CN104496338A - 一种聚合物水泥基防水涂料 - Google Patents

一种聚合物水泥基防水涂料 Download PDF

Info

Publication number
CN104496338A
CN104496338A CN201410617552.7A CN201410617552A CN104496338A CN 104496338 A CN104496338 A CN 104496338A CN 201410617552 A CN201410617552 A CN 201410617552A CN 104496338 A CN104496338 A CN 104496338A
Authority
CN
China
Prior art keywords
cement
waterproof coating
polymer
base waterproof
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410617552.7A
Other languages
English (en)
Inventor
张庆彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410617552.7A priority Critical patent/CN104496338A/zh
Publication of CN104496338A publication Critical patent/CN104496338A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚合物水泥基防水涂料，由聚丙烯酸酯乳液、水泥、粉煤灰、氢氧化铝、减水剂、消泡剂和膨胀剂组成。本发明的聚合物水泥基防水涂料制备方法简单，原料价格低廉，对于生产设备要求不高；防水效果好，经测定，本发明的聚合物水泥基防水涂料在浸水后的附着度能够达到0.9以上，而在抗透水性方面完全不透水。

Description

一种聚合物水泥基防水涂料
技术领域
本发明是针对中国发明专利申请201210502907.9的分案申请，具体涉及一种聚合物水泥基防水涂料，属于涂料领域。
背景技术
防水涂料是在常温下呈无固定形状的粘稠液态高分子合成材料经涂布后，通过溶剂的挥发或水分的蒸发或反应固化后在基层面上形成坚韧的防水膜的材料的总称。目前，市场上的防水材料有两大类：一是聚氨脂类防水涂料。这类材料一般是由聚氨脂与煤焦油作为原材料制成。它所挥发的焦油气毒性大，且不容易清除，因此于2000年在我国被禁止使用。尚在销售的聚氨脂防水涂料，是用沥青代替煤焦油作为原料。但在使用这种涂料时，一般采用含有甲苯、二甲苯等有机溶剂来稀释，因而也含有毒性；另一类为聚合物水泥基防水涂料。它由多种水性聚合物合成的乳液与掺有各种添加剂的优质水泥组成，聚合物（树脂）的柔性与水泥的刚性结为一体，使得它在抗渗性与稳定性方面表现优异。它的优点是施工方便、综合造价低，工期短，且无毒环保。因此，聚合物水泥基已经成为防水涂料市场的主角。
发明内容
本发明的目的在于提供一种价格低廉、防水性好的聚合物水泥基防水涂料。上述目的是通过如下技术方案实现的：
一种聚合物水泥基防水涂料，由如下重量份的组分组成：
聚丙烯酸酯乳液              60-70份
水泥                                  10-20份
粉煤灰                               10-15份
氢氧化铝                             0.5-2份
减水剂                              0.05-0.1份
消泡剂                               0.2-0.5份
膨胀剂                               0.1-0.15份 。
本发明所述的聚丙烯酸酯乳液是指丙烯酸酯的聚合物乳液，单体包括但不限于甲基丙烯酸甲酯、丙烯酸丁酯、甲基丙烯酸羟乙酯、甲基丙烯酸 。作为优选，本发明中的聚丙烯酸酯乳液为60-65重量份 ，更优选65重量份。
本发明所述的水泥包括但不限于硅酸盐水泥、铝酸盐水泥、硫铝酸盐水泥、铁铝酸盐水泥、氟铝酸盐水泥、磷酸盐水泥；优选为硅酸盐水泥和磷酸盐水泥，更优选为硅酸盐水泥。一般而言，在本发明中，水泥的用量优选10-18重量份，更优选18重量份。
本发明所述的减水剂可以为聚羧酸系减水剂（PC）、萘系高效减水剂(PNS)和密胺系高效减水剂(PMS)，包括但不限于PERAMIN CONPAC 149S，Peramin SMF等。减水剂的用量优选为0.05-0.08份，更优选0.05份。
本发明所述的消泡剂可以为有机硅氧烷、聚醚、硅和醚接枝、含胺、亚胺和酰胺类，包括但与限于牌号为AGITAN 217、AGITAN 701 、AGITAN 260、AGITAN 305、AGITAN 315 、AGITAN P 800、AGITAN P 813、AGITAN P 823的那些消泡剂。减水剂的用量优选为0.25-0.3份，更优选0.25份。
本发明所述的膨胀剂可以为明矾石膨胀剂、硫铝酸钙膨胀剂、氧化钙膨胀剂、铁屑膨胀剂、氧化钙-硫铝酸钙复合膨胀剂等，优选为硫铝酸钙膨胀剂。膨胀剂的用量优选为0.1份。
本发明的聚合物水泥基防水涂料一般可以通过如下的方法制备：
按比例称量各组分，将聚丙烯酸酯乳液倒入搅拌釜中搅拌，搅拌时间为3-5分钟，然后将水泥、粉煤灰、氢氧化铝、减水剂、消泡剂和膨胀剂依次加入搅拌釜中继续搅拌，直至混合均匀，即得成品。
本发明的有益效果在于：
1、制备方法简单，原料价格低廉，对于生产设备要求不高；
2、  防水效果好，经测定，本发明的聚合物水泥基防水涂料在浸水后的附着度能够达到0.9以上，而在抗透水性方面完全不透水。
具体实施方式
实施例1
将60重量份聚丙烯酸酯乳液倒入搅拌釜中搅拌，搅拌时间为3分钟，然后将18份硅酸盐水泥、13份粉煤灰、1份氢氧化铝、0.05份PERAMIN CONPAC 149S、0.25份AGITAN P 813和0.1份硫铝酸钙膨胀剂依次加入搅拌釜中继续搅拌，直至混合均匀，即得成品。
实施例2
将65重量份聚丙烯酸酯乳液倒入搅拌釜中搅拌，搅拌时间为5分钟，然后将15份硅酸盐水泥、10份粉煤灰、2份氢氧化铝、0.05份PERAMIN CONPAC 149S、0.25份AGITAN P 823和0.1份硫铝酸钙膨胀剂依次加入搅拌釜中继续搅拌，直至混合均匀，即得成品。
实施例3
将65重量份聚丙烯酸酯乳液倒入搅拌釜中搅拌，搅拌时间为5分钟，然后将18份硅酸盐水泥、15份粉煤灰、1份氢氧化铝、0.05份PERAMIN CONPAC 149S、0.25份AGITAN P 823和0.1份硫铝酸钙膨胀剂依次加入搅拌釜中继续搅拌，直至混合均匀，即得成品。
实施例4
将实施例1-3制得的聚合物水泥基防水涂料用于防水性能测试，测试结果如下表所示：
。

Claims (7)

1. 一种聚合物水泥基防水涂料，由如下重量份的组分组成：
聚丙烯酸酯乳液              60-70份
水泥                                  10-20份
粉煤灰                               10-15份
氢氧化铝                             0.5-2份
减水剂                              0.05-0.1份
消泡剂                               0.2-0.5份
膨胀剂                               0.1-0.15份 。
2. 如权利要求1所述的聚合物水泥基防水涂料，其中所述水泥选自硅酸盐水泥、铝酸盐水泥、硫铝酸盐水泥、铁铝酸盐水泥、氟铝酸盐水泥、磷酸盐水泥的一种或几种。
3. 如权利要求1或2所述的聚合物水泥基防水涂料，其中所述减水剂选自聚羧酸系减水剂（PC）、萘系高效减水剂(PNS)和密胺系高效减水剂(PMS)的一种或几种。
4. 如权利要求1-3任一项所述的聚合物水泥基防水涂料，其中所述消泡剂选自有机硅氧烷、聚醚、硅和醚接枝、含胺、亚胺和酰胺类中的一种或几种。
5. 如权利要求1-3任一项所述的聚合物水泥基防水涂料，其中所述的膨胀剂选自明矾石膨胀剂、硫铝酸钙膨胀剂、氧化钙膨胀剂、铁屑膨胀剂、氧化钙-硫铝酸钙复合膨胀剂的一种或几种。
6.  如权利要求1所述的聚合物水泥基防水涂料，由如下重量份的组分组成：
聚丙烯酸酯乳液              65份
水泥                                  18份
粉煤灰                               10份
氢氧化铝                            1份
减水剂                              0.05份
消泡剂                               0.25份
膨胀剂                               0.1份 。
7.  如权利要求1-6任一项所述的聚合物水泥基防水涂料在防水工程中的应用。
CN201410617552.7A 2012-11-30 2012-11-30 一种聚合物水泥基防水涂料 Pending CN104496338A (zh)