CN104475038A - 一种汽车用环保型空气净化剂及其制备方法 - Google Patents

一种汽车用环保型空气净化剂及其制备方法 Download PDF

Info

Publication number
CN104475038A
CN104475038A CN201410742810.4A CN201410742810A CN104475038A CN 104475038 A CN104475038 A CN 104475038A CN 201410742810 A CN201410742810 A CN 201410742810A CN 104475038 A CN104475038 A CN 104475038A
Authority
CN
China
Prior art keywords
parts
air purification
extract
preparation
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410742810.4A
Other languages
English (en)
Other versions
CN104475038B (zh
Inventor
唐丽
吴方丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANNING TIANLIANG FINE CHEMICAL CO., LTD.
Original Assignee
陈素云
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈素云 filed Critical 陈素云
Priority to CN201410742810.4A priority Critical patent/CN104475038B/zh
Publication of CN104475038A publication Critical patent/CN104475038A/zh
Application granted granted Critical
Publication of CN104475038B publication Critical patent/CN104475038B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及空气净化剂，具体为汽车空气净化剂，属于空气净化领域。由生姜提取液、薄荷提取液、老鹳草提取液、桉树油、松节油、山苍子油，混合搅拌得到空气净化液；硅藻土、活性炭粉、二氧化钛粉、高岭土、蒙脱石、沸石、麦饭石，研磨混合，加水搅拌进行造粒、烘干，得到空气净化颗粒；空气净化颗粒加入到空气净化液中进行浸泡，沥干，包装。本发明提供的汽车空气净化剂，利用植物提取的有效物质对空气进行净化，无毒无害，结合硅藻土等物质制成的空气净化颗粒，可以起到吸附的作用，将空气净化液浸入到空气净化颗粒中，将两者功能有机的结合起来，提高了空气净化的功效。

Description

一种汽车用环保型空气净化剂及其制备方法
技术领域
本发明涉及空气净化剂，具体为一种汽车用环保型空气净化剂及其制备方法。属于空气净化的技术领域。
背景技术
目前的汽车用的空气净化剂，有用香精配制成的清新剂，利用香味掩盖汽车内的气味，不能跟不上解决问题，或者用化工原料配制成除味剂，虽然可以消除一些有毒气体成份，但是产生二次污染。或者仅仅依靠物理吸附作用去除异味，比如活性炭吸附，虽然不会产生二次污染，但是吸附效果比较慢。
发明内容
针对上述技术问题，本发明提供一种无毒无害并且能有效去除汽车内气味的净化剂，具体技术方案为：
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液10～13份、薄荷提取液8～10份、老鹳草提取液6～9份、桉树油10～12份、松节油5～7份、山苍子油4～6份；混合搅拌得到空气净化液；
优选地，还加入5-8份的百香果发酵提取液；所述的百香果发酵提取液制备方法如下：取新鲜的百香果的果皮，与蔗糖按照重量比例为1∶1，混合均匀，优选将百香果的果皮破碎至1-2厘米见方的小块后洗干净、沥干，按一层果皮一层蔗糖的顺序放入瓶子中(最后一层必须是糖，需保证瓶中留有1成空间供其发酵)，避光保存在阴暗处15天至3个月，将其最终发酵的产品过滤后，取液体备用，作为本发明的百香果发酵提取液。
此百香果发酵提取液是发明人经过多次试验得到的添加剂，是本发明的发明点，因为加入了本发明中的百香果发酵提取液后的产品在空调的杀菌抑菌方面具有非常独特的效果，而且此百香果发酵提取液的气味芬芳，给人以非常愉悦的感觉，更优选地，如果按照1∶1重量比例，将新鲜的百香果的果皮与菠萝皮进行混合后，再用同样的方法制备百香果发酵提取液，则气味更加芬芳，抑菌的效果非常好，其中的菠萝蛋白酶会使得发酵液更容易成功，是提高生产效率的非常好的解决途径，而且可以缩短发酵时间，15天就可以有单独百香果果皮发酵25天的效果。
硅藻土30～45份、活性炭粉5～8份、二氧化钛粉2～5份、高岭土17～20份、蒙脱石15～18份、沸石20～25份、麦饭石10～13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2～0.25；进行造粒；
(4)造粒后进行烘干，烘干温度为75～85℃，烘1～1.5小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，浸泡10～12小时后，沥干，包装。
其中步骤(4)是本发明的发明点，因为经过发明人的多次试验，温度和烘干时间掌握不好的时候，会对最终产品的净化效果起到非常大的影响，因为会使得挥发性物质过快的出去，并且会影响到缓释效果，故本发明人的烘干方法是本发明产品可以效果很好的一个很关键的部分。
本发明的另外一个发明点是：步骤(5)中的浸泡步骤优选如下：烘干后的空气净化颗粒加入到空气净化液中进行浸泡，室温25摄氏度下浸泡20-30分钟，将温度加热到40-50摄氏度浸泡30-60分钟，再将温度上升到55-65摄氏度浸泡10-20分钟，再将温度降低到室温后保持1-5小时。经过了发明人多次试验，经过了这样的升温降温浸泡之后，可以使得香味物质保持更加持久，而这些温度和浸泡时间的参数是经过发明人无数次试验得到的最优方案。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.5～0.8∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
本发明提供的汽车空气净化剂，利用植物提取的有效物质对空气进行净化，无毒无害，结合硅藻土等物质制成的空气净化颗粒，可以起到吸附的作用，将空气净化液浸入到空气净化颗粒中，将两者功能有机的结合起来，提高了空气净化的功效。
具体实施方式
结合实施例说明本发明的具体技术方案：
实施例1
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液12份、薄荷提取液9份、老鹳草提取液7份、桉树油11份、松节油6份、山苍子油5份；混合搅拌得到空气净化液；
硅藻土40份、活性炭粉7份、二氧化钛粉4份、高岭土18份、蒙脱石17份、沸石22份、麦饭石12份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.25；进行造粒；
(4)造粒后进行烘干，烘干温度为85℃，烘1小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，浸泡10小时后，沥干，包装。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.5∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
实施例2
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液13份、薄荷提取液8份、老鹳草提取液9份、桉树油10份、松节油5份、山苍子油4份；混合搅拌得到空气净化液；
硅藻土45份、活性炭粉8份、二氧化钛粉5份、高岭土17份、蒙脱石15份、沸石20份、麦饭石10份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2；进行造粒；
(4)造粒后进行烘干，烘干温度为75℃，烘1小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，浸泡12小时后，沥干，包装。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.8∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
实施例3
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液10份、薄荷提取液10份、老鹳草提取液6份、桉树油12份、松节油7份、山苍子油6份；混合搅拌得到空气净化液；
硅藻土30份、活性炭粉5份、二氧化钛粉2份、高岭土20份、蒙脱石18份、沸石25份、麦饭石13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2；进行造粒；
(4)造粒后进行烘干，烘干温度为80℃，烘1.2小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，浸泡12小时后，沥干，包装。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.7∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
实施例4
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液10份、薄荷提取液10份、老鹳草提取液6份、桉树油12份、松节油7份、山苍子油6份；混合搅拌得到空气净化液；
硅藻土30份、活性炭粉5份、二氧化钛粉2份、高岭土20份、蒙脱石18份、沸石25份、麦饭石13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2；进行造粒；
(4)造粒后进行烘干，烘干温度为80℃，烘1.2小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，室温25摄氏度下浸泡30分钟，将温度加热到50摄氏度浸泡60分钟，再将温度上升到-65摄氏度浸泡20分钟，再将温度降低到室温后保持5小时。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.7∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
实施例5
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液10份、薄荷提取液10份、老鹳草提取液6份、桉树油12份、松节油7份、山苍子油6份、百香果发酵提取液5份；混合搅拌得到空气净化液；
硅藻土30份、活性炭粉5份、二氧化钛粉2份、高岭土20份、蒙脱石18份、沸石25份、麦饭石13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2；进行造粒；
(4)造粒后进行烘干，烘干温度为80℃，烘1.2小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，室温25摄氏度下浸泡20分钟，将温度加热到40摄氏度浸泡30分钟，再将温度上升到55摄氏度浸泡10分钟，再将温度降低到室温后保持1小时。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.7∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
所述的百香果发酵提取液制备方法如下：取新鲜的百香果的果皮，与蔗糖按照重量比例为1∶1，混合均匀，优选将百香果的果皮破碎至1-2厘米见方的小块后洗干净、沥干，按一层果皮一层蔗糖的顺序放入瓶子中(最后一层必须是糖，需保证瓶中留有1成空间供其发酵)，避光保存在阴暗处3个月，将其最终发酵的产品过滤后，取液体备用，作为本发明的百香果发酵提取液。
实施例6
汽车空气净化剂，由以下原料按照重量份数组成，生姜提取液10份、薄荷提取液10份、老鹳草提取液6份、桉树油12份、松节油7份、山苍子油6份、百香果发酵提取液5份；混合搅拌得到空气净化液；
硅藻土30份、活性炭粉5份、二氧化钛粉2份、高岭土20份、蒙脱石18份、沸石25份、麦饭石13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2；进行造粒；
(4)造粒后进行烘干，烘干温度为80℃，烘1.2小时，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，室温25摄氏度下浸泡20分钟，将温度加热到45摄氏度浸泡45分钟，再将温度上升到60摄氏度浸泡15分钟，再将温度降低到室温后保持3小时。
生姜提取液、薄荷提取液、老鹳草提取液的制备方法为：将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液，残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.7∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
所述的百香果发酵提取液制备方法如下：取新鲜的百香果的果皮和菠萝皮按照重量份1∶1混合后破碎，破碎后的果皮混合物与蔗糖按照重量比例为1∶1混合均匀，按一层果皮一层蔗糖的顺序放入瓶子中(最后一层必须是糖，需保证瓶中留有1成空间供其发酵)，避光保存在阴暗处15天，将其最终发酵的产品过滤后，取液体备用，作为本发明的百香果发酵提取液。
对实施例所制得的汽车空气净化剂与对比例进行比较。对比例1采用活性炭包，对比例2-6分别为商业购买的市售化学除味剂。汽车车厢封闭，48小时后进行测试对比，对比结果如下：
表1 各净化剂使用效果对比
从实验对比结果可见，本发明提供的汽车空气净化剂，不仅具有较好的甲醛去除效果，还可以消除强烈的异味，使用后，不产生异味，而活性炭包去除效率最差，市售的化学除味剂虽然也有较好的去甲醛效果，但是异味不能消除。

Claims (6)

1.一种汽车用环保型空气净化剂的制备方法，其特征在于：由以下原料按照重量份数组成，生姜提取液10～13份、薄荷提取液8～10份、老鹳草提取液6～9份、桉树油10～12份、松节油5～7份、山苍子油4～6份；混合搅拌得到空气净化液；优选地，还加入5-8份的百香果发酵提取液；
硅藻土30～45份、活性炭粉5～8份、二氧化钛粉2～5份、高岭土17～20份、蒙脱石15～18份、沸石20～25份、麦饭石10～13份；
制备过程为：
(1)活性炭粉研磨至250～300目；
硅藻土、高岭土、蒙脱石、沸石、麦饭石研磨至300～350目；
二氧化钛粉研磨至1800～2000目；
(2)以上各原料混合均匀搅拌，得到混合粉；
(3)混合粉加水搅拌，混合粉与水的重量比为1∶0.2～0.25；进行造粒；
(4)造粒后进行烘干，得到空气净化颗粒；
(5)烘干后的空气净化颗粒加入到空气净化液中进行浸泡，浸泡10～12小时后，沥干，包装。
2.根据权利要求1所述的制备方法，其特征在于：所述的生姜提取液、薄荷提取液、老鹳草提取液的制备方法为，(1)将生姜、薄荷、老鹳草分别用机械绞碎，压榨出汁液；(2)残渣加入到乙醇水溶液中，搅拌2小时后，过滤去残渣，滤液和汁液混合得到提取液；乙醇水溶液为乙醇与水体积比为0.5～0.8∶1混合制的；残渣与乙醇水溶液的重量比为1∶1。
3.根据权利要求1或2所述的制备方法，其特征在于：所述的造粒烘干温度为75～85℃，烘1～1.5小时。
4.根据权利要求1所述的制备方法，其特征在于：步骤(5)中的浸泡步骤优选如下：烘干后的空气净化颗粒加入到空气净化液中进行浸泡，室温25摄氏度下浸泡20-30分钟，将温度加热到40-50摄氏度浸泡30-60分钟，再将温度上升到55-65摄氏度浸泡10-20分钟，再将温度降低到室温后保持1-5小时。
5.根据权利要求1所述的制备方法，其特征在于：所述的百香果发酵提取液制备方法如下：取新鲜的百香果的果皮，与蔗糖按照重量比例为1∶1，混合均匀，优选将百香果的果皮破碎至1-2厘米见方的小块后洗干净、沥干，按一层果皮一层蔗糖的顺序放入瓶子中(最后一层必须是糖，需保证瓶中留有1成空间供其发酵)，避光保存在阴暗处15天至3个月，将其最终发酵的产品过滤后，取液体备用，作为本发明的百香果发酵提取液。
6.用权利要求1-5中任意一项所述方法制备的汽车用环保型空气净化剂。
CN201410742810.4A 2014-12-08 2014-12-08 一种汽车用环保型空气净化剂及其制备方法 Active CN104475038B (zh)