CN104420230A - 利用聚氨酯型芳香微胶囊整理剂整理织物的方法 - Google Patents
利用聚氨酯型芳香微胶囊整理剂整理织物的方法 Download PDFInfo
- Publication number
- CN104420230A CN104420230A CN201310401729.5A CN201310401729A CN104420230A CN 104420230 A CN104420230 A CN 104420230A CN 201310401729 A CN201310401729 A CN 201310401729A CN 104420230 A CN104420230 A CN 104420230A
- Authority
- CN
- China
- Prior art keywords
- water
- fabric
- oil
- low
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种利用聚氨酯型芳香微胶囊整理剂整理织物的方法,将乳化剂、水溶性聚合物单体聚乙二醇、水溶性引发剂或扩链一交链剂加入水中搅拌均匀制得水溶液,之后将香精、油溶性聚合物单体1,4-甲苯二异氰酸酯、油溶性引发剂或扩链—交链剂混合均匀后,滴加到上述水溶液中,快速搅拌,加热并保持恒温24h后得微胶囊悬浮液;将微胶囊悬浮液、低温粘合剂加水混合,搅拌均匀之后,对织物进行浸渍处理,轧余率100%,轧余液回用。采用聚氨酯既具有塑料的高强度,又具有橡胶的高弹性,有优异的耐油、耐磨等特性,有效避免了油斑等缺陷;采用浸渍方法处理,轧余液回用,有效提高能源的利用率。
Description
技术领域
本发明属于纺织布处理技术领域,具体涉及一种采用涂层方法处理纯棉织物的工艺。
背景技术
纺织品的芳香整理,不仅可以给人以高雅的享受,更具有医疗保健功能,这一点已通过脑电波的测定得到了证实。日本的二宫教授在其研究报告中指出:机械群发的α波因为柠檬香的存在而大大减弱。另外,茉莉香具有比咖啡大一倍的醒神的效力、薰衣草具有镇静宁神的疗效也都为脑电波所证实。因此,纺织品的芳香整理既具有经济效益,又具有社会效益。根据芳香的心理医疗效果,用不同的香型整理在不同织物上,可具有不同效果。因此,纺织品的芳香整理多年来一直是染整工业的一项工作。若想避免直接上香产生油斑等诸多缺点,同时达到长效、耐水洗的目的,利用微胶囊技术,将香精微胶囊化是一种极好的手段。
发明内容
为了克服现有技术领域存在的上述技术问题,本发明的目的在于,提供一种利用聚氨酯型芳香微胶囊整理剂整理织物的方法,可以在织物使用的过程中缓缓释放出芳香物质,延长使用时间,同时避免油斑等诸多缺点的产生。
本发明提供的利用聚氨酯型芳香微胶囊整理剂整理织物的方法,包括以下步骤: 一、将乳化剂、水溶性聚合物单体聚乙二醇、水溶性引发剂或扩链一交链剂加入水中搅拌均匀制得水溶液,之后将香精、油溶性聚合物单体1,4-甲苯二异氰酸酯、油溶性引发剂或扩链—交链剂混合均匀后,滴加到上述水溶液中,快速搅拌,加热并保持恒温24h后得微胶囊悬浮液;二、将微胶囊悬浮液、低温粘合剂加水混合,搅拌均匀之后,对织物进行浸渍处理,轧余率100%,轧余液回用。
所述微胶囊悬浮液、低温粘合剂加水混合,微胶囊悬浮液、低温粘合剂的质量百分比为:微胶囊悬浮液1%—2%、低温粘合剂1%—2%;余量为水。
本发明提供的利用聚氨酯型芳香微胶囊整理剂整理织物的方法,其有益效果在于,采用聚氨酯既具有塑料的高强度,又具有橡胶的高弹性,有优异的耐油、耐磨等特性,有效避免了油斑等缺陷;采用浸渍方法处理,轧余液回用,有效提高能源的利用率。
具体实施方式
下面结合一个实施例,对本发明提供的利用聚氨酯型芳香微胶囊整理剂整理织物的方法进行详细的说明。
实施例
本实施例的利用聚氨酯型芳香微胶囊整理剂整理织物的方法,包括以下步骤: 一、将乳化剂、水溶性聚合物单体聚乙二醇、水溶性引发剂或扩链一交链剂加入水中搅拌均匀制得水溶液,之后将香精、油溶性聚合物单体1,4-甲苯二异氰酸酯、油溶性引发剂或扩链—交链剂混合均匀后,滴加到上述水溶液中,快速搅拌,加热并保持恒温24h后得微胶囊悬浮液;二、将微胶囊悬浮液1.5g、低温粘合剂1.2g加100g水混合,搅拌均匀之后,对织物进行浸渍处理,轧余率100%,轧余液回用。
利用聚氨酯型芳香微胶囊整理剂整理织物的方法,采用聚氨酯既具有塑料的高强度,又具有橡胶的高弹性,有优异的耐油、耐磨等特性,既可以在织物使用的过程中缓缓释放出芳香物质,延长使用时间,同时避免油斑等诸多缺点的产生有效避免了油斑等缺陷。
Claims (2)
1.一种利用聚氨酯型芳香微胶囊整理剂整理织物的方法,其特征在于:包括以下步骤:一、将乳化剂、水溶性聚合物单体聚乙二醇、水溶性引发剂或扩链一交链剂加入水中搅拌均匀制得水溶液,之后将香精、油溶性聚合物单体1,4-甲苯二异氰酸酯、油溶性引发剂或扩链—交链剂混合均匀后,滴加到上述水溶液中,快速搅拌,加热并保持恒温24h后得微胶囊悬浮液;二、将微胶囊悬浮液、低温粘合剂加水混合,搅拌均匀之后,对织物进行浸渍处理,轧余率100%,轧余液回用。
2.根据权利要求1所述的利用聚氨酯型芳香微胶囊整理剂整理织物的方法,其特征在于:所述微胶囊悬浮液、低温粘合剂加水混合,微胶囊悬浮液、低温粘合剂的质量百分比为:微胶囊悬浮液1%—2%、低温粘合剂1%—2%;余量为水。