CN104448943A - 湿法超细重质碳酸钙的制备方法 - Google Patents

湿法超细重质碳酸钙的制备方法 Download PDF

Info

Publication number
CN104448943A
CN104448943A CN201410745288.5A CN201410745288A CN104448943A CN 104448943 A CN104448943 A CN 104448943A CN 201410745288 A CN201410745288 A CN 201410745288A CN 104448943 A CN104448943 A CN 104448943A
Authority
CN
China
Prior art keywords
calcium carbonate
grinding
add
ground calcium
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410745288.5A
Other languages
English (en)
Inventor
廖煜明
李安平
廖文成
李�杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI LISHENG STONE INDUSTRY Co Ltd
Original Assignee
GUANGXI LISHENG STONE INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI LISHENG STONE INDUSTRY Co Ltd filed Critical GUANGXI LISHENG STONE INDUSTRY Co Ltd
Priority to CN201410745288.5A priority Critical patent/CN104448943A/zh
Publication of CN104448943A publication Critical patent/CN104448943A/zh
Pending legal-status Critical Current

Abstract

本发明的湿法超细重质碳酸钙的制备方法，是将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；具有设计科学合理，工艺简单，安全可靠性，易于控制，操作方便，适合大规模生产，生产成本低等优点。

Description

湿法超细重质碳酸钙的制备方法
技术领域
本发明属于一种碳酸钙粉体的生产方法。
背景技术
目前,碳酸钙已广泛应用于造纸、塑料、塑料薄膜、化纤、橡胶、胶粘剂、密封剂、日用化工、化妆品、建材、涂料、油漆、油墨、油灰、封蜡、腻子、毡层包装、医药、食品(如口香糖、巧克力)、饲料中,其作用有:增加产品体积、降低成本,改善加工性能(如调节粘度、流变性能、硫化性能),提高尺寸稳定性,补强或半补强,提高印刷性能,提高物理性能(如耐热性、消光性、耐磨性、阻燃性、白度、光泽度)等。重质碳酸钙的生产工艺流程有两种。干法生产工艺流程:首先手选从采石场运来的方解石、石灰石、白垩、贝壳等,以除去脉石；然后用破碎机对石灰石进行粗破碎,再用雷蒙(摆式)磨粉碎得到细石灰石粉,最后用分级机对磨粉进行分级,符合粒度要求的粉末作为产品包装入库,否则返回磨粉机再次磨粉。湿法生产工艺流程:先将干法细粉制成悬浮液置于磨机内进一步粉碎,经脱水、干燥后便制得超细重质碳酸钙。
经中国公开专利检索，查到碳酸钙发明专利申请53件；没发现与本专利申请相同的方案。
发明内容
本发明的目的在于；提出一种湿法超细重质碳酸钙的制备方法。
本发明的湿法超细重质碳酸钙的制备方法，包括石块破碎、粉碎、研磨、筛分、活化、干燥、分级，产品收集包装；其特征在于：将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；所述助剂，以重量计，由乙烯基三(β-甲氧基乙氧基)硅烷1-3份，乙二醇3-4份，六偏磷酸钠3-4份，丙烯酸-阳离子丙烯酸酯共聚物3-5份组成。
本发明与现有技术相比其有益效果是：具有设计科学合理，工艺简单，安全可靠性，易于控制，操作方便，适合大规模生产，生产成本低等优点。
具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的实施方式不限于此。
实施例1
本发明的湿法超细重质碳酸钙的制备方法，包括石块破碎、粉碎、研磨、筛分、活化、干燥、分级，产品收集包装；其特征在于：将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；所述助剂，以重量计，由乙烯基三(β-甲氧基乙氧基)硅烷1-3份，乙二醇3-4份，六偏磷酸钠3-4份，丙烯酸-阳离子丙烯酸酯共聚物3-5份组成。
实施例2
本发明的湿法超细重质碳酸钙的制备方法，包括石块破碎、粉碎、研磨、筛分、活化、干燥、分级，产品收集包装；其特征在于：将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；所述助剂，以重量计，由乙烯基三(β-甲氧基乙氧基)硅烷1份，乙二醇4份，六偏磷酸钠3份，丙烯酸-阳离子丙烯酸酯共聚物5份组成。
实施例3
本发明的湿法超细重质碳酸钙的制备方法，包括石块破碎、粉碎、研磨、筛分、活化、干燥、分级，产品收集包装；其特征在于：将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；所述助剂，以重量计，由乙烯基三(β-甲氧基乙氧基)硅烷3份，乙二醇3份，六偏磷酸钠4份，丙烯酸-阳离子丙烯酸酯共聚物3份组成。

Claims (1)

1.一种湿法超细重质碳酸钙的制备方法，包括石块破碎、粉碎、研磨、筛分、活化、干燥、分级，产品收集包装；其特征在于：将直径小于1厘米的碳酸钙粗料，送入磨粉机中，以重质碳酸钙粗粉的重量百分比计，分别加入1-3％碳酸钠、1-3％十二烷基二甲基苄基氯化铵，在85～95℃下研磨致5-10微米后，加水配成固含量为70％～80％的浆料，以重质碳酸钙粉的重量百分比计，加入1-5％加入改性剂，通过泵阀将浆料打入湿法搅拌磨剥机，在研磨介质中研磨，获得制得粒径为0.1～1微米的改性超细碳酸钙粉；所述助剂，以重量计，由乙烯基三(β-甲氧基乙氧基)硅烷1-3份，乙二醇3-4份，六偏磷酸钠3-4份，丙烯酸-阳离子丙烯酸酯共聚物3-5份组成。
CN201410745288.5A 2014-12-08 2014-12-08 湿法超细重质碳酸钙的制备方法 Pending CN104448943A (zh)