CN104419027A - 一种防滑全钢子午线轮胎的制备方法 - Google Patents
一种防滑全钢子午线轮胎的制备方法 Download PDFInfo
- Publication number
- CN104419027A CN104419027A CN201310402769.1A CN201310402769A CN104419027A CN 104419027 A CN104419027 A CN 104419027A CN 201310402769 A CN201310402769 A CN 201310402769A CN 104419027 A CN104419027 A CN 104419027A
- Authority
- CN
- China
- Prior art keywords
- weight part
- carbon black
- rubber
- preparation
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防滑全钢子午线轮胎的制备方法,包括:a)混炼工序:将天然橡胶和顺丁橡胶的混合物加入密炼机中,加压,加入炭黑、白碳黑、偶联剂、硬脂酸、氧化锌、防老剂、促进剂、防焦剂,加压提压砣,排胶制成一段母胶;b)二次成型工序:将一段母胶、炭黑和夹心胶加入密炼机中,加压提压砣,排胶制成二段母胶;c)硫化工序包括:将二段母胶、硫磺、促进剂加入密炼机中,空转提压砣,加压,排胶制成三段母胶。本发明的制备方法,将炭黑用白炭黑予以部分取代,加入偶联剂对白炭黑进行化学改性,有效降低胶料的潘恩效应以及高温下损耗角正切tanδ,可降低约50%的胎面滞后性能、约20%的滚动阻力,同时可提高抗湿滑性能。
Description
技术领域
本发明涉及子午线轮胎的制备方法,具体涉及一种防滑全钢子午线轮胎的制备方法。
背景技术
子午线轮胎具有耐磨、节油、乘坐舒适,以及牵引性、稳定性和高速性能好的特点,目前国际上子午线轮胎占市场的80%,轿车和载重子午线轮胎分别为90%和63%。我国庞大的汽车需求量促进了轮胎行业的快速增长,2007年1-8月中国轮胎产量为3.3836亿条,同比增长23%,子午线轮胎产量为1.53亿条,同比增长36.7%。子午线轮胎达到轮胎总量的45%。表明我国轮胎构架正在向追求高品质和高附加值方向转变。降低胶料的潘恩效应以及高温下损耗角正切tanδ、并提高抗湿滑系数非常重要。
发明内容
本发明的目的是提供一种防滑全钢子午线轮胎的制备方法。
本发明为了实现上述目的,采用的技术解决方案是:
一种防滑全钢子午线轮胎的制备方法,包括混炼工序、二次成型工序、硫化工序,其中:
a)所述混炼工序包括如下步骤 :将80-120重量份的天然橡胶和顺丁橡胶的混合物加入密炼机中,加压45s,加入15-20重量份的炭黑、30-50重量份的白碳黑、5-10重量份的偶联剂、1-3重量份的硬脂酸、3-5重量份的氧化锌、3-6重量份的防老剂、1-1.5重量份的促进剂、0.1-0.3重量份的防焦剂CTP,加压35s,提压砣,在155~165℃的条件下排胶,制成一段母胶;
b)所述二次成型工序包括以下步骤:将一段母胶、5-10重量份的炭黑和5-8重量份的夹心胶加入密炼机中,加压35s,提压砣,在145~150℃的条件下排胶,制成二段母胶;
c)所述硫化工序包括以下步骤:将二段母胶、1-2重量份的硫磺、0.5-1重量份的促进剂加入密炼机中,空转10s,提压砣,加压50s,在110~120℃的条件下排胶,制成三段母胶。
所述步骤a)中天然橡胶70~90重量份,顺丁橡胶10~30重量份。
所述的炭黑:采用N234炭黑;白炭黑:采用高分散高结构白炭黑;偶联剂:采用硅烷偶联剂X50S ;促进剂:采用促进剂CZ。
所述天然橡胶为天然橡胶SMR20或天然橡胶SIR20或天然橡胶SCR5。
所述顺丁橡胶为顺丁橡胶BR9000。
所述防老剂采用防老剂6PPD和或防老剂RD和或防护蜡和或防老剂TMQ。
本发明能够产生的有益效果:将传统轮胎的胎面填充物碳黑用白炭黑予以部分取代,同时加入一定量的硅烷偶联剂对白炭黑进行化学改性,可以有效降低胶料的潘恩效应以及高温下损耗角正切tanδ;且在制备时加入夹心胶,可大大提高抗湿滑系数,使其在冬天的冰雪天气也可使用。
具体实施方式
实施例1
一种防滑全钢子午线轮胎的制备方法,包括混炼工序、二次成型工序、硫化工序,其中
a)所述混炼工序包括如下步骤 :将90重量份的天然橡胶SCR5和10重量份的顺丁橡胶BR9000的混合物加入密炼机中,加压45s,加入15重量份的N234炭黑、50重量份的高分散高结构白炭黑、5重量份的硅烷偶联剂X50S、1重量份的硬脂酸、4.5重量份的氧化锌、3重量份的防老剂(其中2重量份的防老剂6PPD、1重量份的防老剂RD)、1重量份的促进剂CZ、0.3重量份的防焦剂CTP,加压35s,提压砣,在155℃的条件下排胶,制成一段母胶;
b)所述二次成型工序包括以下步骤:将一段母胶、5重量份的N234炭黑和5重量份的夹心胶加入密炼机中,加压35s,提压砣,在150℃的条件下排胶,制成二段母胶;
c)所述硫化工序包括以下步骤:将二段母胶、1.6重量份的硫磺、1重量份的促进剂CZ加入密炼机中,空转10s,提压砣,加压50s,在110℃的条件下排胶,制成三段母胶。
夹心胶为颗粒状,夹心胶要求< 0℃时能够结晶,>0℃时为弹性体,平均直径约2~5mm。
实施例2
一种防滑全钢子午线轮胎的制备方法,包括混炼工序、二次成型工序、硫化工序,其中:
a)所述混炼工序包括如下步骤 :将70重量份的天然橡胶SIR20和30重量份的顺丁橡胶BR9000的混合物加入密炼机中,加压45s,加入20重量份的N234炭黑、30重量份的高分散高结构白炭黑、10重量份的硅烷偶联剂X50S、1重量份的硬脂酸、3重量份的氧化锌、5重量份的防老剂(其中2重量份的防老剂RD、2重量份的防老剂TMQ、1重量份的防护蜡)、1重量份的促进剂CZ、0.1重量份的防焦剂CTP,加压35s,提压砣,在165℃的条件下排胶,制成一段母胶;
b)所述二次成型工序包括以下步骤:将一段母胶、10重量份的N234炭黑和8重量份的夹心胶加入密炼机中,加压35s,提压砣,在145℃的条件下排胶,制成二段母胶;
c)所述硫化工序包括以下步骤:将二段母胶、1.45重量份的硫磺、0.8重量份的促进剂CZ加入密炼机中,空转10s,提压砣,加压50s,在120℃的条件下排胶,制成三段母胶。
实施例3
一种防滑全钢子午线轮胎的制备方法,包括混炼工序、二次成型工序、硫化工序,其中:
a)所述混炼工序包括如下步骤:将85重量份的天然橡胶SMR20和15重量份的顺丁橡胶BR9000的混合物加入密炼机中,加压45s,加入15重量份的N234炭黑、35重量份的高分散高结构白碳黑、5.5重量份的硅烷偶联剂X50S、3重量份的硬脂酸、5重量份的氧化锌、6重量份的防老剂(其中2重量份的防老剂6PPD、2重量份的防老剂RD、1重量份的防老剂TMQ、1重量份的防护蜡)、1.4重量份的促进剂CZ、0.1重量份的防焦剂CTP,加压35s,提压砣,在160℃的条件下排胶,制成一段母胶;
b)所述二次成型工序包括以下步骤:将一段母胶、10重量份的N234炭黑和7重量份的夹心胶加入密炼机中,加压35s,提压砣,在148℃的条件下排胶,制成二段母胶;
c)所述硫化工序包括以下步骤:将二段母胶、1.5重量份的硫磺、0.5重量份的促进剂CZ加入密炼机中,空转10s,提压砣,加压50s,在115℃的条件下排胶,制成三段母胶。
如上述制备方法制成的轮胎胎面胶料与普通胎面胶做如下性能对比:
如上内容,采用本发明所述方法制备的轮胎胎面胶料,通过将传统轮胎的胎面填充物碳黑用白炭黑予以部分取代,同时加入一定量的硅烷偶联剂对白炭黑进行化学改性,在不损失轮胎基本安全性能的情况下,降低轮胎的摩擦系数,同时提高抗湿滑的能力。
当然,上述说明并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的技术人员在本发明的实质范围内所做出的变化、改型、添加或替换,也应属于本发明的保护范围。
Claims (6)
1. 一种防滑全钢子午线轮胎的制备方法,包括混炼工序、二次成型工序、硫化工序,其特征在于:
a)所述混炼工序包括如下步骤 :将80-120重量份的天然橡胶和顺丁橡胶的混合物加入密炼机中,加压45s,加入15-20重量份的炭黑、30-50重量份的白碳黑、5-10重量份的偶联剂、1-3重量份的硬脂酸、3-5重量份的氧化锌、3-6重量份的防老剂、1-1.5重量份的促进剂、0.1-0.3重量份的防焦剂CTP,加压35s,提压砣,在155~165℃的条件下排胶,制成一段母胶;
b)所述二次成型工序包括以下步骤:将一段母胶、5-10重量份的炭黑和5-8重量份的夹心胶加入密炼机中,加压35s,提压砣,在145~150℃的条件下排胶,制成二段母胶;
c)所述硫化工序包括以下步骤:将二段母胶、1-2重量份的硫磺、0.5-1重量份的促进剂加入密炼机中,空转10s,提压砣,加压50s,在110~120℃的条件下排胶,制成三段母胶。
2. 根据权利要求1所述的一种防滑全钢子午线轮胎的制备方法,其特征在于:所述步骤a)中天然橡胶70~90重量份,顺丁橡胶10~30重量份。
3.根据权利要求1所述的一种防滑全钢子午线轮胎的制备方法,其特征在于,所述的炭黑:采用N234炭黑;白炭黑:采用高分散高结构白炭黑;偶联剂:采用硅烷偶联剂X50S ;促进剂:采用促进剂CZ。
4.根据权利要求1或2所述的一种防滑全钢子午线轮胎的制备方法,其特征在于,所述天然橡胶为天然橡胶SMR20或天然橡胶SIR20或天然橡胶SCR5。
5.根据权利要求1或2所述的一种防滑全钢子午线轮胎的制备方法,其特征在于,所述顺丁橡胶为顺丁橡胶BR9000。
6.根据权利要求1所述的一种防滑全钢子午线轮胎的制备方法,其特征在于,所述防老剂采用防老剂6PPD和或防老剂RD和或防护蜡和或防老剂TMQ。