CN104404593A - 一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法 - Google Patents

一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法 Download PDF

Info

Publication number
CN104404593A
CN104404593A CN201410705634.7A CN201410705634A CN104404593A CN 104404593 A CN104404593 A CN 104404593A CN 201410705634 A CN201410705634 A CN 201410705634A CN 104404593 A CN104404593 A CN 104404593A
Authority
CN
China
Prior art keywords
contact angle
chromic acid
lithium alloy
alloy
deoxidizing effect
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410705634.7A
Other languages
English (en)
Inventor
王云飞
吴筱兰
刘诗超
万莹
魏娜
李旭勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Hongdu Aviation Industry Group Co Ltd
Original Assignee
Jiangxi Hongdu Aviation Industry Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Hongdu Aviation Industry Group Co Ltd filed Critical Jiangxi Hongdu Aviation Industry Group Co Ltd
Priority to CN201410705634.7A priority Critical patent/CN104404593A/zh
Publication of CN104404593A publication Critical patent/CN104404593A/zh
Pending legal-status Critical Current

Abstract

本发明涉及铝锂合金铬酸阳极氧化脱氧效果检测领域，具体涉及一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法。其方法为：采用接触角测定仪测试，测定水滴在经脱氧处理后的铝锂合金表面上的接触角，检视水滴的接触角，接触角如果大于0°则脱氧效果不达标，接触角等于0°时，则脱氧效果达标。本发明的有益效果在于：简单准确，快速可靠，提高生产效率，降低劳动强度，缩减检测时间。

Description

一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法
技术领域
本发明涉及铝锂合金铬酸阳极氧化脱氧效果检测领域，具体涉及一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法。
背景技术
近些年来，为了尽可能的减少飞机维护及航行技术的改动，一种高比强度、低密度的铝合金日益受到人们的关注，在铝中加入密度较小的锂元素可以有效地降低合金的整体密度，资料显示，在铝中添加1%（质量比）的锂元素可以使合金密度下降3%，并且其弹性模量增强6%左右。由于铝锂合金在时效处理的时候会析出强化相δ，使其韧性和刚性明显提高。因此铝锂合金被普遍认为是最有潜力的轻质高强度材料之一。虽然铝锂合金具有优异的力学性能，但其化学性能并不稳定，易发生孔蚀、晶间腐蚀、应力腐蚀断裂等。为此，对其进行表面处理变得尤为重要。
目前许多项目采用现有的铬酸阳极氧化对其进行表面处理，以提高其耐蚀性，其中脱氧工艺是保证铝锂合金阳极氧化膜质量的一项关键技术，脱氧目的是除去铝锂合金表面的氧化皮和腐蚀产物，若工艺参数控制不当，脱氧效果差，会造成腐蚀产物除不尽，影响膜层的耐蚀性。
发明内容
本发明的目的在于解决上述问题，提供一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法。
为了实现本发明的目的，本发明采用的技术方案为：
一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法，其方法为：采用接触角测定仪测试，测定水滴在经脱氧处理后的铝锂合金表面上的接触角，检视水滴的接触角，接触角如果大于0°则脱氧效果不达标，接触角等于0°时，则脱氧效果达标。
本发明的有益效果在于：简单准确，快速可靠，提高生产效率，降低劳动强度，缩减检测时间。
附图说明
图1为实例1脱氧时间为3分钟的盐雾试验后的铝锂合金材料外观图片，
图2为实例2脱氧时间为7分钟的盐雾试验后的铝锂合金材料外观图片，
图3为实例3脱氧时间为10分钟的盐雾试验后的铝锂合金材料外观图片，
图4为实例4脱氧时间为15分钟的盐雾试验后的铝锂合金材料外观图片。
具体实施方式
下面结合附图1至图4和实施例对本发明进一步说明：
实施例：
一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法，其方法为：采用接触角测定仪测试，测定水滴在经脱氧处理后的铝锂合金表面上的接触角，检视水滴的接触角，接触角如果大于0°则脱氧效果不达标，接触角等于0°时，则脱氧效果达标。
上述脱氧工艺为：HNO3 7.5%~10.6%(体积比)   Cr6+ 22.6~26.2g/L  HF 16ml/L 温度 25℃。
达到接触角等于0°时，则脱氧处理效果达标，然后再经后续的铬酸阳极氧化、封闭工艺处理的铝锂合金阳极氧化膜膜层连续、颜色均匀、不起粉、不发暗，能通过按ASTM-B117标准进行的336小时盐雾试验。
下面为用接触角测定仪对实验检测的实例：
实例1：对尺寸为75㎜×250㎜×2.3㎜的铝锂合金，按铬酸阳极氧化工艺流程进行铬酸阳极氧化，其中脱氧时间为3min，用接触角测定仪测得接触角为3.4°所得阳极氧化膜经336小时中性盐雾试验，外观有黒斑，不满足生产要求。
实例2：对尺寸为75㎜×250㎜×2.3㎜的铝锂合金，按铬酸阳极氧化工艺流程进行铬酸阳极氧化，其中脱氧时间为7min，用接触角测定仪测得接触角为0°所得阳极氧化膜经336小时中性盐雾试验，外观灰白，未出现腐蚀点，满足生产要求。
实例3：对尺寸为75㎜×250㎜×2.3㎜的铝锂合金，按铬酸阳极氧化工艺流程进行铬酸阳极氧化，其中脱氧时间为10min，用接触角测定仪测得接触角为0°所得阳极氧化膜经336小时中性盐雾试验，外观灰白，未出现腐蚀点，满足生产要求。
实例4：对尺寸为75㎜×250㎜×2.3㎜的铝锂合金，按铬酸阳极氧化工艺流程进行铬酸阳极氧化，其中脱氧时间为15min，用接触角测定仪测得接触角为0°所得阳极氧化膜经336小时中性盐雾试验，外观灰白，未出现腐蚀点，满足生产要求。
本发明的实施例公布的是较佳的实施例之一也，但并不局限于此，本领域的普通技术人员，极易根据上述实施例，领会本发明的精神，并做出不同的引申和变化，但只要不脱离本发明的精神，都在本发明的保护范围内。

Claims (1)

1. 一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法，其方法特征在于：采用接触角测定仪测试，测定水滴在经脱氧处理后的铝锂合金表面上的接触角，检视水滴的接触角，接触角如果大于0°则脱氧效果不达标，接触角等于0°时，则脱氧效果达标。
CN201410705634.7A 2014-11-29 2014-11-29 一种简易判别铝锂合金铬酸阳极氧化脱氧效果的方法 Pending CN104404593A (zh)