CN104418585B - Ceramics and coloured glaze high temperature molding processes - Google Patents
Ceramics and coloured glaze high temperature molding processes Download PDFInfo
- Publication number
- CN104418585B CN104418585B CN201310381498.6A CN201310381498A CN104418585B CN 104418585 B CN104418585 B CN 104418585B CN 201310381498 A CN201310381498 A CN 201310381498A CN 104418585 B CN104418585 B CN 104418585B
- Authority
- CN
- China
- Prior art keywords
- coloured glaze
- raw material
- ceramic
- hours
- ceramics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of ceramics and coloured glaze high temperature molding processes, by weight ceramic raw material:Kaolin 42 50%, feldspar 24 28%, clay 10 12%, small green stone 6 8%, quartz 7 9% and aluminum oxide 3 5% are well mixed, it is ground to the sieving of 400 mesh, it is made ceramic pureed state and is put into kiln and gradually heats up 8 12 hours to 1100 degree, constant temperature 2 hours, it is cooled to room temperature to come out of the stove, is made ceramic;Coloured glaze raw material by weight:Quartz sand 46 50%, ground caustic 22 25%, calcium carbonate antimony oxide 10 12%, aluminum oxide 6 9%, sodium nitrate 6 7%, fluorite 5 6% are well mixed, after crucible furnace is warming up into 1300 DEG C, coloured glaze raw material is put into crucible furnace and is warming up to 1350 DEG C again, insulation 8 hours, the coloured glaze material of melting is coated on above-mentioned ceramic and required moulding is made, temperature is moved back 72 hours.Ceramics of the invention and coloured glaze one integrated mass, without bursting, deforming, type is perfect, both artistic and practical, it is easy to clean, and has artistic appreciation higher.
Description
Technical field
The present invention relates to ceramics, coloured glaze high-temperature molding field, specifically a kind of ceramic and coloured glaze high temperature molding processes.
Background technology
Coloured glaze and the product that ceramics are that two kinds of different raw material make, they belong to the category of silicate material, will
The product of fineness can be just made by high-temperature firing.Both materials are combined together under the condition of high temperature, are often occurred fried
Situations such as splitting, deform.
The content of the invention
Technique is combined under the high temperature conditions with coloured glaze it is an object of the invention to provide a kind of ceramics, make product without bursting,
Deformation, type is perfect, there is artistic appreciation higher.
Concrete scheme of the invention is:
(1) by weight by ceramic raw material:Kaolin 42-50%, feldspar 24-28%, clay 10-12%, small green stone 6-
8%th, quartz 7-9% and aluminum oxide 3-5% is well mixed, and is ground to the sieving of 400 mesh, is then modulated into ceramic pureed state and carries out
It is moulding, dry, be put into kiln gradually intensification 8-12 hours to 1100 degree, constant temperature keep 2 hours, gradually cooled down under Warm status
Come out of the stove to room temperature, form ceramic;
(2) by weight by coloured glaze raw material:Quartz sand 46-50%, ground caustic 22-25%, calcium carbonate antimony oxide 10-12%,
Aluminum oxide 6-9%, sodium nitrate 6-7%, fluorite 5-6% are well mixed, after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze is former
Material is put into and is warming up to 1350 DEG C in crucible furnace again, is incubated 8 hours, and the coloured glaze material of melting is coated on above-mentioned ceramic simultaneously
Required moulding is made, is then placed to move back carried out in warm stove and is moved back temperature 72 hours.
Above-mentioned ceramics and coloured glaze high temperature molding processes, wherein,
The weight portion ceramic raw material:Kaolin 46.5%, feldspar 24%, clay 12%, small green stone 7%, quartz 7.5%
With aluminum oxide 3%;
The weight portion coloured glaze raw material:Quartz sand 50%, ground caustic 22.5%, calcium carbonate antimony oxide 10%, aluminum oxide 6%,
Sodium nitrate 6.5%, fluorite 5%.
Above-mentioned ceramics and coloured glaze high temperature molding processes, wherein,
The weight portion ceramic raw material:Kaolin 44%, feldspar 26%, clay 10.5%, small green stone 6%, quartz
8.5%th, aluminum oxide 5%;
The weight portion coloured glaze raw material:Quartz sand 48.5%, ground caustic 24%, calcium carbonate antimony oxide 10%, aluminum oxide 6%,
Sodium nitrate 6%, fluorite 5.5%.
Above-mentioned ceramics and coloured glaze high temperature molding processes, wherein,
The weight portion ceramic raw material:Kaolin 42%, feldspar 28%, clay 10%, small green stone 8%, quartz 7%, oxygen
Change aluminium 5%;
The weight portion coloured glaze raw material:Quartz sand 46%, ground caustic 24%, calcium carbonate antimony oxide 10.5%, aluminum oxide 8%,
Sodium nitrate 6.5%, fluorite 5%.
Beneficial effects of the present invention are as follows:The technique that is combined under the high temperature conditions with coloured glaze of ceramics, make product without bursting,
Deformation, type is perfect, there is artistic appreciation higher.
Specific embodiment
The present invention is described in further detail with reference to embodiment.
A kind of ceramics and coloured glaze high temperature molding processes, first ceramic raw material by weight:Kaolin 42-50%, feldspar 24-
28%th, clay 10-12%, small green stone 6-8%, quartz 7-9% and aluminum oxide 3-5% are well mixed, and are ground to the sieving of 400 mesh,
Then be modulated into ceramic pureed state and carry out it is moulding, dry, be put into kiln gradually intensification 8-12 hours to 1100 degree, constant temperature keep
2 hours, from Warm status under be gradually cooling to room temperature and come out of the stove, form ceramic;
Coloured glaze raw material by weight again:Quartz sand 46-50%, ground caustic 22-25%, calcium carbonate antimony oxide 10-12%, oxidation
Aluminium 6-9%, sodium nitrate 6-7%, fluorite 5-6% are well mixed, and after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze raw material are put
Enter and be warming up to 1350 DEG C in crucible furnace again, be incubated 8 hours, the coloured glaze material of melting is coated on above-mentioned ceramic and made
Required moulding, then places to move back carried out in warm stove and moves back temperature 72 hours.
First embodiment:
By weight portion ceramic raw material:Kaolin 46.5%, feldspar 24%, clay 12%, small green stone 7%, 7.5% and of quartz
Aluminum oxide 3% be well mixed, be ground to 400 mesh, be then modulated into ceramic pureed state and carry out it is moulding, dry, be put into kiln, by
Edge up warm 8-12 hours to 1100 degree, constant temperature is kept for 2 hours, from Warm status under be gradually cooling to room temperature and come out of the stove, form ceramics
Product.
By weight portion coloured glaze raw material:Quartz sand 50%, ground caustic 22.5%, calcium carbonate antimony oxide 10%, aluminum oxide 6%, nitre
Sour sodium 6.5%, fluorite 5% are well mixed, and after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze raw material are put into crucible furnace again
1350 DEG C are warming up to, 8 hours are incubated, the coloured glaze material of melting is taken out, using jacking gimmick, in the coloured glaze material cladding that will be melted
State ceramic or be coated in the ceramic surface and make required moulding using the mode such as rubbing, rub with the hands, drawing, stretching again, then
Placement to be moved back carried out in warm stove and moves back temperature 72 hours.
Second embodiment:
By weight portion ceramic raw material:Kaolin 44%, feldspar 26%, clay 10.5%, small green stone 6%, quartz 8.5%,
Aluminum oxide 5% be well mixed, be ground to 400 mesh, be then modulated into ceramic pureed state and carry out it is moulding, dry, be put into kiln, by
Edge up warm 8-12 hours to 1100 degree, constant temperature is kept for 2 hours, from Warm status under be gradually cooling to room temperature and come out of the stove;
By weight portion coloured glaze raw material:Quartz sand 48.5%, ground caustic 24%, calcium carbonate antimony oxide 10%, aluminum oxide 6%, nitre
Sour sodium 6%, fluorite 5.5% are well mixed, and after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze raw material are put into crucible furnace again
1350 DEG C are warming up to, 8 hours are incubated, the coloured glaze material of melting is taken out, using jacking gimmick, in the coloured glaze material cladding that will be melted
State ceramic or be coated in the ceramic surface and make required moulding using the mode such as rubbing, rub with the hands, drawing, stretching again, then
Placement to be moved back carried out in warm stove and moves back temperature 72 hours.
3rd embodiment:
By weight portion ceramic raw material:Kaolin 44%, feldspar 26%, clay 10.5%, small green stone 6%, quartz 8.5%,
Aluminum oxide 5% is well mixed;Be ground to 400 mesh, be then modulated into ceramic pureed state and carry out it is moulding, dry, be put into kiln, by
Edge up warm 8-12 hours to 1100 degree, constant temperature is kept for 2 hours, from Warm status under be gradually cooling to room temperature and come out of the stove
By weight portion coloured glaze raw material:Quartz sand 48.5%, ground caustic 24%, calcium carbonate antimony oxide 10%, aluminum oxide 6%, nitre
Sour sodium 6.5%, fluorite 5%.It is well mixed, after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze raw material is put into crucible furnace
1350 DEG C are warming up to again, 8 hours are incubated, the coloured glaze material of melting is taken out, using jacking gimmick, the coloured glaze material cladding that will be melted
Above-mentioned ceramic is coated in the ceramic surface and makes required moulding using the mode such as rubbing, rub with the hands, drawing, stretching again, so
Place to move back carried out in warm stove afterwards and move back temperature 72 hours.
Manufacture craft is combined under coloured glaze of the invention and ceramic high temperature so that coloured glaze is combined with ceramic two kinds of unlike materials
Product together, does not burst, indeformable, keeps the form of original ceramics works, is that coloured glaze is combined product at high temperature with ceramics
Wide prospect has been opened up in the development of product.
Certainly, the present invention can also have other various embodiments, ripe in the case of without departing substantially from spirit of the invention and its essence
Know those skilled in the art and work as and various corresponding changes and deformation, but these corresponding changes and change can be made according to the present invention
Shape should all belong to the protection domain of appended claims of the invention.
Claims (4)
1. a kind of ceramics and coloured glaze high temperature molding processes, it is characterised in that
(1) ceramic raw material by weight:Kaolin 42-50%, feldspar 24-28%, clay 10-12%, small green stone 6-8%, stone
English 7-9% and aluminum oxide 3-5% be well mixed, be ground to 400 mesh sieving, be then modulated into ceramic pureed state and carry out it is moulding,
Dry, be put into kiln gradually intensification 8-12 hours to 1100 degrees Celsius, constant temperature is kept for 2 hours, is gradually cooled down under Warm status
Come out of the stove to room temperature, form ceramic;
(2) coloured glaze raw material by weight:Quartz sand 46-50%, ground caustic 22-25%, calcium carbonate antimony oxide 10-12%, aluminum oxide
6-9%, sodium nitrate 6-7%, fluorite 5-6% are well mixed, and after crucible furnace is warming up into 1300 DEG C, above-mentioned coloured glaze raw material are put into
1350 DEG C are warming up in crucible furnace again, 8 hours are incubated, the coloured glaze material of melting is coated on above-mentioned ceramic and institute is made
The moulding for needing, then places to move back carried out in warm stove and moves back temperature 72 hours.
2. ceramics as claimed in claim 1 and coloured glaze high temperature molding processes, it is characterised in that
The weight portion ceramic raw material:Kaolin 46.5%, feldspar 24%, clay 12%, small green stone 7%, quartz 7.5% and oxygen
Change aluminium 3%;
The weight portion coloured glaze raw material:Quartz sand 50%, ground caustic 22.5%, calcium carbonate antimony oxide 10%, aluminum oxide 6%, nitric acid
Sodium 6.5%, fluorite 5%.
3. ceramics as claimed in claim 1 and coloured glaze high temperature molding processes, it is characterised in that
The weight portion ceramic raw material:Kaolin 44%, feldspar 26%, clay 10.5%, small green stone 6%, quartz 8.5%, oxygen
Change aluminium 5%;
The weight portion coloured glaze raw material:Quartz sand 48.5%, ground caustic 24%, calcium carbonate antimony oxide 10%, aluminum oxide 6%, nitric acid
Sodium 6%, fluorite 5.5%.
4. ceramics as claimed in claim 1 and coloured glaze high temperature molding processes, it is characterised in that
The weight portion ceramic raw material:Kaolin 42%, feldspar 28%, clay 10%, small green stone 8%, quartz 7%, aluminum oxide
5%;
The weight portion coloured glaze raw material:Quartz sand 46%, ground caustic 24%, calcium carbonate antimony oxide 10.5%, aluminum oxide 8%, nitric acid
Sodium 6.5%, fluorite 5%.