CN104479842A - 一种绿色环保混凝土脱模剂及其制备方法 - Google Patents

一种绿色环保混凝土脱模剂及其制备方法 Download PDF

Info

Publication number
CN104479842A
CN104479842A CN201410786232.4A CN201410786232A CN104479842A CN 104479842 A CN104479842 A CN 104479842A CN 201410786232 A CN201410786232 A CN 201410786232A CN 104479842 A CN104479842 A CN 104479842A
Authority
CN
China
Prior art keywords
parts
pine tar
release agent
deionized water
green
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410786232.4A
Other languages
English (en)
Inventor
候鸣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MENGCHENG COUNTY TECHNOLOGY INNOVATION SERVICE CENTER
Original Assignee
MENGCHENG COUNTY TECHNOLOGY INNOVATION SERVICE CENTER
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MENGCHENG COUNTY TECHNOLOGY INNOVATION SERVICE CENTER filed Critical MENGCHENG COUNTY TECHNOLOGY INNOVATION SERVICE CENTER
Priority to CN201410786232.4A priority Critical patent/CN104479842A/zh
Publication of CN104479842A publication Critical patent/CN104479842A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种绿色环保混凝土脱模剂及其制备方法，其组成原料的重量份为：聚乙烯醇35-40、改性松油60-70、氧化锌2-4、水杨酸钠0.4-0.5、酯酸乙酯0.8-1.5、硫酸钠2-4、脱硫石膏4-5、丁二酸0.2-0.4、硬脂酸0.5-1.0、二异氰酸酯0.8-1.0、氯化铵1-2、正硅酸乙酯0.3-0.5、玉米淀粉3-4和去离子水200-250；本发明的松油通过加入硫酸亚铁、碳纤维、竹纤维联合改性，提高脱模剂的吸附性，增强对模具的附着力，使得对混凝土的粘附力小，脱模滑性好，再通过腐植酸钾粉体对其疏水化改性，实现其对混凝土与模具之间的快速分离。

Description

一种绿色环保混凝土脱模剂及其制备方法
技术领域
本发明提供了一种混凝土脱模剂，特别涉及一种绿色环保混凝土脱模剂及其制备方法。
背景技术
混凝土脱模剂又称混凝土隔离剂或脱模润滑剂；是一种涂于模板内壁起润滑和隔离作用，使混凝土在拆模时能顺利脱离模板，保持混凝土形状完整无损的物质，传统的脱模材料是用机油或废机油加柴油，在长期的水利水电、公路、铁路等工程施工中发现，使用废机油涂刷模板，对混凝土表面产生污染，同时对环境也造成不同程度的污染；但是现有脱模剂存在脱模效果不佳、在模板上难以去除，而且对模板养护不力，使得施工效率等受到影响也增加建设成本。
发明内容
本发明的目的在于提供一种绿色环保混凝土脱模剂及其制备方法。
为了实现上述目的本发明采用如下技术方案：
绿色环保混凝土脱模剂，其组成原料的重量份为：聚乙烯醇35-40、改性松油60-70、氧化锌2-4、水杨酸钠0.4-0.5、酯酸乙酯0.8-1.5、硫酸钠2-4、脱硫石膏4-5、丁二酸0.2-0.4、硬脂酸0.5-1.0、二异氰酸酯0.8-1.0、氯化铵1-2、正硅酸乙酯0.3-0.5、玉米淀粉3-4和去离子水200-250。
绿色环保混凝土脱模剂，其组成原料的重量份为：聚乙烯醇38、改性松油65、氧化锌3、水杨酸钠0.4、酯酸乙酯1.2、硫酸钠3、脱硫石膏4.5、丁二酸0.3、硬脂酸0.8、二异氰酸酯0.9、氯化铵1.5、正硅酸乙酯0.4、玉米淀粉3.5和去离子水220。
绿色环保混凝土脱模剂的制备方法，包括以下内容：
（1）改性松油的制备：先将松油加热至50-60℃；然后向其中加入松油质量的3.5-4.0%硫酸亚铁、8-10%碳纤维、10-15%竹纤维；搅拌混合均匀放置2-3小时，然后再加入松油4-5%的腐植酸钾粉体，升温至80-90℃的条件下均匀搅拌1-2小时，自然冷却至室温，调节溶液pH值至2-3；再与去离子水按质量比1:5混合、搅拌30-40分钟，离心分离得滤液即可；
（2）按组成原料的重量份称取各原料，先将聚乙烯醇和去离子水加入反应釜中，搅拌升温至约70-80℃，然后加入步骤（1）的改性松油至完全溶解；再向其中加入其它剩余组成原料，搅拌均匀，温度控制在70-80℃，保温1-2 小时后出料。
本发明的有益效果：
本发明的松油通过加入硫酸亚铁、碳纤维、竹纤维联合改性，提高脱模剂的吸附性，增强对模具的附着力，使得对混凝土的粘附力小，脱模滑性好，再通过腐植酸钾粉体对其疏水化改性，实现其对混凝土与模具之间的快速分离。
具体实施方式
实施例1：绿色环保混凝土脱模剂，其组成原料的重量份（kg）为：聚乙烯醇38、改性松油65、氧化锌3、水杨酸钠0.4、酯酸乙酯1.2、硫酸钠3、脱硫石膏4.5、丁二酸0.3、硬脂酸0.8、二异氰酸酯0.9、氯化铵1.5、正硅酸乙酯0.4、玉米淀粉3.5和去离子水220。
绿色环保混凝土脱模剂的制备方法，包括以下内容：
（1）改性松油的制备：先将松油加热至55℃；然后向其中加入松油质量的3.8%硫酸亚铁、8%碳纤维、12%竹纤维；搅拌混合均匀放置2-3小时，然后再加入松油4.5%的腐植酸钾粉体，升温至85℃的条件下均匀搅拌1-2小时，自然冷却至室温，调节溶液pH值至2-3；再与去离子水按质量比1:5混合、搅拌35分钟，离心分离得滤液即可；
（2）按组成原料的重量份称取各原料，先将聚乙烯醇和去离子水加入反应釜中，搅拌升温至约75℃，然后加入步骤（1）的改性松油至完全溶解；再向其中加入其它剩余组成原料，搅拌均匀，温度控制在75℃，保温1-2 小时后出料。
    上述制得的混凝土脱模剂固含量≤5.5%；对钢板无任何腐蚀危害，干膜时间20-25min；具有很好的耐水性能，混凝土表面光滑，粘附量为3.8g/m2，符合混
凝土脱模剂的使用要求。

Claims (3)

1.一种绿色环保混凝土脱模剂，其特征在于其组成原料的重量份为：聚乙烯醇35-40、改性松油60-70、氧化锌2-4、水杨酸钠0.4-0.5、酯酸乙酯0.8-1.5、硫酸钠2-4、脱硫石膏4-5、丁二酸0.2-0.4、硬脂酸0.5-1.0、二异氰酸酯0.8-1.0、氯化铵1-2、正硅酸乙酯0.3-0.5、玉米淀粉3-4和去离子水200-250。
2.根据权利要求1所述的绿色环保混凝土脱模剂，其特征在于其组成原料的重量份为：聚乙烯醇38、改性松油65、氧化锌3、水杨酸钠0.4、酯酸乙酯1.2、硫酸钠3、脱硫石膏4.5、丁二酸0.3、硬脂酸0.8、二异氰酸酯0.9、氯化铵1.5、正硅酸乙酯0.4、玉米淀粉3.5和去离子水220。
3.一种如权利要求1所述的绿色环保混凝土脱模剂的制备方法，其特征在于包括以下内容：
（1）改性松油的制备：先将松油加热至50-60℃；然后向其中加入松油质量的3.5-4.0%硫酸亚铁、8-10%碳纤维、10-15%竹纤维；搅拌混合均匀放置2-3小时，然后再加入松油4-5%的腐植酸钾粉体，升温至80-90℃的条件下均匀搅拌1-2小时，自然冷却至室温，调节溶液pH值至2-3；再与去离子水按质量比1:5混合、搅拌30-40分钟，离心分离得滤液即可；
（2）按组成原料的重量份称取各原料，先将聚乙烯醇和去离子水加入反应釜中，搅拌升温至约70-80℃，然后加入步骤（1）的改性松油至完全溶解；再向其中加入其它剩余组成原料，搅拌均匀，温度控制在70-80℃，保温1-2 小时后出料。
CN201410786232.4A 2014-12-18 2014-12-18 一种绿色环保混凝土脱模剂及其制备方法 Pending CN104479842A (zh)