CN104496476B - 功能日用骨质瓷 - Google Patents
功能日用骨质瓷 Download PDFInfo
- Publication number
- CN104496476B CN104496476B CN201510014410.6A CN201510014410A CN104496476B CN 104496476 B CN104496476 B CN 104496476B CN 201510014410 A CN201510014410 A CN 201510014410A CN 104496476 B CN104496476 B CN 104496476B
- Authority
- CN
- China
- Prior art keywords
- function
- bone china
- far infrared
- daily
- oxygen ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明功能日用骨质瓷,涉及陶瓷制造技术领域,特别是涉及一种能够长久放射负氧离子和远红外线的功能型日用骨质瓷,具有抗菌杀菌、转换水分子团等功能。其特征在于主要由骨碳29‑33%、石英9‑12%、累托石粘土7‑10%、六环石12‑17%、电气石10‑13%、龙岩土11‑14%、长石7‑10%,另外加增塑剂1‑3%或腐植酸钠0.5‑1.5%等组成。本发明具有长久放射负氧离子和远红外线,抗菌杀菌,去除饮食中的微量有害物质等功能。
Description
技术领域
本发明功能日用骨质瓷,涉及陶瓷制造技术领域,特别是涉及一种能够长久放射负氧离子和远红外线的功能性日用骨质瓷,具有抗菌杀菌、转换水分子团等功能。
技术背景
市场上流通的主要有普通日用瓷器、骨质瓷器、玲珑日用瓷器、釉中釉下彩日用瓷器、日用精陶器、普通陶瓷和精细陶瓷烹调器等。日用陶瓷饮食器具多具有花面装饰,且大多以釉彩装饰,主要有釉上、釉中、釉下等装饰方式。不同的装饰方式在铅、镉等重金属元素含量上有较大区别。如长期食用铅、镉含量过高的产品盛装的食物,就会造成铝在血液中沉积,导致大脑中枢神经,肾脏等器官的损伤,对少年儿童的智力发育也会产生不良影响。
传统陶瓷物料仅局限于硅酸盐矿物的制作。
发明内容
本发明目的在于克服上述普通陶瓷的不足,提供一种集硅酸盐、碳酸盐、镁铝酸盐等多种天然矿物于一身,能够长久放射负氧离子和远红外线的功能性日用骨质瓷,具有抗菌杀菌、激活转换水分子团、溶出有益人体的微量元素等功能。
本发明的实现,通过对组成配方的反复试验,获得具有放射负氧离子和远红外线功能的日用骨质瓷。具体来说,本发明功能日用骨质瓷,主要由骨碳29-33 %、石英9-12%、累托石粘土7-10%、六环石12-17%、电气石10-13%、龙岩土11-14%、长石7-10%,另外加增塑剂1-3%或腐植酸钠0.5-1.5%等组成。
在本发明中:
骨碳:是脱脂后的骨块经1300摄氏度的高温煅烧后而得到的白的晶体或粉末,其主要用于陶瓷工业生产高档骨制瓷器。
石英:是非可塑性原料,其与粘土在高温中生成的莫来石晶体赋予瓷器较高的机械强度和化学稳定性,并能增加坯体的半透明性,是配制白釉的良好原料。
累托石:具有高温稳定性,耐火度高达1650℃,并能在500℃状态下保持结构稳定。还具有高分散性和高塑性,塑性指数可高达50,易粘结成形,烘干或烧结不产生裂纹。在本发明中主要用于产品成型时增加坯体可塑性,降低坯体耐火度。
六环石:是一种天然能量石,氧化铁含量在3%以上。负氧离子放射率1173 个/s.cm3,远红外线波长8-15um,含有高量贵金属锗,以及人体所需的生物电等等。在本发明中主要是实现放射负氧离子和远红外线功能。
电气石:是一种天然环状结构的硅酸盐矿物质,含有铝、铁、镁、钠、锂、钾等元素,具有抗菌杀菌,放射远红外线功能。在本发明中主要是实现放射远红外线功能。
长石:是一类常见的含钙、钠和钾的铝硅酸盐类造岩矿物,是陶瓷原料。硬度波动于6-6.5,比重波动于2-2.5,性脆,有较高的抗压强度,对酸有较强的化学稳定性。
增塑剂:主要作用是削弱聚合物分子之间的次价健,即范德华力,从而增加了聚合物分子链的移动性,降低了聚合物分子链的结晶性,即增加了聚合物的塑性,表现为聚合物的硬度、模量、软化温度和脆化温度下降,而伸长率、曲挠性和柔韧性提高。
腐植酸钠:采用天然含腐植酸的优质低钙低镁风化煤经化学提炼而成,它是多功能的高分子化合物,含有羟基,醌基,羧基等较多的活性基团,具有很大的内表面积,有较强的吸附,交换,络合,螯合能力。
其他物料:其他物料用途不在此一一详述,均为本发明保护范围。
本发明功能日用骨质瓷的生产工艺,基本与陶瓷产品相仿,工艺无特别要求,其特征主要在于原料配方,由骨碳29-33%、石英9-12%、累托石粘土7-10%、六环石12-17%、电气石10-13%、龙岩土11-14%、长石7-10%,另外加增塑剂1-3%或腐植酸钠0.5-1.5%等组成。按规定比例将物料进行加工粉碎成 800-1250目粉料,混配入池加水淘洗后,再用滤泥机滤水,制成含水量30%左右的泥饼进行真空搅拌,增强泥料的塑性,将搅拌好的泥段按规格切分,入成型出坯,再手工修验坯体、干燥、后入窑经1125℃的氧化焰烧制14小时,出窑检选合格者为素瓷。再经覆釉工序,然后二次入窑烧制形成成品。
本发明功能日用骨质瓷,由于采用了上述配方,配方中物料相互搭配,性能互补叠加,具有长久放射负氧离子和远红外线的功能,负氧离子放射量为 1100-2100个/s.cm3,远红外波长3-15um,发射率0.92。
本发明功能日用骨质瓷,自身不含有害重金属。
本发明功能日用骨质瓷能通过与饮食中的水接触,将饮食中的大水分子团、正电位等转换成小水分子团、负电位、富氧性,同时自身可溶出有益人体的微量元素。
本发明功能日用骨质瓷具有抗菌杀菌,去除饮食中的微量有害物质等功能。
具体实施方案
实施例1:将骨碳29-33%、石英9-12%、累托石粘土7-10%、六环石 12-17%、电气石10-13%、龙岩土11-14%、长石7-10%,另外加增塑剂1-3%或腐植酸钠0.5-1.5%等组成。按规定比例将物料进行加工粉碎成800-1250目粉料,混配入池加水淘洗后,再用滤泥机滤水,制成含水量30%左右的泥饼进行真空搅拌,增强泥料的塑性,将搅拌好的泥段按规格切分,入成型出坯,再手工修验坯体、干燥、后入窑经1125℃的氧化焰烧制14小时,出窑检选合格者为素瓷。再经覆釉工序,然后二次入窑烧制形成成品。完成所得产品其热稳定性、透明度、吸水率、铅镉溶出量等均符合骨质瓷标准。功能检测结果,固体负氧离子发射量1100-2100个/s.cm3,远红外线波长3-15um,发射率0.92。
Claims (3)
1.功能日用骨质瓷,其特征在于原料配方主要由骨碳29-33%、石英9-12%、累托石粘土7-10%、六环石12-17%、电气石10-13%、龙岩土11-14%、长石7-10%,另外加增塑剂1-3%或腐植酸钠0.5-1.5%组成。
2.根据从权利要求1所述的功能日用骨质瓷,其特征在于按规定比例将物料进行加工粉碎成800-1250目粉料,混配入池加水淘洗后,再用滤泥机滤水,制成含水量30%的泥饼进行真空搅拌,增强泥料的塑性,将搅拌好的泥段按规格切分,入成型出坯,再手工修验坯体、干燥、后入窑经1125℃的氧化焰烧制14小时,出窑检选合格者为素瓷,再经覆釉工序,然后二次入窑烧制形成成品。
3.根据权利要求1所述功能日用骨质瓷,其特征在于采用了上述特殊配方,配方中物料相互搭配,性能互补叠加,具有长久放射负氧离子和远红外线的功能,负氧离子放射量为1100-2100个/s.cm3,远红外波长3-15um,发射率0.92。