carrying out stippling is subjected to high temperature furnace grilling；
A kind of bright and new beautiful compound of picture, and institute for the boccaro ware that the compound is filled out after high temperature furnace grilling of allowing is provided
State at least a portion；The compound is glass white；
The boccaro ware for filling out the compound is subjected to high-temperature calcination, to burn till finished product；
Characterized in that, first calcining, the second calcining, the maximum temperature of high temperature furnace grilling and high-temperature calcination are raised successively
10-15℃；
First calcining, the second calcining, the initial temperature of high temperature furnace grilling and high-temperature calcination are 750 DEG C；
The maximum temperature of first calcining is 780-800 DEG C.
2. a kind of boccaro ware, it is characterised in that at least a portion on the surface of the boccaro ware is used according to institute in claim 1
The method stated, which is drawn, enamel.