CN104479451A - 印刷烟用接装纸的连接料 - Google Patents
印刷烟用接装纸的连接料 Download PDFInfo
- Publication number
- CN104479451A CN104479451A CN201510023151.3A CN201510023151A CN104479451A CN 104479451 A CN104479451 A CN 104479451A CN 201510023151 A CN201510023151 A CN 201510023151A CN 104479451 A CN104479451 A CN 104479451A
- Authority
- CN
- China
- Prior art keywords
- tipping paper
- polyvinyl butyral
- cigarette tipping
- binder
- butyral acetal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及印刷油墨技术领域,具体来说是一种印刷烟用接装纸连接料,由聚乙烯醇缩丁醛和乙醇制备而成。本发明选用溶解粘度为6秒的聚乙烯醇缩丁醛和乙醇为原料,配方简单,制备方法简便,生产的产品彻底解决安全性指标问题,又满足产品生产的工艺需求。最大限度减少挥发性物质的含量和种类,生产的烟用接装纸安全性指标达到绿色环保产品,符合质量标准要求;此外由于配方简单,可降低企业的生产成本;本发明连接料中挥发性物质种类少、含量低,对人体无害,满足日益严格的环保要求。
Description
技术领域
本发明涉及印刷油墨技术领域,具体来说是一种印刷烟用接装纸的连接料。
背景技术
烟用接装纸为把过滤嘴与卷烟烟支接装起来的专用纸,它主要由纸张、油墨等辅助材料组成,油墨是接装纸的重要组成部分,而油墨的好坏直接决定了产品的美观及各种卫生指标,多数香烟的接装纸包装多数为黄底色,搭配各种烫金,镭射及其他工艺组合而成,油墨在烟用接装纸中占有举足轻重的作用。
印刷接装纸的油墨主要包括颜料和连接料,连接料的作用是将颜料印刷附着到接装纸上,目前连接料主要由有机成分组成,其组成和含量直接影响油墨中挥发性物质和重金属物质的含量现今主要采用的连接料主要是由40秒聚乙烯醇缩丁醛、蓖麻油、松香、二丁酯和乙醇等组合制备而成,存在生产的油墨挥发性物质不但种类多,而且含量也较高,不能满足产品质量要求的缺点。
发明内容
本发明的目的是针对上述背景技术存在的问题,提供一种印刷烟用接装纸的连接料。
为实现上述目的,本发明采用的技术方案是:一种印刷烟用接装纸的连接料,由聚乙烯醇缩丁醛和乙醇制备而成。
进一步的,所述聚乙烯醇缩丁醛的重量百分比为8~15%,余量为乙醇制备成100%。
进一步的,所述聚乙烯醇缩丁醛的重量百分比10.1%。
进一步的,所述聚乙烯醇缩丁醛溶解粘度为6秒。
本发明的另一目的是提供一种印刷烟用接装纸连接料的制备方法,步骤包括:
(1)在反应釜中加入乙醇,搅拌过程中缓慢加入溶解粘度为6秒的聚乙烯醇缩丁醛后继续搅拌1小时;
(2)升温3~4小时,使温度至52~58℃,确保无块状;
(3)维持温度52~58℃,搅拌10小时以上,制成粘度为27″~43″的成品连接料。
本发明的有益技术效果是:
(1)本发明选用溶解粘度为6秒的聚乙烯醇缩丁醛和乙醇为原料,配方简单,制备方法简便,生产的产品彻底解决安全性指标问题,又满足产品生产的工艺需求。最大限度减少挥发性物质的含量和种类,生产的烟用接装纸安全性指标达到绿色环保产品,符合质量标准要求;此外由于配方简单,可降低企业的生产成本;
(2)本发明连接料中挥发性物质种类少、含量低,对人体无害,满足严格的环保要求。
本发明连接料产品检测数据如下表1、表2和表3:
表1 本发明产品无机元素检测结果
表2 发明产品挥发性有机化合物检测结果
表3 发明产品挥发性有机化合物检测结果
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
一种印刷烟用接装纸连接料,由聚乙烯醇缩丁醛和乙醇制备而成,聚乙烯醇缩丁醛的重量百分比10.1%,乙醇的重量百分比为89.9%。
其中,聚乙烯醇缩丁醛溶解粘度为6秒。
制备方法,步骤包括:
(1)在反应釜中加入乙醇89.9%,搅拌过程中缓慢加入溶解粘度为6秒的聚乙烯醇缩丁醛10.1%后继续搅拌1小时;
(2)升温3小时,使温度至55℃,确保无块状;
(3)维持温度55℃,搅拌11小时,制成粘度为35″的成品连接料。
实施例2
一种印刷烟用接装纸连接料,由聚乙烯醇缩丁醛和乙醇制备而成,聚乙烯醇缩丁醛的重量百分比8%,乙醇的重量百分比为92%。
其中,聚乙烯醇缩丁醛溶解粘度为6秒。
制备方法,步骤包括:
(1)在反应釜中加入乙醇92%,搅拌过程中缓慢加入溶解粘度为6秒的聚乙烯醇缩丁醛8%后继续搅拌1小时;
(2)升温3.5小时,使温度52℃,确保无块状;
(3)维持温度52℃,搅拌10小时,制成粘度为27″的成品连接料。
实施例3
一种印刷烟用接装纸连接料,由聚乙烯醇缩丁醛和乙醇制备而成,聚乙烯醇缩丁醛的重量百分比为15%,乙醇的重量百分比为85%。
其中,聚乙烯醇缩丁醛溶解粘度为6秒。
制备方法,步骤包括:
(1)在反应釜中加入乙醇85%,搅拌过程中缓慢加入溶解粘度为6秒的聚乙烯醇缩丁醛15%后继续搅拌1小时;
(2)升温4小时,使温度至58℃,确保无块状;
(3)维持温度58℃,搅拌12小时,制成粘度为43″的成品连接料。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.印刷烟用接装纸的连接料,其特征在于,由聚乙烯醇缩丁醛和乙醇制备而成。
2.根据权利要求1所述印刷烟用接装纸的连接料,其特征在于,所述聚乙烯醇缩丁醛的重量百分比为8~15%,余量为乙醇制备成100%。
3.根据权利要求2所述印刷烟用接装纸的连接料,其特征在于,所述聚乙烯醇缩丁醛的重量百分比10.1%。
4.根据权利要求3所述印刷烟用接装纸的连接料,其特征在于,所述聚乙烯醇缩丁醛溶解粘度为6秒。
5.根据权利要求1~4任一项所述印刷烟用接装纸连接料的制备方法,其特征在于,步骤包括:
(1)在反应釜中加入乙醇,搅拌过程中缓慢加入溶解粘度为6秒的聚乙烯醇缩丁醛后继续搅拌1小时;
(2)升温3~4小时,使温度至52~58℃,确保无块状;
(3)维持温度52~58℃,搅拌10小时以上,制成粘度为27″~43″的成品连接料。