CN104497627B - 一种银掺杂改性染料的制备方法 - Google Patents

一种银掺杂改性染料的制备方法 Download PDF

Info

Publication number
CN104497627B
CN104497627B CN201510000145.6A CN201510000145A CN104497627B CN 104497627 B CN104497627 B CN 104497627B CN 201510000145 A CN201510000145 A CN 201510000145A CN 104497627 B CN104497627 B CN 104497627B
Authority
CN
China
Prior art keywords
parts
obtains
mixture
dyestuff
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510000145.6A
Other languages
English (en)
Other versions
CN104497627A (zh
Inventor
叶澄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG HUANIAN YINGYI NEW MATERIAL TECHNOLOGY Co.,Ltd.
Original Assignee
Wenzhou Hongchengxiang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wenzhou Hongchengxiang Technology Co Ltd filed Critical Wenzhou Hongchengxiang Technology Co Ltd
Priority to CN201510000145.6A priority Critical patent/CN104497627B/zh
Publication of CN104497627A publication Critical patent/CN104497627A/zh
Application granted granted Critical
Publication of CN104497627B publication Critical patent/CN104497627B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种银掺杂改性染料的制备方法，该染料的具体制备步骤如下：1）取聚氨酯改性丙烯酸酯 15份，DI-TMPTA 18份，2,2-二甲基-1,3-丙二醇二苯甲酸酯 20份，MMA 20份，加入搅拌器中，加入聚乙烯醇 15份，高速搅拌和溶解，得到有机混合物；2）取TiO2粉末2份，纳米AgO 2份，缓慢滴加KBH4 15份，然后缓慢搅拌得到混合物，静置2小时；3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到银掺杂改性染料。该染料附着力、牢固性，耐水洗牢度和抗菌性较现有染料有大幅提升。

Description

一种银掺杂改性染料的制备方法
技术领域
本发明涉及一种银掺杂改性染料的制备方法。
背景技术
我国是纺织大国，具有几千年的纺织品加工、出口历史，同时纺织品的生产量极大。因此纺织品印染所需要的染料需求量也极大。由于传统织物以棉、丝为主要原料，因此染料种类有限。近年来随着材料科学的进步，特别是大量人工织物材料的相继研发和广泛使用，对染料的要求也越来越高，传统染料已经不能适应新的人工织物的特点要求，也很难满足现今对于服装面料着色的要求，具体反映在色牢度低，均染性差，抗菌性差等。
发明内容
针对现有技术中的不足，本发明提供了一种银掺杂改性染料的制备方法，该染料由以下重量份数的组分组成：2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，MMA20份，过氧化环已酮4份，DI-TMPTA18份，聚氨酯改性丙烯酸酯15份，TiO2粉末2份，纳米Ag2O2份，2,4-二羟基二苯甲酮5份，聚乙烯醇40份，KBH415份；
该染料的具体制备步骤如下：
1）取聚氨酯改性丙烯酸酯15份，DI-TMPTA18份，2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，MMA20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到银掺杂改性染料；
所述KBH4的质量浓度为1.5mol/L。
步骤1）的搅拌时间为30-60分钟。
步骤2）的搅拌时间为60分钟。
本发明的染料组合物包含DI-TMPTA、聚氨酯改性丙烯酸酯、丙氧基化新戊二醇二丙烯酸酯和MMA的组合，这四种组分单独用于染料中时有其各自的优势，如DI-TMPTA由于其独特的分子结构，将其用于染料组合物中能够有效改善染料的牢固性；MMA用于染料中可以提高染料的均匀能；聚氨酯改性丙烯酸酯可以提高染料的抗变色能力，而在本发明中将上述四种组分组合后使用，不仅具有上述性能，同时可显著提高染料与承印物之间的附着力、牢固性，耐水洗牢度和染色牢度。并且纳米阴离子掺杂在染料中，增强了燃料的抗菌性能，并且其与二氧化钛粉末结合，形成二氧化钛-纳米银复合薄膜，增强了染料的光催化活性能，缩短了上色时间。
具体实施方案
实施例1
1）取聚氨酯改性丙烯酸酯15份，DI-TMPTA18份，2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，MMA20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加1.5mol/L的KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到。
对比例1
1）取聚氨酯改性丙烯酸酯15份，MMA20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加1.5mol/L的KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到。
比较例2
1）取DI-TMPTA18份，2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加1.5mol/L的KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到。
对比例3
1）取聚氨酯改性丙烯酸酯15份，2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加1.5mol/L的KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到。
在相同条件下，对上述4中染料的上染率、染色牢度、耐水洗牢度、匀染性、抗菌性进行测试，设定实施例1的染料各项参数为1，其它染料的各项参数与实施例1的染料各项参数进行比较，比值如下。

Claims (4)

1.一种银掺杂改性染料的制备方法，其特征在于该染料由以下重量份数的组分组成：2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，MMA20份，过氧化环已酮4份，DI-TMPTA18份，聚氨酯改性丙烯酸酯15份，TiO2粉末2份，纳米Ag2O2份，2,4-二羟基二苯甲酮5份，聚乙烯醇40份，KBH415份；
该染料的具体制备步骤如下：
1）取聚氨酯改性丙烯酸酯15份，DI-TMPTA18份，2,2-二甲基-1,3-丙二醇二苯甲酸酯20份，MMA20份，加入搅拌器中，加入聚乙烯醇15份，高速搅拌和溶解，得到有机混合物；
2）取TiO2粉末2份，纳米Ag2O2份，缓慢滴加KBH415份，然后缓慢搅拌得到混合物，静置2小时；
3）取过氧化环已酮4份和2,4-二羟基二苯甲酮5份，加入到步骤1）得到的有机混合物中，高速搅拌10分钟，再加入步骤2）得到的混合物，最后加入聚乙烯醇25份，缓慢搅拌1h，静置4小时后得到银掺杂改性染料。
2.如权利要求1所述的制备方法，其特征在于：所述KBH4的质量浓度为1.5mol/L。
3.如权利要求1所述的制备方法，其特征在于：步骤1）的搅拌时间为30-60分钟。
4.如权利要求1所述的制备方法，其特征在于：步骤2）的搅拌时间为60分钟。
CN201510000145.6A 2015-01-02 2015-01-02 一种银掺杂改性染料的制备方法 Active CN104497627B (zh)