CN104370571A - 一种啤酒工业废料生产的泡沫砖及其制备方法 - Google Patents
一种啤酒工业废料生产的泡沫砖及其制备方法 Download PDFInfo
- Publication number
- CN104370571A CN104370571A CN201410580547.3A CN201410580547A CN104370571A CN 104370571 A CN104370571 A CN 104370571A CN 201410580547 A CN201410580547 A CN 201410580547A CN 104370571 A CN104370571 A CN 104370571A
- Authority
- CN
- China
- Prior art keywords
- parts
- foamed brick
- add
- beer
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种啤酒工业废料生产的泡沫砖,其特征是由下述重量份的原料制得:废玻璃60-70,啤酒废泥20-30,啤酒糟10-20,生石灰5-10,乳酸钙1-2,椰油基羟乙基磺酸钠2-4,汉生胶1-2,偏硅酸钠0.5-1,三聚磷酸钠2-4,单硬脂酸甘油酯0.5-1,油酰基甲基牛磺酸钠0.2-0.4,聚乙烯醇0.5-1,改性助剂2-4,水50-60。本发明的泡沫砖回收利用了啤酒厂废料,既具有良好的外观和性能,又能缓解啤酒厂污染问题,节能环保,降低成本,具有较高的环境和经济效益。
Description
技术领域
本发明涉及建筑材料领域,具体涉及一种啤酒工业废料生产的泡沫砖及其制备方法。
背景技术
泡沫砖属于加气混凝土砌块的一种,通过采用发泡剂通过发泡机物理制泡后,再将气泡加入料浆中混合,浇注,最后制得带有内部气孔的泡沫砖。泡沫砖主要用于非承重墙,具有成本低、轻质、保温隔热效果好等特点,已被广泛应用于工业与民用建筑中,是一种具有良好性能的墙体材料。
玻璃材料是人们日常生活所需、不可缺少的材料。玻璃的大量使用也导致日常生产生活中不可避免地产生大量的废玻璃垃圾。废玻璃的化学性质稳定,既给人们的生产和生活带来了不便,又对环境产生了污染,并且废玻璃的安置占用了大量土地资源。因此,回收利用废玻璃,使废玻璃资源化成为环保节能的一个重要课题。利用废玻璃生产泡沫砖是一种合理利用废玻璃的途径。
啤酒整个生产过程中主要废弃物有啤酒糟和废泥等,随着啤酒工业的发展,啤酒产量大幅度增加,而啤酒酿造所产生的大量副产品及废弃物如果没有很好地被利用,将造成资源的巨大浪费和对周围环境的严重污染。利用啤酒废料制作泡沫砖,既能缓解啤酒厂污染问题,又节约了资源,降低了生产成本。
发明内容
本发明的目的是提供一种啤酒工业废料生产的泡沫砖。
本发明是通过以下技术方案实现的:
一种啤酒工业废料生产的泡沫砖,其特征在于,其是由下述重量份的原料制得:
废玻璃60-70,啤酒废泥20-30,啤酒糟10-20,生石灰5-10,乳酸钙1-2,椰油基羟乙基磺酸钠2-4,汉生胶1-2,偏硅酸钠0.5-1,三聚磷酸钠2-4,单硬脂酸甘油酯0.5-1,油酰基甲基牛磺酸钠0.2-0.4,聚乙烯醇0.5-1,改性助剂2-4,水50-60;
所述改性助剂由下列重量份的原料制成:
纳米氧化锌2-4,纳米二氧化钛3-5,纳米二氧化硅2-4,三乙醇胺2-4,山梨醇1-2,聚乙二醇1-2,没食子酸0.1-0.2,单宁酸0.5-1,异丙醇1-2,硅烷偶联剂KH-550 0.1-0.2;
所述改性助剂的制备方法是:
将纳米氧化锌、纳米二氧化钛和纳米二氧化硅加入适量乙醇后超声分散,再加入硅烷偶联剂KH-550,600-800r/min搅拌10-15min,最后加入其余原料同样条件下搅拌0.5-1h,过滤后将滤饼真空干燥,即得。
所述的啤酒工业废料生产的泡沫砖的制备方法,其特征在于,包括以下步骤:
(1)将啤酒废泥、啤酒糟和生石灰混合后搅拌6-12h,用自来水清洗后干燥至恒重,再加入废玻璃400-600℃处理2-4h,冷却后加入偏硅酸钠、三聚磷酸钠、乳酸钙和改性助剂研磨均匀,过100-150目筛,再加入1/3-1/2量的水,200-400r/min搅拌0.5-1h,得A组分;
(2)将单硬脂酸甘油酯、汉生胶和聚乙烯醇加入余量的水中,80-90℃、800-1000r/min搅拌10-20min,再加入椰油基羟乙基磺酸钠和油酰基甲基牛磺酸钠同样条件下搅拌5-10min,冷却后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,60-80℃保温过夜后150-180℃处理1-2h,再于马弗炉中600-700℃烧结3-6h,冷却后即得。
本发明的优点是:
1. 回收利用啤酒废料制作泡沫砖,既能缓解啤酒厂污染问题,又节约了资源,节能环保,降低了生产成本,具有较高的环境和经济效益;
2. 通过添加复合纳米改性助剂,使泡沫砖具有抗菌防霉性,并且提高了产品的耐磨性、机械强度和抗老化性能等指标,改善产品的光泽度和外观质量,延长使用寿命。
具体实施方式
本发明非限定实施例如下:
一种啤酒工业废料生产的泡沫砖,由下列重量(kg)的组分原料制备而成:
废玻璃65,啤酒废泥25,啤酒糟15,生石灰8,乳酸钙1.5,椰油基羟乙基磺酸钠3,汉生胶1.5,偏硅酸钠0.8,三聚磷酸钠3,单硬脂酸甘油酯0.8,油酰基甲基牛磺酸钠0.3,聚乙烯醇0.8,改性助剂3,水55;
其中,改性助剂由下列重量(kg)的原料制成:
纳米氧化锌3,纳米二氧化钛4,纳米二氧化硅3,三乙醇胺3,山梨醇1.5,聚乙二醇1.5,没食子酸0.15,单宁酸0.8,异丙醇1.5,硅烷偶联剂KH-550 0.15;
改性助剂的制备方法:
将纳米氧化锌、纳米二氧化钛和纳米二氧化硅加入适量乙醇后超声分散,再加入硅烷偶联剂KH-550,800r/min搅拌15min,最后加入其余原料同样条件下搅拌0.5h,过滤后将滤饼真空干燥,即得。
啤酒工业废料生产的泡沫砖的制备方法包括以下步骤:
(1)将啤酒废泥、啤酒糟和生石灰混合后搅拌10h,用自来水清洗后干燥至恒重,再加入废玻璃600℃处理2h,冷却后加入偏硅酸钠、三聚磷酸钠、乳酸钙和改性助剂研磨均匀,过150目筛,再加入1/2量的水, 400r/min搅拌0.5h,得A组分;
(2)将单硬脂酸甘油酯、汉生胶和聚乙烯醇加入余量的水中,90℃、1000r/min搅拌10min,再加入椰油基羟乙基磺酸钠和油酰基甲基牛磺酸钠同样条件下搅拌5min,冷却后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,80℃保温过夜后160℃处理1h,再于马弗炉中650℃烧结4h,冷却后即得。
经检验,本实施例的泡沫砖导热系数:0.041W/(m·K),抗压强度:4.5Mpa。
Claims (2)
1.一种啤酒工业废料生产的泡沫砖,其特征在于,其是由下述重量份的原料制得:
废玻璃60-70,啤酒废泥20-30,啤酒糟10-20,生石灰5-10,乳酸钙1-2,椰油基羟乙基磺酸钠2-4,汉生胶1-2,偏硅酸钠0.5-1,三聚磷酸钠2-4,单硬脂酸甘油酯0.5-1,油酰基甲基牛磺酸钠0.2-0.4,聚乙烯醇0.5-1,改性助剂2-4,水50-60;
所述改性助剂由下列重量份的原料制成:
纳米氧化锌2-4,纳米二氧化钛3-5,纳米二氧化硅2-4,三乙醇胺2-4,山梨醇1-2,聚乙二醇1-2,没食子酸0.1-0.2,单宁酸0.5-1,异丙醇1-2,硅烷偶联剂KH-550 0.1-0.2;
所述改性助剂的制备方法是:
将纳米氧化锌、纳米二氧化钛和纳米二氧化硅加入适量乙醇后超声分散,再加入硅烷偶联剂KH-550,600-800r/min搅拌10-15min,最后加入其余原料同样条件下搅拌0.5-1h,过滤后将滤饼真空干燥,即得。
2.根据权利要求1所述的一种啤酒工业废料生产的泡沫砖的制备方法,其特征在于,包括以下步骤:
(1)将啤酒废泥、啤酒糟和生石灰混合后搅拌6-12h,用自来水清洗后干燥至恒重,再加入废玻璃400-600℃处理2-4h,冷却后加入偏硅酸钠、三聚磷酸钠、乳酸钙和改性助剂研磨均匀,过100-150目筛,再加入1/3-1/2量的水,200-400r/min搅拌0.5-1h,得A组分;
(2)将单硬脂酸甘油酯、汉生胶和聚乙烯醇加入余量的水中,80-90℃、800-1000r/min搅拌10-20min,再加入椰油基羟乙基磺酸钠和油酰基甲基牛磺酸钠同样条件下搅拌5-10min,冷却后加入高速打泡机制得泡沫,得B组分;
(3)将A组分与B组分混合后搅拌均匀,加入模具固化成型,60-80℃保温过夜后150-180℃处理1-2h,再于马弗炉中600-700℃烧结3-6h,冷却后即得。