CN104478304A - 一种环保泡沫混凝土砌块的配方 - Google Patents
一种环保泡沫混凝土砌块的配方 Download PDFInfo
- Publication number
- CN104478304A CN104478304A CN201410624426.4A CN201410624426A CN104478304A CN 104478304 A CN104478304 A CN 104478304A CN 201410624426 A CN201410624426 A CN 201410624426A CN 104478304 A CN104478304 A CN 104478304A
- Authority
- CN
- China
- Prior art keywords
- formula
- foam concrete
- environment
- water
- building block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种环保泡沫混凝土砌块配方,属于建筑材料领域。本发明的环保泡沫混凝土砌块配方按质量比由如下原料组成:水泥280~300kg;粉煤灰80~120kg;建筑垃圾100~120kg;水185kg;浓度为10%的发泡剂水溶液17~18kg;浓度为10%的稳泡剂水溶液0.9kg;经搅拌、发泡、成型、切割,最后风干凝结制得成品。由于本发明的环保泡沫混凝土砌块使用了粉煤灰、建筑垃圾等废料,并且无需煅烧,更加节能环保。
Description
技术领域
本发明涉及建筑行业,具体涉及一种环保泡沫混凝土砌块的配方。
背景技术
目前,市场上的环保砖配方主要用到的环保材料有建筑垃圾、秸秆、煤渣等,这类材料的应用符合物尽其用、变废为宝的资源节约型社会发展方向。中国专利(申申请号-: CN201410198114 )公开了一种环保砖及其生产方法,其用到的配方主要为:煤矸石、建筑垃圾、煤渣、花岗岩碎渣、水、秸秆。以这类原料制得砖块需要高温煅烧,因此在保证原料环保的情况下,无法兼顾生产过程的节能环保。
发明内容
本发明的目的在于提供一种配方简单、节能环保的泡沫混凝土砌块的配方。
本发明的环保泡沫混凝土砌块配方包含以下原料:水泥、粉煤灰、建筑垃圾、水、发泡剂、稳泡剂。原料按质量百分比组成为:水泥40%~43%;粉煤灰11.5%~17%;建筑垃圾14%~17%;水26.5%;浓度为10%的发泡剂水溶液2.15%~2.4%;浓度为10%的稳泡剂水溶液0.13%。其中,所述建筑垃圾为被粉碎后的细小颗粒,其颗粒平均粒径为0.2~0.4mm;所述稳泡剂水溶液由硬脂酸钙、明矾、早强减水剂以及水配制而成。
由于配方采用以上原料,本发明的有益效果是:
主料仅包含三种材料:水泥、粉煤灰和建筑垃圾,其配方简单,原料环保易得。用此配方生产砌块,可直接凝固成型,无需高温煅烧,使得生产过程更加节能环保。水泥的应用保证了砌块的强度和致密度,砌块的使用寿命更长。
具体实施方式
实施例1
取水泥40kg;粉煤灰17kg;建筑垃圾17kg;水26.5kg;浓度为10%的发泡剂水溶液2.15kg;浓度为10%的稳泡剂水溶液0.13kg。经搅拌、发泡、成型、切割后制得轻质砌块。测算制得的泡沫砌块,其密度小于450kg/m3,不渗水,能一直浮于水面。
实施例2
取水泥42kg;粉煤灰14kg;建筑垃圾15kg;水26.5kg;浓度为10%的发泡剂水溶液2.3kg;浓度为10%的稳泡剂水溶液0.13kg。经搅拌、发泡、成型、切割后制得轻质砌块。测算制得的泡沫砌块,其密度小于450kg/m3,不渗水,能一直浮于水面。
实施例3
取水泥43kg;粉煤灰11.5kg;建筑垃圾14kg;水26.5kg;浓度为10%的发泡剂水溶液2.4kg;浓度为10%的稳泡剂水溶液0.13kg。经搅拌、发泡、成型、切割后制得轻质砌块。测算制得的泡沫砌块,其密度小于450kg/m3,不渗水,能一直浮于水面。
Claims (3)
1.一种环保泡沫混凝土砌块的配方,其特征在于,原料按质量百分比组成为:水泥40%~43%;粉煤灰11.5%~17%;建筑垃圾14%~17%;水26.5%;浓度为10%的发泡剂水溶液2.15%~2.4;浓度为10%的稳泡剂水溶液0.13%。
2.如权利要求1所述的环保泡沫混凝土砌块的配方,其特征在于,所述建筑垃圾为被粉碎后的细小颗粒,其颗粒平均粒径为0.2~0.4mm。
3.如权利要求1所述的环保泡沫混凝土砌块的配方,其特征在于,所述稳泡剂水溶液由硬脂酸钙、明矾、早强减水剂以及水配制而成。