CN104402496A - 一种含茶皂素的泡沫砖及其制备方法 - Google Patents
一种含茶皂素的泡沫砖及其制备方法 Download PDFInfo
- Publication number
- CN104402496A CN104402496A CN201410580936.6A CN201410580936A CN104402496A CN 104402496 A CN104402496 A CN 104402496A CN 201410580936 A CN201410580936 A CN 201410580936A CN 104402496 A CN104402496 A CN 104402496A
- Authority
- CN
- China
- Prior art keywords
- tea saponin
- add
- water
- component
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种含茶皂素的泡沫砖,其特征是由下述重量份的原料制得:废玻璃40-50,硅灰石粉5-10,轻质碳酸钙10-20,氯化钙5-10,茶皂素2-4,椰子油脂肪酸二乙醇酰胺1-2,辛烯基琥珀酸淀粉钠0.5-1,阿拉伯胶1-2,六偏磷酸钠2-4,硅酸铝纤维1-2,硼砂1-2,复合填料10-15,水40-60。本发明的泡沫砖添加天然活性物质茶皂素作为主要发泡剂,发泡性能好,发泡均匀、孔径合适,能提高制品的性能及外观,且安全环保。
Description
技术领域
本发明涉及建筑材料领域,具体涉及一种含茶皂素的泡沫砖及其制备方法。
背景技术
泡沫砖属于加气混凝土砌块的一种,通过采用发泡剂通过发泡机物理制泡后,再将气泡加入料浆中混合,浇注,最后制得带有内部气孔的泡沫砖。泡沫砖主要用于非承重墙,具有成本低、轻质、保温隔热效果好等特点,已被广泛应用于工业与民用建筑中,是一种具有良好性能的墙体材料。
玻璃材料是人们日常生活所需、不可缺少的材料。玻璃的大量使用也导致日常生产生活中不可避免地产生大量的废玻璃垃圾。废玻璃的化学性质稳定,既给人们的生产和生活带来了不便,又对环境产生了污染,并且废玻璃的安置占用了大量土地资源。因此,回收利用废玻璃,使废玻璃资源化成为环保节能的一个重要课题。利用废玻璃生产泡沫砖是一种合理利用废玻璃的途径。
茶皂素是一种天然表面活性剂,起泡性好,具有起泡快、泡沫体积大、泡沫细腻、泡沫强度大、维持时间长的优点,同时抗酸碱盐性能强,安全环保,还有驱虫、灭菌、防腐等功效,有较高的利用价值。
发明内容
本发明的目的是提供一种含茶皂素的泡沫砖。
本发明是通过以下技术方案实现的:
一种含茶皂素的泡沫砖,其特征在于,其是由下述重量份的原料制得:
废玻璃40-50,硅灰石粉5-10,轻质碳酸钙10-20,氯化钙5-10,茶皂素2-4,椰子油脂肪酸二乙醇酰胺1-2,辛烯基琥珀酸淀粉钠0.5-1,阿拉伯胶1-2,六偏磷酸钠2-4,硅酸铝纤维1-2,硼砂1-2,复合填料10-15,水40-60;
所述复合填料由下列重量份的原料制成:
麦饭石粉10-15,高岭土10-15,糯米粉5-10,竹炭粉5-10,维生素C磷酸酯镁1-2,水杨酸钠1-2,羟丙基二淀粉磷酸酯0.5-1,酒石酸钾钠2-4,聚丙烯酸钠0.5-1,麦芽糖醇1-2;
所述复合填料的制备方法是:
将麦饭石粉、高岭土、酒石酸钾钠和麦芽糖醇混合后研磨均匀,200-300℃处理1-2h,用水反复洗涤后加入糯米粉、竹炭粉和适量水60-80℃搅拌0.5-1h,冷却至常温,加入其余原料继续搅拌10-15min,干燥后研磨均匀,过400-600目筛,即得。
所述的含茶皂素的泡沫砖的制备方法,其特征在于,包括以下步骤:
(1)将废玻璃、硅灰石粉、轻质碳酸钙和氯化钙混合后200-300℃处理1-2h,加入六偏磷酸钠、硅酸铝纤维、硼砂和复合填料混合均匀,研磨后过100-150目筛,再加入1/3-1/2量的水,200-400r/min搅拌0.5-1h,得A组分;
(2)将辛烯基琥珀酸淀粉钠和阿拉伯胶加入余量的水中,60-80℃搅拌10-20min,冷却后加入椰子油脂肪酸二乙醇酰胺和茶皂素搅拌5-10min后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,先100-150℃烘干1-2h,再于马弗炉中600-800℃烧结2-4h,冷却后即得。
本发明的优点是:
1. 添加天然活性物质茶皂素作为主要发泡剂,发泡性能好,发泡均匀、孔径合适,能提高制品的性能及外观,且安全环保;
2. 通过添加复合填料,改善了泡沫砖的机械性能,并使泡沫砖具有一定的吸附性,对有害微生物和有机物质具有一定的净化能力,起到净化居住环境的作用。
具体实施方式
本发明非限定实施例如下:
一种含茶皂素的泡沫砖,由下列重量(kg)的组分原料制备而成:
废玻璃45,硅灰石粉8,轻质碳酸钙15,氯化钙8,茶皂素3,椰子油脂肪酸二乙醇酰胺1.5,辛烯基琥珀酸淀粉钠0.8,阿拉伯胶1.5,六偏磷酸钠3,硅酸铝纤维1.5,硼砂1.5,复合填料12,水50;
其中,复合填料由下列重量(kg)的原料制成:
麦饭石粉12,高岭土12,糯米粉8,竹炭粉8,维生素C磷酸酯镁1.5,水杨酸钠1.5,羟丙基二淀粉磷酸酯0.8,酒石酸钾钠3,聚丙烯酸钠0.8,麦芽糖醇1.5;
复合填料的制备方法:
将麦饭石粉、高岭土、酒石酸钾钠和麦芽糖醇混合后研磨均匀,200℃处理1h,用水反复洗涤后加入糯米粉、竹炭粉和适量水80℃搅拌0.5h,冷却至常温,加入其余原料继续搅拌15min,干燥后研磨均匀,过400目筛,即得。
含茶皂素的泡沫砖的制备方法包括以下步骤:
(1)将废玻璃、硅灰石粉、轻质碳酸钙和氯化钙混合后200℃处理2h,加入六偏磷酸钠、硅酸铝纤维、硼砂和复合填料混合均匀,研磨后过150目筛,再加入1/2量的水,200r/min搅拌1h,得A组分;
(2)将辛烯基琥珀酸淀粉钠和阿拉伯胶加入余量的水中, 80℃搅拌10min,冷却后加入椰子油脂肪酸二乙醇酰胺和茶皂素搅拌5min后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,先150℃烘干1h,再于马弗炉中800℃烧结2h,冷却后即得。
经检验,本实施例的泡沫砖导热系数:0.032W/(m·K),抗压强度:3.9Mpa。
Claims (2)
1.一种含茶皂素的泡沫砖,其特征在于,其是由下述重量份的原料制得:
废玻璃40-50,硅灰石粉5-10,轻质碳酸钙10-20,氯化钙5-10,茶皂素2-4,椰子油脂肪酸二乙醇酰胺1-2,辛烯基琥珀酸淀粉钠0.5-1,阿拉伯胶1-2,六偏磷酸钠2-4,硅酸铝纤维1-2,硼砂1-2,复合填料10-15,水40-60;
所述复合填料由下列重量份的原料制成:
麦饭石粉10-15,高岭土10-15,糯米粉5-10,竹炭粉5-10,维生素C磷酸酯镁1-2,水杨酸钠1-2,羟丙基二淀粉磷酸酯0.5-1,酒石酸钾钠2-4,聚丙烯酸钠0.5-1,麦芽糖醇1-2;
所述复合填料的制备方法是:
将麦饭石粉、高岭土、酒石酸钾钠和麦芽糖醇混合后研磨均匀,200-300℃处理1-2h,用水反复洗涤后加入糯米粉、竹炭粉和适量水60-80℃搅拌0.5-1h,冷却至常温,加入其余原料继续搅拌10-15min,干燥后研磨均匀,过400-600目筛,即得。
2.根据权利要求1所述的一种含茶皂素的泡沫砖的制备方法,其特征在于,包括以下步骤:
(1)将废玻璃、硅灰石粉、轻质碳酸钙和氯化钙混合后200-300℃处理1-2h,加入六偏磷酸钠、硅酸铝纤维、硼砂和复合填料混合均匀,研磨后过100-150目筛,再加入1/3-1/2量的水,200-400r/min搅拌0.5-1h,得A组分;
(2)将辛烯基琥珀酸淀粉钠和阿拉伯胶加入余量的水中,60-80℃搅拌10-20min,冷却后加入椰子油脂肪酸二乙醇酰胺和茶皂素搅拌5-10min后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,先100-150℃烘干1-2h,再于马弗炉中600-800℃烧结2-4h,冷却后即得。