CN104450042A - 高温无石墨粉剂芯棒润滑剂 - Google Patents

高温无石墨粉剂芯棒润滑剂 Download PDF

Info

Publication number
CN104450042A
CN104450042A CN201410620089.1A CN201410620089A CN104450042A CN 104450042 A CN104450042 A CN 104450042A CN 201410620089 A CN201410620089 A CN 201410620089A CN 104450042 A CN104450042 A CN 104450042A
Authority
CN
China
Prior art keywords
mandrel bar
temperature
lubricant
good
graphite powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410620089.1A
Other languages
English (en)
Other versions
CN104450042B (zh
Inventor
唐鹏飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HENGYANG JINHUA SCIENCE AND TECHNOLOGY Co Ltd
Original Assignee
HENGYANG JINHUA SCIENCE AND TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HENGYANG JINHUA SCIENCE AND TECHNOLOGY Co Ltd filed Critical HENGYANG JINHUA SCIENCE AND TECHNOLOGY Co Ltd
Priority to CN201410620089.1A priority Critical patent/CN104450042B/zh
Publication of CN104450042A publication Critical patent/CN104450042A/zh
Application granted granted Critical
Publication of CN104450042B publication Critical patent/CN104450042B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开的一种高温无石墨粉剂芯棒润滑剂，其特征在于，由以下重量百分比原料混合制成：硼砂20～40％，三聚磷酸钠10～30％，硬脂酸钙5～30％，氧化钙5～20％。本发明喷涂在芯棒上能形成一层致密的熔融隔热润滑膜，且在高温下不凝固分解，抗挤压性能强，润滑性能好，能降低芯棒消耗及提高钢管内表面质量。本发明在1000℃左右高温轧制条件下，附着力好，成膜均匀，轧制电流降低，芯棒使用寿命延长，钢管内壁质量好。

Description

高温无石墨粉剂芯棒润滑剂
技术领域
本发明涉及用于热轧无缝钢管的无石墨粉剂润滑材料，特别涉及一种高温无石墨粉剂芯棒润滑剂。
背景技术
热轧管机组采用芯棒轧制生产无缝钢管，在轧管过程中，芯棒处于1000℃左右的钢管中，并且在承受极高的轧制压力状态下，要与钢管生产相对滑动，因此，高性能的芯棒润滑剂就成为热轧管机组生产的关键性材料。该润滑剂具有较高的耐高温，抗极压性能，可以提高钢管内表面质量，降低轧制电流，延长芯棒使用寿命。但是目前的无石墨粉剂润滑材料很难达到上述性能。
发明内容
本发明所要解决的技术问题在于针对目前用于热轧无缝钢管的无石墨粉剂润滑材料所存在上述诸多问题而提供一种高温无石墨粉剂芯棒润滑剂，该高温无石墨粉剂芯棒润滑剂具有良好的水溶性，使用方便，易于喷涂，不堵喷咀，且无石墨，无环境污染。润滑效果显著，轧管机组电流降低明显，润滑剂的消耗指标大大降低，且钢管内表面质量明显提高，轧制后钢管的尺寸精度也有明显提高，废品基本消除。
本发明所要解决的技术问题可以通过以下技术方案来实现：
一种高温无石墨粉剂芯棒润滑剂，由以下重量百分比原料混合制成：
由于采用了如上的技术方案，本发明喷涂在芯棒上能形成一层致密的熔融隔热润滑膜，且在高温下不凝固分解，抗挤压性能强，润滑性能好，能降低芯棒消耗及提高钢管内表面质量。
本发明在1000℃左右高温轧制条件下，附着力好，成膜均匀，轧制电流降低，芯棒使用寿命延长，钢管内壁质量好。
具体实施方式
实施例1
一种高温无石墨粉剂芯棒润滑剂，由以下重量百分比原料混合制成：硼砂40％，三聚磷酸钠20％，硬脂酸钙20％，氧化钙10％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
上述组分均匀混合后喷涂在芯棒上能形成一层致密均匀，粘附力好的熔融隔热润滑膜，且在高温下不凝固分解，抗挤压性能强，润滑性能好，能降低芯棒消耗及提高钢管内表面质量，且易于喷涂，不堵喷咀。
实施例2
一种高温无石墨粉剂芯棒润滑剂，由以下重量百分比原料混合制成：硼砂20％，三聚磷酸钠30％，硬脂酸钙30％，氧化钙20％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
上述组分均匀混合后喷涂在芯棒上能形成一层致密均匀，粘附力好的熔融隔热润滑膜，且在高温下不凝固分解，抗挤压性能强，润滑性能好，能降低芯棒消耗及提高钢管内表面质量，且易于喷涂，不堵喷咀。
实施例3
一种高温无石墨粉剂芯棒润滑剂，由以下重量百分比原料混合制成：硼砂35％，三聚磷酸钠25％，硬脂酸钙25％，氧化钙15％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
上述组分均匀混合后喷涂在芯棒上能形成一层致密均匀，粘附力好的熔融隔热润滑膜，且在高温下不凝固分解，抗挤压性能强，润滑性能好，能降低芯棒消耗及提高钢管内表面质量，且易于喷涂，不堵喷咀。
对比例1
一种无石墨粉剂润滑材料，由以下重量百分比原料混合制成：硼砂30％，三聚磷酸钠25％，硬脂酸锌25％，氯化钙20％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
将上述组分按比例搅拌均匀，形成一层致密润滑膜，该润滑膜能隔热。硬脂酸锌与氧化钙组合能提高耐磨性，但耐磨性能提升不显著。
对比例2
一种无石墨粉剂润滑材料，由以下重量百分比原料混合制成：硼砂35％，磷酸钙20％，硬脂酸锌25％，氯化钙20％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
上述组分在混合均匀下能自主生成抗极压能力强的润滑膜。该膜致密、隔热，在高温下轧管摩擦偶对相对滑动速度不论大小时，都有良好的润滑性。但使用后发现润滑剂不易于喷涂，堵塞喷咀。
对比例3
一种无石墨粉剂润滑材料，由以下重量百分比原料混合制成：硼砂40％，三聚磷酸钾30％，硬脂酸钙15％，氧化钙15％。
将上述各组分物质混合，通过充分有效搅拌加工得混合粉剂并得到规定颗粒度，包装保存，入库。
硼砂与三聚磷酸钾及硬脂酸钙熔融后生成致密润滑膜，三聚磷酸钾，硬脂酸钙，氧化钙组分组合在生产上能大大降低润滑剂的消耗指标，基本消除废品，但是润滑膜附着较差，成膜不太均匀。

Claims (1)

1.一种高温无石墨粉剂芯棒润滑剂，其特征在于，由以下重量百分比原料混合制成：
CN201410620089.1A 2014-11-05 2014-11-05 高温无石墨粉剂芯棒润滑剂 Active CN104450042B (zh)